• 대한안전경영과학회지
• /
• 제9권1호
• /
• pp.51-63
• /
• 2007

It is noted that the disaster such as fire, explosion, collapse has been rapidly increased caused by strength deterioration of steel structures at petrochemical plant during fire. In this regard, it is stressed out that the legal requirement for fire proofing for steel structures at petrochemical plant should be carefully reviewed since the current legal requirement such as Industrial Safety & Health Law, Architectural Law has a conflict and different way of approach. In addition, it is our point of view that the present law should be revised to consolidate into single law including engineering design criteria to reflect unreasonable legal requirement. It is further our point of view that the performance certificate for fire proofing like UL-1709, basis of maintenance should be appropriately and reasonably provided in line with global practice.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2022년도 봄 학술논문 발표대회
• /
• pp.103-104
• /
• 2022

Cracks may occur in reinforced concrete (RC) structures due to various physical and chemical factors, and the growth of cracks causes deterioration of the structure's performance. It is important to prevent the expansion of cracks through periodic diagnosis of cracks in structures. In order to enable free crack exploration even in a narrow space, a construction robot using a Mecanum wheel that can move up, down, left and right and rotate in place was designed. High-quality crack images were periodically collected through the camera, and the image fragments stored during the exploration were combined into a single photo after the exploration was completed. The robot detected cracks with a width of 0.2 mm or more on the concrete probe surface with an accuracy of about 90% or more.

• Structural Engineering and Mechanics
• /
• 제39권6호
• /
• pp.795-812
• /
• 2011

Estimation of damage probability of buildings under a future earthquake is an essential issue to ensure the seismic reliability. Fragility curves are useful tools for showing the probability of structural damage due to earthquakes as a function of ground motion indices. The purpose of this study is to compare the damage probability of R/C buildings with low and high level of strength and ductility through fragility analysis. Two different types of sample buildings have been considered which represent the building types mentioned above. The first one was designed according to TEC-2007 and the latter was designed according to TEC-1975. The pushover curves of sample buildings were obtained via pushover analyses. Using 60 ground motion records, nonlinear time-history analyses of equivalent single degree of freedom systems were performed using bilinear hysteretic model and peak-oriented hysteretic model with stiffness - strength deterioration for each scaled elastic spectral displacement. The damage measure is maximum inter-story drift ratio and each performance level considered in this study has an assumed limit value of damage measure. Discrete damage probabilities were calculated using statistical methods for each considered performance level and elastic spectral displacement. Consequently, continuous fragility curves have been constructed based on the lognormal distribution assumption. Furthermore, the effect of hysteresis model parameters on the damage probability is investigated.

• 한국기계가공학회지
• /
• 제7권2호
• /
• pp.23-30
• /
• 2008

As a basic machining process, turning is a widely used machining process in which a single-point cutting tool removes material from the surface of a rotating material. A common method of evaluating machining performance is to measure the surface roughness. In a turning operation, it is important to select cutting conditions for achieving high cutting performance. As a rule, cutting conditions can be classified into feed rate, depth of cut and insert radius. While cutting process even though cutting conditions are optimized, the average roughness can be deterioration due to wear of the cutting tool edge. In this study, the aim is to maintain the average roughness even though the cutting condition is irregularly changing within the predictable range due to the working environment. First, the surface roughness model influenced by cutting conditions is constructed based on the experimental results in a turning operation, Second, applying the sliding mode control theory to the turning operation model which is composed of the surface roughness model and the motor transfer function, the surface roughness is closed to the desired value. Finally, the effectiveness of this approach is demonstrated through the computer simulation.

• Nuclear Engineering and Technology
• /
• 제52권10호
• /
• pp.2346-2352
• /
• 2020

Dual-energy x-ray absorptiometry (DXA) is the noninvasive method to diagnose osteoporosis disease characterized by low bone mass and deterioration of bone tissue. Many global companies and research groups have developed the various DXA detectors using a direct photon-counting detector such as a cadmium zinc telluride (CZT) sensor. However, this approach using CZT sensor has some drawback such as the limitation of scalability by high cost and the loss of efficiency due to the requirement of a thin detector. In this study, a SiPM based DXA system was developed and its performance evaluated experimentally. The DXA detector was composed of a SiPM sensor coupled with a single LYSO scintillation crystal (3 × 3 × 2 ㎣). The prototype DXA detector was mounted on the dedicated front-end circuit consisting of a voltage-sensitive preamplifier, pulse shaping amplifier and constant fraction discriminator (CFD) circuit. The SiPM based DXA detector showed the 34% (at 59 keV) energy resolution with good BMD accuracy. The proposed SiPM based DXA detector showed the performance comparable to the conventional DXA detector based on CZT.

• Current Applied Physics
• /
• 제18권12호
• /
• pp.1534-1539
• /
• 2018

SnSe single crystal showed a high thermoelectric zT of 2.6 at 923 K mainly due to an extremely low thermal conductivity $0.23W\;m^{-1}\;K^{-1}$. It has anisotropic crystal structure resulting in deterioration of thermoelectric performance in polycrystalline SnSe, providing a low zT of 0.6 and 0.8 for Ag and Na-doped SnSe, respectively. Here, we presented the thermoelectric properties on the K-doped $K_xSn_{1-x}Se$ (x = 0, 0.1, 0.3, 0.5, 1.5, and 2.0%) polycrystals, synthesized by a high-temperature melting and hot-press sintering with annealing process. The K-doping in SnSe efficiently enhances the hole carrier concentration without significant degradation of carrier mobility. We find that there exist widespread Se-rich precipitates, inducing strong phonon scattering and thus resulting in a very low thermal conductivity. Due to low thermal conductivity and moderate power factor, the $K_{0.001}Sn_{0.999}Se$ sample shows an exceptionally high zT of 1.11 at 823 K which is significantly enhanced value in polycrystalline compounds.

• 한국전기전자재료학회논문지
• /
• 제32권2호
• /
• pp.165-173
• /
• 2019

Lithium anodes (13, 15, 17, and 20 wt% Li) were fabricated by mixing molten lithium and iron powder, which was used as a binder to hold the molten lithium, at about $500^{\circ}C$ (discharge temp.). In this study, the effect of applied pressure and lithium content on the discharge properties of a thermal battery's single cell was investigated. A single cell using a Li anode with a lithium content of less than 15 wt% presented reliable performance without any abrupt voltage drop resulting from molten lithium leakage under an applied pressure of less than $6kgf/cm^2$. Furthermore, it was confirmed that even when the solid electrolyte is thinner, the Li anode of the single cell normally discharges well without a deterioration in performance. The Li anode of the single cell presented a significantly improved open-circuit voltage of 2.06 V, compared to that of a Li-Si anode (1.93 V). The cut-off voltage and specific capacity were 1.83 V and $1,380As\;g^{-1}$ (Li anode), and 1.72 V and $1,364As\;g^{-1}$ (Li-Si anode). Additionally, the Li anode exhibited a stable and flat discharge curve until 1.83 V because of the absence of phase change phenomena of Li metal and a subsequent rapid voltage drop below 1.83 V due to the complete depletion of Li at the end state of discharge. On the other hand, the voltage of the Li-Si anode cell decreased in steps, $1.93V{\rightarrow}1.72V(Li_{13}Si_4{\rightarrow}Li_7Si_3){\rightarrow}1.65V(Li_7Si_3{\rightarrow}Li_{12}Si_7)$, according to the Li-Si phase changes during the discharge reaction. The energy density of the Li anode cell was $807.1Wh\;l^{-1}$, which was about 50% higher than that of the Li-Si cell ($522.2Wh\;l^{-1}$).

• Journal of Korean Neurosurgical Society
• /
• 제50권3호
• /
• pp.216-223
• /
• 2011

Objective : The purposes of this study are to estimate postoperative survival and ambulatory outcome and to identify prognostic factors thereafter of metastatic spinal tumors in a single institute. Methods : We reviewed the medical records of 182 patients who underwent surgery for a metastatic spinal tumor from January 1987 to January 2009 retrospectively. Twelve potential prognostic factors (age, gender, primary tumor, extent and location of spinal metastases, interval between primary tumor diagnosis and metastatic spinal cord compression, preoperative treatment, surgical approach and extent, preoperative Eastern Cooperative Oncology Group (ECOG) performance status, Nurick score, Tokuhashi and Tomita score) were investigated. Results : The median survival of the entire patients was 8 months. Of the 182 patients, 80 (44%) died within 6 months after surgery, 113 (62%) died within 1 year after surgery, 138 (76%) died within 2 years after surgery. Postoperatively 47 (26%) patients had improvement in ambulatory function, 126 (69%) had no change, and 9 (5%) had deterioration. On multivariate analysis, better ambulatory outcome was associated with being ambulatory before surgery (p=0.026) and lower preoperative ECOG score (p=0.016). Survival rate was affected by preoperative ECOG performance status (p<0.001) and Tomita score (p<0.001). Conclusion : Survival after metastatic spinal tumor surgery was dependent on preoperative ECOG performance status and Tomita score. The ambulatory functional outcomes after surgery were dependent on preoperative ambulatory status and preoperative ECOG performance status. Thus, prompt decompressive surgery may be warranted to improve patient's survival and gait, before general condition and ambulatory function of patient become worse.

• Structural Engineering and Mechanics
• /
• 제76권6호
• /
• pp.687-708
• /
• 2020

Openings in steel plate shear walls (SPSWs) are usually used for decorative designs, crossing locations of multiple utilities and/or structural objectives. However, earlier studies showed that generating an opening in an SPSW has a negative effect on the cyclic performance of the SPSW. Therefore, this study proposes tripling or doubling the steel-sheet-plate (SSP) layer and stiffening the opening of the SPSW to provide a solution to undesirable opening effects, improve the SPSW performance and provide the infill option of potential strengthening measures after the construction stage. The study aims to investigate the impact of SSP doubling with a stiffened opening on the cyclic behaviour, expand the essential data required by structural designers and quantify the SPSW performance factors. Validated numerical models were adopted to identify the influence of the chosen parameters on the cyclic capacity, energy dissipation, ductility, seismic performance factors (SPF) and stiffness of the suggested method. A finite Element (FE) analysis was performed via Abaqus/CAE software on half-scale single-story models of SPSWs exposed to cyclic loading. The key parameters included the number of SSP layers, the opening size ratios corresponding to the net width of the SSP, and the opening shape. The findings showed that the proposed assembly method found a negligible influence in the shear capacity with opening sizes of 10, 15, 20%. However, a deterioration in the wall strength was observed for openings with sizes of 25% and 30%. The circular opening is preferable compared with the square opening. Moreover, for all the models, the average value of the obtained ductility did not show substantial changes and the ultimate shear resistance was achieved after reaching a drift ratio of 4.36%. Additionally, the equivalent sectional area of the SSP in the twin and triple configuration of the SPSWs demonstrated approximately similar results. Compared with the single SSP layer, the proposed configuration of the twin SSP layer with a stiffened opening suggest to more sufficiency create SSP openings in the SPSW compared to that of other configurations. Finally, a tabular SPF quantification is exhibited for SPSWs with openings.

• 한국산업융합학회 논문집
• /
• 제25권6_3호
• /
• pp.1147-1154
• /
• 2022

Now that the development of autonomous driving is progressing, LiDAR has become an indispensable element. However, LiDAR is a device that uses lasers, and laser side effects may occur. One of them is the much-talked-about eye-safety, and developers have been satisfying this through laser characteristics and operation methods. But eye-safety is just one of the problems lasers pose. For example, irradiating a laser with a specific energy level or higher in a dusty environment can cause deterioration of the dust particles, leading to a sudden explosion. For this reason, the dust ignition proof regulations clearly state that "a source with a pulse period of less than 5 seconds is considered a continuous light source, and the average energy does not exceed 5 mJ/mm 2 or 35 mW" [2]. Energy of output optical power is limited by the law. In this way, the manufacturer cannot define the usage environment of the LiDAR, and the development of a LiDAR that can be used in such an environment can increase the ripple effect in terms of use in application fields using the LiDAR. In this paper, we develop a LiDAR with low optical power that can be used in environments where high power lasers can cause problems, evaluate its performance. Also, we discuss and present one of the directions for the development of LiDAR with laser power limited by dust ignition proof regulations.