• 한국재료학회지
• /
• 제15권7호
• /
• pp.473-479
• /
• 2005

Thermoelectric $Zn_4Sb_3$ alloys were synthesized by a conventional powder metallurgy process consisting of solid state reaction and hot pressing. Single phase $Zn_4Sb_3$ was successfully produced by the annealing of cold compact starting with the mixed elemental powders, and subsequent hot pressing yielded single phase bulk specimens without microcracks. Phase transformations in this alloy system during synthesis were investigated using XRD, SEM and EDS. Thermoelectric properties as a function of temperature were investigated from room temperature to 600 K and compared with results of analogue studies. Transport properties at room temperature were also evaluated. Thermoelectric properties of single phase $Zn_4Sb_3$ materials produced by this process are comparable to the published data. Synthesis by solid state reaction and hot pressing offers a potential processing route to produce a bulk $Zn_4Sb_3$.ٓ

• 한국재료학회지
• /
• 제27권12호
• /
• pp.710-715
• /
• 2017

We synthesized YOF(yttirum oxyfluoride) powders through solid state reactions using $Y_2O_3$ and $YF_3$ as raw materials. The synthesis of crystalline YOF was started at $300^{\circ}C$ and completed at $500^{\circ}C$. The atmosphere during synthesis had a negligible effect on the synthesis of the YOF powder under the investigated temperature range. The particle size distribution of the YOF was nearly identical to that of the mixed $Y_2O_3$ and $YF_3$ powders. When the synthesized YOF powders were used as a raw material for the suspension plasma spray(SPS) coating, the crystalline phases of the coated layer consisted of YOF and $Y_2O_3$, indicating that oxidation or evaporation of YOF powders occurred during the coating process. Based on thermogravimetric analysis, the crystalline formation appeared to be affected by the evaporation of fluoride because of the high vapor pressure of the YOF material.

• Transactions on Electrical and Electronic Materials
• /
• 제13권5호
• /
• pp.225-228
• /
• 2012

In order to synthesize LED phosphor materials, we have applied three novel synthesis techniques, "melt synthesis", "fluidized bed synthesis" and "vapor-solid hybrid synthesis", in contrast with the conventional solid state reaction technique. These synthesis techniques are also a general and powerful tool for rapid screening and improvements of new phosphor materials.

• 한국분말재료학회지
• /
• 제29권6호
• /
• pp.485-491
• /
• 2022

Lithium lanthanum titanium oxide (LLTO) is a promising ceramic electrolyte because of its high ionic conductivity at room temperature, low electrical conductivity, and outstanding physical properties. Several routes for the synthesis of bulk LLTO are known, in particular, solid-state synthesis and sol-gel method. However, the extremely low ionic conductivity of LLTO at grain boundaries is one of the major problems for practical applications. To diminish the grain boundary effect, the structure of LLTO is tuned to nanoscale morphology with structures of different dimensionalities (0D spheres, and 1D tubes and wires); this strategy has great potential to enhance the ion conduction by intensifying Li diffusion and minimizing the grain boundary resistance. Therefore, in this work, 0D spherical LLTO is synthesized using ultrasonic spray pyrolysis (USP). The USP method primarily yields spherical particles from the droplets generated by ultrasonic waves passed through several heating zones. LLTO is synthesized using USP, and the effects of each precursor and their mechanisms as well as synthesis parameters are analyzed and discussed to optimize the synthesis. The phase structure of the obtained materials is analyzed using X-ray diffraction, and their morphology and particle size are analyzed using field-emission scanning electron microscopy.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2009년도 춘계학술대회 논문집
• /
• pp.134-137
• /
• 2009

Commercially available elemental powders of Cu, Zn, Sn and Se were employed for crystallizing a stannite-type $Cu_2ZnSnSe_4$ compound by means of solid state reaction. $Cu_2ZnSnSe_4$ reaction chemistry was also modeled based on differential-thermal analysis and X-ray powder diffraction results. It was observed that Se tends to react preferably with Cu to form CuSe and $CuSe_2$ phases at low reaction temperature. The formation of $Cu_5Zn_8$ intermetallic phase was found to be the intermediate reaction path for the binary ZnSe formation. A solid state reaction at $320^{\circ}C$ reacted elemental powderst obinary selenides of CuSe, ZnSe and SnSe completely. The crystallization of $Cu_2ZnSnSe_4$ was was detected to begin at $300^{\circ}C$ and its weight fraction increased with an increase of reaction temperature, which most probably formed from the reaction between $Cu_2SnSe_3$ and ZnSe.

• 에너지공학
• /
• 제20권2호
• /
• pp.103-108
• /
• 2011

다중음이온 양극활물질인 $Li_2MnSiO_4$/C을 액상법과 고상법으로 각각 합성한 후 탄소로 그 표면을 코팅하여 구조 및 전기화학적인 특성을 비교하였다. XRD 측정에서 $Li_2MnSiO_4$/C의 피크를 잘 나타내었으나 고상법에서 제조한 시편의 경우 약간의 불순물이 있음을 확인하였다. FE-SEM, HR-TEM 측정을 통해 액상법에 의한 시편은 수십 나노 크기의 입자로 구성된 반면 고상법에 의한 것은 500~600 nm로 합성된 것을 확인 하였다. 전기화학적 측정에서는 액상법으로 합성한 $Li_2MnSiO_4$/C가 고상법으로 한 것 보다 우수한 특성을 모습을 보였는데, 액상법에 의한 시료의 초기 충전 용량은 235 mAh/g, 초기 방전 용량은 189 mAh/g을 각각 나타 내어 고상법에 의한 시료 보다 나은 초기 충방전 용량을 나타냈다. 그러나 사이클 특성은 저조하였으며 10사이클 후에 62%의 용량 잔존율을 보였다.

• 한국표면공학회지
• /
• 제56권4호
• /
• pp.259-264
• /
• 2023

As the demand for lithium-ion batteries, a key power source in electric vehicles and energy storage systems, continues to increase for achieving global carbon neutrality, there is a growing concern about the environmental impact of disposing of spent batteries. Extensive research is underway to develop efficient recycling methods. While hydrometallurgy and pyrometallurgy methods are commonly used to recover valuable metals from spent cathode materials, they have drawbacks including hazardous waste and complex processes. Hence, alternative recycling methods that are environmentally friendly are being explored. However, recycling spent cathode materials still remains complex and energy-intensive. This study focuses on a novel approach called solid-state synthesis, which aims at regenerating the performance of spent cathode materials. The method offers a simpler process and reduces energy consumption. Optimal heat treatment conditions were identified based on experimental results, contributing to the development of sustainable recycling technologies for lithium-ion batteries.

• 공업화학
• /
• 제10권5호
• /
• pp.772-777
• /
• 1999

$Y_2Ba_1Cu_1O_5(Y211)$ 분말은 출발물질로서 $Y_2O_3(99.9%)$, $BaCO_3(99.9%)$, and CuO(99.9%) 분말을 사용하여 고상반응법과 발화합성법을 이용하여 제조하였다. $Y_2Ba_1Cu_1O_5(Y211)$ 분말에 대한 상형성과 반응속도는 열처리 온도와 반응시간에 따른 시료들을 X-선 회절분석을 이용하여 연구하였다. X-선 회절선으로부터 측정된 전화율($X_{211}$)과 반응특성으로부터 상 형성속도가 분말의 입자크기에 의해 지배되는 것을 알 수 있었다. 그리고 발화합성법으로 제조된 Y211상의 활성화에너지(${\Delta}E_a$)는 고상반응법에 의해 제조된 것의 149.46 kJ/mol과 비교할 때 136.42 kJ/mol을 나타내었다. $Y_2Ba_1Cu_1O_5$계에서의 활성화에너지 값은 발화합성법이 고상반응법보다 더욱 효율적인 방법임을 보였다.

• 한국세라믹학회지
• /
• 제46권2호
• /
• pp.170-174
• /
• 2009

$BaTiO_3$ powder was synthesized by the solid-state reaction of fine $BaTiO_3$ and $TiO_2$ raw materials. Fine grinding media of 50 and 300 microns were used for obtaining fine particulate mixture of $BaTiO_3$ and $TiO_2$ with high homogeneity. Effect of the size of grinding media on the synthesis mechanism of $BaTiO_3$ was discussed on the basis of the particulate morphology and thermogravimetry data for the mixture powders. By using the finer grinding media, $BaTiO_3$ was formed at the lower temperature and the particle size with the relatively narrower distribution could be obtained. $BaTiO_3$ powder with the average size of 100 nm was synthesized by the solid reaction in vacuum atmosphere.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2003년도 추계학술발표강연 및 논문개요집
• /
• pp.93-93
• /
• 2003

Tungsten and tungsten heavy alloys have widespread application as radiation shielding devices and heavy duty electrical contacts. High density and good room temperature mechanical properties have generated interest in evaluating tungsten and tungsten alloys as kinetic energy penetrators against armor. Nowdays ultra fine-grained tungsten powders are in great interest because higly dense structures can be obtained at low temperature, pressure and lower sintering time. Several physical md chemical methods are available for the synthesis of nanometric metal Powders: ball milling, laser abalation, vapor condensation, chemical precipitation, metallic wire explosion i.e. However production rates of the above mentioned methods are low and further efforts are needed to find out large-scale synthesis methods. From this point of view solid state combustion method ( known as SHS) represents undoubted interest.