We have used acetic acids ethanol and distilled water as a solvent to synthesize $La_{2/3}Sr_{1/3}Mn_{0.99}{^{57}}Fe_{0.01}O_3$(LSMFO) precursor. Crack-free LSMFO granular polycrystalline thin films have been deposited on thermally oxidized silicon substrates by spin coaling. The dependence of crystallization, surface morphology, magnetic and transport properties on annealing temperature was investigated. With increasing annealing temperature, the metal-semiconductor (insulator) transition temperature and the magnetic moment decrease while the resistivity increases. The lattice constants remain almost unchanged. For LSMFO thin films, spin-dependent interfacial tunneling and/or scattering magnetoresistance were observed. Our results indicate that the annealing temperature is very important in determining the intrinsic and extrinsic magnetotransport properties.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.6
• /
• pp.504-510
• /
• 2002

Recently, thin film capacitors of high dielectric constant and low leakage current are applied to integrated devices. In this study, (Ba, Sr)$TiO_3$ (BST) thin films for low cost were prepared by Sol-Gel method. BST solution was spin-coated on Pt/$SiO_2$/Si substrate at 4,000 rpm for 10 seconds. Coating process was repeated 3 times and then sintered at $700^{\circ}C$ for 30 minutes. Structural and electrical characteristics of each specimen were analyzed by TG-DTA, SEM, fractal phenomenon, voltage-current and dielectric factor. Thickness of BST ceramics thin films are about 2,600~2,800 ${\AA}$ at depositing 3 times. Dielectric constant of thin films was decreased in 1 kHz~1 MHz. Dielectric constant and loss to frequency were 250 and 0.02 in $(Ba_{0.7}Sr_{0.3})TiO_3$ (BST3). Leakage current of BST3 was $10^{-9}\sim10^{-11}$/ A under 3 V.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.9
• /
• pp.1001-1005
• /
• 2004

Rye-sensitized solar cell (DSSC) is a new class of solar cell, which consists of nanoporous TiO$_2$ electrode, dye-sensitizer, electrolyte, and counter electrode. Such cell is operated in sunlight via the principle of photosynthetic electrochemistry. In order to obtain the good dispersion of nano size TiO$_2$ particles In slurry, the pH of solvent, the sort and quantify of solvent additive and the quantity of surfactant were adjusted. As results, the lower the pH of solvent was the lower the viscosity of the slurry became. The addition of ethylene glycol and propylene glycol to dilute HNO$_3$ brought about the lowering of viscosity and the enhancement of stability in slurry. The addition of surfactant lowered the viscosity of slurry. It was possible to obtain the homogeneous and uniformly dispersed mesoporous TiO$_2$ film using the dilute HNO$_3$ solvent of pH 2 with the addition of ethylene glycol and neutral surfactant. DSSC was assembled with TiO$_2$ electrode and Pt electrode, and its photoelectric property was measured using the monochromatic wavelength in the rangee of 350∼700 nm.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.11
• /
• pp.1014-1019
• /
• 2006

The influence of the number of solution coatings on the densification of the PZT thick films was studied. PZT powder and PZT precursor solution was prepared by a sol-gel method and PZT thick films were fabricated by the screen-printing method on the alumina substrates. The powder and solution of composition were (A) PZT(80/20)/PZT(20/80), (B) PZT(70/30)/PZT(30/70) and (C) PZT(60/40)/PZT(40/60), (D) PZT(52/48)/PT. The coating and drying procedure was repeated 4 times. And then the PZT precursor solution was spin-coated on the PZT thick films. A concentration of a coating solution was 0.5 moth and the number of coating was repeated from 0 to 6. The porosity of the thick films was decreased with increasing the number of coatings and the PZT thick films with 6-times coated showed the dense microstructure and thickness of about $60{\mu}m$. A grain size was increased with increasing the coating number. All PZT thick films showed the typical XRD patterns of a typical perovskite polycrystalline structure. The relative dielectric constant of PZT thick films was improved 30-100% as the number of coatings.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.109-112
• /
• 1999

The PZT(10/90)/(90/17) heterolayered thin films were fabricated by the spin-coaling on the Pt/Ti/SiO$_2$/Si substrate using the PZT(10/90) and PZT(70/10) metal alkoxide solutions. The effect of heterolayered thin films on the ferroelectrics and electrical properties have been investigated. The lower PZT layers provided the nucleation site for the formation of a perovskite phase of the upper PZT films. Dielectric constant increased with increasing the number of coatings, and it was about 569.9 at PZT-6 heterolayered films.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.11
• /
• pp.922-927
• /
• 2001

Single-layer green ELs was fabricated with using molecularly-dispersed Bu-PBD into poly-N-vinylcarbazole(PVK) which has low operating voltage and high quantum efficiency. A EL cell structure of glass substrate/indium-tin-oxide/PVK:Bu-PBD:C6(∼ 100nm)/Ca(20nm)/Al(20nm) was employed with variable doping concentration. The keys to obtain high quantum efficiency was excellent film forming capability of molecularly dispersed into PVK and appropriate combination of cathode for avoiding exciplex. We obtained the turn-on voltage of 4.2V and quantum efficiency of 0.52% at 0.lmol% of C6 concentration which has been improved about a factor of 50 in comparison with the undoped cell. The PL peak wavelengths wouldn\`t be turned by changing the concentration of the C6 dopant. Green EL emission peak and FWHM were 520nm and 70nm respectively. PL emission peak was obtained at 495nm.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.12
• /
• pp.1092-1098
• /
• 2006

The influence of the concentration of precursor solution and the number of solution coatings on the densification of the $Pb(Zr_xTi_{1-x})O_3$ (PZT) thick films was studied. PZT powder and PZT precursor solution were prepared by3 sol-gel method and PZT thick films were fabricated by the screen-printing method on the alumina substrates. The composition of powder and precursor solution were PZT(70/30) and PZT(30/70), respectively. The PZT precursor solution was spin-coated on the PZT thick films. A concentration of a coating solution was 0.5 to 2.0 mol/L[M] and the number of coating was repeated from 0 to 6. The XRD patterns of all PZT thick films shelved typical perovskite polycrystalline structure. The porosity of the thick films was decreased with increasing the number of coatings and 6-time coated films with 1.5 M showed the dense microstructure and thickness of about $60{\mu}m$. The relative dielectric constant of the PZT thick film was increased with increasing the number of solution coatings and the thick films with 1.5 M, 6-time coated showed the 698. The remanent polarization the 1.5 M and 6-time coated PZT thick films was $38.3{\mu}C/cm^2$.

• Transactions of the Korean Society for Noise and Vibration Engineering
• /
• v.15 no.9 s.102
• /
• pp.1077-1083
• /
• 2005

Electro-Active Paper (EAPap) is one of attractive electro-active polymer (EAP) materials for artificial muscles due to its many advantages such as light weight, biologically degradable, low cost, large displacement output, low actuation voltage and low power consumption. However, drawbacks of EAPap actuators include low force output and humidity dependence. To enhance the performance of EAPap, conductive polymer (PPy) and SWNT/conductive polymer (PANI) are coated on EAPap PPy as conductive polymer is coated on cellulose EAPap by means of electrochemical deposition. Two different dopants are used in PPy through conducting polymer processing. SWNTS are mixed with PANI in emeraldine base along with different dopants. The compound materials are coated on cellulose EAPap using spin coating system. The performance of PPy/EAPap and SWNT/PANI/EAPap are evaluated in terms of bending displacement, blocked force, and the effects of dopants, humidity, coaling time, voltage and frequency are investigated. Comparing with EAPap actuators, SWNT/PANI/EAPap actuators show $200\%$ improvement of bending displacement and $300\%$ increment of blocked force.