• 한국신재생에너지학회:학술대회논문집
• /
• 2009.11a
• /
• pp.171-171
• /
• 2009

The electrodes are usually made of a porous mixture of carbon-supported platinum and ionomers. $SnO_2$ particles provide as supports that have been used for DMFCs, and it have high catalytic activities toward methanol oxidation. The main advantage of $SnO_2$ supported electrodes is that it has strong chemical interactions with metallic components. The high activity to a synergistic bifunctional mechanism in which Pt provides the adsorption sites for CO, while oxygen adsorbs dissociative on $SnO_2$. The reaction between the adsorbed species occurs at the Pt/$SnO_2$ boundary. The morphological observations were characterized by FESEM and transmission electron microscopy (TEM). $SnO_2$ particles crystallinity was analyzed by the X-ray diffraction (XRD). The surface bonded state of the $SnO_2$ particles and electrode materials were observed by the X-ray photoelectron spectroscopy (XPS). The electric properties of the Pt/$SnO_2$ catalyst for methanol oxidation have been investigated by the cyclic voltametry (CV) in 0.1M $H_2SO_4$ and 0.1M MeOH aqueous solution. The peak current density of methanol oxidation was increased as the $SnO_2$ content in the anode catalysts increased. Pt/$SnO_2$ catalysts improve the removal of CO ads species formed on the platinum surface during methanol electro-oxidation.

• Journal of the Korean Vacuum Society
• /
• v.10 no.3
• /
• pp.289-297
• /
• 2001

Highly-porous $SnO_2$thin films were prepared for recognizing and detecting of the inflammable gases, like butane, propane, LPG, carbon monoxide. To obtain sensing films, Sn, Pt/Sn, Au/Sn, and Pt,Au/Sn films were deposited employing a thermal evaporator for Sn film and a sputter for novel metals of Pt or/and Au. These films were annealed for 2 h at $700^{\circ}C$ to form $SnO_2$-based thin films. The films showed the tetragonal structure and also exhibited many defects and porosity, which could give high sensitivity to thin films. The thin films showed high sensitivity and reproductivity to the tested gases(butane, propane, LPG, and carbon monoxide) to even to low gas concentrations in range of workplace environmental standards. Especially, Pt/$SnO_2$film showed the highest sensitivity to butane, LPG, and carbon monoxide. And pure $SnO_2$ film manifested the highest sensitivity to propane. By using the sensing patterns from the films, we could reliably recognize the kinds and the quantities of the tested inflammable gases within the range of the threshold limit values(TLV) and the lower explosion limit(LEL) through the principal component analysis(PCA).

• Korean Chemical Engineering Research
• /
• v.60 no.3
• /
• pp.459-467
• /
• 2022

Redispersion of Pt-Sn particles in Pt, PtSn catalyst which have been sintered by high temperature hydrogen reduction was investigated using oxygen treatment with various temperatures. The aim of this study was to understand the relationship between the catalytic activity for propane dehydrogenation reaction and the change in the physicochemical properties of the catalyst. X-ray diffraction analysis (XRD), CO pulse chemisorption, and H₂ temperature programmed reduction (H₂-TPR) were performed to investigate the state of active metal and interactions between particles of redispersed catalyst. It was confirmed that the dispersion and particle size of platinum, the crystal phase of the catalyst, and the reduction behavior were changed according to the oxygen treatment. As for the catalytic activity in propane dehydrogeantion, sintered PtSn catalyst treated with oxygen at 500 ℃ showed best activity and recovery of initial activity. It was confirm that catalyst after oxygen treatment at 500 ℃ showed high dispersion of Pt and decreased particle size as the results of CO pulse chemisorption and XRD of catalyst, and thus the redispersion of PtSn particles in sintered catalyst was occurred. Catalytic activity was recovered due to redispersion using oxygen treatment, and the activity recovery of the PtSn catalyst was higher than that of Pt catalyst.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.10 no.9
• /
• pp.1641-1647
• /
• 2006

A dual micro gas sensor way for detecting reducing gas and bad order was fabricated using nano sized $SnO_2$ thin film fabrication method. To make nano-sized thin gas sensitive $SnO_2$ thin rilm, thin tin metal layer $2500{\AA}$ thick was oxidized between 600 and $800^{\circ}C$ by thermal oxidation. The gas sensing layers such as $SnO_2,\;SnO_2(+Pt)\;and\;SnO_2(+CuO)$ were patterned by metal shadow mask for simple fabrication process on the silicon substrate. The micro gas sensors with $SnO_2(Pt)$ and $SnO_2(+CuO)$ showed good selectivity to CO gas among reducing gases and good sensitivity to $H_2S$ that is main component of bad odor, separately.

• Journal of Sensor Science and Technology
• /
• v.11 no.5
• /
• pp.279-285
• /
• 2002

Two $SnO_2$ based sensing films(pure $SnO_2$ and $SnO_2$/Pt) and a Pt thin film for temperature sensor on an alumina substrate were designed and fabricated for classifying the indoor environmental gases. By controlling the heating power in the shape of trapezoid, unique four sensing response curves created from both $SnO_2$ film and $SnO_2$/Pt film. Then, various parameters were extracted from sensing response curves and carried out principal component analysis(PCA). The results confirm that a sensor array with the proposed operating mode was extremely effective in classifying indoor environmental gases such as $CO_2$, $C_3H_8$, $C_4H_{10}$.

• Clean Technology
• /
• v.18 no.2
• /
• pp.162-169
• /
• 2012

Pt-Sn/${\theta}-Al_2O_3$ catalyst for n-butane dehydrogenation reaction was prepared by incipient wetness method. To confirm the physicochemical properties of Pt-Sn/${\theta}-Al_2O_3$ catalyst, the characterization was performed using X-ray diffraction (XRD), $N_2$ sorption analysis, temperature programmed desorption of $NH_3$ ($NH_3$-TPD), temperature programmed reduction of $H_2$ ($H_2$-TPR) techniques. Also, the catalytic activities of Pt-Sn/${\theta}-Al_2O_3$ for n-butane dehydrogenation was tested as a function of pretreatment temperature, pretreatment time, reaction temperature, and the partial pressure of n-butane and hydrogen. The sum of selectivities to n-butenes consisting of 1-butene, cis-2-butene, and trans-2-butene was almost constant 95% in the range of conversion of n-butane 5-55%. The activation energy calculated from Arrhenius equation was $82.4kJ\;mol^{-1}$ and the reaction orders of n-butane and hydrogen from Power's law were 0.70 and -0.20, respectively.

• Proceedings of the KIEE Conference
• /
• 2004.07c
• /
• pp.1555-1557
• /
• 2004

The Pt-doped $SnO_2$ thin film for CO sensor applications obtained by RF sputtering from a target of the same compound in an Ar-$O_2$ atmosphere. Pt-SnO2-SiC Schottky diode detection of CO gas Cause the remarkable change in electrical resistivity of the semiconductor. the good gas sensitivity is shown when annealing condition is 600$^{\circ}C$, 1hr in RTP and detected temperature is 350$^{\circ}C$.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2000.04a
• /
• pp.37.1-37.1
• /
• 2000

• 한국신재생에너지학회:학술대회논문집
• /
• 2009.11a
• /
• pp.191-194
• /
• 2009

PtRu based and PtSn based ternary catalysts were prepared by a conventional impregnation method using NaBH4 as reducing agent. The alloy formation, crystalline size and chemical composition of the in-house catalysts were determined by XRD, TEM and EDX, respectively. The chemical compositions of in-house catalysts were quite similar to the nominal value and good alloy formations were also observed. Further, crystalline sizes of ternary catalysts were comparatively smaller than binary catalysts and were approximately 3.5 ~ 5.5 nm. The electrochemical measurements were carried out in the solution 1 M $H_2SO_4$ with 1 M $C_2H_5OH$ at room temperature. LSV results obtained that ternary catalysts were higher current densities and specific activities. Especially, in case of tungsten addition system, Pt5Sn4W/C have the highest specific activities values and was approximately 21.2 and 3.1 times higher than that of PtRu/C and PtSn/C electrocatalyst.

• Journal of Sensor Science and Technology
• /
• v.11 no.6
• /
• pp.342-349
• /
• 2002

New formation technique of metal oxide sensing film was proposed m this paper. Silicon wafer with Pt electrodes was used as a substrate for depositing metal Sn film. Metal Sn was deposited in the state of not continuous film but only island state. The samples were prepared to obtain the optimal condition of metal Sn deposition. The resistances of deposited Sn onto Pt electrodes amounted to $1\;k{\Omega}$, $5\;k{\Omega}$, $10\;k{\Omega}$ and $50\;k{\Omega}$, respectively. Also The sample with $1,500\;{\AA}$ thickness of Sn was prepared m order to compare sensing properties between conventional type and proposing type. After deposition of metal Sn, $SnO_2$ was formed by thermal oxidation method for 3 hrs. in $O_2$ ambient at $700^{\circ}C$. Surface morphology, crystal structure and surface roughness of oxidized-sensing film were examined by SEM, XRD, and AFM, respectively. From the results of these analyses, the optimal deposition condition of Sn was that the Pt electrode resistance became $10\;k{\Omega}(300\;{\AA})$. Also, the sensing characteristics of fabricated sensing film for various concentrations of butane, propane and carbon monoxide gases were measured at he operating temperatures of $250^{\circ}C$, $300^{\circ}C$ and $350^{\circ}C$, respectively. Although catalyst as not added to the sensing film, it has exhibited the high sensitivity to all the test gases.