• Journal of the Microelectronics and Packaging Society
• /
• v.7 no.2
• /
• pp.13-19
• /
• 2000

Shear strengths of BGA solder joints on Cu pads were studied for Cu-containing Sn (0, 1.5, and 2.5 wt.% Cu) and Sn-40Pb (0 and 0.5wt.% Cu) solders, with emphasis on the roles of the Cu-Sn intermetallic layer thickness and the roughness of the interface between the intermetalic layer and solder. The shear strength test was performed for as-soldered solder joints with various soldering reaction times up to 4 min. The addition of Cu to the pure Sn solder results in an enhanced growth of the intermetallic layer whereas the effect of Cu addition to the Sn-40Pb solder is primarily on the reduction of the roughness of the intermetallic/solder interface. The critical thickness of the intermetallic layer for a maximum shear strength depends on the solder materials, which was measured to be ~ 2.3 $\mu\textrm{m}$ for Sn-Cu solders and ~ 1.2 $\mu\textrm{m}$ for Sn-Pb-Cu solders. The shear strength at the critical intermetallic layer thickness seems to increase as the intermetallic/solder interface becomes rougher. This is in accordance with the observation that the sheared fracture occurred initially within the solder tends to shift towards the intermetallic/solder interface as the intermetallic layer grows above the critical thickness.

• Journal of Welding and Joining
• /
• v.20 no.4
• /
• pp.505-509
• /
• 2002

Pb is considered to be eliminated from solder, due to its toxicity. However, melting temperatures of most Pb-free solders are known higher than that of Sn37Pb. Therefore, there is a difficulty to apply Pb-free solders to electronic industry. Since Sn3Ag8Bi5In has relatively lower melting range as $188~200^{\circ}C$, on this study. Wettability and soldering characteristics of Sn3Ag8Bi5In solder in BGA were investigated to solve for what kind of problem. Zero cross time, wetting time, and equilibrium force of Sn3Ag8Bi5In solder for Cu and plated Cu such as Sn, Ni, and Au/Ni-plated on Cu were estimated. Plated Sn on Cu showed best wettability for zero cross time, wetting time and equilibrium farce. Shear strength of the reflowed joint with Sn3Ag8Bi5In ball in BGA was investigated. Diameter of the ball was 0.5mm, UBM(under bump metallurgy) was $Au(0.5\mu\textrm{m})Ni(5\mu\textrm{m})/Cu(18\mu\textrm{m})$ and flux was RMA type. For the reflow soldering, the peak reflow temperature was changed in the range of $220~250^{\circ}C$, and conveyor speed was 0.6m/min.. The shear strength of Sn3Ag8Bi5In ball showed similar level as those of Sn37Pb. The soldered balls are aged at $110^{\circ}C$ for 36days and their shear strengths were evaluated. The shear strength of Sn3Ag8Bi5In ball was increased from 480gf to 580gf by aging for 5 days.

• Proceedings of the KWS Conference
• /
• 1998.10a
• /
• pp.141-142
• /
• 1998

• Proceedings of the KWS Conference
• /
• 2001.10a
• /
• pp.147-148
• /
• 2001

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2002.11a
• /
• pp.65-65
• /
• 2002

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2004.11a
• /
• pp.32-32
• /
• 2004

• Journal of Welding and Joining
• /
• v.25 no.2
• /
• pp.82-88
• /
• 2007

Sn-3.0Ag-0.5Cu lead fee solder was generally utilized in electronics assemblies. But it is insufficient to research about activation energy(Q) that is applying to evaluate the solder joint reliability of environmental friendly electronics assemblies. Therefore this study investigated Q values which are needed to IMC formation and growth of Sn-3.0Ag-0.5Cu/Cu and Sn-40pb/Cu solder joints during aging treatment. We bonded Sn-3.0Ag-0.5Cu and Sn-40Pb solders on FR-4 PCB with Cu pad$(t=80{\mu}m)$. After reflow soldering, to observe the IMC formation and growth of the solder joints, test specimens were aged at 70, 150 and $170^{\circ}C$ for 1, 2, 5, 20, 60, 240, 960, 15840, 28800 and 43200 min, respectively. SEM and EDS were utilized to analysis the IMCS. From these results, we measured the total IMC$(Cu_6Sn_5+Cu_3Sn)$ thickness of Sn-3.0Ag-0.5Cu/Cu and Sn-40Pb/Cu interface, and then obtained Q values for the IMC$(Cu_6Sn_5,\;Cu_3Sn)$ growth of the solder joints.

• Journal of Welding and Joining
• /
• v.18 no.6
• /
• pp.42-47
• /
• 2000

The object of this study is to estimate Sn-Ag-Bi-Ga solder alloy as a substitute for Sn-37Pb alloy. For Sn-Ag-Bi-Ga alloys, Ag, Bi and Ga contents are varied. (Ag : 1~5%, Ga : 3%, Bi : 3~6%) Comparing to Sn-37Pb alloy Sn-Ag-Bi-Ga alloys have wider melting temperature range up to max. $18.7^{\circ}C$. With increasing Ag, Bi contents, the wettability of the alloys increased up to max. 6.6 mN. The vickers hardness of the alloys was max. 46.4 Hv. The ultimate tensile stress of the alloys was max. 60.3 MPa and the elongation was max. 1.2%. The joint strength between circuit board and solder was max. 55.5 N and the joint strength between connector and solder was max. 176.1 N. There were no cracks in this alloys after thermal shock test.

• Clean Technology
• /
• v.11 no.3
• /
• pp.153-164
• /
• 2005

This study found a reliable evaluation for four kinds of pb-Free plating solutions and it's layers, through pure Sn, SnAg, SnBi and SnCu. These four kind of solutions are widely used to pb-Free plating. Hull-cell, Harring-blum, coverage, throwing power, current efficiency, stability, life-time, composition, hardness, roughness, abrasion, scratch, solderability, corrosion, contact angle, morphology, SIR(Surface insulation resistance) and Whisker test were experimented. Also, Using ICP, XRF, FE-SEM, EDS, temperature/humidity chamber, solderability tester, hardness tester, roughness tester, abrasion tester, salt spray tester, contact angle tester, SIR tester, and microscope. In this paper could be shown the systematic and various analysis for reliability about four kinds of pb-Free plating solutions, processes and it's deposit surface.

• Journal of the Microelectronics and Packaging Society
• /
• v.7 no.2
• /
• pp.47-53
• /
• 2000

The fluxless wetting properties of TSM-coated glass substrate were evaluated by the wetting balance method. We could estimate the wettability of the TSM with new parameters obtained from the wetting balance test for one side-coated specimen. It was more effective in wetting to use Cu as a wetting layer and Au as a protection layer than to use Au itself as a wetting layer. The SnSb solder showed better wettability than SnAg, SnBi, and SnIn solders. The contact angle of the one side-coated glass substrate to the Pb-free solders could be calculated from the farce balance equation by measuring the static force and the tilt angle.