• Composites Research
• /
• v.13 no.6
• /
• pp.55-62
• /
• 2000

The strength test was done for the Carbon/Carbon rotor disk which is the critical part of a carbon/carbon brake system in an operating time. The loading fixture was designed for the static strength test of a single carbon/carbon brake disk using finite element analysis. To simulate the real dynamic system in a static condition, the friction surface of the rotor disk was fixed and static load was applied to the rotor slot in the circumferential direction. The described failure mechanism of the brake disk can be described as matrix cracking occurred first at the contact surface of the rotor slot, subsequent delamination from the cracked contact surface, and the final fracture at the notch of the rotor.

• Journal of Advanced Marine Engineering and Technology
• /
• v.12 no.3
• /
• pp.57-67
• /
• 1988

Although handicapped by the inability to bridge the size gap between small laboratory sample and large engineering component, the V charpy test sample method does possess certain advantages, such as each of preparation, simplicity of test method, speed, low cost in test machinery, and low cost per test. On the other hand, the COD test method does posses advantages, which reduce the size gap between the laboratory sample and actual engineering component. Consequently, the correlation between V charpy absorbed energy and the critical COD value is required for estimating critical COD value from the simple V charpy test results. In this paper, the high tensile strength steel AH36 plate specimens having a single edge cracked notch were investigated to find out the correlation between V charpy absorbed energy and critical COD value in the welded parts under such various welding methods as shielded metal arc welding, the submerged arc welding and the electro gas welding by means of V charpy impact test and static 3-point bending test. Main results obtained are as follow ; 1. The relationships between V charpy absorbed energy Wc' and critical COD value ($\delta_c$)show; $\delta_c$=0.0065 Wc'+0.1906. 2. Ductile- brittle transition behaviours can be estimated by means of fracture appearance and general yielding behaviours. 3. The V charpy absorbed energy of SMAW is higher than that of SAW, EGW and similar relationships are obtained in the COD tests.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 2004.10a
• /
• pp.40-48
• /
• 2004

The object of this study is to investigate the effect of joinability by using acoustic emission (AE) signals and doing a pattern recognition for weld heat affected zone (HAZ) in tensile testing. This study was carried out an SWS 490A high tension steel for electric shielded metal arc welding (SMAW), $CO_2$ gas arc welding and TIG welding. And correspondingly, the root openings are 3, 4 and 2.8mm. The results of the tensile test of weld HAZ come out electric shield arc welding > $CO_2$ gas arc welding > TIG welding in case of single welding. It is believed that this is a phenomenon where difference of its root opening or base metal thickness. Also, the technique of AE is ideally suited to study variables which control time and stress dependent fracture or damage process in metallic materials.

• Journal of Welding and Joining
• /
• v.28 no.2
• /
• pp.79-83
• /
• 2010

In this study, newly developed welding consumables for EGW were welded in EH 36 TM steel plates and their welded joints were evaluated in point of mechanical properties and microstructures compared with imported consumables. Newly developed welding consumables were evaluated as good arc stability and slag fluidity, substantially the same with imported products. The tensile strength of all welded joints were sufficient to meet the requirements specified in a ship’s classification(490~640MPa) and all areas of fracture were heat affected zone(HAZ). Charpy absorbed energy values of all EG welded metals were sufficient to meet the requirements of classification(min. 34J) and those of newly developed wires were evaluated to be better than those of imported wires. As a result observing microstructures of single and tandem EG welded metals through optical and scanning electron microscope (OM&SEM), no grain boundary ferrite(PF(G)) were created in a prior austenite grain boundary and a volume fraction of a fine acicular ferrite were observed very high.

• Carbon letters
• /
• v.11 no.4
• /
• pp.285-292
• /
• 2010

Novel unsaturated polyester composites with PAN-based nanofiber, stabilized PAN nanofiber, and carbonized nanofiber webs have been fabricated, respectively, and the effects of the nanofiber web content on their electrical resistivity, the thermal stability, dynamic storage modulus, and fracture surfaces were studied. The result demonstrated that the introduction of just one single layer (which is corresponding to 2 wt.%) of the carbonized nanofiber web to unsaturated polyester resin (UPE) could contribute to reducing markedly the electrical resistivity of the resin reflecting the percolation threshold, to improving the storage modulus, and to increasing the thermal stability above $350^{\circ}C$. The effect on decreasing the resistivity and increasing the modulus was the greatest at the carbonized PAN nanofiber web content of 8 wt.%, particularly showing that the storage modulus was increased about 257~283% in the measuring temperature range of $-25^{\circ}C$ to $50^{\circ}C$. The result also exhibited that the carbonized PAN nanofibers were distributed uniformly and compactly in the unsaturated polyester, connecting the matrix three-dimensionally through the thickness direction of each specimen. It seemed that such the fiber distribution played a role in reducing the electrical resistivity as well as in improving the dynamic storage modulus.

• Macromolecular Research
• /
• v.13 no.5
• /
• pp.453-459
• /
• 2005

Natural fiber henequen/unsaturated polyester (UPE) composites were fabricated by means of a compression molding technique using chopped henequen fibers treated at various electron beam (EB) dosages. The interfacial shear strength (IFSS), dynamic mechanical properties, and thermal expansion behavior were investigated through a single fiber microbonding test, fractographic observation, dynamic mechanical analysis, and thermomechanical analysis, respectively. The results indicated that the interfacial and dynamic mechanical properties significantly depended on the level of the EB treatment irradiated onto the henequen fiber surfaces. The effect of EB treatment on the IFSS, storage modulus and fracture surface of the henequen/UPE composites agreed with each other. The results of this study also suggested that the modification of henequen fiber surfaces at 10 kGy EB is the most effective for improving the interfacial properties of the henequen/UPE composites.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.9
• /
• pp.1325-1333
• /
• 2001

Critical defects in pressure vessels and pipes are generally found in the form of a semi-elliptical surface crack, and the analysis of which is consequently an important problem in engineering fracture mechanics. Furthermore, in addition to the traditional single parameter K or J-integral, the second parameter like T-stress should be measured to quantify the constraint effect. In this work, the validity of the line-spring finite element is investigated by comparing line-spring J-T solutions to the reference 3D finite element J-T solutions. A full 3D-mesh generating program for semi-elliptical surface cracks is employed to provide such reference 3D solutions. Then some structural characteristics of the surface-cracked T and L-joints are studied by mixed mode line-spring finite element. Negative T-stresses observed in T and L-joints indicate the necessity of J-T two parameter approach for analyses of surface-cracked T and L-joints.

• Journal of Technologic Dentistry
• /
• v.33 no.1
• /
• pp.47-54
• /
• 2011

Purpose: To investigate shear bonding strength between dental zirconia ceramics with different surface treatment and metal bracket. Methods: Zirconia ceramics(LAVA, 3M ESPE, USA) were divided to 4 groups according to their surface treatment; no surface treatment(G1), sand blasting(G2), silane coating(G3), and sand blasting+silane coating(G4). Specimens were bonded to metal bracket using resin bond($Transbond^{TM}XT$, 3M Unitek, USA). Shear bond strength was measured using universal test machine(3366 INSTRON. U.S.A) with cross head speed of 1 mm/min. Microstructural investigation for fracture surface was performed after shear test. Results: Shear bonding strengths of single surface treatment groups (G2 and G3) were higher than no treatment group(G1). Combined Treatment Group (G4) showed the highest shear bond strength of 9.15MPa. Microstructural observation shows that higher shear bonding strength was obtained when debonding was occurred at metal bracket/resin interface rather than zirconia ceramic/resin interface. Conclusion: Surface treatment of zirconia is necessary to obtain higher bonding strength. Combined treatment can be more effective when surface the surfaces are kept clean and homogeneous.

• Journal of the Korean Ceramic Society
• /
• v.28 no.3
• /
• pp.189-196
• /
• 1991

Si(OC2H5)4, commercial AlN and Y2O3 powder were used as the precusor of Si3N4, AlN, Y2O3, respectively. After Si3N4 powder was synthesized by carbothermal reduction and nitridation at 135$0^{\circ}C$ for 13h in N2 atmosphere, characteristics of synthesized powder and the ceramics sintered at 178$0^{\circ}C$ for 1h under 30MPa were investigated. In order to evaluate the reliability of sintered body, Weibull modulus was investigated. Premixing of carbon black as a reduction agent had no effect on Si(OH)4 formation, and Si3N4 powder synthesized from Si(OC2H5)4 was $\alpha$-Si3N4 single phase. Mechanical properties of sintered body were measured as follows : flexural strength ; 750MPa, fracture toughness ; 3.71Mn/3/2, hardness : 17.4GPa, thermal shock resistence temperature ; $600^{\circ}C$. Flexural strength at room temperature was 750MPa and was retained up to 110$0^{\circ}C$. The Weibull modulus of sintered body was 10.7.

• The Journal of the Korean dental association
• /
• v.54 no.3
• /
• pp.198-205
• /
• 2016

The purpose of this paper was to investigate the significance of splinted and non-splinted implant-supported restorations with an internal connection for multiple consecutively missing teeth. Upon examination of the effects of fixture-abutment connection, the distribution of occlusal load was favorable in splinted implant-prosthesis with an external connection, but effect of strain distribution was not significant in splinted implant-prosthesis with an internal connection. In splinted implant-prostheses for short implants, strain distribution was not affected by the method of retention. For cement-retained prostheses, the effect of strain distribution due to splinting was not significant. In clinical studies, non-splinted prostheses with an internal connection for multiple consecutively missing teeth showed high survival rate, mild marginal bone loss, and stable periodontal condition. However, failure to achieve optimal proximal contact between single-unit prostheses may lead to food impaction, and veneer fracture may be inevitable when the framework provides inadequate support in the proximal region. In conclusion, splinted implant-prosthesis is not an indication in all cases, and clinical consideration of its use should be based on the patient's oral condition, such as location and number of implants, formation of proximal contact, canine guidance, existence of parafunctional habit, and oral hygiene, when multiple consecutively missing teeth are replaced by internal connection type implant.