• 한국마이크로전자및패키징학회:학술대회논문집
• /
• 한국마이크로전자및패키징학회 2003년도 기술심포지움 논문집
• /
• pp.68-71
• /
• 2003

The reaction of ultra-small eutectic 58Bl-42Sn solder bump with Au/Ni/Ti and Au/Cu/Ti UBMs during reflow was studied. The eutectic Bi-Sn solder bumps of $46{\mu}m$ diameter were fabricated by using the evaporation method and were reflowed using the rapid thermal annealing system. The intermetallic compound was characterized using a SEM, an EDS, and an XRD. The $(Cu_xAu_{1-x})_6Sn_5$ compounds formed at the interface between Bi-Sn solder and Au/Cu/Ti UBM. On the other hand, in the Bi-Sn solder bump on Au/Ni/Ti UBM, the faceted and rectangular intermetallic compounds were observed on the solder bump surface and inside the solder bump as well as at the UBM interface. These intermetallic compounds were Identified as $(Au_{l-x-y}Bi_xNi_y)Sn_2$ phase.

• Journal of Welding and Joining
• /
• 제31권3호
• /
• pp.4-10
• /
• 2013

In electronic industry, the trend of future electronics will be flexible, bendable, wearable electronics. Until now, there is few study on bonding technology and reliability of bonding joint between chip with micro solder bump and flexible substrate. In this study, we investigated joint properties of Si chip with eutectic Sn-58Bi solder bump on Cu pillar bump bonded on flexible substrate finished with ENIG by flip chip process. After flip chip bonding, we observed microstructure of bump joint by SEM and then evaluated properties of bump joint by die shear test, thermal shock test, and bending test. After thermal shock test, we observed that crack initiated between $Cu_6Sn_5IMC$ and Sn-Bi solder and then propagated within Sn-Bi solder and/or interface between IMC and solder. On the other hands, We observed that fracture propated at interface between Ni3Sn4 IMC and solder and/or in solder matrix after bending test.

• 마이크로전자및패키징학회지
• /
• 제10권2호
• /
• pp.61-67
• /
• 2003

고집적 플립 칩 기술을 위한 $50{\mu}m$ 직경의 극미세 58Bi-42Sn 솔더 범프와 Au/Ni/Ti UBM의 계면 반응에 따른 금속간 화합물을 분석하였다. 증발증착법과 lift-off 방법으로 극미세 Bi-Sn 솔더 범프를 형성하고 급속열처리 장비를 이용하여 리플로 공정을 실시하였다. 리플로 공정에서의 냉각속도를 변화시키면서 제작한 솔더 범프의 표면과 단면을 주사전자현미경으로 관찰하였다 $Au(0.1{\mu}m)$/Ni/Ti UBM 위의 극미세 58Bi-42Sn 솔더 범프의 표면과 내부에서 facet 특성을 갖는 다각형의 금속간 화합물들이 다수 관찰되었다. 주사전자현미경의 EDS 분석과 X-선 회절분석으로 확인한 결과 이 금속간 화합물은 $(Au_xBi_yNi_{1-x-y})Sn_2$상임을 확인하였다.

• 마이크로전자및패키징학회지
• /
• 제8권1호
• /
• pp.45-51
• /
• 2001

UBM층과의 젖음 특성 및 표면 산화정도가 미세 피치를 갖는 저 융점 솔더 범프의 볼 형성에 미치는 영향을 연구하였다. Au/Cu/Cr 과 Au/Ni/Ti UBM 위에 공정 조성에 가까운 In-Ag와 공정 조성의 Bi-Sn 솔더를 솔더 층의 증착 순서를 달리하여 증발 증착한 후 lift-off 공정과 열처리 공정을 사용하여 솔더 범프를 형성하였다. In-Ag솔더의 경우 In이 UBM 층과 접한 범프가, 또한 Bi-Sn 솔더의 경우 Sn을 먼저 UBM층위에 먼저 증착시켜 리플로 한 범프가 솔더 볼 형성 경향이 다른 범프에 비해 높았다. 구형의 솔더 범프 형성 정도는 UBM 층과의 젖음 특성에 따라 크게 달라졌다.

• 한국표면공학회지
• /
• 제35권1호
• /
• pp.11-16
• /
• 2002

As environmental concerns increasing, the electronics industry is focusing more attention on lead free solder alternatives. In this research, we have researched wettability of intermediate solder of Sn3Ag9Bi5In, which include In and Bi and has similar melting temperature to Sn37Pb eutectic solder. We investigated the wetting property of Sn3Ag9Bi5In. To estimate wettability of Sn3Ag9Bi5In solder on various substrates, the wettability of Sn3Ag9Bi5In solder on high-pure Cu-coupon was measured. Cu-coupon that plated Sn, Ni and Au/Ni and Si-wafer adsorbed Ni/Cu under bump metallurgy on one side. As a result, the wetting property of Sn3Ag9Bi5In solder is a little better than that of Sn37Pb and Sn3.5Ag.

• 마이크로전자및패키징학회지
• /
• 제12권2호
• /
• pp.95-103
• /
• 2005

42Sn-58Bi 솔더(이하 wt.$\%$에 의한 표기)와 무전해 Ni-P/치환 Au under bump metallurgy (UBM) 간의 계면 반응을 intermetallic compound (IMC)의 형성과 성장, UBM의 감소, 그리고 범프 전단강도의 영향 관점에서 시효 처리 전 후에 어떠한 변화가 생기는 지를 알아보고자 하였다. 치환 Au 층을 $5{\mu}m$ 두께의 무전해 Ni-P ($14{\~}15 at.\%$ P)위에 세 가지 각기 다른 두께, 즉 $0{\mu}m$(순수한 무전해 Ni-P UBM), $0.1{\mu}m$, $1{\mu}m$로 도금하였다. 그 후 42Sn-58Bi 솔더 범프를 세 가지 다른 UBM 구조에 스크린프린팅 방식으로 형성하였다. 범프 형성 직후에는 세 가지 다른 UBM구조에서 솔더와 UBM 사이에 공통적으로 $Ni_3Sn_4$ IMC (IMC1) 만이 형성됐다. 하지만, 이를 $125^{\circ}C$에서 시효 처리를 할 경우 특이하게 Au를 함유한 UBM 구조에서는 $Ni_3Sn_4$ 위로 또 다른 4원계 화합물 (IMC2)이 관찰되었다. 원자 비로 $Sn_{77}Ni{15}Bi_6Au_2$인 4원계 화합물로 확인되었다. $Sn_{77}Ni{15}Bi_6Au_2$ 층은 솔더 조인트의 접합성에 매우 치명적인 영향을 미쳤다. 시효 처리를 거친 Au를 함유한 UBM 구조에서 솔더 범프의 전단 강도 값은 시효 처리 전에 비해 $40\%$ 이상의 감소를 보였다.

• 마이크로전자및패키징학회지
• /
• 제19권3호
• /
• pp.15-20
• /
• 2012

In electronics industry, the coming electronic devices will be expected to be high integration and convergence electronics. And also, it will be expected that the coming electronics will be flexible, bendable and wearable electronics. Therefore, the demands and interests of bonding technology between flexible substrate and chip for mobile electronics, e-paper etc. have been increased because of weight and flexibility of flexible substrate. Considering fine pitch for high density and thermal damage of flexible substrate during bonding process, the micro solder bump technology for high density and low temperature bonding process for reducing thermal damage will be required. In this study, we researched on bonding technology of chip and flexible substrate by using 25um Cu pillar bumps and Sn-Bi solder bumps were formed by electroplating. From the our study, we suggest technology on Cu pillar bump formation, Sn-Bi solder bump formation, and bonding process of chip and flexible substrate for the coming electronics.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2001년도 추계학술발표대회 개요집
• /
• pp.156-158
• /
• 2001

• Journal of Welding and Joining
• /
• 제20권4호
• /
• pp.505-509
• /
• 2002

Pb is considered to be eliminated from solder, due to its toxicity. However, melting temperatures of most Pb-free solders are known higher than that of Sn37Pb. Therefore, there is a difficulty to apply Pb-free solders to electronic industry. Since Sn3Ag8Bi5In has relatively lower melting range as $188~200^{\circ}C$, on this study. Wettability and soldering characteristics of Sn3Ag8Bi5In solder in BGA were investigated to solve for what kind of problem. Zero cross time, wetting time, and equilibrium force of Sn3Ag8Bi5In solder for Cu and plated Cu such as Sn, Ni, and Au/Ni-plated on Cu were estimated. Plated Sn on Cu showed best wettability for zero cross time, wetting time and equilibrium farce. Shear strength of the reflowed joint with Sn3Ag8Bi5In ball in BGA was investigated. Diameter of the ball was 0.5mm, UBM(under bump metallurgy) was $Au(0.5\mu\textrm{m})Ni(5\mu\textrm{m})/Cu(18\mu\textrm{m})$ and flux was RMA type. For the reflow soldering, the peak reflow temperature was changed in the range of $220~250^{\circ}C$, and conveyor speed was 0.6m/min.. The shear strength of Sn3Ag8Bi5In ball showed similar level as those of Sn37Pb. The soldered balls are aged at $110^{\circ}C$ for 36days and their shear strengths were evaluated. The shear strength of Sn3Ag8Bi5In ball was increased from 480gf to 580gf by aging for 5 days.

• ETRI Journal
• /
• 제38권6호
• /
• pp.1163-1171
• /
• 2016

Integration technologies involving flexible substrates are receiving significant attention owing the appearance of new products regarding wearable and Internet of Things technologies. There has been a continuous demand from the industry for a reliable bonding method applicable to a low-temperature process and flexible substrates. Up to now, however, an anisotropic conductive film (ACF) has been predominantly used in applications involving flexible substrates; we therefore suggest low-temperature lead-free soldering and bonding processes as a possible alternative for flex-on-flex applications. Test vehicles were designed on polyimide flexible substrates (FPCBs) to measure the contact resistances. Solder bumping was carried out using a solder-on-pad process with Solder Bump Maker based on Sn58Bi for low-temperature applications. In addition, thermocompression bonding of FPCBs was successfully demonstrated within the temperature of $150^{\circ}C$ using a newly developed fluxing underfill material with fluxing and curing capabilities at low temperature. The same FPCBs were bonded using commercially available ACFs in order to compare the joint properties with those of a joint formed using solder and an underfill. Both of the interconnections formed with Sn58Bi and ACF were examined through a contact resistance measurement, an $85^{\circ}C$ and 85% reliability test, and an SEM cross-sectional analysis.