• Journal of the Korean Ceramic Society
• /
• v.26 no.2
• /
• pp.267-275
• /
• 1989

YBa2Cu3O7-x oxide superconductors were fabricated by sintering and hotisostatic pressing (HIP), and their microstructures and properties were compared with each other. Thougha part of the second phase was observed along grain boundaries, their structures were consisted of single (123) phase and they had many porosities. But, porosities were remakably reduced by Hiping and the densification was brought about. The structure of (123) compound also showed a number of twins, which are typical of high Tc superconductors. The on-set temperature of YBa2Cu3O7-x compound sintered at 96$0^{\circ}C$ in oxygen and hipped at 88$0^{\circ}C$ was highest, but that shwoed 0 resistance at 87$^{\circ}$K, which is a little lower than the compound sintered at 96$0^{\circ}C$. HIP treatment also increased the critical current density of as-sintered compound. However, its value was low, which may be ascribed to the many pores of starting-sintered compact and partially to the second phase along grain boundaries.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.136-137
• /
• 2006

Crack initiation and short crack propagation was studied on the polished notched surfaces of Cr-Mo prealloy sintered steels with 7.35 $g.cm^{-3}$ sintered density. An ultrasonic resonance test system operating in push-pull mode at 20 kHz and R=-1 was used. It showed that crack initiation took place in several places, small cracks growing oriented to the local pore structure rather than to stress orientation. Their growth rate is markedly higher than the corresponding one of long cracks. Finally, several microcracks join to form a dominant crack.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.555-556
• /
• 2006

The study examines hardness pattern of SH737-2Cu-.9C samples transient liquid phase sintered at different temperatures viz. $1120^{\circ}C$, $1180^{\circ}C$ and $1250^{\circ}C$, heat treated by various methods and then tempered at different temperatures. Sintered samples were characterized for density and densification parameter, and austenitized at $900^{\circ}C$, subsequently cooled by four different methods viz. annealing, normalizing, oil and brine quenching. Hardness pattern was found minimum for air cooled and maximum for brine quenched, and samples sintered at $1250^{\circ}C$ had relatively higher hardness. The O.Q and B.Q samples were then tempered at $200^{\circ}C$, $400^{\circ}C$, $600^{\circ}C$ and $700^{\circ}C$. Hardness pattern typically showed secondary hardness taking place, with maximum around $600^{\circ}C$.

• Journal of Powder Materials
• /
• v.10 no.4
• /
• pp.249-254
• /
• 2003

WC-6wt%Co hard metal powders were sintered by a 2.45 GHz multimode microwave applicator in Ar atmosphere. Microwave sintering of WC-6wt%Co powder lowered the sintering temperature and shortened the processing time in less than two hours than by a conventional method. Microstructures of the sintered specimen were studied with scanning electron microscope (SEM) and no abnormal grain growth was observed. Mechanical properties were similar to the values of the specimens sintered by a conventional method. Specimen sintered at 135$0^{\circ}C$ for 30 minutes ,hewed 99%, 20.5 GPa and 8.1 MPa$\sqrt{m}$ of theoretical density, hardness and fracture strength, respectively.

• Journal of Ceramic Processing Research
• /
• v.13 no.spc2
• /
• pp.174-176
• /
• 2012

Piezoelectric 0.93(Na0.5K0.5)NbO3-0.07BiTiO3 (NKN-BTO) ceramics were fabricated by the mixed-oxide method and their structural and dielectric properties was investigated with the variation of sintering temperature. All specimens were crystallized in the perovskite single phase without any formation of a second phase such as pyrochlore. The average grain size of the NKN-BTO specimen sintered at 1130 ℃ is 0.32 ㎛. The specimen sintered at 1100 ℃ showed the highest relative density of 98%. Electromechanical coupling factor, relative dielectric constant and dielectric loss of the NKN-BTO specimens sintered at 1110 ℃ were 0.31, 1222 and 0.02, respectively. Curie temperature of the specimen sintered at 1110 ℃ was 445 ℃.

• Journal of Ocean Engineering and Technology
• /
• v.20 no.5 s.72
• /
• pp.77-81
• /
• 2006

In this study, monolithic liquid phase sintered SiC (LPS-SiC) was made by the hot pressing method with nano-SiC powder, whose particle size is 30 nm and less on the average. Alumina ($Al_{2}O_{3}$), yttria ($Y_{2}O_{3}$), and silica ($S_{i}O_{2}$) were used for sintering additives. To investigate the effects of $S_{i}O_{2}$, the $Al_{2}O_{3}/Y_{2}O_{3}$ composition was fixed and the ratio of $S_{i}O_{2}$ was changed, with seven different ratios tested. And to investigate the effects of the sintering temperature, the sintering temperature was changed, with $1760^{\circ}C,\;1780_{\circ}C$, and $1800_{\circ}C$ being used with a $S_{i}O_{2}$ ratio of 3 wt%. The materials were sintered for 1 hour at $1760^{\circ}C,\;1780^{\circ}C$ and $1800^{\circ}C$ under a pressure of 20 MPa. The effects on sintering from the sintering system used, as well as from the composition of the sintering additives, were investigated by density measurements. Mechanical properties, such as flexural strength, were investigated to ensure the optimum conditions for a matrix of SiCf/SiC composites. Sintered densityand the flexural strength of fabricated LPS-SiC increased with an increase in sintering temperature. Particularly, the relative density of a sintered body at $1800^{\circ}C$ with a non-content of $S_{i}O_{2}$, a specimen of AYSO-1800, was 95%. Also, flexural strength was about 750MPa.

• Journal of the Korean Ceramic Society
• /
• v.53 no.2
• /
• pp.162-166
• /
• 2016

0.75BF-0.25BT ceramics were prepared by sintering at $980-1040^{\circ}C$ in air or under atmosphere powder. A sample with 1 mole %-excess $Bi_2O_3$ was also prepared to compensate for $Bi_2O_3$-evaporation. Physical and piezoelectric properties of these three samples were compared. When the sintering temperature increased from $980^{\circ}C$ to $1040^{\circ}C$, the density of the sample sintered in air decreased continuously due to Bi-evaporation. Due to the suppression of Bi-evaporation, the sample sintered under atmosphere powder had a higher density at sintering temperatures above $1000^{\circ}C$ than did the sample sintered in air. The addition of 1 mole %-excess $Bi_2O_3$ successfully compensated for Bi-evaporation and kept the density at the higher value until $1020^{\circ}C$. Grain size increased continuously when the sintering temperature increased from 980 to $1040^{\circ}C$, irrespective of the sintering atmosphere. When the sintering temperature increased, the piezoelectric constant ($d_{33}$) and the electromechanical coupling factor ($k_p$) increased for all samples. The sample with 1 mole % excess-$Bi_2O_3$ showed the highest density and the best piezoelectric properties at sintering temperature of $1020^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.26 no.3
• /
• pp.305-314
• /
• 1989

Effect of pH variation in starting solution for the making of hydroxyapatite powder was studied in relation to the sinterability of the powder and their mechanical properties of the sintered hydroxyapatite ceramics. The sinterability of hydroxyapatite powder prepared at different pH was found to be improved with increase in pH value of the starting solutions. Thus the powders prepared from the higher pH solutions including 10.5, 11.0 and 11.5 could be well densified almost upto theoretical density by firing for 1 hr at 1,00$0^{\circ}C$. But the powder based on pH 10 exhibited less sinterability even being fired at much higher temperature of 1,10$0^{\circ}C$, it gave only 90-95% of theoretical density. On the other hand the powder prepared on the lowest pH value 9.5 could not be well densified and it could obtain only 78% of theoretical density even by firing at 1,30$0^{\circ}C$ for 1hr. It was found that prismatic crystals of whitlockite were always included in the sintered bodies based on the lower pH values as a minority crystalline phase together with the major crystalline phase of hydroxyapatite and its inclusion might impair the sinterability of powder. However in the case of the higher pH, the powder contained only hydroxyapatite as a crystalline phase on sintering without any minorities. The sphere shape of crystals might help effectively the densification of the bodies. The best mechanical properties could be obtained from the body of pH 11 sintered at 1,10$0^{\circ}C$, which gave 99.5% of theoretical density, 662Kg/$\textrm{mm}^2$ of vickers hardness and 1,352Kg/$\textrm{cm}^2$ of diameteral compression strength.

• Journal of the Korean Ceramic Society
• /
• v.53 no.1
• /
• pp.99-104
• /
• 2016

High purity Si-C (99.999%) powder prepared by mechanical alloying was added to a commercial SiC powder as a sintering additive. Reaction bonded silicon carbide balls and jars with high purity (99.98%) were used for the mechanical alloying. As a result, the purity of the sintered Si-C was higher than 99.99%. When sintered at $2200^{\circ}C$ under 50 MPa pressure for 1 h, SiC containing 10 wt% of high purity Si-C showed a relative density of 95.3%, similar to the relative density of commercial SiC (95%). However, the relative density of SiC decreased to 90.6% without the additive when the applied pressure decreased to 40 MPa. In contrast, the relative density was nearly unaffected by the decrease of the pressure when using the Si-C additive. Therefore, the addition of Si-C powder promoted the densification of SiC above $2000^{\circ}C$ under 40 MPa pressure.

• Journal of Powder Materials
• /
• v.15 no.5
• /
• pp.345-351
• /
• 2008

The effects of the dopant (Mn) ratio on the microstructure and thermoelectric properties of $FeSi_2$ alloy were studied in this research. The alloy was fabricated by a combination process of ball milling and high pressure pressing. Structural behavior of the sintered bulks were systematically investigated by XRD, SEM, and optical microscopy. With increasing dopan (Mn) ratio, the density and ${\varepsilon}-FeSi$ phase of the sintered bulks increased and maximum density of 94% was obtained in the 0.07% Mn-doped alloy. The sintered bulks showed fine microstructure of ${\alpha}-Fe_{2}Si_{5}$, ${\varepsilon}-FeSi$ and ${\beta}-FeSi_2$ phase. The semiconducting phase of ${\beta}-FeSi_2$ was transformed from ${\alpha}-Fe_{2}Si_{5}+{\varepsilon}-FeSi$ phase by annealing.