• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1997.04a
• /
• pp.53-61
• /
• 1997

The effect of sintering condition on tribological behavior in the Cu-base sintered friction materials was studied through pin-on-disk type wear tester. Especially, the experiment was focused on making a comparative study between presstwed sintering and pressureless sintering. Pressureless sintering process showes more stable friction coefficient and lower wear rate than pressure sintering process. This result is related to pore size and density of pore in the sintered materials.

• Journal of Powder Materials
• /
• v.7 no.4
• /
• pp.218-227
• /
• 2000

It is well known that the Cu-Cr alloys are very difficult to be made by conventional sintering methods. This difficulty originates both from limited solubility of Cr in the Cu matrix and from limited sintering temperature due to high vapor pressures of Cr and Cu components at the high temperature. Densification of Cu-50%Cr Powder compacts by conventional Powder metallurgy Process has been studied. Three kinds of sintering methods were tested in order to obtain high-density sintered compacts. Completely densified Cu-Cr compacts could be obtained neither by solid state sintering method nor by liquid phase sintering method. Both low degree of shrinkage and evolution of large pores in the Cu matrix during the solid state sintering are attributed to the anchoring effect of large Cr particles, which inhibits homogeneous densification of Cu matrix and induces pore generation in the Cu matrix. In addition, the effect of undiffusible gas coming from the reduction of Cu-oxide and Cr-oxide was observed during liquid phase sintering. A two-step sintering method, solid state sintering followed by liquid phase sintering, was proved to have beneficial effect on the fabrication of high-dendsity Cu-Cr sintered compacts. The sintered compacts have properties similar to those of commercial products.

• Journal of Powder Materials
• /
• v.1 no.2
• /
• pp.190-197
• /
• 1994

The densification behavior during a sintering of M2 and T15 grade high speed steel powder compacts was reported. Sintered densities over 98% theoretical were achieved by a liquid phase sintering in vacuum for both grades. The optimum sintering temperature range where full densification could be achieved without excessive carbide coarsening and incipient melting was much narrower in M2 than in T15 grade. The sintering response was mainly affected by the type of carbides present. The primary carbides in M2 were identified as $M_6C$ type whereas those in T15 were MC type which provides wider sintering range. The addition of elemental carbon up to 0.3% lowered the optimum sintering temperature for both grades, but had little effect on expanding the sintering range and sintered structure.

• Journal of the Korean Ceramic Society
• /
• v.36 no.11
• /
• pp.1198-1204
• /
• 1999

The effect of sintering atmosphere on the grain sizes and phase distributions in 3Y-ZrO2 and 8Y-ZrO2 was investigated O2 and N2 were used as sintering atmospheres. In the case of 3Y-ZrO2 the sintered density was higher in N2 than in O2 while in the case of 8Y-ZrO2 contrary results were obtained. The observation can be explained by the nitrogen solubility into the zirconia lattice. That is nitrogen gas can behave as a diffusive gas contrary to the behavior in other oxides depending on the amount of Y2O3. In 3Y-ZrO2 tetragonal phase was retained at room temperature irrespective of sintering atmospheres. Grain sizes of two specimens were below 2㎛ and larger in O2 thin in N2 Under a given stress the transformability of tetragonal phase into monoclinic phase was higher in O2 than N2. The results are discussed on the basis of an effect of the grain size and non-transformable ttragonal(t') phase.

• Bulletin of the Korean Chemical Society
• /
• v.32 no.11
• /
• pp.3952-3958
• /
• 2011

The effect of sintering temperature on the electrochemical property of $LiMn_2O_4$ was investigated. Results showed that the particle size was increased at higher sintering temperatures while the initial capacity was decreased after high temperature sintering. Capacity fading, on the other hand, was suppressed at lower sintering temperatures since the sintering at higher temperatures (${\geq}800^{\circ}C$) increased the Mn ions with a lower oxidation state ($Mn^{+3}$), which induced structural instability during cycling due to dissolution of Mn ions into the electrolyte. In particular, $LiMn_2O_4$ sintered above $830^{\circ}C$ showed severe capacity fading (capacity loss was 38% of initial capacity) by lower coulombic efficiency due to the abnormally increased particle size.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.557-558
• /
• 2006

In all conventional sintered PM products, the pores present are of two types, primary and secondary. Primary pores forming during compaction and latter during sintering, due to penetration of formed liquid through the matrix grain boundary. Effect of carbon addition on diffusion of Cu in SH737-2Cu system was investigated. After compaction and transient liquid phase sintering at $1120^{\circ}C$ and $1180^{\circ}C$, samples were characterized for densification, showing rise in sintering density and reduction in swelling on carbon addition. Quantitative microstructural characterization (shape factor and pore size) revealed bimodal distribution for 0% carbon, more rounded pores for 0.9% carbon and higher sintering temperature, and pore coarsening at higher sintering temperature.

• The Journal of Advanced Prosthodontics
• /
• v.16 no.1
• /
• pp.25-37
• /
• 2024

PURPOSE. To investigate the effect of sintering programs and surface treatments on surface properties, phase transformation and flexural strength of monolithic zirconia. MATERIALS AND METHODS. Zirconia specimens were sintered using three distinct sintering programs [classic (C), speed (S), and superspeed (SS)] (n = 56, each). One sample from each group underwent scanning electron microscopy (SEM) and grain size analysis following sintering. Remaining samples were divided into five subgroups (n = 11) based on the surface treatments: control (CL), polish (P), glaze (G), grind + polish (GP), and grind + glaze (GG). One sample from each subgroup underwent SEM analysis. Remaining samples were thermally aged. Monoclinic phase volume, surface roughness, and three-point flexural strength were measured. Monoclinic phase volume and surface roughness were analyzed by Kruskal-Wallis and Dunn tests. Flexural strength was analyzed by two-way ANOVA and Weibull analysis. The relationships among the groups were analyzed using Spearman's correlation analysis. RESULTS. Sintering program, surface treatment, and sintering × surface treatment (P ≤ .010) affected the monoclinic phase volume, whereas the type of surface treatment and sintering × surface treatment affected the surface roughness (P < .001). Type of sintering program or surface treatment did not affect the flexural strength. Weibull analysis revealed no significant differences between the m and σ_o values. Monoclinic phase volume was positively correlated with surface roughness in the SGG and SSP groups. CONCLUSION. After sintering monolithic zirconia in each of the three sintering programs, each of the surface treatments can be used. However, for surface quality and aging resistance, G or GG can be recommended as a surface finishing method.

• Journal of Powder Materials
• /
• v.18 no.6
• /
• pp.562-567
• /
• 2011

This paper reports the effect of sintering processes and additives on the microstructures and mechanical properties of $ZrB_2$-SiC composite ceramics. We fabricated sintered bodies of $ZrB_2$-20 vol.% SiC with or without sintering additive, such as C or $B_4C$, densified by spark plasma sintering as well as hot pressing. While almost full densification was achieved regardless of sintering processes or sintering additives, significant grain growth was observed in the case of spark plasma sintering, especially with $B_4C$. With sintered bodies, mechanical properties, such as flexural strength and Vickers hardness, were also examined.

• Journal of Powder Materials
• /
• v.10 no.3
• /
• pp.181-185
• /
• 2003

Resistance sintering under ultra-high pressure if developed to fabricate W-Cu composite containing 5 to 80v/o copper. The consolidation was carried out under pressure of 6 to 8 GPa and input power of 18 to 23 kW for 50 seconds. The densification effect and microstructure of these W-Cu composites are investigated. The effect of W particle size on ,sintering density was also studied. The micro hardness was measured to evaluate the sintering effect.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.276-277
• /
• 2006

In order to accelerate the sintering of Al-Bronze powder covered with passive oxide film, we focused on the way to add Al-Ca fluoride consisting of $AlF_3$ and $CaF_2$, examined the effect of the $CaF_2$ mixing rate in Al-Ca fluoride, the amount of the added Al-Ca fluoride and the sintering temperature on sintering properties of Al-Bronze powder and considered the mechanism of the sintering acceleration. Al-Bronze powder was sintered most effectively by adding Al-Ca fluoride with the $CaF_2$ mixing rate of 20mass%. If the amount of added fluoride was over 0.05mass% and the sintering temperature was over 1123K, the sintering acceleration of the Al-Bronze powder appears. Regarding the mechanism of the sintering acceleration, it was presumed that $Al_2O_3$ film on the surface of the Al-Bronze particles was removed in the process of the formation of gaseous AlOF by the reaction with $AlF_3$, and the reaction was accelerated further by the presence of the liquid phase which is formed in Al-Ca fluoride.