• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.6 no.2
• /
• pp.102-111
• /
• 1997

This paper deals with the machinability based on turning of WC-Co allows with the coated and the sintered diamond tools. The main conclusions obtained are as follows. (1) When machining WC-10%Co alloy, the flank wear of sintered diamond tool increases more largely with the increase of cutting speed in comparison with coated diamond tool. The tool wear decreases with the increase of the grain size and nose radius of sintered diamond tool. (2) When machining WC-20%Co alloy, the tool wear and cutting force decrease with the decrease of rake angle. Their exists a certain cutting speed range to exhibit the smallest tool wear in machining the WC-20%Co alloy, and this critical cutting speed becomes higher by 2 times in the case of coated diamond tool compared with sintered diamond tool. (3) The machinability becomes better with the increase of Co content. The effects of cutting speed and feed rate on the roughness of machined surface become smaller with the increase of Co content.

• The Korean Journal of Ceramics
• /
• v.3 no.3
• /
• pp.169-172
• /
• 1997

Sintered diamond/(WC-Co) composites were prepared by spark plasma sintering technique. Tribological properties were measured at temperatures from RT to $500^{\circ}C$ in sliding tests with alumina ball. They show coefficient of friction of 0.1 and below at RT and wear of the diamond composites is hardly detected. Effects of diamond grit size, diamond content and test temperature on the coefficient of friction and the wear are discussed. The wear scars were analyzed.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 1996.03a
• /
• pp.41-46
• /
• 1996

In this study, unsintered and pre-sintered low purity alumina ceramics were machined with various tools to clarify the machinability, optimum tool materials and optimum cutting conditions. The main conclusions obtained were as follows. (1)In the case of dry cutting, the sintered diamond and natural diamond tools exhibit better performance in machining of the ceramic pre-sintered at lower temperature, and the tool lives of both tools in machining the ceramics pre-sintered at high temperature becomes extremely short. (2)The performance of CBN tool becomes better in dry machining of the ceramics pre-sintered at higher temperature. (3)When the pre-sintered ceramics were wet machined with sintered diamond, the tool life becomes considerably long, and higher cutting speed can be used than in the case of the CBN and ceramic tools, the tool lives becomes shorter at wet cutting than at dry cutting, especially exhibiting extremely short tool life in wet cutting with ceramic tool.

• Journal of Korea Foundry Society
• /
• v.12 no.4
• /
• pp.317-325
• /
• 1992

Diamond is the hardest material known to humans, also possesses the highest thermal conductivity and a very low thermal expansion coefficient. Therefore, these properties of diamond make them logical choices for many difficult grinding application. Bonding material is a very important factor to performance of a grinding wheel. Grinding glass constitutes one of the major application areas of diamond grinding wheels, and Cu-Sn tin bronze matrix is widely used as a metal bond of diamond wheel in grinding glass but these studies are rarely reported. The bronze test pieces excluding diamond are sintered by the method of hot sizing respectively at $600^{\circ}C$, $650^{\circ}C$, $700^{\circ}C$, with a composition(Cu-10wt%Sn) on ${\alpha}$ phase and two compositions(Cu-20wt%Sn and Cu-23wt%Sn) on ${\alpha}+{\beta}$ phase. The rupture strength of Cu-10wt%Sn is highest. The bronze bonded diamond wheels are manufactured by same conditions as the bronze test pieces. The results of grinding ratio of wheels are highest in case of Cu-10wt%Sn bonded wheel sintered at $650^{\circ}C$ and grinding power is highest in same composition sintered at $700^{\circ}C$.

• Laser Solutions
• /
• v.11 no.2
• /
• pp.8-14
• /
• 2008

Sintered specimen which used for a blade of diamond tool was manufactured in order to verify $CO_2$ laser weldability depend on sintered temperature. Five kind of specimen were prepared and the range of temperature is from $600^{\circ}C$ to $1000^{\circ}C$ at intervals of $100^{\circ}C$. As a result of the sintered density test, the porosity rate appeared in the range of $2.1%{\sim}21.4%$. After welding, the most segments had exceeds the minimum fracture stress (600MPa, The Standard Safety of Europe) at the welding strength test except on the sintered at $600^{\circ}C$. In case of the sintered at $700^{\circ}C$, even satisfied the safety allowable stress but cannot get the good quality for bead appearance because of humping defect. In the conclusion, we could know that it showed not only relatively soundness bead but also enough welding strength when the sintered blade of diamond tool is included less than 4% of porosity rate.

• Journal of the Korean Society of Industry Convergence
• /
• v.23 no.1
• /
• pp.25-32
• /
• 2020

Generally, high-temperature, high-pressure, high-priced sintering equipment is used for diamond sintering, and conductivity is a problem for improving the surface modification of the sintered body. In this study, to improve the efficiency of diamond sintering, we identified a new process and material that can be sintered at low temperature, and attempted to develop a composite thin film that can be discharged by doping boron gas to improve the surface modification of the sintered body. Sintered bodies were sintered by mixing Si and two diamonds in different particle sizes based on CIP molding and HIP molding. In CVD deposition, CVD was performed using WC-Co cemented carbide using CH₄ and H₂ gas, and the specimen was made conductive using boron gas. According to the experimental results of the sintered body, as the Si content is increased, the Vickers hardness decreases drastically, and the values of tensile strength, Young's modulus and fracture toughness greatly increase. Conductive CVD deposited diamond was boron deposited and discharged. As the amount of boron added increased, the strength of diamond peaks decreased and crystallinity improved. In addition, considering the release processability, tool life and adhesion of the deposition surface according to the amount of boron added, the appropriate amount of boron can be confirmed. Therefore, by solving the method of low temperature sintering and conductivity problem, the possibility of solving the existing sintering and deposition problem is presented.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 1996.03a
• /
• pp.170-176
• /
• 1996

A Sintered carbide roller mold for reflectors which is used for cover of automobile lamp and beacon plate of highway has been developed. The geometry of sintered carbide roller mold has been determined from the analysis of reflector geometry. An acute angle diamond wheel and dressing system also has been designed and developed to manufacture the sintered carbide roller mold.

• Journal of the Korean Ceramic Society
• /
• v.30 no.5
• /
• pp.420-426
• /
• 1993

The machinability of ceramics has been experimentally studied. The experiments were conducted on alumina cernmics of various purity, quartz, and cordierite using the sintered diamond tools and CBN tools. Tool wasre, surface roughness, and cutting resistence were measured and analysed. It was found that the workpieces could be machined with the diamond and CBN tools, but the sintered diamond tools were more efficient for the machining of the high strength ceramics. The machining of alumina ceramics with sintered diamond tools showed that (1) wet machining prolonged tool life comparing with dry machining, (2) workpiecewith higher purity had better surface roughness, (3) severe cutting conditions led to the chipping and fracture of tool and increase of the surface roughness and cutting resistance, (4) 20~40m/min of cutting speed, 0.01~0.02mm/rev of feed, and 0.1~0.2mm of cutting depth are suggested as proper cutting conditions for the high strength ceramics.

• The Korean Journal of Ceramics
• /
• v.2 no.4
• /
• pp.212-215
• /
• 1996

This paper focuses the strength and wear resistance of CVD diamond films. The strength of free-standing CVD diamond films synthesized by microwave plasm CVD, DC plasma CVD, RF plasma CVD and arc discharge plasma jet CVD has been measured by three-point bending test. The wear resistance of CVD diamod films has been evaluated by the pin-on-disk type testing. diamond films coated on the base of sintered tungsten carbide pin by hot filament CVD have been rubbed with a sintered diamond disk in muddy water. Volume removed wear of CVD diamond has been compared with stellite, WC alloy and bearing steel.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.5 no.2
• /
• pp.73-82
• /
• 1996

A simtered carbide roller mold for reflector which is used for coverof automobile lamp and beacon plate of highway has been developed. The geometry of sintered carbide roller mold has been determined from the analysis of reflector geometry. An acute angle diamond wheel and dressing system also has been designed and developed to manufacture the sintered carbide roller mold.