• Journal of the Korean Society for Precision Engineering
• /
• v.26 no.2
• /
• pp.101-108
• /
• 2009

A fretting wear test rig for dry ambient condition, which employs a piezoelectric actuator, has been developed. It is driven and loaded in a very simple manner with acceptable experimental accuracy. By using the rig, Inconel 690 tube has been tested under the normal load of 10 and 15N with sliding amplitude of less than $100{\mu}m$ during $10^6$cycles. The wear resistance of the material has been characterized in terms of the wear coefficient based on the work rate model. SEM micrographs show the complex structures of the scars, which consist of risen peaks, plate-type thin layers and locally exposed bare surfaces. The cracks spread over the layers give clue to the fretting wear mechanism of the material.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.23 no.6 s.165
• /
• pp.952-960
• /
• 1999

The effects of binder on the mechanical properties of the preforms and metal matrix composites (MMCs) were studied. Fibers were $9Al_2O_3{\cdot}2B_2O_3(Alborex)$, HTZ and $Al_2O_3$ fibers(Saffil) and binders were organic binder, inorganic binder, polyacrylamide under various PH conditions. Compressive strength of the preform increased with the addition of inorganic binder. The polyacrylamide did not improve the permeability of the preforms. PH of the slurry should be controlled because it affects the viscosity of the slurry. Good preforms were obtained under following conditions : 3 wt% inorganic binder, 0.1 wt% organic binder, 0.1 wt% polyacrylamide and PH 9. Tensile tests of MMCs were conducted at $20^{\circ}C,\;150^{\circ}C,\;250^{\circ}C,\;350^{\circ}C$ using MTS(100KN USA). Wear tests were conducted under various sliding speeds. High temperature($250^{\circ}C$) tensile strengths of Alborex/Saffil/AC8A and HTZ/AC8A are 80% and 75% of the room temperature tensile strengths respectively. The tensile and wear properties of the Alborex/Saffil/AC8A are superior to that of the HTZ/AC8A. The wear behavior of HTZ/AC8A shows more orthotropic characteristic than that of Alborex/Saffil/AC8A.

• Journal of Welding and Joining
• /
• v.12 no.4
• /
• pp.102-109
• /
• 1994

The thick and hard alloyed layer was formed on the surface of Aluminum Cast Alloy(AC2B) by PTA overlaying process with Cr, Cu and Ni metal powders under the condition of overlaying current 150A, overlaying speed 150mm/min and different powder feeding rate 5-20g/min. The characteristics of hardening and were resistance of alloyed layer have been investigated in relation to microstructure of alloyed layer. As a result, it was made clear that Cu powder was the most superier one in three metal powders used due to an uniform hardness distribution of Hv 250-350, good wear resistance and freedom from cracking in alloyed layer of which microstructure consisted of hypereutectic. On the contrary, irregular hardness distribution was usually obtained in Cr or Ni alloyed layers of which hardness was increased as Cr or Ni contents and reached to maximum hardness of about Hv 400-850 at about 60wt% Cr or 40wt% Ni in alloyed layer. However the cracking occurred in these alloyed layers with higher hardness than Hv 250-300 at more than 20-25wt% of Cr or Ni contents in alloyed layer. Wear rate of alloyed layer was decreased to 1/10 in Cu alloyed layer and 1/5 or 1/3 in Cr or Ni alloyed layer with same hardness of about Hv 300 in comparison with that of base metal at higher sliding speed.

• Journal of Korea Foundry Society
• /
• v.14 no.5
• /
• pp.471-479
• /
• 1994

Al-2%Si-2%Mg alloy containing SiC particle in 20, $70{\mu}m$ were prepared by mean of squeeze casting with various pressure 50, 100, 150 and 220MPa respectively. The specimens were made by casting into $50{\Phi}{\times}100{\ell}$ mold under various squeeze conditions(pressures, pressurizing temperature, particle sizes). Mechanical properties(hardness, tensile strength, elongation and wear characteristics) were evaluated at room temperature with those various fabrication factors. It became feasible to make favorable Al-SiCp composite free from casting defects by the injection of Ar gas during melting and 100MPa pressure squeeze casting. However, pressure of 50MPa was not sufficient to avoid completely porosity formation as a result of precessing and shrinkage during solidification. As the particle size is smaller and the squeeze pressure is higher, the hardness and tensile strength at room temperature are higher. Cell size became smaller gradually with increase of squeeze pressure. With increase of squeeze pressure(MPa), wear behaviors of those composites were changed from adhesive into abrasive wear, and the tendency of above behavior became outstanding with increasing sliding speed. The chemical reaction(4Al＋3SiC${\rightarrow}$$Al_4C_3+3Si$) is more accelerated at interface between SiCp and matrix with increase of squeeze pressure. Therefore $Al_4C_3$ intercompound and Si peak intensity is increased at interface.

• Journal of the Korean Society for Heat Treatment
• /
• v.5 no.2
• /
• pp.122-132
• /
• 1992

This study has been performed to investigate into some effects of the power density and traverse speed of laser beam on the optical microstructure, hardness and wear characteristics of medium carbon low alloy steel treated by laser surface hardening technique. The results obtained from the experiment are summarized as follows : (1) Optical micrograph has shown that finer lath martensite is formed and the amount of undissolved complex carbides increases as the traverse speed increases under the condition of a given power density, whereas the coarsening of lath martensite and the reduction of undissolved complex carbides occur with increasing the power density at a given traverse speed. (2) Hardness measurements have revealed that as the traverse speed increases, hardness values of outermost surface layer more of less decrease under low power densities, but are uniformly distributed under high power densities, also showing that they are uniformly distributed at low traverse speeds and more or less decrease at high traverse speeds with increasing the power density. (3) The effective case depth has been found to decrease from 0.26 mm to 0.17 mm with increasing the traverse speed from 1.5 m/min to 3.0 m/min at a given power density of $25.48{\times}10^3w/cm^2$ and to increase from 0.20 mm to 0.36 mm with increasing the power density from $19.11{\times}10^3w/cm^2$ to $38.22{\times}10^3w/cm^2$ at a given traverse speed of 2.0 m/min. (4) Wear test has exhibited that the amount of weight loss of laser surface hardened specimen with respect to sliding distance at a given load increases with increasing traverse speed at a given power density and decreses with increasing power density at a given traverse speed.

• Journal of Drive and Control
• /
• v.11 no.2
• /
• pp.30-35
• /
• 2014

The pumps of electro-hydrostatic actuators operate most frequently in boundary lubrication speed range, as they compensate for the position control errors as a control element. When conventional swash plate type piston pumps are applied to electro-hydrostatic actuators, the frictional power losses as well as the wear rate of sliding components, such as piston shoes can increase drastically under the boundary friction condition. In this paper, the power losses of the piston shoes were investigated which were engendered by a frictional solid-to-solid contact and leakage flow rate of their hydrostatic bearing. In order to reduce them, DLC-coating was applied to the swash plate and the ball joint of pistons along with its effects were demonstrated. In addition, it was also shown that the wear rate of the piston shoes could be markedly reduced using the DLC-coated swash plate.

• 제어로봇시스템학회:학술대회논문집
• /
• 1997.10a
• /
• pp.261-264
• /
• 1997

A contactless eddy current type braking system is developed to take advantages of the recent brake system which uses hydraulic force can show high efficiency in a certain velocity region, but not in a high velocity region, and has initial response delay time and pressure build-up time which make stopping distance longer. These are the limits of mechanical brake system of a contact type, which makes a concept brake system required. So, in this paper, the contactless brake system .of a inductive current type is chosen instead of hydraulic brake system. This brake system can be used almost forever for being no wear and contributed to lightening weight of a vehicle. Besides, the contactless brake system can be used as that of electric or solar car with anti-lock brake system. The analysis of induced electromotive force and braking torque obtained with theoretical approximate model, the design of a braking system and a nonlinear controller, and the results of simulation of the ABS, experiment are included.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.28-28
• /
• 2003

고온가압소결(Hot Pressing) 된 다이아몬드 공구용 Co-Fe, Co-Ni계 금속본드의 상온 건식 미끄럼 마멸시험을 행하고, 조성에 따른 각 본드의 마멸 특성을 비교하고 마멸 기구를 규명하였다. 미끄럼 마멸시험은 pin-on-disk 형태의 마멸시험기를 사용하여 각 조성의 성분, 적용하중 그리고 마멸상대재를 변수로 상온, 대기 중에서 실시되었다. 마멸속도는 마멸시험 전후의 시편의 무게 감량을 이론밀도와 거리로 나누어 계산되었다. 마멸기구의 규명을 위하여 시험된 시편의 마멸면과 마멸단면을 SEM과 EDS를 이용하여 분석하였다. 시험 결과 Co-Fe system의 경우 그 마멸속도는 마멸상대재의 영향보다는 Fe 첨가에 따른 시편의 미세조직과 기계적 성질의 차이에 따라 크게 변화하였다. 그러나 Co-Ni system의 마멸속도는 마멸 상대재에 따라 크게 변화하는 것이 관찰되었다. $Al_2$O$_3$를 상대재로 마멸된 경우에는 마멸속도가 시편/상대재 접촉면에서 형성되는 산화층의 영향을 크게 받았고, glass bead(83% SiO$_2$)를 상대재로 한 경우에는 시편의 경도와 마멸속도는 서로 반비례하였다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.26-26
• /
• 2003

본 연구에서는 누적압연접합공정(ARB)을 통하여 5052 알루미늄 합금의 결정립을 약 0.2$\mu\textrm{m}$ 크기로 미세화 하였다. 누적압연에 의한 변형량 증가에 따른 미세 조직 변화와 결정립 간의 상대적인 방위각 차이를 TEM을 이용하여 관찰하였다. 누적 변형량을 함수로 상온 인장특성을 분석하였고, 초미세립 소재를 후속 열처리한 후 미세 조직 변화를 관찰하여 제조된 초미세립 소재의 열적 안정성을 평가하였다. 상온 대기 중에서 pin-on-disk 형태의 마멸시험기를 사용하여 초미세립 소재의 미끄럼 마멸시험을 변형량과 하중을 변수로 행하였다. 강소성 변형에 의해 제조된 5052 알루미늄 합금 소재의 마멸저항성은 강소성 변형 전과 비교하여 소재의 경도가 크게 증가하였음에도 불구하고 오히려 감소하였다. 마멸시험 후 마멸면의 SEM, 마멸단면의 OM 관찰과 마멸면 직하의 깊이에 따른 경도측정을 통하여 초미세립 소재의 마멸기구를 분석하였고 마멸표면의 변형 층을 관찰하였다. 또한 마멸면 직하 조직의 TEM 관찰을 통해서 마멸시험 중의 미세 조직 변화를 연구하였다.

• Tribology and Lubricants
• /
• v.21 no.6
• /
• pp.272-277
• /
• 2005

Continuously variable transmission (CVT) of toroidal type has a elliptical shape of contact zone under the elastohydrodynamic lubrication (EHL) condition, where the power is transmitted only by shearing the lubricant. Due to the small contact area of elliptical shape, the traction of the shear behaviors of lubricant over the contact zone is under extremely high contact pressure over 1.0GPa. During the power transmission by shearing the fluid, many kinds of mechanical movements occur such as squeezing, sliding, rolling and spin. Among the movements, the spin effect that is the most undesirable contact behavior in transmitting the power frequently makes significant abnormal wear damage. In this work, the analysis of elliptical contact of EHL with spin effect is performed, which will give very useful information to understand the traction behaviors in toroidal type of CVT system.