• Proceedings of the Korea Concrete Institute Conference
• /
• 1997.04a
• /
• pp.598-604
• /
• 1997

In recent years, strengthening by epoxy-bonded steel plates, carbon fiber sheets, aramid fiber sheets and so on, is spotlighted. Among them, the method using steel plates is most widely applied. Most studies have dealt with strengthening by epoxy-bonded steel plates. However the actual behavior of strengthened RC beams are not well established. Particularly, the studies on the separation load thar affects failure load of the beam are relatively insufficient. In this study, test parameters are the magnitude of pre-load, plate length, plate thickness, existence and spacing of anchor bolt, the number of plate layer and the height of side strengthening, 17reinforced concrete beams are strengthened by steel plates according to test parameters. Deflection, failure load, strains of reinforcing bar, concrete and plate are measured from tests(4 points loading). The failure mode, and separation load are analyzed from these measured data. The difference between Robert's theory and test results is discussed, and the prediction equation for separation load in the case of rip off is proposed.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1996.03a
• /
• pp.73-80
• /
• 1996

Commerical purity aluminium , copper and STS 304 stainless steel sheets are welded by ultrasonic welding. The microstructures, x-ray diffraction profiles of planes , pole figures of the surface of original metal sheets are compared with those of the weld interface. The microstructures show disturbance and dark areas in the weld interface and grain refinement in the vicinity of the interface. The x-ray diffraction intensity of each plane in weld interface decreased in all metal sheets with exception of 9200) in steel sheet. The microstructure and x-ray diffraction intensity is affected by the mixture of deformation, heating and vibratin duringthe ultrasonic welding. Therefore, after the ultrasonic welding, the positions of the peak intensity in the pole figures are changed, the value of the maximum pole intensity is decreased in Al, is increased in copper and stainless steel. Very strong {100} <001> texture, strong {100} <001>,{123}<634> textures in original Al surface are transformed into weak, {100}<001>, {110}<112> and {112}<111> components in weld surface, weak (110) fiber is slightly changed to (110) fiber in copper, (100)and ${\gamma}$ fiber components are transformed into strong ${\gamma}$ fiber component in stainless steel.

• Steel and Composite Structures
• /
• v.33 no.5
• /
• pp.729-746
• /
• 2019

The nonlinear behavior of single- and multi-story steel plate shear walls (SPSWs) strengthened with three different patterns of fiber reinforced polymer (FRP) laminates (including single-strip, multi-strip and fully FRP-strengthened models) is studied using the finite element analysis. In the research, the effects of orientation, width, thickness and type (glass or carbon) of FRP sheets as well as the system aspect ratio and height are investigated. Results show that, despite an increase in the system strength using FRP sheets, ductility of reinforced SPSWs is decreased due to the delay in the initiation of yielding in the infill wall, while their initial stiffness does not change significantly. The content/type/reinforcement pattern of FRPs does affect the nonlinear behavior characteristics and also the mode and pattern of failure. In the case of multi-strip and fully FRP-strengthened models, the use of FPR sheets almost along the direction of the infill wall tension fields can maximize the effectiveness of reinforcement. In the case of single-strip pattern, the effectiveness of reinforcement is decreased for larger aspect ratios. Moreover, a relatively simplified and approximate theoretical procedure for estimating the strength of SPSWs reinforced with different patterns of FRP laminates is presented and compared with the analytical results.

• Journal of Welding and Joining
• /
• v.34 no.4
• /
• pp.40-47
• /
• 2016

The Zn coating on automotive galvanized steel sheets can improve corrosion resistance. However, the boiling temperature of Zn is lower than the melting temperature of steel and it causes well-known spatter and porosity problem. One of most prominent solutions is a pretreatment of Zn coating by an additional welding arc prior to the main welding process. In this research, GTA and GMA are selected as heat sources for pretreatment and main welding processes, respectively. The authors suggested three possible mechanisms to reduce weld defects by the GTA pretreatment: (1) Formation of gap between the sheets; (2) Evaporation of Zn layer; (3) Oxidation of Zn layer. Among them, Zn Oxidation is the most important mechanism to reduce weld defects in the GTA-GMA hybrid process.

• Corrosion Science and Technology
• /
• v.23 no.4
• /
• pp.296-301
• /
• 2024

Steels have excellent mechanical properties and weldability. They are also economically producible. Thus, they are widely applied in various industries. However, they have a disadvantage in that rust can occur after a certain period of time. To compensate for this, Zn, which has excellent sacrificial corrosion resistance, can be coated on steels. With global zinc consumption increasing at the current rate, depletion is expected in the near future. Recently, POSCO has developed innovative Al-Zn-Si alloy coated steel sheets with better corrosion resistance than Zn coating. In this study, corrosion resistance, weldability, friction characteristics, and so on were evaluated compared to GI steel sheets to evaluate their applicability to automotive steel sheets. It showed excellent corrosion resistance even at a lower coating weight compared to GI steel sheet. It was also excellent in terms of galling and welding LME. Its spot welding life, electrodeposition coating, and bendability were equally excellent. This is presumed to be related to the formation of the Al-Zn-Si alloy phase at the interface of the coating layer.

• Corrosion Science and Technology
• /
• v.19 no.2
• /
• pp.57-65
• /
• 2020

As competition among global automakers intensifies, demand for materials that are better in price and performance is increasing. While steel and plastic materials compete for automotive fuel tanks, plastic materials have advantages such as light weight for automobiles. However, they have high prices. Accordingly, in this paper, four types of Zn-X plated steel sheets, electroplating (X = none, Sn) and galvannealed (X = Fe, Fe-Mg), were manufactured and their applicability as a fuel tank material was evaluated. Nano-composite coating solution with good conductivity was treated on the surface of plated steels using a roll coater and then cured through induction furnace to improve corrosion resistance. Quality characteristics such as corrosion resistance, fuel resistance to diverse gasoline and diesel fuels, and seam weldability were evaluated for the above plated steels. Their properties were compared and analyzed with conventional Zn-Ni electroplating steels. Among the above plated steels, Zn-Fe-Mg galvannealed steels coated with nano-composite coating exhibited better properties than other steels. Detailed experimental results suggest that evenly distributed Mg elements on the coating layer play a key role in the enhanced quality performance.

• Steel and Composite Structures
• /
• v.20 no.4
• /
• pp.833-849
• /
• 2016

Pre-stressing of existing structures using steel cables, FRP cables or FRP laminates has been successfully tried in the past. Retrofitting of beams using pre-stressed laminates does not utilize the full strength of the FRP due to de-bonding of the laminates before the fibre fracture. In the present study attempt has been made to overcome this problem by replacing the FRP laminates by the FRP sheets. In the present paper the effect of initial damage level and pre-stress level on strength, stiffness, cracking behaviour and failure mode of girders retrofitted using pre-stressed CFRP sheets has been studied. The results indicate that rehabilitation of initially damaged girders by bonding pre-stressed CFRP sheets improves the flexural behaviour of beams appreciably. However, it has been observed that with increase in pre-stressing force the load carrying capacity of the girders increases up to a particular level up to which the mode of failure is fibre fracture. Thereafter, the mode of failure shifts from fibre fracture to de-bonding and there is no appreciable increase in load carrying capacity with further increase in pre-stressing force.

• The Transactions of the Korean Institute of Electrical Engineers P
• /
• v.58 no.2
• /
• pp.190-195
• /
• 2009

Thin-gauged 3% silicon steel sheets having a highly grain-oriented texture have been developed as a core material for applications of middle-frequency (400 Hz ${\sim}$ 10 kHz) devices. The newly developed sheets with a tension coating showed an excellent reduction in iron loss at 400 Hz (iron loss at 1.0 T and 400 Hz = 4.677 W/kg, iron loss at 1.5 T and 400 Hz = 9.742 W/kg) due to high magnetic induction, $B_{10}$(measured induction at 1000 A/m), of over 1.9 T. In cases of frequencies below 400 Hz, magnetic induction, $B_{10}$, of the sample plays a major role to reduce its iron loss as excitation induction increases, whereas, in case of frequency of 1 kHz, thickness dependence becomes dominant due to a lower iron loss at relatively thinner sample. The sheets with a high magnetic induction, therefore, are favorable for high excitation induction (over 1.0 T) and low excitation frequency (below 400 Hz) applications, whereas the sheets that can reduce eddy current loss by reducing thickness or domain wall width are advantageous for low excitation induction (below 1.0 T) and high excitation frequency (around 1 kHz) applications.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2005.10a
• /
• pp.220-226
• /
• 2005

To achieve the weight reduction of a vehicle, Magnesium alloys are widely used in automobile parts because of its lightweight characteristics. Magnesium alloys also have advantages in recycling, stiffness, NVH , heat protection. But Magnesium alloy parts are mainly manufactured by diecasting processes, their productivity was not so high compared to by sheet metal working. We are developing vehicle hood using magnesium sheets. In this study we designed magnesium alloy hood which have equivalent mechanical characteristics to steel hood. Using finite element method we decided thickness of magnesium sheets under some design requirements and we changed the shape of hood inner panel and hinge reinforcements. Outer and inner panel thickness was 1.3mm, 1.5mm respectively. Panel dentibility analysis was performed to conform the new magnesium design by nonlinear FEM package. Formability and hemming of Magnesium sheets are the subjects for further study because they have poor stretchability compared to steel sheets.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1996.04a
• /
• pp.176-180
• /
• 1996

Continuous wave CO$_{2}$laser beam welding and formability of zinc coated steel shets were investigated. First, optimal welding condition could be obtained in but welding by using the data for heat input and welding velocity. The highest value of Erichsen test is 79.3% compare to that of base matel. Secondly, Formability of laser welds was investigated by using ball punch tester. Finally, the forming results of butt-welded sheets showed that the joing design was important to apply the laser welded blank in the automotive production.