• Journal of the Korean Ceramic Society
• /
• v.40 no.9
• /
• pp.832-836
• /
• 2003

Multi-layer ceramic composites were prepared by tape casting followed by hot pressing using silicon nitride layer with silicon nitride whiskers, silicon nitride layer with silicon carbide particles and boron nitride-alumina layer. The whiskers were aligned during the casting. As the whisker content of the silicon nitride layer was increased up to 10 wt％, the flexural strength of the multi-layer composite was increased. However, further increase of the whisker content in the layer resulted in a rapid decrease of the strength of the composite. The results suggest that the strength of multi-layer ceramic composite showing non-catastrophic failure behavior can be significantly improved by incorporating the aligned whiskers in the layers.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.15 no.2
• /
• pp.61-67
• /
• 2005

In this study a new growing method of silicon nitride whiskers in the inside of large pores made intentionally during the sintering was conducted. Pore size, pore vol%, and nitrogen pressure were used as experimental variables. Silicon nitride whiskers were well grown in the inside of pores with low pore vol% range from 14 to 27 but not grown with high pore vol% such as 39 and 50. On the other hand, pore size and nitrogen pressure did not have any influence on the whisker growth. Therefore the most important factor to grow silicon nitride whisker in the inside of large pores during sintering was to make pores isolated or closed.

• The Korean Journal of Ceramics
• /
• v.5 no.2
• /
• pp.119-124
• /
• 1999

Silicon nitride ceramics with highly oriented microstructure were prepared by tape casting a slurry containing 5 wt% of the silicon nitride whiskers. The whiskers were aligned in the casting direction and worked as seeds for the grain growth. The anisotropy was observed from the sintering shrinkage, Vickers indentation crack lengths, and XRD patterns. The cracks were much longer on the surface normal to the aligned grains than on the tape casting surface where the lateral cracks were also observed. The effect of sintering additives and the annealing treatment on the indentation crack length was examined. The sample with higher silica content had longer cracks than the one with lower silica content. The crack length anisotropy increased after annealing at 2123K.

• The Korean Journal of Ceramics
• /
• v.4 no.4
• /
• pp.331-335
• /
• 1998

R-curve, of three kinds of silicon nitride-based ceramics were measured, using single edge notched beam (SENB) method at room and at elevated temperatures, up to $1200^{\circ}C$. Stable fraacture was seen on ceramic materials with SENB specimens if the machined notch is deep enough, even though the crack resistance did not increase with crack length. Hot pressed silicon nitride did not show the rising R-curve behavior at room temperature, but it showed some rising at $1000^{\circ}C$ and above. Si3N4 reinforced with SiC whiskers showed no rising behavior at room and elevated temperatures, as it has smaller grain size, compare to the monolithic specimen. Gas pressure sintered silicon nitride had very large and elongated grains, and it showed rising R-curve even at room temperature. However, it showed some creep behavior at $1200^{\circ}C$ and the calculated R-curve on this condition did not show a good result. We cannot apply this technique on this condition for obtaining the R-curve.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2005.05a
• /
• pp.92-92
• /
• 2005

• Journal of the Korean Ceramic Society
• /
• v.36 no.10
• /
• pp.1007-1015
• /
• 1999

The Si3N4 composites reinforced with carbon-coated SiC whiskers were fabricated by hot-pressing at 180$0^{\circ}C$ for 2 hours to examine the effects of carbon-coated whiskers on the mechanical properties of SiC whisker reinforced Si3N4 composites. The flexural strength of the Si3N4 composites and Si3N4 monolith respectively. The weak interfacial bond between carbon-coated SiC whiskers and Si3N4 matrix which enhances the crack deflection and whisker pull-out could contribute to the improvement of mechanical properties of the composites.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2012.05a
• /
• pp.97.1-97.1
• /
• 2012

Porous ceramics are widely used for applications such as catalysis supports, gas distributors and filters such as DPF. For these purpose, it is important to have proper porosity controlling pore structure while maintaining mechanical and thermal properties. In this work, we have prepared the porous ceramic structures made of reaction bonded silicon nitride with hierarchical pore structures. Uni-directionally aligned pore channels, which are mostly filled with ${\beta}$-Si3N4 whiskers, were achieved by an ice-templating method. The structures of the pore channels and the walls are controllable by the processing conditions, such as solid concentration, freezing rate of the slurry, and additives. We have investigated and characterized the influences of the conditions on the microstructures and the properties, such as porosity, pore size distribution, lamellar thickness, wavelength, and orientations. The compressive strength test and flow test was performed to determine the structural integrity and air permeability.

• Journal of the Korean Ceramic Society
• /
• v.36 no.4
• /
• pp.432-443
• /
• 1999

The self-toughened Si3N4 ceramics where needle-like coarse ${\beta}$-Si3N4 grains were dispersed within fine-grain-ed matrix were prepared via hot-prssing at 1730$^{\circ}C$ for 2 h using 5 vol% ${\beta}$-Si3N4 whiskers as a seed. In this study the microstructures and mechanical properties of self-toughened Si3N4 ceramics were investigated. The flexural strength of self-toughened Si3N4 ceramics was increased from 600-800 MPa of the Si3N4 monolith to 830-1025 MPa. The KIC was also increased from 4.0-5.0MPa$.$m1/2 of the Si3N4 monolith to 5.8-6.5MPa$.$m1/2$.$The needle-like coarse Si3N4 grains in self-toughened ceramics were considered to induce various toughening mechanisms including the crack deflection pull-out and bridging and to contribute to KIC improvement. In ad-dition to toughening mechanisms the KIC improvement was considered to be partially indebted also to the orien-tation of large ${\beta}$-Si3N4 grains and to the promoting effect of ${\beta}$-Si3N4 whiskers on the ${\alpha}$ to ${\beta}$ transtion.

• Journal of the Korean Ceramic Society
• /
• v.36 no.5
• /
• pp.483-489
• /
• 1999

Gas pressure sintered silicon nitride based composites with 3 wt% $\beta$-Si3N4 whiskers were prepared and change of properties according to the whisker orientation and sintering temperature was studied. The tapes with whiskers were fabricated by two different method ; conventional tape casting and a modified tape casting by using guide pins,. Orientations of the whiskers were controlled by different stacking sequences of the sheets cut from the tape. Samples were fully densified by gas pressure sintering at 2148-2273K. As the sintering temperature increased size of the large elongated grains increased. In case of unidirectional samples sintering shrinkage normal to the whisker alignment direction was larger than that of parallel to the direction and the shrinkage anisotropy increased slightly as sintering temperature increased. As sintering temperature increased the crack length parallel to whisker alignment direction became shorter but that normal to the direction did not depend on sintering temperature. In case of cross-plied samples the anisotropy of mechanical properties disappeared.

• Journal of the Korean Ceramic Society
• /
• v.36 no.5
• /
• pp.547-554
• /
• 1999

The self-reinforced Si3N4 ceramics were prepared by pressureless-sintering using ${\beta}$-Si3N4 whiskers as a seed. Effects of ${\beta}$-Si3N4 whiskers on microstructure and mechanical properties and the ${\alpha}$ to ${\beta}$ phase transition of Si3N4 were investigated. The self-reinforced Si3N4 ceramics were densified(relative density$\geq$98%) by pressureless-sintering (1800$^{\circ}C$ 2h) using 8mol% Y2O3 and 6mol% Al2O3 as sintering aids and 5 vol% ${\beta}$-Si3N4 whiskers within self-reinforced Si3N4 ceramic seemed to hinder the densification owing to their acicular shapes but accelerated the ${\alpha}$ to ${\beta}$ phase transition because they acted as pre-existing nuclei. It was found that the more ${\beta}$-Si3N4 nucei the faster ${\alpha}$ to ${\beta}$ phase transition.