• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1990년도 추계학술대회 논문집
• /
• pp.71-77
• /
• 1990

This paper is studied on the sintering characteristics of Ni-Zn ferrites. The specimen ferrites was composed of 20 mol% NiO, 30mol% ZnO, 50 mol% Fe$_2$O$_3$, and 0.0025 mol%, 0.005 mol%, 0.01 mol% Nb$_2$O$\_$5/, Bi$_2$O$_3$, V$_2$O$\_$5/, wee used as minor additives. Sintering was carried out at 1100$^{\circ}C$. As results from the experiments, the high value of initial permeability of 6X10$^2$∼9X10$^2$ can be achieved at 500KHz∼1000KHz. The value of loss factor 1X10￣$^2$∼2X10$^2$ can be achieved at 500KHz∼1000KHz. The lowest 1/(${\mu}$XQ) value was obtained in the specimen with the addition of 0.005mol% fracyion for V$_2$O$\_$5/.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집
• /
• pp.438-441
• /
• 2001

In this study, microstructure and piezoelectric characteristics of PNW-PMN-PZT ceramics manufactured using attrition milling method were investigated. Sintering temperature of the ceramics was varied from 1180$^{\circ}C$ to 1240$^{\circ}C$ .With increasing sintering temperature, dielectric constant was increased. In the specimen sintered at 1120$^{\circ}C$, electromechemical coupling factor(Kp) and density showed the maxinum values of 0.546 and 7.78(g/$\textrm{cm}^2$), respectively In the specimen sintered at 1160$^{\circ}C$, mechanical quality factor(Qm) also showed the maximum value of 1,943.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.274-275
• /
• 2007

In this study, in order to develop low temperature sintering ceramics for multilayer piezoelectric actuator application. At the PMN-PZN-PZT ceramics, the influence of the ball-mill time on piezoelectric characteristics was investigated. All the specimens improved according to the increase of the ball-mill time increase. The specimen showed the optimum value when ball-mill time is 60 hour. Their optimum values were density=$7.93g/m^3$, ${\varepsilon}_r=1371$, kp=0.551, Qm=1609, $d_{33}=321pC/N$, respectively.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2007년도 제38회 하계학술대회
• /
• pp.1337-1338
• /
• 2007

In this study, in order to develop low temperature sintering ceramics for multilayer piezoelectric actuator, 0.07Pb$(Mn_{1/3}Nb_{2/3})O_{3}-xPb(Ni_{1/3}Nb_{2/3})O_{3}-(0.93-x)Pb(Zr,Ti)O_{3}$ ceramics system were fabricated using $Li_{2}CO_{3}-Bi_{2}O_{3}$-CuO sintering aids and the specimens were sintered at $930^{\circ}C$. Thereafter their piezoelectric and dielectric characteristics were investigated with the amount of PNN substitution. At 9[mol%] PNN substitution, electromechanical coupling factor (kp), mechanical quality factor (Qm) and piezoelectric constant ($d_{33}$) showed the optimum value of 0.60, 1323 and 387pC/N, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 하계학술대회 논문집 Vol.6
• /
• pp.344-345
• /
• 2005

The characteristics of varistors based on M.Matstuokas with one another ZnO powder (50nm, 100nm, 300nm) have been investigated. The optimum calcination and sintering temperature was also selected for each samples. Varieties of sintering conditions were found according to powder size. As the result of analysises on each operating voltages. We obtained the most high voltage in a sample with 50nm ZnO powder.

• 한국전기전자재료학회논문지
• /
• 제17권5호
• /
• pp.492-496
• /
• 2004

In this study, (0.96 －x)(PSN-PZT)－xBF－0.04 PNW＋0.3wt%MnO$_2$＋0.6wt%CuO ceramics were fabricated with the variations of the amount of BiFeO$_3$substitution and sintering temperature for the development of modified ceramics which can be sintered in the low temperature($\leq$100$0^{\circ}C$ ), and their microstructural, dielectric and piezoelectric characteristics were investigated. As the amount of BiFeO$_3$ substitution was increased, the density, mechanical quality factor(Q$_{m}$) and electromechanical coupling factor(k$_{p}$) showed the maximum value at each of sintering temperature. At sintering temperature of 98$0^{\circ}C$ and BiFeO$_3$substitution of 2 mol%, the density, dielectric constant and electromechanical coupling factor(k$_{p}$) showed the maximum value of 7.84 g/㎤, 1415 and 0.49, respectively. And at sintering temperature of 95$0^{\circ}C$ and BiFeO$_3$substitution of 3mol%, mechanical quality factor showed the maximum value of 1062. 1062.

• E2M - 전기 전자와 첨단 소재
• /
• 제8권2호
• /
• pp.158-164
• /
• 1995

Solid solutions Sr$_{2}$(Ta$_{1-x}$ Nb$_{x}$)$_{2}$O$_{7}$, (x=0.0-1.0), composed of strontium tantalate(Tc=-107.deg. C) and strontium-niobate(Tc=1342.deg. C) were prepared by the conventional mixed oxide method and the flux method(molten salt synthesis method). Phase relation, sintering temperature, grain-orientation and dielectric properties for sintered ceramic samples were investigated with different compositions. Both Curie temperature and dielectric constant at Curie temperature were increased, and sintering behavior and the degree of grain-orientation were improved with the increase of Nb content. The single phase Sr$_{2}$(Ta/sib 1-x/Nb$_{x}$)$_{2}$O$_{7}$ powder was synthesized by using the flux method at lower temperatures, and sintering temperature was also reduced by using the flux method-derived powder than using the mixed oxide-derived powder. Sintering characteristics and dielectric properties of the specimens prepared by the flux method were better than those derived through the conventional mixed oxide method.thod.hod.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 추계학술대회 논문집
• /
• pp.255-256
• /
• 2007

In the study, in order to develop low temperature sintering ceramics for multilayer piezoelectric actuator, PMN-PNN-PZT ceramics were fabricated using $Na_2CO_3,\;Li_2CO_3$ as sintering aids and their dielectric and piezoelectric properties were investigated according to the variations of $MnO_2$ as additives and sintering aids. At the sintering temperature of $900^{\circ}C$ and 0.1wt% $MnO_2$ as sintering aids, density, electromechanical coupling factor$(k_p)$, mechanical quality factor$(Q_m)$, piezoelectric constant$(d_{33})$, and dielectric constant $({\varepsilon}_r)$ showed the optimum value of $7.87[g/cm^3]$, 0.61, 1131, 1127 and 376, respectively, for multilayer piezoelectric actuator application.

• 한국해양공학회지
• /
• 제20권5호
• /
• pp.77-81
• /
• 2006

In this study, monolithic liquid phase sintered SiC (LPS-SiC) was made by the hot pressing method with nano-SiC powder, whose particle size is 30 nm and less on the average. Alumina ($Al_{2}O_{3}$), yttria ($Y_{2}O_{3}$), and silica ($S_{i}O_{2}$) were used for sintering additives. To investigate the effects of $S_{i}O_{2}$, the $Al_{2}O_{3}/Y_{2}O_{3}$ composition was fixed and the ratio of $S_{i}O_{2}$ was changed, with seven different ratios tested. And to investigate the effects of the sintering temperature, the sintering temperature was changed, with $1760^{\circ}C,\;1780_{\circ}C$, and $1800_{\circ}C$ being used with a $S_{i}O_{2}$ ratio of 3 wt%. The materials were sintered for 1 hour at $1760^{\circ}C,\;1780^{\circ}C$ and $1800^{\circ}C$ under a pressure of 20 MPa. The effects on sintering from the sintering system used, as well as from the composition of the sintering additives, were investigated by density measurements. Mechanical properties, such as flexural strength, were investigated to ensure the optimum conditions for a matrix of SiCf/SiC composites. Sintered densityand the flexural strength of fabricated LPS-SiC increased with an increase in sintering temperature. Particularly, the relative density of a sintered body at $1800^{\circ}C$ with a non-content of $S_{i}O_{2}$, a specimen of AYSO-1800, was 95%. Also, flexural strength was about 750MPa.

• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2006년 창립20주년기념 정기학술대회 및 국제워크샵
• /
• pp.162-165
• /
• 2006

In this study, Liquid Phase Sintered SiC (LPS-SiC) was fabricated by hot pressing method with $\beta$-SiC powder whose a particle size is 30nm and less on the average in argon condition at 1780 and $1800^{\circ}C$ under 20MPa. Alumina ($Al_2O_3$), yttria ($Y_2O_3$) and silica ($SiO_2$) were used for sintering additives. To investigate effects of particle-size and temperature on $SiO_2$, LPS-SiC was fixed $Al_2O_3$, $Y_2O_3$ and then particle-size of $SiO_2$ were changed as two kinds. The system of particle-size and temperature on sintering additives which affects a property of sintering os well os the influence depending on particle-size and temperature of sintering additives were investigated by measurement of sintering properties. Such as measurement of sintering density, vikers hardness and observing of microstructure were investigated to make sure of the optimum condition which is about matrix of $SiC_f/SiC$ composites. Base on the composition of sintering additives, microstructure and sintering property correlation, the effect of particle-size of sintering additives are discussed. An experimental method to investigate the dynamic characteristics of bums in extreme environmental condition is established.