• Journal of the Semiconductor & Display Technology
• /
• v.2 no.1
• /
• pp.21-24
• /
• 2003

Sludged silicon powders that are generated during silicon ingot slicing process have potential usage as silicon source in fabricating silicon carbide powders by adding carbon. A thermodynamic calculation is performed to consider a plausible formation condition for the silicon carbide powders. A thin silicon oxide layer around silicon powder is sufficient to supply equilibrium oxygen partial pressure at the formation temperature($1400^{\circ}C$) of the silicon carbide in the Si-C-O ternary system. Formation of silicon carbide by using the sludged silicon powders is more efficient than by using silicon oxide powders.

• Journal of the Microelectronics and Packaging Society
• /
• v.10 no.3
• /
• pp.67-71
• /
• 2003

Sawing silicon ingot with abrasive slurry generates sludge that includes abrasive powders, cutting oil, and silicon powders. The abrasive powders and cutting oil are being separated and reused. Mixing the remained stodged silicon powders with carbon powders and subsequent heat-treatment are conducted to produce silicon carbide. The size of SiC whiskers and powders was smaller than the conventionally grown silicon carbide whiskers that were synthesized by adding micron-size metal impurities. Impurity related mechanism is attributed to the formation of the silicon carbide whiskers, as metal impurities are contained in the stodged silicon powders.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1091-1092
• /
• 2006

Silicon nitride - silicon carbide composite was developed by using an abrasive SiC powders as a raw material. The composites were prepared by mixing abrasive SiC powder with silicon, pressing and sintering at $1400^{\circ}C$ under nitrogen atmosphere in atmosphere controlled vacuum furnace. The proportion of silicon in the initial mixtures varied from 20 to 50 wt%. After sintering, crystalline phases and microstructure were characterized. All composites consisted of ${\alpha}-Si_3N_4$ and ${\beta}-Si_3N_4$ as the bonding phases in SiC matrix. Their physical and mechanical properties were also determined. It was found that the density of the obtained composites increased with an increase in the $Si_3N_4$ content formed in the reaction.

• Journal of the Korean Ceramic Society
• /
• v.37 no.4
• /
• pp.376-380
• /
• 2000

Carbon nanofibers with an average diameter of 100nm were reacted with SiO vapor generated from a mixture of Si and SiO2 to produce silicon carbide nanofibers at temperature ranging 1200∼1500$^{\circ}C$ under vacuum. The nanofiber reacted at 1200$^{\circ}C$ for two hours consisted of silicon carbide with an average crystallite size of 10-20nm, amorphous silica and a significant amount of unreacted carbon. The surface area of silicon carbide nanofiber, obtained after removal of amorphous silica and unreacted carbon from converted carbon nanofibers at 1200$^{\circ}C$, was as high as 150㎡/g. With increasing reaction temperature to 1500$^{\circ}C$, the surface area was decreased to 14㎡/g. Growth of SiC crystallite size with increasing conversion temperature of carbon nanofiber was confirmed from Scherrer formula using the (111) diffraction line and TEM images of converted carbon nanofibers.

• Journal of the Korean Ceramic Society
• /
• v.35 no.5
• /
• pp.486-492
• /
• 1998

Silicon carbide (SiC) thin films were deposited on the porous silicon substrates by chemical vapour de-position(CVD) using MTS as a source material. The deposited films were ${\beta}$-SiC with poor crystallity con-firmed by XRD measurement. It was considered that the films showed the mixed characteistics of cry-stalline and amorphous SiC where amorphous SiC where amorphous SiC played a role of buffer layer in interface between as-dep films and Si substrate. The buffer layer reduced lattice mismatch to some extent the generally occurs when SiC films are deposited on Si. The low temperature (10K) PL (phtoluminescence) studies showed two broad bands with peaks at 600 and 720 for the films deposited at 1100$^{\circ}C$ The maximum PL peak of the crystalline SiC was observed at 600 nm and the amrophous SiC of 720 nm was also confirmed. PL peak due the amorphous SiC was smaller than that of the crystalline SiC, PL of porous Si might be disapperared due to densification during heat treatment.

• The Korean Journal of Ceramics
• /
• v.4 no.3
• /
• pp.245-248
• /
• 1998

Porous carbon fiber composites (CFCs) having variable specific surface area ranging 35~1150 $\m^2$/g were reacted to produce silicon carbide fiber composites with SiO vapor generated from a mixture of Si and $SiO_2$ at 1673 K for 2 h under vacuum. Part of SiO vapor generated during conversion process condensed on to the converted fiber surface as amorphous silica. Chemical analysis of the converted CFCs resulting from reaction showed that the products contained 27~90% silicon carbide, 7~18% amorphous silica and 3~63% unreacted carbon, and the composition depended on the specific carbide, 7~18% amorphous silica and 3~63% unreacted carbon, and the composition depended on the specific surface area of CFCs. CFC of higher specific surface area yielded higher degree of conversion of carbon to silicon and conversion products of lower mechanical strength due to occurrence of cracks in the converted caron fiber. As the conversion of carbon to silicon carbide proceeded, pore size of converted CFCs increased as a result of growth of silicon carbide crystallites, which is also linked to the crack formation in the converted fiber.

• The Korean Journal of Ceramics
• /
• v.3 no.4
• /
• pp.229-234
• /
• 1997

Silicon carbide-carbon fiber composites have been prepared by partially Infiltrating porous carbon fiber composites with liquid silicon at a reaction temperature of $1670^{\circ}C$. Reaction between molten silicon and the fiber preform yielded silicon carbide-carbon fiber composites composed of aggregates of loosely bonded SiC crystallites of about 10$\mu\textrm{m}$ in size and preserved the appearance of a fiber. In addition, the SiC/C fiber composites had carbon fibers coated with a dense layer consisted of SiC particles of sizes smaller than 1$\mu\textrm{m}$. The physical and mechanical properties of SiC/C fiber composites were discussed in terms of infiltrated pore volume fraction of carbon preform occupied by liquid silicon at the beginning of reaction. Lower bending strength of the SiC/C fiber composites which had a heterogeneous structure in nature, was attributed to the disruption of geometric configuration of the original carbon fiber preform and the formation of the fibrous aggregates of the loosely bonded coarse SiC particles produced by solution-precipitation mechanism.

• Journal of the Korean institute of surface engineering
• /
• v.47 no.6
• /
• pp.354-361
• /
• 2014

In order to utilize silicon carbide (SiC) as an inner part of fluidized bed reactor (FBR) for manufacturing poly-silicon, we have carried out the thermodynamic calculation on the overall reactions including poly-silicon synthesis and compatibility of SiC with FBR process. The resources of silicon included $SiH_4(MS)$, $SiHCl_3(TCS)$ and $SiCl_4(STC)$ and the thermodynamic yield of the FBR with MS, TCS and STC were compared each other with variable range of temperature, pressure and hydrogen to silicon ratio. The silicon yield of MS, TCS and STC were 100%, 28% and 4%, respectively, throughout the conventional FBR conditions. Silicon carbide having high hardness and strength showed strong resistance to granule collisions during the FBR process using a lab-scale reactor. And it also showed quite good compatibility with the typical FBR processes of MS and TCS resources.

• Journal of the Korean Ceramic Society
• /
• v.49 no.6
• /
• pp.561-565
• /
• 2012

Due to their unique combination of properties, Si-based ceramics, such as silicon carbide (SiC), silicon nitride ($Si_3N_4$) and silicon oxide ($SiO_2$ as fused silica), have a range of industrial applications in fields such as the chemical industry, aluminum manufacturing, oil and gas production and solar cell production. For each materials group, examples of typical applications from various industry sectors are presented while taking into account the property fingerprint.

• Korean Journal of Materials Research
• /
• v.27 no.5
• /
• pp.263-269
• /
• 2017

Fe-Si-Cr ferroalloy is predominantly produced by carbothermic reduction. In this study, silicothermic and carbothermic mixed reduction of chromite ore to produce Fe-Si-Cr alloy is suggested. As reductants, silicon and silicon carbide are evaluated by thermochemical calculations, which prove that silicon carbide can be applied as a raw material. Considering the critical temperature of the change from the carbide to the metallic form of chromium, thereduction experiments were carried out. In these high temperature reactions, silicon and silicon carbide act as effective reductants to produce Fe-Si-Cr ferroalloy. However, at temperatures lower than the critical temperature, silicon carbide shows a slow reaction rate for reducing chromite ore. For the proper implementation of a commercial process that uses silicon carbide reductants, the operation temperature should be kept above the critical temperature. Using equilibrium calculations for chromite ore reduction with silicon and silicon carbide, the compositions of reacted metal and slag were successfully predicted. Therefore, the mass balance of the silicothermic and carbothermic mixed reduction of chromite ore can be proposed based on the calculations and the experimental results.