[ $YBa_2Cu_3O_{7-{\delta}}$ ] superconductor films have been prepared on silver substrates by electrophoretic deposition. As silver does not react with $YBa_2Cu_3O_{7-{\delta}}$ compound and has little influence on its superconductivity, it is usually doped in $YBa_2Cu_3O_7$ to improve the strength of the material and eliminate micro cracks. It has been proved that Ag additive can lower the melting temperature of $YBa_2Cu_3O_{7-{\delta}}$ and act as linking bridge among $YBa_2Cu_3O_{7-{\delta}}$ particles, thus in this paper Ag doped $YBa_2Cu_3O_{7-{\delta}}$ thick films are prepared by electrophoretic co deposition. As there are only some referenced experience formula and models for co electrophoretic deposition and does not exist unified explanation, the behavior of Ag particles during co electrophoretic deposition is also studied.

• Archives of Metallurgy and Materials
• /
• 제64권3호
• /
• pp.913-916
• /
• 2019

For the reliable applications of silver nanowires, AgNW, which is used as a conductive transparent film in electronic devices, the isothermal degradation behaviors of AgNW films with and without overcoating were investigated. Accelerated isothermal degradation was performed as a function of temperature, time, and atmosphere. Electrical resistance and optical transmittance were measured and correlated with the microstructural damages, such as formation of oxide particles and fragmentations of AgNW, which were quantitatively determined from the scanning electron micrographs. The overcoating retarded the formation of oxide particles and subsequent fragmentations as well as resulting degradation in electrical resistance without affecting the optical transmittance.

• 대한화학회지
• /
• 제53권6호
• /
• pp.761-764
• /
• 2009

은 콜로이드 용액을 이용하여 은이 침적된 생체활성 세라믹 복합체를 제조하였다. 제조된 은 콜로이드 용액과 생체활성 세라믹 복합체의 물리적 특성은 각각 X-선 회절분석기, 라만분광기, 전자현미경으로 분석하였다. X-선 회절분석 자료에 의하면 은 나노입자의 표면에 염소이온이 화학적으로 결합한다는 사실을 알 수 있었다. 또한 전자현미경 분석에서는 은이 침적된 생체활성 세라믹 복합체의 표면에 염화은이 균일하게 분포하는 것을 알 수 있었다. 따라서 생체활성 세라믹 복합체 표면의 염화은이 생체활성 세라믹 복합체의 하이드록시아파타이트 형성을 강하게 방지한다는 사실을 확인할 수 있었다.

• 방사선산업학회지
• /
• 제4권4호
• /
• pp.353-357
• /
• 2010

Silver nanoparticles (AgNPs) can be used in the areas such as integrate circuit, cell electrode and antimicrobial deodorant. In this study, AgNPs have been prepared by using $AgNO_3$ aqueous solution in the carboxymethyl cellulose (CMC) hydrogel. CMC powders were dissolved in deionized water, and then irradiated by a gamma-ray with a radiation dose of 50 kGy to make CMC hydrogel. CMC hydrogels were dipped into $1.0{\times}10^{-2}M$ $AgNO_3$ solution for 1 hour. After that, the swollen hydrogels were irradiated by gamma-ray for the formation of AgNPs. The characteristics of silver nanoparticles in the CMC hydrogels were monitored by UV-Vis and the morphological study and dispersed coefficient of particles were investigated by FE-SEM/EDX. It was observed that the sodium salt in the CMC is crucial to the formation of silver nanoparticle. Finally, antibacterial tests indiacted that the hydrogel containing silver nanoparticle has antibacterial activity.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2005년도 International Meeting on Information Displayvol.II
• /
• pp.1491-1494
• /
• 2005

We have studied ink-jet printing method for patterning conductive line on flexible plastic substrates. Synthesized silver nano-particles of ${\sim}$20nm were used for the conductive ink and the printed patterns exhibit a smooth line whose linewidth is below 100 ${\mu}m$. This ink-jet printing technique can be applied to flexible displays and electronics.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2007년도 춘계학술발표대회 및 제12회 신소재 심포지엄
• /
• pp.13.1-13.1
• /
• 2007

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2009년 추계학술발표대회
• /
• pp.217-220
• /
• 2009

Conductive adhesives have been investigated for use in microelectronics packaging as a lead-free solder substitute due to their advantages, such as low bonding temperature. However, high resistivity and poor mechanical behavior may be the limiting factors for the development of conductive adhesives. The metal fillers and the polymer resins provide electrical and mechanical interconnections between surface mount device components and a substrate. As metal fillers used in conductive adhesives, silver is the most commonly used due to its high conductivity and the stability. However the cost of conductive adhesives with silver fillers is much higher than usual lead-free solders and silver has poor electro-migration performance. So, copper can be a promising candidate for conductive filler metal due to its low resistivity and low cost, but oxidation causes this metal to lose its conductivity. In this study, electrically conductive adhesives (ECAs) using surface modified copper fillers were developed. Especially, in order to overcome the problem associated with the oxidation of copper, copper particles were coated with silver, and the silver-coated copper was tested as a filler metal. Especially the effect of silver coating on the electrical resistance just after curing and after aging was investigated. As a result, it was found that the electrical resistance of ECA with silver-coated copper filler was clearly lower and more stable than that of ECA with pure copper filler after curing process. And, during high temperature storage test, the degradation rate of electrical resistance for ECA with silver coated copper filler was quite slower than that for ECA with pure copper filler.

• Environmental Analysis Health and Toxicology
• /
• 제30권
• /
• pp.3.1-3.6
• /
• 2015

Objectives This study aims to evaluate the size-dependent toxicity of spherical silver nanoparticles (Ag NPs) to an endemic benthic organism, Glyptotendipes tokunagai. Methods Ag nanoparticles of three nominal sizes (50, 100, and 150 nm) capped with polyvinyl pyrrolidone (PVP-Ag NPs) were used. Their physicochemical properties, acute toxicity (48 hours), and bioaccumulation were measured using third instar larvae of G. tokunagai. Results The aggregation and dissolution of PVP-Ag NPs increased with exposure time and concentration, respectively, particularly for 50 nm PVP-Ag NPs. However, the dissolved concentration of Ag ions was not significant compared with the median lethal concentration value for $AgNO_3$ (3.51 mg/L). The acute toxicity of PVP-Ag NPs was highest for the smallest particles (50 nm), whereas bioaccumulation was greatest for the largest particles (150 nm). However, larger PVP-Ag NPs were absorbed and excreted rapidly, resulting in shorter stays in G. tokunagai than the smaller ones. Conclusions The size of PVP-Ag NPs significantly affects their acute toxicity to G. tokunagai. In particular, smaller PVP-Ag NPs have a higher solubility and stay longer in the body of G. tokunagai, resulting in higher toxicity than larger PVP-Ag NPs.

• 공업화학
• /
• 제24권6호
• /
• pp.663-667
• /
• 2013

다양한 이온성 액체를 사용하여 은이 담지된 이산화티타늄 입자를 제조하였다. 합성에 사용된 이온성 액체의 종류에 따라 입자의 물성이 변하는 것을 관찰하였다. 이는 이온성 액체의 특성이 은 입자들의 결합에 영향을 주기 때문이다. 제조된 입자의 촉매 성능을 측정하기 위하여 산소분위기에서 벤질알코올의 산화반응을 실시하였다. 그 결과 1-octyl-3-methylimidazolium tetrafluoroborate를 이용하여 합성한 $Ag/TiO_2$ 입자가 가장 우수한 촉매 활성을 나타내었다.

• Journal of Electrochemical Science and Technology
• /
• 제2권3호
• /
• pp.157-162
• /
• 2011

We report a simple route for synthesizing multi-dimensional structured silicon anode materials from commercially available bulk silicon powders via metal-assisted chemical etching process. In the first step, silver catalyst was deposited onto the surface of bulk silicon via a galvanic displacement reaction. Next, the silver-decorated silicon particles were chemically etched in a mixture of hydrofluoric acid and hydrogen peroxide to make multi-dimensional silicon consisting of one-dimensional silicon nanowires and micro-scale silicon cores. As-synthesized silicon particles were coated with a carbon via thermal decomposition of acetylene gas. The carbon-coated multi-dimensional silicon anodes exhibited excellent electrochemical properties, including a high specific capacity (1800 mAh/g), a stable cycling retention (cycling retention of 89% after 20 cycles), and a high rate capability (71% at 3 C rate, compared to 0.1 C rate). This process is a simple and mass-productive (yield of 40-50%), thus opens up an effective route to make a high-performance silicon anode materials for lithiumion batteries.