• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.22 no.1
• /
• pp.177-189
• /
• 1998

The contents of this paper include a non-destructive technique for evaluating the degradation of the boiler superheater tube in a fossil power plant through an electrochemical polarization test. Correlation between Ip of polarization parameter and SP-DBTT for the superheater tubes in long-term use was obtained. 1.0Cr-0.5Mo steel was degraded by softening, and the degree of degradation was dependent upon carbides with Cr and Mo elements. Since brittle fracture at low temperature and ductile fracture mode at high temperature were shown, similarity between standard Charpy and small punch tests could be found. In addition, SP-DBTT showing the degree of degradation was higher, as the time-in use of the materials got longer. Electrolyte including picric acid of 1.3 g in distilled water of 100ml at 25.deg. C temperature and sodium tridecylbenzene sulfonate with 1g could be applied to evaluate the degradation of 1.0Cr-0.5Mo steel by means of the electrochemical polarization test. Ip and Ipa values measured through the electrochemical test are the appropriate parameters for representing the degradation of the superheater tube(1.0Cr-0.5Mo steel) for the fossil power plant. It is poassible to evaluate the degradation of materials with different time histories electrochemically, by Ip value only, at field test.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.19 no.6
• /
• pp.411-419
• /
• 1999

It has been well recognized that a long term service at elevated temperature of $350^{\circ}C{\sim}550^{\circ}C$ induces embrittlement damage due to carbide precipitation and/or P, Sb and Sn segregation at grain boundaries and thereby deteriorates the grain boundary strength of heat resisting components in the energy-related plants. Therefore, it is very important to assess quantitatively the extent of embrittlement damage of heat resisting components to secure the reliable and efficient service condition and to prevent brittle failure in service. However, because fracture tests are limited in size and number of specimen obtained from the structural components, nondestructive test method is required. In this study, the optimum electrochemical parameters are investigated and discussed to evaluate nondestructive embrittlement damage for aged 2.25Cr-1Mo steels by means of electrochemical polarization test method (ECPTM) in proper corrosive environment. In addition, the electrochemical test results are compared with embrittlement degree evaluated by semi-nondestructive SP test.