In the present study, an original spark plasma sintering-reactive synthesis (SPS-RS) method for minerallike ceramic materials based on SrAl₂Si₂O₈ feldspar-like skeleton structure was used for the first time, promising solid-state matrices for reliable immobilization of high-energy ⁹⁰Sr. The method is based on the "in-situ" reaction of a mixture of SrO, Al₂O₃ and SiO₂ oxides when heated by a unipolar pulsed current under compacting pressure. The phase and elemental composition structure were studied. The dynamics of the consolidation of the reaction mixture of oxides was studied in the range of 900-1200 ℃. The study found the temperature of the high-speed (minutes) SPS-RS formation of single-phase SrAl₂Si₂O₈ composition ceramic in the absence of intermediate reaction products with a relative density of up to 99.2% and compressive strength up to 145 MPa and a strontium leaching rate of 10^-4g/cm²·day.

• 한국결정성장학회지
• /
• 제24권4호
• /
• pp.176-182
• /
• 2014

상온 압축 성형 후 고상 반응 소결 공정을 통하여 $Mg_3Sb_2$ 소결체를 제조하고자 하였다. Mg과 Sb의 성분의 몰비와 반응온도에 따른 결정상의 변화를 조사하였다. 773~843 K에서 얻어진 고상반응 소결체들은 전형적인 $Mg_3Sb_2$ 결정상을 형성하였으나 소결체의 위치에 따라 약간 다른 상적 구성을 보였다. 소결체 하단 부위에서 전형적으로 얻어지는 결정상이 얻어졌으며 823 K 온도에서는 Mg : Sb = 3.15 : 1.85 조성일 때, 843 K 온도에서는 Mg의 몰 수가 3.10 이상인 모든 조성에서 ${\alpha}-Mg_3Sb_2$ 상과 정확히 일치하는 결정상이 얻어졌다. 미량 남아있는 Mg 성분은 응고 후 냉각 시 ${\alpha}-Mg_3Sb_2$ 상으로부터 석출된 것으로 보인다.

• 센서학회지
• /
• 제16권3호
• /
• pp.234-239
• /
• 2007

Crystallographically {h00}-oriented $0.94(Bi_{0.5}Na_{0.5})TiO_{3}-0.06BaTiO_{3}$ (0.94BNT-0.06BT) ceramics was prepared by the Reactive Templated Grain Growth (RTGG) method using the $Bi_{4}Ti_{3}O_{12}$ template. The sheets prepared by tape-casting of slurries containing the templates and starting materials are cut, laminated, and pressed. Then burn-out and sintering was conducted. Also, to compare with the 0.94BNT-0.06BT ceramics prepared by the RTGG method another 0.94BNT-0.06BT ceramics was prepared by the solid-state method. In the optimum of this experiments range, the degree of orientation of the 0.94BNT-0.06BT ceramics prepared by the RTGG method was texture fraction${\approx}92%$ and the piezoelectric constant($d_{33}$) and coupling factor($k_{p}$) was obtained to $d_{33}{\approx}205{\;}pC/N$, $k_{p}{\approx}0.33%$, respectively.