• Journal of Advanced Marine Engineering and Technology
• /
• 제25권5호
• /
• pp.1108-1114
• /
• 2001

The fatigue crack propagation behavior of the SA516-Grade 70 steel which is used for pressure vessels was experimentally examined under the condition of at room temperature, $150^{\circ}C$, $250^{\circ}C$ and $370^{\circ}C$ with stress ration of R=0.1 and 0.3. The fatigue crack propagation rate , da/dN, related with the stress intensity factor range, $\vartriangle$N, was influenced by the stress ration within the stable growth of fatigue crack(Region II) with an increase in $\vartriangle$N. The resistance to the fatigue crack growth at high temperature is higher in comparison with that at room temperature, and the resistance attributed to the extent of plasticity-induced by compressive residual stress according to the cyclic loads. Fractographic examinations revels that the differences of the fatigue crack growth characteristics between room and high temperatures are mainly explained by the crack and oxide-induced by high temperature.

• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2000년도 추계학술대회 논문집
• /
• pp.147-153
• /
• 2000

The fatigue crack propagation behavior of the SA516/70 steel which is used for pressure vessels was examined experimentally at room temperature, $150^{\circ}C$, $250^{\circ}C$ and $370^{\circ}C$ with stress ratio of R=0.1 and 0.3. The fatigue crack propagation rate da/dN related with the stress intensity factor range $\Omega\textrm{K}$ was influenced by the stress ratio within the stable growth of fatigue crack(Region II) with an increase in $\Omega\textrm{K}$. The resistance to the fatigue crack growth at high temperature is higher in comparison with that at room temperature, and the resistance attributed to the extent of plasticity-induced by compressive residual stress according to the cyclic loads. Fractographic examinations reveal that the differences of the fatigue crack growth characteristics between room and high temperatures are mainly explained by the crack closure and oxide-induced by high temperature.

• 한국해양공학회지
• /
• 제15권2호
• /
• pp.105-110
• /
• 2001

The fatigue crack propagation behavior of the SA516/70 steel which is used for pressure vessels was examined experimentally at room temperature, 150$^{\circ}C $, 250$^{\circ}C $ and 370$^{\circ}C $ with stress ratio of R=0.1 and 0.3. The fatigue crack propagation rate da/dN related with the stress intensity factor range $\Delta K$ was influenced by the stress ratio within the stable growth of fatigue crack(Region II) with an increase in $\Delta K$. The resistance to the fatigue crack growth at high temperature is higher in comparison with that at room temperature, and the resistance attributed to the extent of plasticity-induced by compressive residual stress according to the cyclic loads. Fractographic examinations reveal that the differences of the fatigue crack growth characteristics between room and high temperature are mainly explained by the crack closure and oxide-induced by high temperature.

• 비파괴검사학회지
• /
• 제18권4호
• /
• pp.278-291
• /
• 1998

연속섬유강화 복합재료의 경우 보강섬유의 파괴, 모재의 파괴, 섬유와 모재의 분리, 층간파괴 등의 복합적인 파괴현상이 동반되고 특히 균열성장과 균열성장 정지가 균열가교 현상 때문에 반복되므로 안정성장과 불안정성장이 불규칙하게 반복된다. 따라서 주균열 성장의 개시점과 불안정 파괴점에서의 파괴인성치를 정확하게 결정한다는 것은 매우 어려운 것이다. 본 연구에서는 CFRP에 대하여 파괴인성 실험과 병행하여 실시간으로 결함을 검출하는 새로운 방법인 AE분석법 및 비디오 마이크로 스코프를 이용하여 파괴과정을 기록하여 검토, 분석함으로서 손상의 정도와 파괴기구를 규명하였을 뿐만 아니라 주균열 성장의 개시점, 균열가교 역할을 하는 섬유다발의 파단점, 균열의 불안정 파괴 개시점을 찾아 이를 기초로 균열진전 저항곡선에 의한 파괴인성치를 평가하여 신뢰성 있는 파괴인성 측정법을 제시하였다.

• Journal of Advanced Marine Engineering and Technology
• /
• 제29권8호
• /
• pp.855-861
• /
• 2005

Fracture toughness defined near the initiation of stable crack growth is investigated by R-curve and Direct Current electric Potential Determination(DCPD) under mode I plane strain conditions for CT specimen with 25.4mm thickness of SS400 steel. Fracture toughness. $J_{IC}$lit near crack tip of CT specimen by R-curve is 17.14 $kg_{f}/mm$ and however. its value by DCPD is 22.82 $Rg_{f} mm$ The value of fracture toughness by DCPD is larger than that by R-curve. Therefore, it is suggested that the evaluation of fracture toughness by R-curve is optimum than by DCPD, when considering amount of crack growth about each of fracture toughness.

• 대한기계학회논문집
• /
• 제12권5호
• /
• pp.1097-1103
• /
• 1988

본 연구에서는 이 좁은 벤트내에 자료가 모이는 피로균열의 특성을 이용하여 표면피로균열의 성장거동을 파괴역학적으로 해석, 연구하여 균열의 성장특성과 $S-N_{f}$ 곡선의 추정을 마이크로 컴퓨터로 계산하였다.

• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2003년도 추계학술대회 논문집
• /
• pp.138-144
• /
• 2003

Rencentely, the request for the light weight is more incresed in the area of industrial environment and machinery and consistent effort is needed to accomplish high strength of material for the direction of light weight. we got the following characteristic from crack growth test carried out in the range of stress ration of 0.1, 0.3 and 0.6 by means of opening mode displacement. At the content stress ratio, the threshold stress intensity factor crack range ${\Delta}K_{th}$in the early stage of fatigue crack growth (Region I) and dtress intensity factor range ${\Delta}K$ in the stable of fatigue crack growth (Region II) with an increase in ${\Delta}K$. Fatigue life shows more improvement in the Shot-peened material than in the Un-peening material. And compressive residual stress of surface on the Shot peening processed operate resistance force of fatigue. So we can obtain fallowings. (1) The fatigue crack growth rate on stage II is conspicuous with the size of compressive residual stress and is depend on Paris equation. (2) Although the maxium compressive residual stress is deeply and widely formed from surface, fatigue life does not improve than when maxium compressive residual stress is formed in surface. (3) The threshold stress intensity factor range is increased with increasing compressive residual stress.

• 대한기계학회논문집
• /
• 제13권6호
• /
• pp.1183-1192
• /
• 1989

본 논문에서는 평면변형률 상태하에서 안정하게 성장하는 균열선단에 집중 되어있는 강소성역의 해석에 역점을 두어 재결정법과 탄.소성유한요소법을 도입하여 안정 성장균열 선단에 형성되는 균열 성장저항에 직접적인 영향을 미치고 있는 소성 역의 크기나 형태에 대한 실험 및 해석을 하였다.

• 대한기계학회논문집A
• /
• 제26권5호
• /
• pp.828-834
• /
• 2002

In this paper, for the mixed mode fatigue problem, the method of determining testing load was proposed. It is based on the plastic zone size and the limited maximum stress intensity factor by ASTM STANDARD E 647-00. The application method of maximum tangential stress criterion and the stress intensity factor for the finite width specimen was proposed. In the result of applying the method to mixed mode fat gut test for A5052 H34, it obtained the satisfactory experimental results on the stable crack growth.

• Nuclear Engineering and Technology
• /
• 제49권4호
• /
• pp.752-759
• /
• 2017

The fatigue crack growth behavior of Type 347 (S347) and Type 347N (S347N) stainless steel was evaluated under the operating conditions of a pressurized water reactor (PWR). These two materials showed different fatigue crack growth rates (FCGRs) according to the changes in dissolved oxygen content and frequency. Under the simulated PWR conditions for normal operation, the FCGR of S347N was lower than that of S347 and insensitive to the changes in PWR water conditions. The higher yield strength and better corrosion resistance of the nitrogen-alloyed Type 347 stainless steel might be a main cause of slower FCGR and more stable properties against changes in environmental conditions.