• Journal of the Korean Ceramic Society
• /
• v.41 no.9
• /
• pp.642-646
• /
• 2004

Na$_2$Si$_2$O$_{5}$ added to the solution affects the hydration of 4CaOㆍAl$_2$O$_3$ㆍFe$_2$O$_3$ with calcium sulfate. The reaction between 4CaOㆍAl$_2$O$_3$ Fe$_2$O$_3$and CaSO$_4$ㆍ 2$H_2O$ decrease with increasing amount of Na$_2$Si$_2$O$_{5}$ in solution, owing to low hydraulic reactivity of 4CaOㆍAl$_2$O$_3$ㆍFe$_2$O$_3$by the adsorption of silicate ions on the surface of 4CaOㆍAl$_2$O$_3$ㆍ Fe$_2$O$_3$ particles. The dissolution rate of 4CaOㆍAl$_2$O$_3$ㆍ Fe$_2$O$_3$ particles deceased with the increase of the concentration of silicate ion in solution. When the 4CaOㆍAl$_2$O$_3$ㆍFe$_2$O$_3$ particles was hydrated in gypsum - Na$_2$Si$_2$O$_{5}$ solution, the hydration was retarded and the rate could not discriminate between formation of ettringite and that of monosulfate, and it stopped in high concentration of silicate ions. However, silicate ion did not any effect on the dissolution rate of gypsum.ypsum.

• YAKHAK HOEJI
• /
• v.44 no.6
• /
• pp.545-551
• /
• 2000

Magnesium trisilicate was prepared by reacting Magnesium sulfate solution with Sodium silicate solution in this study. The optimum synthesis conditions base on the yield of the product were established by applying Box-Wilson experimental design. It was found that the optimum synthesis conditions of Magnesium trisilicate were as follows; Reacting temperature : $57{\sim}90^{\circ}C$, Concentration of reactant solution : $19.1{\sim}20.0%$, Molar concentration ratio of two reactants : [Sod.silicate]/[Mg.sulfate] : $1.47{\sim}1.80$, Temperature of washing water : $45{\sim}48^{\circ}C$, Drying temperature : $65{\sim}82^{\circ}C$. The antacidic capacity of the five Magnesium trisilicate samples which shows the maximum antacidic efficacy was tested by pharmacopeia acid consuming capacity test. The five Magnesium trisilicate samples were identified by chemical analysis.

• Journal of Powder Materials
• /
• v.27 no.4
• /
• pp.287-292
• /
• 2020

The subject of this study is a zeolite generated as a by-product of recycling LAS (lithium-aluminum-silicate) resources, a kind of glass and ceramic produced by induction. The zeolite by-product is modified into Mg-zeolite using Mg as a cation to absorb Pb, a heavy metal generated from water pollution caused by recent industrial wastewater. An ion-exchange method is used to carry out the modification process, from zeolite byproduct to Mg-zeolite, and simultaneously absorb the Pb in the heavy-metal solution (99.032 mg/L). It is found that the sodium zeolite in the raw material residue can be modified to magnesium zeolite by reacting it with a mixture solution at 1 M concentration for 24 h. As a result, it is found that the residual Pb (0.130 mg/L) in the heavy metal solution is shown to be absorbed by 99.86%, with successful formation of a Mg-modified zeolite.

• Applied Chemistry for Engineering
• /
• v.17 no.4
• /
• pp.386-390
• /
• 2006

Colloidal silica which has high surface area and excellent surface properties are chemically stable inorganic materials and used for various applications in industry. Silica sol was prepared from sodium silicate solution by acid neutralization method and ion exchange treatment to remove sodium ions. Through the experimental analysis for controlling factors of particle growth rate, such as temperature, pH, and aging time, the uniform size distribution of silica sol could be obtained. The size distribution and shape of silica sol was measured by TEM and dynamic light scattering method. Zeta potential change and gelling phenomena of silica sol and its rheological properties also investigated.

• YAKHAK HOEJI
• /
• v.33 no.2
• /
• pp.111-117
• /
• 1989

The optimum reaction conditions for the acid consuming capacity of aluminum silicate synthesized from the reaction of sodium silicate solution and potassium aluminum sulfate solution were investigated by Box-Wilson experimental design, and the micromeritic properties were examined by the means of BET $N_2$ adsorption, Hg penetrometer and methylen blue adsorption. The chemical composition of the samples were analyzed by gravitic method. The results were found to be as follows: optimum reaction temperature $54.7^{\circ}C$, both concentrations of reactant soln 15.7%, reactants molar ratio (Al/Si) 0.5 and drying temperature $65.0^{\circ}C$. The acid consuming capacity of the sample prepared by above optimum conditions was 68 ml and the chemical composition was $Al_2O_3{\cdot}3.6SiO_2{\cdot}3H_2O$. The relationship between acid consuming capacity and micromeritic properties could not found in the range of experiments. Therefore, it is assumed that the acid consuming mechanism of aluminum silicate depends on the neutralization of $Al_2O_3$ and buffer action of $SiO_2$ in sample.

• Journal of the Korean Ceramic Society
• /
• v.44 no.9
• /
• pp.465-470
• /
• 2007

This paper presents an experimental study of the sulfate resistance of mortars and pastes exposed to sodium sulfate solutions up to one year. In order to check deterioration modes due to sulfate attack, the sodium sulfate solution was varied at three concentration steps (3,380, 10,140 and 33,800 ppm of $SO_4^{2-}$ ions), and maintained at ambient temperature. The tests include a visual examination, expansion and compressive strength loss measurements as well as x-ray diffraction tests. The experimental data indicated that the use of cement with a low $C_3A$ content and low silicate ratio has a beneficial effect on the sulfate attack of mortars. In contrast, the mortars with a high $C_3A$ content and high silicate ratio became severely degraded due to the formation of ettringite, gypsum and/or thaumasite in the cement matrix.

• Clean Technology
• /
• v.12 no.3
• /
• pp.171-174
• /
• 2006

The adsorbent for removal of heavy metal ions is prepared reutilizing the leached sludge generated in process of making the red mud coagulant we have develope. The pellet-type adsorbent is made by heat-treating a mixture of 10g of the leached sludge, 1g of kaolin, and 2 g of sodium silicate solution at $600^{\circ}C$ for 2 hours. In experiments of batch adsorption, the adsorbent shows good performance in adsorption of $Pb^{2+}$ ion.

• Korean Journal of Materials Research
• /
• v.16 no.6
• /
• pp.355-359
• /
• 2006

Fine silica powders were synthesized via w/o emulsion method using sodium silicate, ammonium sulfate, Triton N-57, and cyclohexane as silica source, precipitating agent, surfactant, and oil phase, respectively. The powders were prepared under a conventional process and an ultrasonic process using the same reactants at room temperature for 1 hr varying the concentration of $Na_2SiO_3$ solution and the mol ratio of $H_2O$/surfactant, respectively. The particle size of the silica powder was reduced with decreasing the concentration of sodium silicate solution and with increasing the mol ratio of $H_2O$/surfactant under with and without ultrasounds. The size of powder with ultrasounds was smaller than that without ultrasounds, which indicates that the application of ultrasound in the synthesis of silica powder is an efficient way to reduce particle size.

• Journal of Sericultural and Entomological Science
• /
• v.37 no.2
• /
• pp.132-136
• /
• 1995

This study was carried out to elucidate the effective of some swelling agents on the soaking treatment of raw silk. The swelling of raw silk is commonly practiced by soaking in warm water, However, it is not enough to weaving of raw silk. Therefore, the combination of some chemical agents were tested to improve the swelling ratio of raw silk. The pretreatment of raw silk in 0.4N sodium carbonate aqueous solution before soaking in the mixed solution of Emulon 1 g/l, Emanol 0.5 g/l and 0.04N sodium silicate increased the swelling ratio by 57%, compared to the nontreatment. In SEM observation, the surface of raw silk soaked in swelling agents was swollen and smoothed.

• Journal of the Korean Ceramic Society
• /
• v.45 no.7
• /
• pp.401-404
• /
• 2008

Willemite ($Zn_2SiO_4$) are a wide range of applications such as a phosphor host and an important crystalline phase in glass ceramics, electrical insulators, glazes, and pigments. In this study, Willemite precursors were synthesized with zinc silicate gels from mixture of zinc nitrate solution and various sodium silicate solution by the geopolymer technique. To examine the crystallization behavior, precursors were have been monitored by the XRD. A pure willemite phase was obtained at $900^{\circ}C$. TEM investigations revealed that the sample with 50 nm particle size was obtained via heat-treated at $900^{\circ}C$ for W-3.