• 한국세라믹학회지
• /
• 제31권5호
• /
• pp.499-504
• /
• 1994

PbTiO3 thin films were prepared by sol-gel spin coating method using metal alkoxide and diethanolamine (DEA). The precipitation of the PbTiO3 sol occurred at pH 7.3 with HNO3 addition, regardless of the amount of DEA. The gelation time of the PbTiO3 sol was reduced with increasing amount of HNO3 and/or water. When the PbTiO3 films prepared by 0.2 molar coating solution were annealed at $650^{\circ}C$ for 30 min, dense and single phase perovskite films were obtained. Dielectric constant and loss tangent of the film were 239 and 0.01 at 1 kHz, respectively.

• Korean Chemical Engineering Research
• /
• 제43권6호
• /
• pp.740-744
• /
• 2005

$La(NO_3)_3{\cdot}xH_2O$, $Sr(NO_3)_2$, $Co(NO_3)_2{\cdot}6H_2O$, $Fe(NO_3)_3{\cdot}9H_2O$를 출발물질로 하고 La와 Sr의 몰비를 변화시켜 perovskite형 산화물인 $La_{1-x}Sr_xCo_{1-y}Fe_yO_{3-{\delta}}$ 졸을 제조하였다. 또한, 여러 조건에서 합성된 졸의 특성을 확인하기 위해 viscometer, FT-IR, TG-DTA, XRD 등을 사용하여 분석을 행하였다. 제조된 perovskite형 산화물 졸은 1.16 cp의 평균점도를 나타내었으며 조성에 관계없이 pH 0.5 정도의 강산성을 나타내었다. 용액 중의 La 함량이 많아질수록 동일 부피에서의 용액의 점도가 낮았고, 점도가 급격하게 증가하는 겔화시간이 증가하였다.

• Korean Chemical Engineering Research
• /
• 제54권6호
• /
• pp.767-774
• /
• 2016

졸-겔법에 의해 출발물질로 aluminum isopropoxide를 사용하여, 메탄올용매 내에서 가수분해 시킨 후 해교제인 초산, 질산 또는 염산을 각각 첨가하여 해교 시켜 3종류의 alumina sol을 제조하였다. 또한 이 sol에 실란커플링제인(3-glycidyloxypropyl) trimethoxysilane을 첨가하여 코팅 용액을 제조한 후, 이용액을 polycarbonate 기재 위에 담금 코팅 후 열 경화시켜 코팅 도막을 형성하였다. 이 과정 중 해교제의 종류 변화가 코팅 도막의 물성에 미치는 영향을 연구하였다. 그 결과 해교제로서 강산인 염산이나 질산을 사용한 코팅 도막은 H나 2H의 연필경도와 5B의 부착력을 나타내어 우수한 물성을 나타내었다. 반면에 해교제로서 약산인 초산을 사용한 경우에는 HB의 연필경도와 3B의 부착력을 보여 좋지 못한 물성을 나타내었다.

• 접착 및 계면
• /
• 제18권1호
• /
• pp.13-24
• /
• 2017

본 연구에서는 50 wt%의 매우 높은 담지량과 70%의 높은 고형분을 가지면서도 물속이나 다양한 제품에 나노 입자 형태로 분산이 가능한 새로운 형태의 소수성 항균 물질 담지 나노 입자를 제조하였다. 실란 기능화 양친성 고분자 전구체(Alkoxysilane-functionalized Amphiphilic Polymer Precursor; 이하 AAPP)와 다양한 실란 화합물을 이용하여 전형적인 Hydrolytic Sol-Gel 공정으로 제조된 수분산 유-무기 하이브리드 나노 입자들을 제조하고, 이를 이용하여서 나노 침전법을 사용하여서 소수성 항균물질을 고함량으로 담지할 수 있는 새로운 공정으로 소수성 항균물질인 Eugenol이 담지된 유-무기 하이브리드 형태의 나노입자 제조하였다. 나노 입자 제조시 제조 조건의 변화에 따른 나노 입자들의 크기, 담지량, 항균 활성 및 방출거동 등에 영향을 미치는 인자들을 조사하였다. 나노 입자의 종류에 관계없이 Minimal Inhibitory Concentration (MIC)는 50 mg/ml로 동일하였고, 모든 균주에서 99 %에 해당하는 우수한 항균력과 Pseudomonas aeruginosa (PSE)를 제외하고는 2주 이상의 항균 지속력을 나타내었다. 특히, Tetraethoxysilane (TEOS)를 첨가한 경우에는 견고한 무기물 도메인으로 인해 가장 높은 담지량 (50 wt.%)과 서방출 (Sustained release)을 나타내었고, Hexanediol (HD)을 첨가한 경우에는 HD 자체의 항균력과 용매로서의 역할도 하였기 때문에 가장 높은 항균력과 70%의 고형분을 나타내었다.

• 폴리머
• /
• 제24권1호
• /
• pp.8-15
• /
• 2000

본 연구에서는 초임계 이산화탄소를 반응 연속상으로 하여 졸-에멀젼-겔 방법에 의한 신합성 공정을 통해 1-6 $\mu\textrm{m}$의 평균 입자 크기를 갖는 페놀릭/퍼퍼랄(phenolic/furfural, P/F) 겔 입자를 성공적으로 제조하였다. 이때 초임계 이산화탄소에 잘 녹는 폴리디메틸실록산(poly-(dimethylsiloxane), PDMS)은 초임계 이산화탄소내에서 P/F 용액을 분산시키는 효과적인 안정제로 사용되었다. 입자 크기와 입자 크기 분포에 미치는 영향을 알아보기 위하여 고형분과 안정제 함량비를 변화시켜 실험한 결과, P/F 입자의 평균 입자 크기는 고형분의 함량비가 증가함에 따라 증가했으나, 안정제의 함량비에 따른 변화는 크지 않았다. 또한 P/F 겔 입자의 구조 및 열 안정성은 IR 분석과 TGA를 통해 확인하였다.

• 한국재료학회지
• /
• 제24권11호
• /
• pp.599-603
• /
• 2014

$NaLa_{1-x}(MoO_4)_2:Eu^{3+}/Yb^3$ phosphors with doping concentrations of $Eu^{3+}$ and $Yb^{3+}$ ($x= Eu^{3+}+Yb^{3+}$, $Eu^{3+}=0.05$, 0.1, 0.2 and $Yb^{3+}= 0.2$, 0.45) were successfully synthesized by the microwave-modified sol-gel method, and the upconversion and spectroscopic properties were investigated. Well-crystallized particles showed a fine and homogeneous morphology with particle sizes of $2-5{\mu}m$. Under excitation at 980 nm, $NaLa_{0.5}(MoO_4)_2:Eu_{0.05}Yb_{0.45}$ particles exhibited a strong 525-nm emission band and a weak 550-nm emission band in the green region, and a very weak 665-nm emission band in the red region. The strong 525-nm emission in the green region corresponds to the $^7F_1{\rightarrow}^5D_1$ transition and the weak 550-nm emission in the green region corresponds to the $^7F_0{\rightarrow}^5D_2$ transition, while the very weak emission 665-nm band in the red region corresponds to the $^5D_0{\rightarrow}^7F_3$ transition. The Raman spectra of the doped particles indicated the domination of strong peaks at higher frequencies of 762, 890, 1358 and $1430cm^{-1}$ and weak peaks at lower frequencies of 323, 388 and $450cm^{-1}$ induced by the disorder of the $[MoO4]^{2-}$ groups with the incorporation of the $Eu^{3+}$ and $Yb^{3+}$ elements into the crystal lattice or by a new phase formation.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 하계학술대회 논문집
• /
• pp.80-80
• /
• 2009

Recently, multiferroics have attracted much attention due to their numorous potentials. In this work, we attemped to utilize the multiferroics as an alternative material for ferroelectrics. Ferroelectric materials have been stadied to ferroelectric random access memories, however, some inevitable problems prevent it from inplementation. multiferroics shows a ferroelectricity and has low process temperature $BiFeO_3$(BFO) films have good ferroelectric properties but poor leakage characterization. Thus we tried, in this work, to adopt $HfO_2$ insulating layer for metal-ferroelectric-insulator-semiconductor(MFMIS) structure to surpress to leakage current. $BiFeO_3$(BFO) thin films were fabricared by using a sol-gel method on $HfO_2/Si$ structure. Ferroelectric BFO films on a p-type Si(100)wafer with a $HfO_2$ buffer layer have been fabricated to form a metal-ferroelectric-insulator-semiconductor (MFIS) structure. The $HfO_2$ insulator were deposited by using a sol-gel method. Then, they were carried out a rapid thermal annealing(RTA) furnace at $750\;^{\circ}C$ for 10 min in $N_2$. BFO films on the $HfO_2/Si$ structures were deposited by sol-gel method and they were crystallized rapid thermal annealing in $N_2$ atomsphere at $550\;^{\circ}C$ for 5 min. They were characterized by atomic force microscopy(AFM) and Capacitance-voltage(C-V) curve.

• E2M - 전기 전자와 첨단 소재
• /
• 제9권3호
• /
• pp.251-258
• /
• 1996

Sol-Gel derived ferroelectric Pb(Z $r_{0.52}$ $Ti_{0.48}$) $O_{3}$ thin films have been fabricated on Pt/Ti/ $SiO_{2}$/Si substrate. Two kinds of fast annealing methods, F-I (six times of intermediate and final annealing) and F-II(one final annealing after six times of intermediate annealing) were used for preparation of multi-coated PZT thin films. As the annealing temperature was increased, high capacitance could be obtained, for instance, 2700.angs.-thick PZT thin film annealed at 680.deg. C had a capacitance value of approximately 20nF at 1kHz. In addition, it is found that the dielectric constant is a function of the perovskite phase fraction. In case of F-I method, PZT thin film had a remanent polarization(Pr) of 8-15.mu.C/c $m^{2}$ and a coercive field( $E_{c}$) of 35-44kV/cm according to annealing temperature, whereas PZT film fabricated by F-II method had as high as 24-25.mu.C/c $m^{2}$ and 48-59kV/cm, respectively. As a result of measuring Curie temperature, PZT thin film had a range of 460-480.deg. C by F-I method and more or less higher range of 525-530.deg. C by F-II method, which implied that different microstructures could cause the different Curie temperature. Through I-V measurement, leakage current of PZT thin film fabricated by F-I and F-II methods was 64nA/c $m^{2}$ and 2.2.mu.A/c $m^{2}$ in the electric field of 100kV/cm, respectively.y.y.y.

• Bulletin of the Korean Chemical Society
• /
• 제28권12호
• /
• pp.2288-2292
• /
• 2007

The catalytic activities of nickel-based catalysts were estimated for oxidizing acetaldehyde of VOCs exhausted from industrial facilities. The catalysts were prepared by sol-gel methods of SiO2 and SiO2-TiO2 as a xerogel followed by impregnating Al2O3 powder with the nickel nitrate precursor. The crystalline structure and catalytic properties for the catalysts were investigated by use of BET surface area, X-ray diffraction (XRD), Xray photoelectron spectroscopy (XPS) and temperature programmed reduction (TPR) techniques. These results show that nickel oxide is transformed to NiAl2O4 spinel structure at the calcination temperature of 400 °C in response to the steps with after- and co-impregnation of Al2O3 powder in sol-gel process. The NiAl2O4 could suppress the oxidation reaction of acetaldehyde by catalysts. The NiO is better dispersed on SiO2-TiO2/Al2O3 support than SiO2/Al2O3 and SiO2-TiO2-Al2O3 supports. From the testing results of catalytic activities for oxidation of acetaldehyde, Catalysts showed a big difference in conversion efficiencies with the way of the preparation of catalysts and the loading weight of nickel. The catalyst of 8 wt.% Ni/TiO2-SiO2/Al2O3 showed the best conversion efficiency on acetaldehyde oxidation with 100% conversion efficiency at 350 °C.

• Korean Chemical Engineering Research
• /
• 제56권3호
• /
• pp.327-334
• /
• 2018

출발물질로서 테트라에톡시실란(TEOS)과 메틸트리메톡시실란(MTMS)을 사용하여 졸-겔법에 의해 발수성 코팅용액을 제조하였다. 이 용액을 냉연강판 위에 스핀 코팅하고 열처리하여 비불소계 발수 코팅 도막을 제조 하였다. 이 과정 중 MTMS/TEOS의 몰 비, 물 농도 및 암모니아 농도가 코팅 도막의 발수성에 미치는 영향을 연구하였다. MTMS/TEOS의 몰 비를 1~20으로 변화시켜 제조 한 코팅 도막의 접촉각은 MTMS/TEOS 몰 비가 10 일 때 최대 수치인 $108^{\circ}$를 나타내었다. 반면에 물의 첨가량을 증가시킴에 따라 코팅 도막의 접촉각이 증가하여 발수성이 향상되었다. 또한 암모니아의 첨가량이 커질수록실리카입자의 크기가커져 실리카입자의표면 거칠기가증가하므로 발수성이 증가하였다.