• Journal of the Korea Institute of Building Construction
• /
• v.13 no.2
• /
• pp.139-147
• /
• 2013

The purpose of this study was to investigate the durability performance of concrete that includes rice husk ash. Chloride diffusion coefficient obtained through a rapid chloride penetration test and depth of $CO_2$ penetration obtained through a rapid carbonation test were used to evaluate latent durability. Durability characteristics for rice husk ash replacement and age were determined. Through the experiment, it was found that when the replacement ratio of rice husk ash was increased from 0% to 10%, the compressive strength of concrete containing rice husk ash was similar to that of concrete containing silica fume. This shows that the durability performance of concrete containing rice husk is excellent compared to other concretes containing admixtures.

• Advances in concrete construction
• /
• v.7 no.2
• /
• pp.75-85
• /
• 2019

The present study is focused on the mechanical and durability properties of ternary blended cement concrete mix of different grades 30 MPa, 50 MPa and 70 MPa. Three mineral admixtures (fly ash, silica fume and lime sludge) were used as a partial replacement of cement in the preparation of blended concrete mix. The durability of ternary blended cement concrete mix was studied by exposing it to acids HCl and $H_2SO_4$ at 5% concentration. Acid mass loss factors (AMLF), acid strength loss factor (ASLF) and acid durability factor (ADF) were determined, and the results were compared with the control mix. Chloride ions penetration was investigated by conducting rapid chlorination penetration test and accelerated corrosion penetration test on control mix and ternary blended cement concrete. From the results, it was evident that the usage of these mineral admixtures is having a beneficiary role on the strength as well as durability properties. The results inferred that the utilization of these materials as a partial replacement of cement have significantly enhanced the compressive strength of blended concrete mix in 30 MPa, 50 MPa and 70 MPa by 42.95%, 32.48% and 22.79%. The blended concrete mix shown greater resistance to acid attack compared to control mix concrete. Chloride ion ingress of the blended cement concrete mix was low compared to control mix implying the beneficiary role of mineral admixtures.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.2 no.4
• /
• pp.297-306
• /
• 2014

Recently nano-materials are gaining more importance in the construction industry due to its enhanced energy efficiency, durability, economy, and sustainability. Nano-silica addition to cement based materials can control the degradation of the fundamental calcium-silicate-hydrate reaction of concrete caused by calcium leaching in water as well as block water penetration and therefore lead to improvements in durability. In this paper, the influence of synthesized nano silica from locally available rice husk on the mechanical properties and corrosion resistant properties of OPC (Ordinary Portland Cement) has been studied by conducting various experimental investigations. Micro structural properties have been assessed by conducting Scanning Electron Microscopy, Thermo gravimetry and Differential Thermal Analysis, X-Ray Diffraction analysis, and FTIR studies. The experimental results revealed that NS reacted with calcium hydroxide crystals in the cement paste and produces Calcium Silicate Hydrate gel which enhanced the strength and acts as a filler which filled the nano pores present in concrete. Hence the strength and corrosion resistant properties were enhanced than the control.

• Elastomers and Composites
• /
• v.29 no.1
• /
• pp.18-29
• /
• 1994

The purpose of this study is to investigate reinforced effect between silica treated by coupling agents and rubber matrix under the configuration chemical bonds, and the effect of silica particles coated by organic polymers using aluminum chloride as the catalyst. In vulcanization characteristies were tested by Curastometer. The M-series vulcanizates were reached to the fastest optimum cure $time(t_{90})$ and R-series vulcanizates with the same formula had the shorted optimum cure times. Tensile characteristics measuring with a tensile tester revealed that the M-series vulcanizate was the best in the physical properties, such as tensile strength. In 100% modulus, however, the S-series vulcanizates appeared to be better than the other vulcanizates. Also, hardness showed the following order : S-series>R-series>M-series with the order of elongation R-series>M-series>S-series. In SEM test, shapes of chemical treated silicas were observed. The dispersion of filler in the SBR composite appeard uniformly. In RDS test for the dynamic characteristics, G' indicates that S-3 shows the highest value with the next order M-3>R-3, and the order of damping values are as followe: M-3>M-3>R-3.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2009.05b
• /
• pp.239-242
• /
• 2009

As the high-rise building increase due to the gravitation of population to big cities recently, it requires high quality and high performance of Concrete. As a result, people are keenly interested in Meta-kaolin as new admixture favorable from an economic perspective, which has strength and endurance with admixture at the same level like Silica-fume. Accordingly, as to Meta-kaolin, this study was to set by three levels like domestic one, foreign one, and Silica-fume, the water-binding material ratio 25%, and four level substitute like 0, 10, 20, and 30(%) in order to compare and analyze the quality durability of high-concrete according to the substitute of Meta-kaolin applicable with replacement of Silica-fume. As a result of performing experiment it was found that when water-binding material ratio increases, resistance of neutralization, carbonation, salt damage and sulfate decrease, and when replacement ratio of mineral admixture increases, depth of accelerating carbonation gets greater. Also, the combination of SF and MK-B favored resistance to chloride ion penetration better than MK-A, and it was found that when replacement ratio of binding material increases, the resistance to sulphuric acid increases. Therefore, based on this study, it was understood that meta-kaolin is useable in replacement of silicafume.

• Analytical Science and Technology
• /
• v.24 no.2
• /
• pp.94-104
• /
• 2011

Mesoporous silica was synthesized in a water solvent and in an ethanol solvent with the non and cationic cetyltrimethyl ammonium chloride (CTAC) by varying the amount of the amphiphilic acrylic urethane oligomer (AAU) and the pH of the solution. The adsorption of the MX (3-chloro-4 (dichloromethyl)-5-hydroxy-2-(5H)-furanone) in drinking water was studied using the synthesized mesoporous silica as an adsorbent. The most appropriate silica was synthesized in acidic conditions in the water solvent and in alkali conditions in the ethanol solvent. The average pore sizes of the synthesized mesosilica were 3 nm and more. The mesoporous silica synthesized by the addition of the AAU oligomer showed excellent adsorption characteristics. With respect to the co-surfactant, the best adsorption characteristics were obtained when the P64,a non-ionic surfactant with a high molecular weight, was used to synthesize the silica than when other co-surfactants were used. The adsorption rate decreased as the MX concentration in the water increased. Different adsorption equilibrium conditions were reached depending on the adsorbate MX concentration in the adsorbent and the solution. It was seen that perfect adsorption does not occur due to such equilibrium conditions.

• Corrosion Science and Technology
• /
• v.8 no.2
• /
• pp.74-80
• /
• 2009

The high alkaline property in the concrete pore solution protects the embedded steel in concrete from corrosion due to aggressive ions attack. However, a continuous supply of those ions, in particular, chlorides altogether with a pH fall in electrochemical reaction on the steel surface eventually depassivate the steel to corrode. To mitigate chloride-induced corrosion in concrete structures, finely grained mineral admixtures, for example, pulverized fuel ash (PFA), ground granulated blast furnace slag (GGBS) and silica fume (SF) have been often advised to replace ordinary Portland cement (OPC) partially as binder. A consistent assessment of those partial replacements has been rarely performed with respect to the resistance of each binder to corrosion, although the studies for each binder were extensively looked into in a way of measuring the corrosion rate, influence of microstructure or chemistry of chlorides ions with cement hydrations. The paper studies the behavior of steel corrosion, chloride transport, pore structure and buffering capacity of those cementitious binders. The corrosion rate of steel in mortars of OPC, 30% PFA, 60% GGBS and 10% SF respectively, with chloride in cast ranging from 0.0 to 3.0% by weight of binder was measured at 7, 28 and 150 days to determine the chloride threshold level and the rate of corrosion propagation, using the anodic polarization technique. Mercury intrusion porosimetry was also applied to cement pastes of each binder at 7 and 28 days to ensure the development of pore structure. Finally, the release rate of bound chlorides (i.e. buffering capacity) was measured at 150 days. The chloride threshold level was determined assuming that the corrosion rate is beyond 1-2 mA/$m^3$ at corrosion and the order of the level was OPC > 10% SF > 60% GGBS > 30% PFA. Mercury intrusion porosimetry showed that 10% SF paste produced the most dense pore structure, followed by 60% GGBS, 30% PFA and OPC pastes, respectively. It was found that OPC itself is beneficial in resisting to corrosion initiation, but use of pozzolanic materials as binders shows more resistance to chloride transport into concrete, thus delay the onset of corrosion.

• Advances in concrete construction
• /
• v.3 no.4
• /
• pp.317-331
• /
• 2015

This paper presents the effect of different micro-silica (MS) contents of 5, 10 and 15 wt.% as partial replacement of cement on mechanical and durability properties of high volume fly ash - recycled aggregate concretes (HVFA-RAC) containing 50% class F fly ash (FA) and 35% recycled coarse aggregate (RCA) as partial replacement of cement and natural coarse aggregate (NCA), respectively. The measured mechanical and durability properties are compressive strength, indirect tensile strength, elastic modulus, drying shrinkage, water sorptivity and chloride permeability. The effects of different curing ages of 7, 28, 56 and 91 days on above properties are also considered in this study. The results show that the addition of MS up to 10% improved the early age (7 days) strength properties of HVFA-RAC, however, at later ages (e.g. 28-91 days) the above mechanical properties are improved for all MS contents. The 5% MS exhibited the best performance among all MS contents for all mechanical properties of HVFA-RAC. In the case of measured durability properties, mix results are obtained, where 10% and 5% MS exhibited the lowest sorptivity and drying shrinkage, respectively at all ages. However, in the case of chloride ion permeability a decreasing trend is observed with increase in MS contents and curing ages. Strong correlations of indirect tensile strength and modulus of elasticity with square root of compressive strength are also observed in HVFA-RAC. Nevertheless, it is established in this study that MS contributes to the sustainability of HVFA-RAC significantly by improving the mechanical and durability properties of concrete containing 50%less cement and 35% less natural coarse aggregates.

• International Journal of Highway Engineering
• /
• v.12 no.3
• /
• pp.113-119
• /
• 2010

This study presents experimental findings on the performance of cement concrete pavement incorporating mineral admixtures such as ground granulated blastfurnace slag and silica fume. Flexural strength, compressive strength, charge passed, diffusion coefficient of chloride ions and initial surface absorption of cement concrete pavement incorporating mineral admixtures were periodically measured and the corresponding results were compared to those of plain concrete pavement. As a result, strength behaviors of concrete pavement were dependent on the types of mineral admixtures. However, it was true that incorporation of silica fume had a beneficial effect on compressive strength development. Furthermore, the application of mineral admixtures led to a lower diffusion coefficient of chloride ions compared to plain concrete pavement. Based on the experimental results, the present study would be helpful to design high-performance cement concrete pavement.

• Korean Journal of Soil Science and Fertilizer
• /
• v.16 no.1
• /
• pp.36-41
• /
• 1983

These studies were carried out to investigate the effects of potassium salts on the changes of chemical properties in submerged soil. Rice plants were cultured in submerged soil using potassium salts. Obtained results were as follows. In the submerged soil cultured with rice plants the value of pH was higher in the potassium chloride plot than in the potassium sulfate plot. The leaching of cations such as calcium, magnesium, potassium and ammonium were higher in the potassium chloride plot than in the potassium sulfate plot. On the other hand, the leaching of phosphate ion was slightly higher in the potassium sulfate plot than in the potassium chloride plot. The leaching of iron was higher in the planted plot than in the non-planted plot, but that of silica was higher in the non-planted plot than in the planted plot. However, the leaching of iron and silica was not affected by potassium salts.