• Journal of Electrochemical Science and Technology
• /
• v.10 no.4
• /
• pp.424-432
• /
• 2019

Planar BiVO₄ and 3 wt% Mo-doped BiVO₄ (abbreviated as Mo:BiVO₄) film were prepared by the facile spin-coating method on fluorine doped SnO₂(FTO) substrate in the same precursor solution including the Mo precursor in Mo:BiVO₄ film. After annealing at a high temperature of 450℃ for 30 min to improve crystallinity, the films exhibited the monoclinic crystalline phase and nanoporous architecture. Both films showed no remarkably discrepancy in crystalline or morphological properties. To investigate the effect of surface passivation exploring the Al₂O₃ layer, the ultra-thin Al₂O₃ layer with a thickness of approximately 2 nm was deposited on BiVO₄ film using the atomic layer deposition (ALD) method. No distinct morphological modification was observed for all prepared BiVO₄ and Mo:BiVO₄ films. Only slightly reduced nanopores were observed. Although both samples showed some reduction of light absorption in the visible wavelength after coating of Al₂O₃ layer, the Al₂O₃ coated BiVO₄ (Al₂O₃/BiVO₄) film exhibited enhanced photoelectrochemical performance in 0.5 M Na₂SO₄ solution (pH 6.5), having higher photocurrent density (0.91 mA/㎠ at 1.23 V vs. reversible hydrogen electrode (RHE), briefly abbreviated as V_RHE) than BiVO₄ film (0.12 mA/㎠ at 1.23 V_RHE). Moreover, Al₂O₃ coating on the Mo:BiVO₄ film exhibited more enhanced photocurrent density (1.5 mA/㎠ at 1.23 V_RHE) than the Mo:BiVO₄ film (0.86 mA/㎠ at 1.23 V_RHE). To examine the reasons, capacitance measurement and Mott-Schottky analysis were conducted, revealing that the significant degradation of capacitance value was observed in both BiVO₄ film and Al₂O₃/Mo:BiVO₄ film, probably due to degraded capacitance by surface passivation. Furthermore, the flat-band potential (V_FB) was negatively shifted to about 200 mV while the electronic conductivities were enhanced by Al₂O₃ coating in both samples, contributing to the advancement of PEC performance by ultra-thin Al₂O₃ layer.

• Journal of Electrochemical Science and Technology
• /
• v.9 no.4
• /
• pp.282-291
• /
• 2018

The pristine fluorine-doped $SnO_2$ (abbreviated as FTO) inverse opal (IO) was developed using a 410 nm polystyrene bead template. The nanolayered copper tungsten oxide ($CuWO_4$) was decorated on the FTO IO film using a facile electrochemical deposition, subsequently followed by annealing at $500^{\circ}C$ for 90 min. The morphologies, crystalline structure, optical properties and photoelectrochemical characteristics of the FTO and $CuWO_4$-decorated FTO (briefly denoted as $FTO/CuWO_4$) IO film were investigated by field emission scanning electron microscopy, X-ray diffraction, UV-vis spectroscopy and electrochemical impedance spectroscopy, showing FTO IO in the hexagonally closed-pack arrangement with a pore diameter and wall thickness of about 300 nm and 20 nm, respectively. Above this film, the $CuWO_4$ was electrodeposited by controlling the cycling number in cyclic voltammetry, suggesting that the $CuWO_4$ formed during 4 cycles (abbreviated as $CuWO_4$(4 cycles)) on FTO IO film exhibited partial distribution of $CuWO_4$ nanoparticles. Additional distribution of $CuWO_4$ nanoparticles was observed in the case of $FTO/CuWO_4$(8 cycles) IO film. The $CuWO_4$ layer exhibits triclinic structure with an indirect band gap of approximately 2.5 eV and shows the enhanced visible light absorption. The photoelectrochemical (PEC) behavior was evaluated in the 0.5 M $Na_2SO_4$ solution under solar illumination, suggesting that the $FTO/CuWO_4$(4 cycles) IO films exhibit a photocurrent density ($J_{sc}$) of $0.42mA/cm^2$ at 1.23 V vs. reversible hydrogen electrode (RHE, denoted as $V_{RHE}$), while the FTO IO and $FTO/CuWO_4$(8 cycles) IO films exhibited a $J_{sc}$ of 0.14 and $0.24mA/cm^2$ at $1.23V_{RHE}$, respectively. This difference can be explained by the increased visible light absorption by the $CuWO_4$ layer and the favorable charge separation/transfer event in the cascading band alignment between FTO and $CuWO_4$ layer, enhancing the overall PEC performance.

• Journal of Sensor Science and Technology
• /
• v.21 no.6
• /
• pp.395-401
• /
• 2012

The bond strength of three types of $TiO_2$ coatings onto fluorine-doped $SnO_2$ (FTO) glass was investigated with the aid of a tape test according to ASTM D 3359-95. Transmittance was then measured using an UV-vis spectrophotometer in the wavelength range of 300 nm to 800 nm to evaluate the extent of adhesion of $TiO_2$ nanorods/nanoparticles on FTO glass. A sharp interface between the coating layer and the substrate was observed for single $TiO_2$ coating ($TiO_2$ nanorods/FTO glass), which may be detrimental to the bonding strength. In multicoating sample ($TiO_2$ nanorod/$TiO_2$ nanoparticle/$TiO_2$ nanoparticle/FTO glass), the tape test was not performed due to severe peeling-off prior to the test. On the other hand, the dual coating sample ($TiO_2$ nanorod/$TiO_2$ nanoparticle/FTO glass) showed minimum variation of transmittance (4%) after the test, suggesting that the topcoat adheres well with the FTO substrate due to the presence of the $TiO_2$ nanoparticle buffer layer. The use of a $TiO_2$ nanorod electrode layer with good adhesion may be attributed to the excellent dye sensitized solar cell performance.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.256-256
• /
• 2010

투명전극부터 디스플레이 산업에 이르기까지 광범위하게 응용되어지고 있고 개발되어지고 있는 투명전도산화물(TCO)은 ZnO, In2O3, SnO2 등을 기본으로 하는 n-type 재료가 대부분이다. 그러나 투명전도 산화물을 이용한 light emitting diode(LED), 투명한 태양전지, p-형 TFT와 같은 투명전자소자의 개발을 위해서는 p-type 소재가 필수적이다. p-type TCO 소재는 비교적 연구 개발 실적이 매우 부진한 실정이었다. 1997년 넓은 밴드갭을 가지는 ABO2(delafossite) 산화물이 p-type으로서 안정적이라는 것을 보고함에 따라 이에 대한 연구가 활발히 진행되고 있다. 현재 ABO2 형태를 가진 Delafossite구조 산화물이 가장 유망한 p-type 투명전도체 소재로 거론되고 있다. Delafossite 구조가 p-type 투명전도체에 적합한 결정구조인 이유는 밴드갭이 넓고 공유결합에 유리하기 때문이다. Delafossite구조는 상온에서 2종류의 polytype(상온에서 Rhombohedaral구조와 hexagonal 구조)이 존재하며 이들은 각각 3R 및 2H의 결정 구조를 가지고 있다. ABO2의 delafossite구조에서 Cu+의 배열은 c-축을 따라 Cu-O-Cr-O-Cu의 연속적인 층 구조로서 2차원연결로 보여 진다. 보고된 Cu- base delafossite구조를 가지는 재료들은 CuAlO2, CuGaO2, CuInO2 등 여러가지가 있다. 본 연구에서는 PLD를 이용하여 c-plane 사파이어 기판위에 성장된 delafossite구조인 CuCrO2박막의 특성을 알아보았다. p-type 특성을 위하여 CuCrO2에 Zn를 첨가하였으며 그에 따른 구조적 전기적 특성을 조사하였다. 성장온도와 산소분압을 $500{\sim}700^{\circ}C$, 0~10mTorr로 변화시켜 특성을 연구하였다. 성장온도 $700^{\circ}C$, 산소분압 10mTorr에서 c-plane 사파이어 기판위에 c-축 배향의 에피성장된 CuCrO2:Zn 박막을 얻을 수 있었다. Mg를 도핑함에 따른 p-type 특성보다 현저히 떨어지는 것을 확인하였다. 또한 동일한 조건임에도 특정한 이차상의 존재를 통해 도핑된 Zn의 위치를 추측할 수 있었다. 온도와 분압에 따른 결정성과 표면상태를 SEM을 통해서 확인하였다.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.06a
• /
• pp.51.3-51.3
• /
• 2010

Due to the recent public awareness of global warming and sustainable economic growth, there has been a growing interest in alternative clean energy sources. Hydrogen is considered as a clean fuel for the next generation. One of the technical challenges related to the use of hydrogen is safe monitoring of the hydrogen leak during separation, purification and transportation. For detecting various gases, chemiresistor-type gas sensors have been widely studied and used due to their well-established detection scheme and low cost. However, it is known that many of them have the limited sensitivity and slow response time, when used at low temperature conditions. In our work, a sensor based on Schottky barriers at the electrode/sensing material interface showed promising results that can be utilized for developing fast and highly sensitive gas sensors. Our hydrogen sensor was designed and fabricated based on indium oxide (In2O3)-doped tin oxide (SnO2) semiconductor nanoparticles with platinum (Pt) nanoclusters in combination with interdigitated electrodes. The sensor showed the sensitivity as high as $10^7%$ (Rair/Rgas) and the detection limit as low as 30 ppm. The sensor characteristics could be obtained via optimized materials synthesis route and sensor electrode design. Not only the contribution of electrical resistance from the film itself but also the interfacial effect was identified as an important factor that contribute significantly to the overall sensor characteristics. This promises the applicability of the developed sensor for monitoring hydrogen leak at room temperature.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.857-860
• /
• 2002

The material that is both conductive in electricity and transparent to the visible-ray is called transparent conducting thin film. It has many field of application such as solar cell, liquid crystal display, transparent electrical heater, selective optical filter, and a optical electric device. In this study, indium tin oxide (ITO ; Sn-doped $In_2O_3$) thin films were deposited on $SiO_2$/soda-lime glass plates by a dc magnetron sputtering technique. The crystallinity and electrical properties of the films were investigated by X-ray diffraction(XRD), atomic force microscopy (AFM) scanning and 4-point probe. The optical transmittance of ITO films in the range of 300-1000nm were measured with a spectrophotometer. As a result, we obtained polycrystalline structured ITO films with (222), (400), and (440) peak. Transmittance of all the films were higher than 90% in the visible range.

• Journal of the Korean Ceramic Society
• /
• v.48 no.1
• /
• pp.94-98
• /
• 2011

A Sn-doped $In_2O_3$ (ITO) nanowire photoelectrode was produced using a simple metal evaporation method at low synthesis temperature (< $540^{\circ}C$). The nanowire electrodes have large surface area compared with that of flat ITO thin film, and show low electrical resistivity of $5.6{\times}10^{-3}{\Omega}cm$ at room temperature. In order to apply ITO nanowires to the photoelectrodes of dye-sensitized solar cell (DSSC), those surfaces were modified by $TiO_2$ nanoparticles using a chemical bath deposition (CBD) method. The conversion efficiency of the fabricated $TiO_2$/ITO nanostructure-based DSSC was obtained at 1.4%, which was increased value by a factor of 6 than one without ITO nanowires photoelectrode. This result is attributed to the large surface area and superior electrical property of the ITO nanowires photoelectrode, as well as the structural advantages, including short diffusion length of photo-induced electrons, of the fabricated $TiO_2$/ITO nanostructure-based DSSC.

• Transactions on Electrical and Electronic Materials
• /
• v.16 no.2
• /
• pp.99-102
• /
• 2015

Thin film transistors (TFTs) with amorphous 2 wt% silicon-doped zinc tin oxide (a-2SZTO) channel layer were fabricated using an RF magnetron sputtering system, and the effect of post-annealing treatment time on the structural and electrical properties of a-2SZTO systems was investigated. It is well known that Si can effectively reduce the generation of oxygen vacancies. However, it is interesting to note that prolonged annealing could have a bad effect on the roughness of a-2SZTO systems, since the roughness of a-2SZTO thin films increases in proportion to the thermal annealing treatment time. Thermal annealing can control the electrical characteristics of amorphous oxide semiconductor (AOS) TFTs. It was observed herein that prolonged annealing treatment can cause bumpy roughness, which led to increase of the contact resistance between the electrode and channel. Thus, it was confirmed that deterioration of the electrical characteristics could occur due to prolonged annealing. The longer annealing time also decreased the field effect mobility. The a-2SZTO TFTs annealed at 500℃ for 2 hours displayed the mobility of 2.17 cm²/Vs. As the electrical characteristics of a-2SZTO annealed at a fixed temperature for long periods were deteriorated, careful optimization of the annealing conditions for a-2SZTO, in terms of time, should be carried out to achieve better performance.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.262.1-262.1
• /
• 2013

ZnO 나노구조는 전기적 성질과 화학적인 안정성 때문에 가스센서, 투명 전극 및 태양전지와 같은 전자소자와 광소자에 널리 사용되고 있다. ZnO 박막을 증착하는 방법은 Physical Vapor Deposition과 Chemical Vapor Deposition이 있으나 나노 구조를 가진 SnO2를 형성하기 어렵다. 전기 화학적 증착(Electrochemical Deposition: ECD)은 낮은 온도에서 진공 공정이 필요하지 않기 때문에 경제적이며 빠른 성장 속도를 가지고 있기 때문에 ZnO 나노 구조를 효과적으로 형성 할 수 있다. 본 연구에서는 Indium Tin Oxide (ITO) 기판 위에 ZnO 나노 구조를 형성시켜 전기적 및 구조적 특성을 관찰하였다. 0.1 M zinc nitrate와 0.1 M potassium chloride를 용매에 각각 용해하여 ZnO 나노구조를 성장하였다. ZnO 나노구조를 성장하기 위하여 인가전압을 -0.75 V부터 -2.5 V까지 0.5 V 간격으로 변화하였다. X-선 회절 분석결과에서 ZnO의 피크의 크기가 큰 전기화적적 성장 전압구간과, 주사전자현미경 분석결과에서 나노 구조가 가장 잘 나타난 성장 전압구간을 다시 0.1 V 간격으로 세분화하여 최적화 조건을 분석하였다. X-선 회절 실험으로 형성한 ZnO 나노구조의 피크가 (110) (002)로 나타났다. X-선 회절 분석의 intensity의 값이 (002)방향이 가장 크게 나타났으므로 우선적으로 (002) 방향으로 ZnO 나노구조가 성장됨을 알 수 있었다. 주사전자현미경상은 grain size가 200~300 nm 사이의 ZnO 나노구조가 형성되며, grain size가 전기화학적 증착 장치의 성장전압이 커짐에 따라 커지는 것을 알 수 있었다.

• Korean Journal of Materials Research
• /
• v.20 no.12
• /
• pp.676-680
• /
• 2010

Most TCOs such as ITO, AZO(Al-doped ZnO), FTO(F-doped $SnO_2$) etc., which have been widely used in LCD, touch panel, solar cell, and organic LEDs etc. as transparent electrode material reveal n-type conductivity. But in order to realize transparent circuit, transparent p-n junction, and introduction of transparent p-type materials are prerequisite. Additional prerequisite condition is optical transparency in visible spectral region. Oxide based materials usually have a wide optical bandgap more than ~3.0 eV. In this study, single-phase transparent semiconductor of $SrCu_2O_2$, which shows p-type conductivity, have been synthesized by 2-step solid state reaction at $950^{\circ}C$ under $N_2$ atmosphere, and single-phase $SrCu_2O_2$ thin films of p-type TCOs have been deposited by RF magnetron sputtering on alkali-free glass substrate from single-phase target at $500^{\circ}C$, 1% $H_2$/(Ar + $H_2$) atmosphere. 3% $H_2$/(Ar + $H_2$) resulted in formation of second phases. Hall measurements confirmed the p-type nature of the fabricated $SrCu_2O_2$ thin films. The electrical conductivity, mobility of carrier and carrier density $5.27{\times}10^{-2}S/cm$, $2.2cm^2$/Vs, $1.53{\times}10^{17}/cm^3$ a room temperature, respectively. Transmittance and optical band-gap of the $SrCu_2O_2$ thin films revealed 62% at 550 nm and 3.28 eV. The electrical and optical properties of the obtained $SrCu_2O_2$ thin films deposited by RF magnetron sputtering were compared with those deposited by PLD and e-beam.