• Journal of the Korean Ceramic Society
• /
• v.29 no.10
• /
• pp.773-778
• /
• 1992

The effect of temperature on the structural changes of petroleum raw coke during calcination was studied and then the properties of carbon solids prepared from those calcined coke using binder were examined. The notable structural change of raw coke was observed in the range from 800$^{\circ}C$ to 900$^{\circ}C$ from the results of volatile matter, porosity, X-ray diffraction and scanning electron microscopy. The bending strength, density of the carbon solid carbonized at 1400$^{\circ}C$ was 400 kg/$\textrm{cm}^2$ and 1.40g/㎤, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.581-584
• /
• 2001

For the first time, a totally solid state electric double layer capacitor has been fabricated using an alkaline polymer electrolyte and an activated carbon powder as electrode material. The polymer electrolyte serves both as separator as well as electrode binder. The capacitor has a three-layer structure; electrode-electrolyte-electrode. A cyclic voltammetry and constant current discharge have been used for the determination of the electro chemical performance of capacitors.

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2003.11a
• /
• pp.202-206
• /
• 2003

In this study, a modified bituminization technology has been developed, which needs no grinding of the granular resin waste, and enables the solid form to keep its shape stability as good as that of a cemented solid from Also, the study intended to apply the developed technology to the practical treatment of radioactive resin waste. In the experiment, the granular type resin was used and the straight-run distillation bitumen with penetration rate 60/70 was used as the solidifying agent. The PE was used as the additive. The shape stability increased remarkably with the additive of PE, which act as a binder in the solid form. The shape of the solid form was maintained without failure during the long-term exposure test when the additive content of spent PE is more than 10wt%. The proper ranges of bitumen content, PE content and operating temperature are 30-50wt%, 10-20wt% and $180^{\circ}C$ respectively. The bituminized solid form of radioactive resin waste by the technology of this study has the remarkably superior quality than the conventional solid forms, partially for the shape stability.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2011.11a
• /
• pp.420-421
• /
• 2011

In this study, Instead of using urethane curative systems, which have long been used as solid propellants, a triazole curative system has been introduced into a new binder recipe in which azide groups in the polymer react with triple bonds of a dipolarophile curative.

• Journal of the Korean Ceramic Society
• /
• v.37 no.7
• /
• pp.721-725
• /
• 2000

In this study, the dispersion stability of nano-sized CeO2 particles, synthesized by hydrothermal method in aqueous was evaluated from observing the surface potential behavior of CeO2 particle synthesized by solid state reaction. The isoelectric point(IEP) of nano-sized CeO2 synthesized by hydrothermal synthesis was found to be pH 9 contrary to the isoelectric point of micro-sized CeO2 synthesized by solid state reaction at pH 6.7. IEP was shifted to pH 2.0 as the addition of D-3019 from 0.1 to 1.0 wt%. The surface potential of CeO2 particles synthesized by hydrothermal synthesis was reduced as the addition of B-1001 used as a binder without change of IEP because the absorption of B-1001 polymer on the CeO2 particles shifted the shear plane of CeO2 particles outward away from the surface. This surface potential behavior was well correlated with the dispersion stability of slurry.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1996.04b
• /
• pp.35-40
• /
• 1996

Friction and wear behavior of MoS$_{2}$ bonded films were evaluated at a Block-on-Ring typed tribo-tester, and their properties were compared with those of Falex tester in terms of the wear life of the films. Test results showed that friction and wear properties were significantly affected by the test methods of different contact configuration, and the wear life at a Block-on-Ring type tribo-tester was mostly governed by the resin binder. To obtain long wear life of the films, various combinations of solid-resin-content ratio and chemical resin modification were attempted and evaluated. Adhesion properties of resin binders were also measured and compared by using a scratch tester.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.2 no.3
• /
• pp.247-254
• /
• 2014

The present study prepared lightweight foam-soil concrete mixtures classified into three groups. Considering the sustainablility, workability, and compressive strength development of such concrete, high-volume supplementary cementitious materials (SCMs) were used as follows: 20% cement, 15% fly ash, and 65% ground granulated blast-furnace slag. As main test parameters selected for achieving the compressive strength of 1MPa and dry density of $1,000kg/m^3$, the unit solid content (dredged soil and binder) ranged between 900 and $1,807kg/m^3$, and soil-to-binder ratio varied between 3.0 and 7.0. Test results revealed that the flow of the lightweight foam-soil concrete tended to decrease with the increase of unit soil content. The compressive strength of such concrete increased with the increase with the unit binder content, whereas it decreased as soil-to-binder ratio increased, indicating that the compressive strength can be formulated as a function of its dry density and soil-to-binder ratio.

• Journal of Technologic Dentistry
• /
• v.34 no.2
• /
• pp.113-119
• /
• 2012

Purpose: Zirconia blocks for all ceramic dentures are divided into two groups. One is pre-heated block and the other is binder added block. In this study, the possibility of recycling the remained parts of binder added block after CAD/CAM machining with slip casting process was investigated. Methods: Owing to the binder added block contain large amount of organic matter, Binder burn-out was must be carried out before ball milling for preparing the casting slip. Binder burn-out was accomplished at $600^{\circ}C$ for 10 hours. Ball milling was performed with 5mm zirconia ball and 60mm polyethylene bottle. From 0% to 5% at 1% intervals of alumina was added to zirconia powder for preparing slip. Solid casting was achieved with plaster mold. Cast bodies were dried and sintered at $1,500^{\circ}C$ for 1 hour. Linear shrinkage, apparent porosity, water absorption, bulk density, and flexural strength were tested. Microstructures were observed by SEM, EDS and XRD analysis were executed. Results: Optimum slips for casting was prepared with 300g ball, 100g powder, and 180g distilled water. Cast body without alumina showed 26% of linear shrinkage, 6.07 of apparent density, and 470MPa of three point bend strength. On the other hand, as received zirconia block, which was sintered at the same conditions, showed 23% of linear shrinkage, 6.10 of apparent density, and 680MPa of three point bend strength. When 3% of alumina was added to zirconia, sintered body showed 23% of linear shrinkage, 6.10 of apparent density, and 780MPa of three point bend strength. SEM photomicrographs and EDS analysis showed alumina particles uniformly dispersed in zirconia matrix, and XRD analysis showed no phase transformation of tetragonal zirconia particles was occurred when alumina was added. Conclusion: According to the all of this experimental results, 3% of alumina added cast zirconia body showed excellent mechanical properties more than as received binder containing zirconia block.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2004.10a
• /
• pp.1128-1131
• /
• 2004

SFF(solid freeform fabrication) is another name of RP(rapid prototyping). The SFFS for office type wishes to develop system that can produce small object such as hand phone, cup, accessory etc. with high speed, and also intend suitable system in office environment by compact design, and buy easily by inexpensive price. As can manufacture high speed in existent SFF process technology, representative process that have competitive power in price is 3DP (three dimensional printing) technology. The 3DP technology is way to have general two dimensional printing technology and prints to three dimension, is technology that make three-dimensional solid freeform that want binder doing jetting selectively on powder through printer head. We designed and manufactured SFFS for office based on 3DP process technology design and manufactured, and composed head system so that use 3 printer heads at the same time to improve the fabrication speed of system. We used printer head of INCJET company and cartridge used HP45 series model who can buy easily in general city. And we directly fabricated three dimensional solid freeform using developed SFFS for office type.

• Journal of Powder Materials
• /
• v.24 no.3
• /
• pp.223-228
• /
• 2017

Nanopowders provide better details for micro features and surface finish in powder injection molding processes. However, the small size of such powders induces processing challenges, such as low solid loading, high feedstock viscosity, difficulty in debinding, and distinctive sintering behavior. Therefore, the optimization of process conditions for nanopowder injection molding is essential, and it should be carefully performed. In this study, the powder injection molding process for Fe nanopowder has been optimized. The feedstock has been formulated using commercially available Fe nanopowder and a wax-based binder system. The optimal solid loading has been determined from the critical solid loading, measured by a torque rheometer. The homogeneously mixed feedstock is injected as a cylindrical green body, and solvent and thermal debinding conditions are determined by observing the weight change of the sample. The influence of the sintering temperature and holding time on the density has also been investigated. Thereafter, the Vickers hardness and grain size of the sintered samples have been measured to optimize the sintering conditions.