• Journal of Ceramic Processing Research
• /
• 제13권spc1호
• /
• pp.145-148
• /
• 2012

Spherical silica aerogel powders were fabricated via an emulsion polymerization method from a water glass. A water-in-oil emulsion, in which droplets of a silicic acid solution are emulsified with span 80 (surfactant) in n-hexane, was produced by a high power homogenizer. After gelation, the surface of the spherical silica hydrogels was modified using a TMCS (trimethylchlorosilane)/n-hexane solution followed by solvent exchange from water to n-hexane. Hydrophobic silica wet gel droplets were dried at 80 ℃ under ambient pressure. A perfect spherical silica aerogel powder between1 to 12 ㎛ in diameter was obtained and its size can be controlled by mixing speed. The tapping density, pore volume, and BET surface area of the silica aerogel powder were approximately 0.08 g·cm-3, 3.5 ㎤·g-1 and 742 ㎡·g-1, respectively.

• 공업화학
• /
• 제22권2호
• /
• pp.209-213
• /
• 2011

낮은 열전도율, 높은 비표면적과 기공률을 갖는 소수성 실리카 에어로겔 과립을, 저가의 물유리를 실리카 전구체로 사용하고 상압건조하여 제조하였다. 별도의 과립화 첨가제 및 과립화 기구를 사용하지 않고, 산도(~5)를 변화시켜 모노리스 형태의 습윤겔을 먼저 제조하여, 용매치환/소수성화 동시공정과 상압건조공정 과정에서 습윤겔이 깨져 0.5~2 mm 크기의 과립형태 실리카 에어로겔을 제조하였다. 제조된 실리카 에어로겔 과립은 비표면적, 평균기공크기, 기공부피가 각각 $593m^2/g$, 34.9 nm, $4.4cm^3/g$으로 실리카 에어로겔 분말과 거의 유사한 다공도를 가지고 있으며, 열전도율도 $20^{\circ}C$에서 19.8 mW/mK으로 나타나 같은 조건에서 제조된 실리카 에어로겔 분말과 거의 같은 단열성을 나타내었다.