• Tribology and Lubricants
• /
• 제12권4호
• /
• pp.18-27
• /
• 1996

An interlaboratory wear testing was performed in order to understand the friction behaviors and the wear mechanisms of the sintered composites. The specimens were the sintered bronze matrix composites having various contents of friction additives, friction control agents and reinforcements. The variation of the wear characteristics according to the constituents of the composites as well as the wear conditions was investigated by SEM, EPMA, OM, the hardness testing and the measurement of friction. The specimen having glass fiber as the matrix reinforcement showed a remarkable increase in wear resistance as increasing the content of glass fiber. Graphite particles in the composites exhibited the lubricating effect and also resulted in the lowering strength of the matrix. Addition of Mo powder to the composites led to the deterioration of wear properties at the room temperature, however, an enhanced wear properties were obtained in the containing Mo at an elevated temperature.

• 한국세라믹학회지
• /
• 제26권3호
• /
• pp.409-415
• /
• 1989

Si3N4-TiN electro-conductive ceramic composites with 7wt% Al2O3＋3wt% Y2O3 or 5wt% MgO as sintering aids were fabricated by pressureless sintering at 1,80$0^{\circ}C$ for 1h. The 3pt. flexural strength, KIC and Vickers hardness were measrued in order to investigate the effects of TiN on the mechanical properties. Also oxidation behavior was observed by measuring the weight gain after exposure to air at 1,10$0^{\circ}C$ for 100h. the reaction products between Si3N4 and TiN was not detected by XRD and EDS. Mechanical properties of the composites were not influenced by the addition of TiN less than 30vol%, but oxidation resistance of the composites was rapidly decreased with the amount of added TiN.

• 한국재료학회지
• /
• 제9권6호
• /
• pp.577-582
• /
• 1999

전도성 $Si_3N_4$-TiN 세라믹 복합재료를 제조하기 위해 성형체를 $1450^{\circ}C$에서 20시간 질화처리한 후 $1950^{\circ}C$에서 3.5시간 가스압소결 기술에 의해 후소결하였다. 초기 분말로 약 $10\mu\textrm{m}$로 된 상용 Si분말, 100mesh와 325mesh로된 Ti분말, 그리고 미세한 $\2.5mu\textrm{m}$ TiN분말을 사용하였다. Ti분말울 사용한 $Si_3N_4$-TiN 소결체에서 상대밀도 및 파괴인성값은 다량의 조대한 기공의 존재로 인하여 낮은 값을 보였다. 그러나 TiN분말을 사용한 $Si_3N_4$-TiN 복합체에서 파괴인성, 파괴강도 및 전기저항은 각각 $5.0MPa{\cdot}m^{1/2}$, 624MPa 그리고 $1400{\omega}cm$였다. 복합체에서 TiN 업자의 분산은 $Si_3N_4$ 업자의 조대한 봉상형태로의 성장올 방해하며 $Si_3N_4$/TiN 계면에 강한 변형장울 만든다. $Si_3N_4$-TiN 복합체의 전기전도도 및 기계적 특성을 향상시키기 위해 TiN 업자가 균일하게 분산 된 미세조직 제어가 요망된다.