• Journal of the Korean Ceramic Society
• /
• v.40 no.6
• /
• pp.589-593
• /
• 2003

Silica based Planar Lightwave Circuits (PLC) have been applied to various kinds of wave-guided optical passive devices. SiO$_2$ (buffer) and GeO$_2$-SiO$_2$ (core) thick films have been deposited by Flame Hydrolysis Deposition (FHD). The SiO$_2$ films were produced by the flame hydrolysis reaction of halide materials such as SiCl$_4$, POCl$_3$ and BCl$_3$ into an oxy-hydrogen torch. The P concentration increased from 2.0 to 2.8 at％ on increasing the POCl$_3$/BCl$_3$ flow ratio. The refractive index increased from 1.4584 to 1.4605 on increasing the POC1$_3$/BC1$_3$ flow ratio from 0.6 to 2.6. The refractive index of GeO$_2$-SiO$_2$ films was controlled by the GeCl$_4$ flow rate. The refractive index increased from 1.4615 to 1.4809 on increasing the GeCl$_4$ flow rate from 30 to 120 sccm.

• Advances in Energy Research
• /
• v.5 no.1
• /
• pp.13-29
• /
• 2017

The roles of Na, Mn, W and silica, and the synergistic effects between each metal in the $MnNa_2WO_4/SiO_2$ catalyst have been investigated for oxidative coupling of methane (OCM). The crystallisation of amorphous silica during calcination at $900^{\circ}C$ was promoted primarily by Na, but Mn and W also facilitated this process. The interaction between Na and Mn tended to increase the extent of conversion of $Mn_3O_4$ to $Mn_2O_3$. The formation of $Na_2WO_4$ was dependent on the order in which Na and W were introduced to the catalyst. The impregnation of W before Na resulted in the formation of $Na_2WO_4$, but this did not occur when the impregnation order was reversed. $MnWO_4$ formed in all cases where Mn and W were introduced into the silica support, regardless of the impregnation order; however, the formation of $MnWO_4$ was inhibited in the presence of Na. Of the prepared samples in which a single metal oxide was introduced to silica, only $Mn/SiO_2$ showed OCM activity with significant oxygen conversion, thus demonstrating the important role that Mn plays in promoting oxygen transfer in the reaction. The impregnation order of W and Na is critical for catalyst performance. The active site, which involves a combination of Na-Si-W-O, can be formed in situ when distorted $WO_4^{2-}$ interacts with silica during the crystallisation process facilitated by Na. This can only occur if the impregnation of W occurs before Na addition, or if the two components are introduced simultaneously.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.268-268
• /
• 2012

Adsorption and desorption of toluene from bare and $TiO_2$-coated silica with a mean pore size of 15 nm was studied using breakthrough curves and temperature programmed desorption. Thicknesses of $TiO_2$ films prepared by atomic layer deposition on silica were < 2 nm, and ~ 5 nm, respectively. For toluene adsorption, both dry and humid conditions were used. $TiO_2$-thin film significantly improved toluene adsorption capacity of silica under dry condition, whereas desorption of toluene from the surface as a consequence of displacement by water vapor was more pronounced for $TiO_2$-coated samples with respect to the result of bare ones. In the TPD experiments, silica with a thinner $TiO_2$ film (thickness < 2 nm) showed the highest reactivity for toluene oxidation to $CO_2$ in the absence and presence of water. We show that the toluene adsorption and oxidation reactivity of silica can be controlled by varying thickness of $TiO_2$ thin films.

• Journal of the Korean Chemical Society
• /
• v.53 no.3
• /
• pp.233-243
• /
• 2009

We have investigated the infrared spectra for CO adsorbed on silica supported nickel(Ni-Si$O_2$), silica supported copper(Cu-Si$O_2$), silica supported nickel-copper alloys(Ni/Cu-Si$O_2$) of several compositions with varying CO pressures(0.2 $torr{\sim}$50 torr) at room temperature and on pumping to vacumn at room temperature within the frequency range of 1500 $cm^{-1}{\sim}2500\;cm^{-1}$. Four bands(2059.6 $cm^{-1},\;{\sim}$2036.5 $cm^{-1},\;{\sim}$ 1868.7 $cm^{-1},\;{\sim}$ 1697.1 $cm^{-1}$) were observed for Ni-Si$O_2$, two bands($\sim$2115.5 $cm^{-1},\;{\sim}$1743.0 $cm^{-1}$) were observed for Cu-Si$O_2$ and five bands(${\sim}2123.2\;cm^{-1}$, 2059.6 $cm^{-1},\;{\sim}$2036.4 $cm^{-1},\;{\sim}$1899.5 $cm^{-1},\;{\sim}$1697.1 $cm^{-1}$) were observed for Ni/Cu-Si$O_2$. These absorption bands correspond with those of the previous reports approximately. The bands below 1800 $cm^{-1}$ were only observed with Ni metal or Ni/Cu alloy crystal plane containing step at room temperature and the ${\sim}1697.1\;cm^{-1}$ bands observed with Ni-Si$O_2$ and Ni/Cu-Si$O_2$ may be ascribed to CO molecule adsorbed on the adsorption sites near step. The bands below 2000 $cm^{-1}$ were rarely observed with Cu metal crystal plane at room temperature and the 1743.0 $cm^{-1}$ bands may be ascribed to CO molecule adsorbed on the adsorption sites near step. The band shifts of adsorbed CO with varing Cu contents from 0 to 0.5 mole fraction at the same CO pressure or at the same pumping time to vacumn were below 21 $cm^{-1}$. and comparatively small than those with other ⅠB metal addition. It may means ligand effect of Cu d electron is small.

• KOREAN JOURNAL OF CROP SCIENCE
• /
• v.26 no.3
• /
• pp.226-232
• /
• 1981

To clarify the relationship between rice cool injury and the contents of silica and phosphorus in the soils and the rice plant, the investigation was carried out at ripening stage of rice from the different altitudes with different varieties throughout Yeongnam area. The rate of fertilized spikelets were decreased with elevation increase and the situation was distincted in the Japonica cross Indica hybrid varieties. The higher rates of $SiO_2/P_2 O_5$ content in the leaves and stems or lower rates of that in the soils show the higher fertilization rates. The result seems to be caused by the different solubility and uptakes of silica and by the different availability and transformation of phosphorus. A positive correlation was observed between the content of silica in rice plant and the fertilization rates. The fertilization rate in Japonica varieties was higher than that of Indica cross Japonica hybrid varieties in the case of the same content of silica in plant as far as observed, but the increasing rate of fertilized grains due to increase of silica content was prominented in the hybrid varieties which probably demand more silica. Within the certain limit of silica and phosphorus content in rice plant, the more uptaking of silica might lessen the cool injury.

• Bulletin of the Korean Chemical Society
• /
• v.33 no.7
• /
• pp.2369-2377
• /
• 2012

The gas-phase dehydration of glycerol to acrolein was carried out over silicotungstic acid ($H_4SiW_{12}O_{40}{\cdot}xH_2O$, HSiW) catalysts supported on $SiO_2$, ${\eta}-Al_2O_3$, and silica-aluminas with different Al contents. The HSiW catalysts supported on silica-aluminas showed higher glycerol conversions and acrolein yields during the initial 2 h at $315^{\circ}C$ than did $SiO_2$- and ${\eta}-Al_2O_3$-supported HSiW catalysts. Among the tested catalysts, HSiW/$Si_{0.9}Al_{0.1}O_x$ exhibited the highest space-time yield during the initial 2 h. The loaded HSiW species can change the acid types and suppress the formation of carbonaceous species on Al-rich silica-aluminas. The deactivated HSiW supported on silica-aluminas can be fully regenerated after calcination in air at $500^{\circ}C$. As long as the molar ratio between water and glycerol was in the range of 2-11, the acrolein selectivity increased significantly with increasing water content in the feed, while the surface carbon content decreased owing to the suppression of heavy compounds.

• Korean Journal of Materials Research
• /
• v.26 no.4
• /
• pp.182-186
• /
• 2016

Zircon, having excellent thermal, chemical, and mechanical properties, is utilized in refractory materials, electronic materials, chemical machines, structural materials, etc. However, zircon generally shows thermal dissociation to zirconia($ZrO_2$) and silica($SiO_2$) around the sintering temperature of $1540^{\circ}C$, and when zircon particles are small and impurities are present, thermal dissociation is known to occur at around $1100^{\circ}C$. This reduces the mechanical properties of $ZrSiO_4$. In this research, the effect of adding $SiO_2$ and 3Y-TZP to $ZrSiO_4$ has been studied in order to suppress dissociation and improve the mechanical properties. Addition of $SiO_2$ suppressed the dissociation of $ZrSiO_4$ at lower temperatures. It also enabled optimum packing between the particles, resulting in a dense microstructure and good mechanical properties. When 3Y-TZP was added, recombination with the dissociated $SiO_2$ resulted in good mechanical properties by suppressing the generation of pores and the densification of the microstructure.

• Bulletin of the Korean Chemical Society
• /
• v.29 no.7
• /
• pp.1320-1322
• /
• 2008

Phosphomolybdic acid supported on silica gel (PMA-$SiO_2$) is an efficient catalyst for the activation of TMSCN for the facile cyanosilylation of various aldehydes. Cyano transfer from TMSCN to aldehyde proceeds smoothly at rt in presence of 0.8 mol % of PMA-$SiO_2$ leading to a range of cyanosilylether in excellent yield (mostly over 93%) within short reaction time (30 min). The catalyst can be recovered and reused several times without loss of activity.

• Analytical Science and Technology
• /
• v.20 no.5
• /
• pp.413-418
• /
• 2007

Poly(vinylpyrrolidone) stabilized cadmium sulfide (CdS) nanoparticles were loaded onto the surface of silica ($SiO_2$) nanoparticles by using ${\gamma}$-irradiation. TEM micrograph reveals the presence of ~20nm sized CdS nanoparticles on the surface of $SiO_2$ nanoparticles. XRD patterns confirm the crystalline. PL spectra of the simple PVP-stabilized CdS nanoparticle and $SiO_2$@CdS composite confirm the differences in the emission characteristics between them. Two prominent emission peaks were noted around 550 nm and 600 nm for PVP-stabilized CdS nanoparticles). The emission peaks noted for the PVP-stabilized CdS nanoparticles were found to be blue shifted for $SiO_2$@CdS composites. Besides, an additional emission peak around 450 nm was noticed for the $SiO_2$@CdS composite. The presence of CdS nanoparticles influence the emission characteristics and induce quantum confinement effect.

• Journal of the Korean Ceramic Society
• /
• v.31 no.7
• /
• pp.695-702
• /
• 1994

Current study was undertaken to explain the structural evolution and corresponding changes in the properties of calcium aluminate glasses with the variation of SiO2 doping concentration. Calcium aluminate glasses in the compositional ranges of (100-x)(0.6CaO+0.4Al2O3)+xSiO2(where x=0~60) were fabricated. DTA analysis confirmed an anomalous behavior in glass transition temperature (Tg) with the maximum of 887$^{\circ}C$ and minimum of 859$^{\circ}C$ when x=5 and 50, respectively. densities and refractive indices monotonically decreased with increasing SiO2 content and IR transmitting cutoff shifted to shorter wavelength side when the amount of added SiO2 exceeded 5 mole%. IR fundamental vibration absorption peaks showed the change that NBOs were inclined to SiO4 tetrahedron in the low-silica region and NBO per SiO4 tetrahedra changed from 2 to 0 with increasing silica content. Based on the analysis of IR fundamental vibration absorption peaks, the model of the structural change can be proposed in three step: 1) SiO4 scavenged the NBOs located at AlO4-tetrahedra, which resulted in the increased of Tg values, 2) NBOs located in the main network again with a decrease in Tg, and 3) dominated by the decrease in the relative amount of NBOs in the glass system, where Tg re-increased.