• Korean Journal of Materials Research
• /
• v.25 no.8
• /
• pp.423-428
• /
• 2015

Impedancemetric $NO_x$ (NO and $NO_2$) gas sensors were designed with a stacked-layer structure and fabricated using $LaCr_xCo_{1-x}O_3$ (x = 0, 0.2, 0.5, 0.8 and 1) as the receptor material and $Li_{1.3}Al_{0.3}Ti_{1.7}(PO_4)_3$ plates as the solid-electrolyte transducer material. The $LaCr_xCo_{1-x}O_3$ layers were prepared with a polymeric precursor method that used ethylene glycol as the solvent, acetyl acetone as the chelating agent, and polyvinylpyrrolidone as the polymer additive. The effects of the Co concentration on the structural, morphological, and $NO_x$ sensing properties of the $LaCr_xCo_{1-x}O_3$ powders were investigated with powder X-ray diffraction, field emission scanning electron microscopy, and its response to 20~250 ppm of $NO_x$ at $400^{\circ}C$ (for 1 kHz and 0.5 V), respectively. When the as-prepared precursors were calcined at $700^{\circ}C$, only a single phase was detected, which corresponded to a perovskite-type structure. The XRD results showed that as the Co concentration of the $LaCr_xCo_{1-x}O_3$powders increased, the crystal structure was transformed from an orthorhombic phase to a rhombohedral phase. Moreover, the $LaCr_xCo_{1-x}O_3$ powders with $0{\leq}x<0.8$ had a rhombohedral symmetry. The size of the particles in the $LaCr_xCo_{1-x}O_3$powders increased from 0.1 to $0.5{\mu}m$ as the Co concentration increased. The sensing performance of the stack-structured $LaCr_xCo_{1-x}O_3/Li_{1.3}Al_{0.3}Ti_{1.7}(PO_4)_3$ sensors was found to divide the impedance component between the resistance and capacitance. The response of these sensors to NO gas was more sensitive than that to $NO_2$ gas. Compared to other impedancemetric sensors, the $LaCr_{0.8}Co_{0.2}O_3/Li_{1.3}Al_{0.3}Ti_{1.7}(PO_4)_3$ sensor exhibited good reversibility and reliable sensingresponse properties for $NO_x$ gases.

• Journal of the Korean Ceramic Society
• /
• v.56 no.2
• /
• pp.197-204
• /
• 2019

An electrochemical oxygen permeating membrane (OPM) is fabricated using Zr_0.895Sc_0.095Ce_0.005Gd_0.005O_2-δ (ScCeGdZ) as the solid electrolyte and aLa_0.7Sr_0.3MnO₃-bScCeGdZ composite (LZab, electrode) as the electrode. The crystal phase of the electrode and the microstructure of the membrane is investigated with X-ray diffraction and scanning electron microscopy. The electrochemical resistance of the membrane is examined using 2-p ac impedance spectroscopy, and LZ55 shows the lowest electrode resistance among LZ82, LZ55 and LZ37. The oxygen permeation is studied with an oxygen permeation cell with a zirconia oxygen sensor. The oxygen flux of the OPM with LZ55 is nearly consistent with the theoretical value calculated from Faraday's Law below a critical current. However, it becomes saturated above the critical current due to the limit of the oxygen ionic conduction of the OPM. The OPM with LZ55 has a very high oxygen permeation flux of ~ 3.5 × 10^-6 mol/㎠s in I = 1.4 A/㎠.

• Nuclear Engineering and Technology
• /
• v.28 no.2
• /
• pp.118-128
• /
• 1996

The lattice parameters of stoichiometric $UO_2$ and $U_{1-y}Er_{y}O_2$ in the range of y=0.01 to y =0.33 were determined with use of X-ray diffraction data. Oxygen potentials have been measured by means of a thermogravimetric method in the range of 1200~$1500^{\circ}C$ and $10^{-14}$ $\leq$ $Po_2$ $\leq$ $10^{-3}$ for pure $UO_2$ and $U_{1-y}Er_{y}O_{2{\pm}x}$ solid solutions with y=0.02, y=0.06 and y=0.20, respectively. Their oxygen partial pressures were maintained by controlling $CO_2$/CO mixture atmosphere, and the $Po_2$ values corresponding to x of $U_{1-y}Er_{y}O_{2{\pm}x}$ solid solutions were measured with an electrolyte oxygen sensor. The lattice parameter decreases linearly with an increase in the erbium content. The change of the lattice parameter can be expressed in a linear equation of y as a($\AA$) =5.4695-0.220y for 0 $\leq$y$\leq$0.33. The experimental coefficient of y -0.220 in $U_{1-y}Er_{y}O_2$ was an intermediate value between the calculated values -0.273 and -0.156 in the case of $U^{5+}$ and $U^{6+}$, respectively. The (equation omitted) has been found to undergo abrupt increase in the range of -360 to -270 kJ/mole for y=0.06 and -320 to -220 H/mole for y=0.20, respectively, in the temperature range of 1200-$1500^{\circ}C$. (equation omitted) increases with erbium content, but the effect of the dopant for x =0.01 is less significant than that for stoichiometry. The oxygen potentials for $UO_2$ and $U_{0.98}Er_{0.02}O_{2+x}$ can be approximately represented by the $U^{5+}$/$U^{4+}$ model but those for y$\geq$ 0.06 in $U_{1-y}Er_{y}O_{2{\pm}x}$ solid solutions cannot be interpreted by the mean uranium valence model.