• Tribology and Lubricants
• /
• v.29 no.2
• /
• pp.85-90
• /
• 2013

The effects of contact pressure on the sliding wear behavior of mild steel in a pin-on-disc type apparatus were investigated. Sliding wear tests were conducted with various combinations of the load and apparent area of contact. The wear behavior of mild steel as a function of sliding speed was independent of contact pressure. However, the wear rate at different sliding speeds was influenced by the load regardless of the apparent area of contact. This was attributed to the fact that there may be no difference in the real area of contact for any combination of the load and apparent area of contact.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1997.04a
• /
• pp.608-613
• /
• 1997

This study discusses the developmentof hydraulic rotary actuator design technology for industriol machinery and earthmoving equipment. The lubrication and wear analysis of sliding components of the machinery are very important parameters to sterngth the design technique. The analysis and were test are performed for the selected materials of the above mentioned coupled sliding members using the experimental results. One can selsct the better combination of sliding components.

• Journal of the Korean Society for Heat Treatment
• /
• v.12 no.2
• /
• pp.136-144
• /
• 1999

The study on the wear characteristics of compound layers formed during gaseous nitrocarburising in the medium carbon boron steels and the plain carbon steel has been carried out by using a pin-on-disc type wear test machine under the oil lubricating condition at room temperature and by varying applied loads, sliding speeds and wear distances. Values of friction coefficient measured at the sliding speed of 0.4m/sec under the oil lubricating condition have been shown to decrease considerably with increasing applied load and become gradually a constant value as load is increased to a higher value, showing that the transition load for friction coefficient appears at an applied load of 247.2N. The length and volume wear rates of compound layer have been revealed to relatively constantly increase, also showing that the wear life per unit thickness of compound layer turns out to be superior as porous layer has a denser and thinner appearance. As the sliding speed increases during wear test performed by varying sliding speed at a load of 63.2N under the oil lubricating condition for medium carbon boron steel nitrocarburised in gas atmosphere, the wear rate has been found to increase, the friction coefficient to decrease and the wear life per unit thickness of compound layer to decrease considerably.

• Korean Journal of Materials Research
• /
• v.15 no.4
• /
• pp.224-232
• /
• 2005

Dry sliding wear behavior of electro-pressure sintered Fe-Ni and Co-Fe-Ni compacts was investigated. Pin-on-disk wear tests were performed on the sintered Fe-Ni, Co-Fe-Ni disk specimens against alumina $(Al_2O_3)$ and silica $(SiO_2)$ ball counterparts at various loads ranging from 3N to 12N. A constant sliding speed of 0.1m/sec was employed. Wear rate was calculated by dividing the weight loss measured after the test by specific gravity and sliding distance. Worn surfaces and cross sections of them were examined by a scanning electron microscopy, and wear mechanism of the compacts was investigated. Wear characteristics of the compacts were discussed as a function of composition of the compacts. Relationship between the wear rate and mechancial properties of the compact was explored, and effects of the oxide layer that was formed on wearing surface of the compacts on the wear were also studied.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.16 no.3
• /
• pp.121-126
• /
• 2006

HVOF thermal spray coating of Co-alloy T800 is progressively replacing the classical hard coatings such as chrome plating because of the very toxic $Cr^{6+}$ ion known as carcinogen causing lung cancer. For the study of the possibility of replacing of chrome plating, the wear properties of HVOF Co-alloy T800 coatings are investigated using the reciprocating sliding tester both at room and at an elevated temperature of $1000^{\circ}F\;(538^{\circ}C)$. The possibility as durability improvement coating is studied for the application to the high speed spindles vulnerable to frictional heat and wear. Wear mechanisms at the reciprocating sliding wear test are studied for the application to the systems similar to the sliding test such as high speed spindles. Wear debris and frictional coefficients of T800 coatings both at room and at an elevated temperature of $1000^{\circ}F\;(538^{\circ}C)$ are drastically reduced compared to those of non-coated surface of parent substrate Inconel 718. This study shows that the coating is recommendable for the durability improvement coatings on the surfaces vulnerable to frictional heat. The sliding surfaces are weared by the mixed mechanisms such as oxidative wear, abrasion by the sliding ball slurry erosion by the mixture of solid particles and small drops of the melts and semi-melts of the attrited particles cavitation by the relative motions among the coating, sliding ball, the melts and semi-melts. and corrosive wear. The oxide particles and the melts and semi-melts play roles as solid and liquid lubricant reducing the wear and friction coefficient.

• Transactions of Materials Processing
• /
• v.20 no.7
• /
• pp.479-484
• /
• 2011

Dry sliding wear behavior of AISI 52100 steel that has a pearlite or bainite microstructure was characterized to explore the effect of microstructure on the wear of the steel. Isothermal heat treatments were employed to obtain the different microstructures. Pin-on-disk type wear tests of the steel disk were performed at loads of 25~125N in air against an alumina ball. Sliding speed and wear distance used were 0.1m/sec and 300m, respectively. Worn surfaces, wear debris and cross-sections of the worn surfaces were examined with SEM to investigate the wear mechanism of the steel. Hardness of the steel was also evaluated. Wear rate of the steel was correlated with the hardness and the microstructure. On the whole, wear resistance increased with an increase in hardness. However, the pearlite microstructure showed superior wear resistance as compared to the bainite microstructure with a similar hardness. The effect of the microstructure on the wear rate was attributed to the morphological differences of the carbide in the microstructure, which was found to have a significant effect on strain hardening during the wear.

• Transactions of Materials Processing
• /
• v.26 no.6
• /
• pp.365-371
• /
• 2017

During sling wear of a ferrous metal, a surface layer is formed. Its microstructure, constituting phases, and mechanical property are different from those of the original wearing material. Since wear occurs at the layer, it is important to characterize the layer and understand how wear rate changes with different layers. Various layers are formed depending on external wear conditions such as load, sliding speed, counterpart material, and environmental conditions. In this research, sliding wear tests of pure iron were carried out against two different counterparts (AISI 52100 bearing steel and $Al_2O_3$) in the air and in an inert Ar gas atmosphere. Pure iron was employed to exclude other effects from secondary phases in steel on the wear. Wear tests were performed at room temperature. Worn surfaces, wear debris, and cross-sections were analyzed after the test. It was found that these two different counterparts and environments produced diverse layers, resulting in significant changes in wear rate. Against the bearing steel, pure iron showed higher wear rate in an Ar atmosphere due to severe adhesion than that in the air. On the contrary, the iron showed much higher wear rate in the air against $Al_2O_3$. Different layers and wear rates were analyzed and discussed by oxidation, severe plastic deformation, and adhesion at wearing surfaces.

• Journal of Korea Foundry Society
• /
• v.14 no.5
• /
• pp.447-454
• /
• 1994

Wear resistance and wear mechanism of hypereutectic Al-($15{\sim}40$)wt%Si alloys were investigated. Primary Si particles under $20{\mu}m$ size were formed in hypereutectic Al-Si alloy powders due to rapid solidification. But the Si particles of extruded bars were finely distributed in smaller size than that of atomized powders. The wear mechanism of hypereutectic Al-Si alloys was divided into three types of wear phenomena, which were abrasive wear, delamination wear and severe adhesive wear according to sliding speed and load. At low sliding speed and load, wear mechanism was abrasive wear, so Al-15wt%Si alloy showed the best wear resistance. At high sliding speed and load, wear mechanism was adhesive wear, and Al-40wt%Si alloy showed the best wear resistance.

• Journal of Korea Foundry Society
• /
• v.24 no.4
• /
• pp.202-208
• /
• 2004

Effects of Co addition on sliding wear properties of multi-component white cast iron were investigated. The microstructures of multi-component white cast iron containing from 0%Co to 10%Co exhibited little difference. However, the hardness increased with an increase of the Co content. Increasing the Co content, wear properties were improved and the iron oxide on worn surface was increased in the low sliding speed range of the steady-state wear region. Hence, Co addition was effective to improve the wear properties of multi-component white cast iron by accelerating the corrosive wear as well as the enhancement effect of hardness.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1999.03b
• /
• pp.144-148
• /
• 1999

The relationship between oxidation and sliding wear behavior of Fe-28 at%. Al alloys with B2 ordered structure has been investigated. Sliding wear tests of the alloys have been carried out under various environmental conditions using a pin-on-disk wear tester. The wear rate of the ordered alloys in an oxygen atmoshpere was found to be much lower than in an oxygen atmosphere showed that Fe2O oxides formed on the wearing surface. The oxide layer prevented direct contact of the two mating materials and therefore improved wear resistance of the Fe-Al intermetallic alloy. It was found that the surface Al2O3 oxide layer which provides good oxidation resistance and improved mechanical properties broke down easily and didnot function properly as an oxidation barrier.