• The Korean Journal of Ceramics
• /
• v.3 no.4
• /
• pp.249-252
• /
• 1997

Highly oriented ZnO thin films were fabricated by dip-coating technique using zinc acetate 2-methoxyethanol 2-aminoethanol solution as starting materials, and effects of substrates on the film's orientation were investigated. Product films were obtained by prefiring at 300, 400, 500 and 550℃ for 10 min, followed by final heat-treatment at the same temperatures as prefiring for 1h. c-axis oriented films on glass substrates were prepared by heat treatment of prefiring films at 300-550℃, while films on alumina showed polycrystalline structure. Films with c-axis orientation exhibited lower specific resistivities than those of polycrystalline films with partial crack and pore.

• Journal of the Korean Ceramic Society
• /
• v.47 no.6
• /
• pp.633-637
• /
• 2010

In this study, lithium manganese oxide spinel ($LiMn_{1.9}Fe_{0.1}Nb_{0.0005}O_4$) as a cathode material of lithium ion secondary batteries is synthesized with spray drying, and in order to increase its crystallinity and electrochemical properties, the granulated $LiMn_{1.9}Fe_{0.1}Nb_{0.0005}O_4$ particle surface is coated with lithium titanium oxide spinel ($Li_4Ti_5O_{12}$) through a sol-gel method. The granulated particles present a higher tap density and lower specific surface area. The crystallinity and discharge capacity of the $Li_4Ti_5O_{12}$ coated material is relatively higher than uncoated material. With the coating layer, the discharge capacity and cycling stability are increased and the capacity fading is suppressed successfully.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1097-1098
• /
• 2006

The Powder characteristics and sintering behavior of $SiO_2$ coated $BaTiO_3$ were studied. Silica coated $BaTiO_3$ powders were prepared by sol-gel method. The particle size of the $BaTiO_3$ powders were $\sim35$ nm and the thickness of the $SiO_2$ coating layer was $\sim5$ nm. As the $SiO_2$ content increased, the $SiO_2$ layers improved the powder dispersion. The Zeta potential of $SiO_2$ coated $BaTiO_3$ was getting close to that of pure silica with a more negative charge, compared with that of the uncoated $BaTiO_3$. The onset temperature of shrinkage curves shifted to higher temperatures with increasing $SiO_2$ contents

• Journal of the Korean Ceramic Society
• /
• v.35 no.6
• /
• pp.610-618
• /
• 1998

Alumina were added to ceria based ceramic powders upto 9.7 vol% and composite powders were sprayed by plasma spraying process in order to improve the mechanical properties such as hardness fracture tough-ness and thermal shock resistance. The ceria based coating sprayed without alumina has the typical colum-nar and lamellar structure. Alumina addition has lowered the amount of columnar and lamellar sturcture Added alumina was segreagated in the grain boundary and grain of ceria based crystal accompanied with pore. The maximum value of density and the minimum value of porosity were observed at the sprayed coating with 4.8 vol% alumina. The hardness fracture toughness and thermal shock resistance were increased with alumina addition. The improvement of mechanical properties of plasma sparyed ceria based coatings result-ed from the disapperance of the columnar and lamellar sturcture by addition of alumina.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.551-552
• /
• 2007

Coating films were prepared from silane-terminated Colloidal silaca(CS) and UV-curable acrylate resin. The silane-terminated CSs were synthesized from CS and methyltrimethoxysilane(MTMS) and then treated with 3-methacryloxypropyltrimethoxysilane(MAPTMS)/3-glycidoxypropyltrimethoxysilane( GPTMS)/vinyltrimethoxysilane(VTMS) by sol-gel process, respectively. The silane-terminated CS and acrylate resin were hybridized using UV-curing system. Thin films of hybrid material were prepared using spin coater on the glass. Their hardness, contact angle and transmittance improved with the addition of silane-terminated CS.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2001.06a
• /
• pp.42-48
• /
• 2001

Chromium carbides have the excellent wear properties as transition metal carbides. Their tribological applications were studied recently. The nano-sized ceramic could enhance the mechanical and electronical properties of materials. In this study, it was observed to test the wear of the coated surface of nano-sized chromium carbides. The nano-sized chromium carbides were produced by sol-gel processing. Coating surface of produced powders was obtained front plasma spraying. Wear test of coating surface was held increasing temperature. The friction coefficient and the wear loss were testified in dry environment. And the worn surfaces were analyzed by XRD and SEM.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.05b
• /
• pp.42-45
• /
• 2001

The high permittivity are applied to DRAM and FRAM. (Ba,Sr)$TiO_3$ (EST) thin films were prepared by Sol-Gel method. BST solution was made and spin-coated on $Pt/SiO_2/Si$ substrate at 4000 [rpm] for 10 seconds in a time coating. Coated specimens were dried at $90[^{\circ}C]$ for 5 minutes. Coating process was repeated from 3 times to 5 times and then sintered at $750[^{\circ}C]$ for 30 minutes. Each specimen was analyzed structure and electrical characteristics. Thickness of BST ceramics thin films are about 2600-2800[$\AA$] in 3 times. Dielectric constant of thin films was little decreased at 1[KHz]~1[MHz]. Dielectric constant and loss to frequency were 250 and 0.02 in BST3. The property of leakage current was stable When the applied voltage was 0~3[V] Leakage current was $10^{9}\sim10^{11}$[A] at 0~3[V].

• Environmental Engineering Research
• /
• v.7 no.4
• /
• pp.227-237
• /
• 2002

Chemical vapor deposition (CVD), ion beam sputtering (IBS) and sol-gel method were used to prepare TiO$_2$ thin films for degradation of hazardous organic compounds exemplified by 2-chlorophenol (2-CP). The influence of supporting materials and coating methods on the photocatalytic activity of the TiO$_2$ thin films were also studied. TiO$_2$ thin films were coated onto various supporting materials including steel cloth (SS), copper cloth, quartz glass tube (QGT), and silica gel (SG). Results indicate that SS (37 μm)- TiO$_2$ thin film prepared by IBS method improves the photodegradation of 2-CP. Among all supporting materials studied, SS(37 μm) is found to be the best support.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.40 no.9
• /
• pp.631-637
• /
• 2003

We have evaluated structural and electric, ferroelectric properties of PZT(30/70) thick film prepared by using 1,3-propanediol based sol-gel method on Pt/Ti/SiO$_2$/Si substrates. Rapid thermal annealing (RTA) is used to reduce the thermal stress and final furnace annealing is processed at $650^{\circ}C$. As the results of SEM analysis, we find that we get 350 nm in thickness for one coating and 1 $\mu$m for three times of coating. In the results of C-D analysis at 1 kHz, dielectric constant ($\varepsilon$$_{r}$) and dissipation factor were 886 and 0.03, respectively. C-V curve is shaped as a symmetrical butterfly. Leakage current density at 200 kV/cm is 1.23${\times}$10$^{-5}$ A/cm$^2$ and in the results of hysteresis loops measured at 150 kV/cm, the remnant polarization (P$_{r}$) and the coercive field (E$_{c}$) are 33.8 $\mu$C/cm$^2$ and 56.9 kV/cm, respectively. PZT(30/70) thick film exhibits relatively good ferroelectric, electric properties.s..

• Journal of Sensor Science and Technology
• /
• v.10 no.2
• /
• pp.101-107
• /
• 2001

A highly selective, sensitive and reliable ozone sensing $In_2O_3$ thin film was fabricated by a sol-gel method. The fabricated film is operated at a relatively lower temperature than ever developed thin films and saved operating power. $In_2O_3$ films deposited by sol-gel technique has been recently attracted because it is an economical and energy saving method and precisely controlled microstructure. Indium alkoxide precursor was synthesized from the reaction between indium hydroxide and butanol. PVA binder was used to improve adhesion of the films. The $In_2O_3$ thin films were obtained by spin coating from 1 to 5 times followed by drying at $100^{\circ}C$ and calcining at $600^{\circ}C$ for 1h. The film thickness was controlled by the number of coating time. The morphology and the thickness of the $In_2O_3$ films were examined by a SEM and XRD. The $In_2O_3$ thin films show a high sensitive to ozone gas at operating temperature of $250^{\circ}C$. The $In_2O_3$ sensor has very good selectivity to $CH_4$, CO, $C_4H_{10}$ and ethanol.