• Advances in concrete construction
• /
• v.15 no.6
• /
• pp.359-376
• /
• 2023

Ultra-high-performance concrete (UHPC) has become an attractive cast-in-place repairing material for existing engineering structures. The present study aims to investigate age-dependent high-early-strength UHPC (HESUHPC) material properties (i.e., compressive strength, elastic modulus, flexural strength, and tensile strength) as well as interfacial shear properties of HESUHPC-normal strength concrete (NSC) composites cured at different season temperatures (i.e., summer, autumn, and winter). The typical temperatures were kept for at least seven days in different seasons from weather forecasting to guarantee an approximately consistent curing and testing condition (i.e., temperature and relative humidity) for specimens at different ages. The HESUHPC material properties are tested through standardized testing methods, and the interfacial bond performance is tested through a bi-surface shear testing method. The test results quantify the positive development of HESUHPC material properties at the early age, and the increasing amplitude decreases from summer to winter. Three-day mechanical properties in winter (with the lowest curing temperature) still gain more than 60% of the 28-day mechanical properties, and the impact of season temperatures becomes small at the later age. The HESUHPC shrinkage mainly occurs at the early age, and the final shrinkage value is not significant. The HESUHPC-NSC interface exhibits sound shear performance, the interface in most specimens does not fail, and most interfacial shear strengths are higher than the NSC-NSC composite. The HESUHPC-NSC composites at the shear failure do not exhibit a large relative slip and present a significant brittleness at the failure. The typical failures are characterized by thin-layer NSC debonding near the interface, and NSC pure shear failure. Two load-slip development patterns, and two types of main crack location are identified for the HESUHPC-NSC composites tested in different ages and seasons. In addition, shear capacity of the HESUHPC-NSC composite develops rapidly at the early age, and the increasing amplitude decreases as the season temperature decreases. This study will promote the HESUHPC application in practical engineering as a cast-in-place repairing material subjected to different natural environments.

• Journal of the Korean Society for Precision Engineering
• /
• v.29 no.5
• /
• pp.531-537
• /
• 2012

Fretting fatigue tests were conducted to investigate the effect of contact pressure on fretting fatigue behavior in aluminum alloy A7075-T6. Test results showed that when the contact pressure is so low that gross or partial slip occurs at the pad/specimen interface, fretting fatigue damage increases with the contact pressure. However, when the contact pressure is high enough to prevent slip at the interface, fretting fatigue damage decreases with the contact pressure. In order to understand how the contact pressure influence the fretting fatigue damage, finite element analyses were conducted and the analysis results were used to evaluate critical plane fretting fatigue damage parameters and their components. It is revealed that fretting fatigue damage estimated with the parameters exhibits the same variation as that in the tests. Moreover, the variation of fretting fatigue damage is closely related with that of the maximum normal stress on the critical plane rather than the strain amplitude on the critical plane.

• Transactions of the Korean Society for Noise and Vibration Engineering
• /
• v.26 no.1
• /
• pp.55-62
• /
• 2016

Nuclear fuels are always exposed to hot temperature and high speed coolant flow during the reactor operation. Thus the fuel rod accompanies small amplitude vibration due to the turbulent flow. The random vibration causes friction between the fuel rod and the grid structure which provides the lateral supports. The friction is critical to the fuel rod fretting wear, and it degrades fuel performance when a severe wear is developed. LuGre friction model is introduced in the paper, and the performance was evaluated comparing to the classical Coulomb model. It is shown that the developed friction force considering the Coulomb friction is not enough to stop or delay the motion while the stick-slip can be simulated using LuGre friction model. Numerical solutions of the two dimensional spacer grid cell model with the modern friction are also reviewed, and it is discussed that the new friction model simulates well the nonlinear mechanism.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2006.11a
• /
• pp.290-293
• /
• 2006

From the hydraulic experiment, it was concluded that upwelling could be enhanced when the relative structure height (the ratio of structure height to water depth) was 0.3 and stratification parameter was 3.0. In addition, the optimum size of rubbers was determined that the effect of the mean horizontal length of block was affected incident velocity than size of block. In the numerical experiment, the relation between the shape of rubber and stratification parameter was verified, ana the hydraulic characteristics of 3-D flow field around the artificial structures were investigated. Phenomena of flow field around the artificial upwelling structures corresponded with the results of hydraulic experiment. The position with maximum velocity in artificial upwelling structure was the center of top of its front side and the slip stream occurred at the inside and behind-bottom of artificial upwelling structures. The velocity of slip stream and early amplitude of velocity were higher in the inside than the behind-bottom.

• Journal of the Korean earth science society
• /
• v.35 no.5
• /
• pp.354-361
• /
• 2014

Fault plane solutions in North Korea and the northern part of the Yellow Sea ($37.5^{\circ}N-40.5^{\circ}N$, $124.5^{\circ}E-128.5^{\circ}E$) was studied for the earthquakes that occurred from November, 2008 to May, 2013. The analysis was based on the data collected from seismic networks in Korea and China. Fault plane solutions were obtained from P and SH wave polarities and SH/P amplitude ratioes. Most earthquakes exhibited predominantly strike-slip fault characteristics with NNE-SSW or WNW-ESE nodal planes. The P-axes trends are mainly NE-SW or ENE-WSW direction in the northern part of the Yellow Sea and inland area of North Korea except some areas in the Hwanghae province. Fault plane solutions and main axis of stress field in the study region were similar to those observed in the southern part of the Korean Peninsula.

• Journal of the Korean earth science society
• /
• v.27 no.3
• /
• pp.341-347
• /
• 2006

Focal mechanisms were analyzed for the seven earthquakes which occurred in the southwestern part of the Korea Peninsula from 2001 to 2005. Grid searches are performed to fit distributions of P-wave first-motion polarities and SH/P amplitude ratios for each event. The focal mechanism solutions imply that most of the events have strike-slip sense including partially thrust component. The compressional axes of the solutions are predominantly ENE-WSW or NE-SW indirections. This result is similar to the directions of the principal compressional axes for major earthquakes occurred around the Korea Peninsula.

• Journal of the Earthquake Engineering Society of Korea
• /
• v.10 no.3 s.49
• /
• pp.101-111
• /
• 2006

This paper proposes a method for modeling new fault ground motion due to moderate size earthquakes in Stable Continental Regions (SCRs) for the first time. The near fault ground motion is characterized by a single long period velocity pulse of large amplitude. In order to model the velocity pulse, its period and peak amplitude need be determined in terms of earthquake magnitude and distance from the causative fault. Because there have been observed very few new fault ground motions, it is difficult to derive the model directly from the recorded data in SCRs. Instead an indirect approach is adopted in this work. The two parameters, the period and peak amplitude of the velocity pulse, are known to be functions of the rise time and the slip velocity. For Western United States (WUS) that belongs active tectonic regions, there art empirical formulas for these functions. The relations of rise time and slip velocity on the magnitude in SCRs are derived by comparing related data between Western United States and Central-Eastern United States that belongs to SCRs. From these relations, the functions of these pulse parameters for NFGM in SCRs can be expressed in terms of earthquake magnitude and distance. A time history of near fault ground motion of moderate magnitude earthquake in stable continental regions is synthesized by superposing the velocity pulse on the for field ground motion that is generated by stochastic method. As an demonstrative application, the response of a single degree of freedom elasto-plastic system is studied.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.31 no.2 s.257
• /
• pp.197-204
• /
• 2007

Fretting is a contact damage process that occurs between two contact surfaces. Fretting fatigue reduces fatigue strength of the material due to low amplitude oscillatory sliding and changes in the contact surfaces of strongly connected machine and structure such as bolt, key, pin, fixed rivet and connected shaft, which have relative slip of repeatedly extreme low frequency amplitude. In this research, the fretting fatigue behavior of 2024-T3511 and 7050-T7451 aluminum alloys used mainly in aircraft and automobile industry were experimentally estimated. Based on this experimental wort the following results were obtained: (1) A significant decrease of fatigue lift was observed in the fretting fatigue compared to the plain fatigue. The fatigue limit of 2024-T3511 aluminum alloy decreased about 59% while 7050-T7451 aluminum alloy decreased about 75%. (2) In 7050-T7451 specimen using ATSI4030 contact pad, crack was initiated more early stage than using 2024-T3511 contact pad. (3) In all specimens, oblique cracks were initiated at contact edge. (4) Tire tracks and rubbed scars were observed in the oblique crack region of fracture surface.

• Journal of the Society of Naval Architects of Korea
• /
• v.48 no.6
• /
• pp.516-527
• /
• 2011

This paper considers a numerical analysis of ship maneuvering performance in the high amplitude incident waves by adopting linear and nonlinear ship motion analysis. A time-domain ship motion program is developed to solve the wave-body interaction problem with the ship slip speed and rotation, and it is coupled with a modular type 4-DOF maneuvering problem. Nonlinear Froude-Krylov and restoring forces are included to consider weakly nonlinear ship motion. The developed method is applied to observe the nonlinear ship motion and planar trajectories in maneuvering test in the presence of incident waves. The comparisons are made for S-175 containership with existing experimental data. The nonlinear computation results show a fair agreement of overall tendency in maneuvering performance. In addition, maneuvering performances with respect to wave slope is predicted and reasonable results are observed.

• Journal of the Korean Society for Heat Treatment
• /
• v.6 no.4
• /
• pp.237-242
• /
• 1993

The fatigue behaviors of mechanically alloyed Al-4Mg alloys dispersed with either $Al_2O_3$ or $MgAl_2O_4$ oxide particles were investigated. This study maily concerned with the role of coherency of dispersed particles with the matrix on the fatigue behavior of the alloys. The $MgAl_2O_4$ which has a spinel structure with the lattice parameter of exactly the twice of Al showed the habit relation with the matrix. The mechanically alloyed Al-4Mg alloys showed stable stress responses with fatigue cycles from start to failure regadless of strain amplitudes and of existence of dispersoids. The Al-4Mg alloy dispersed with $MgAl_2O_4$ showed not only the better static mechanical properties but also the better low cycle fatigue resistance than that with $Al_2O_3$, i.e., much higher plastic strain energy dissipated to failure, at low strain amplitude. However, this alloy showed inferior fatigue resistance to that dispersed with $Al_2O_3$ or that without dispersion at high strain amplitude. These results imply that $MgAl_2O_4$ may promote lowering the stacking fault energy of the alloy inherited from the coherency with the matrix so that dislocations shuttle back and forth on the same slip plane without cross slipping to other planes during fatigue at low strain amplitude resulting in long fatigue life.