• Journal of the Korean Ceramic Society
• /
• v.30 no.2
• /
• pp.131-138
• /
• 1993

The effects of silane coupling agents on the injection molding process were investigated using silicone nitride mixtrues with a binder system containing polypropylene as a major binder (55vol% solid loading). The formation of bonding between silicon nitride powder and coupling agents was confirmed through the analyses of powder surface. The use of coupling agents improved mixing characteristics judged by the torque change during mixing process. the coupling agents also reduced molten viscosity of the mixture considerably, which is a main factor to determine the flow of the mixture. However, the bonding between coupling agents and polymers had a negative effect on the debinding process by retarding the thermal decomposition.

• Carbon letters
• /
• v.10 no.3
• /
• pp.190-197
• /
• 2009

Various silanes, amino silane, vinyl silane, sulfur silane (TESPD), and ZS (TESPD/zinc soap complex), are added into chlorinated isobutylene-isoprene copolymer (CIIR)/soft clay/carbon black (CB) and CIIR/hard clay/CB compounds and they are investigated with respect to the vulcanization characteristics, the processability, and the mechanical properties. Comparing hard clay and soft clay filled compounds, hard clay (Suprex) filled system shows a higher die C tear than the soft clay (GK) filled one. The other properties (Mooney, extrusion torque/pressure, torque rise ($M_H-M_L$), modulus at 300%) are close to each other. Among various silanes, the ZS treated hard clay (Suprex) compound shows the highest mechanical property following hard clay(S)/vinyl silane(V) and soft clay(GK)/vinyl silane(V) compounds. The TESPD and the ZS effectively helps a formation of a strong 3-dimensional network structure between silica and CIIR via coupling reaction due to bifunctional nature of TESPD. In addition to that, the ZS added compounds show both a better processability and mechanical properties compared to the S2 ones at low concentration due to improved compatibility between zinc soap and CIIR matrix. Only the ZS added compound shows both improved processabilities (Mooney, Extrusion torque-& pressure) and improved mechanical properties (degree of crosslinking, elongation modulus, tear, and fatigue to failure counts) on both CIIR/hard clay/CB and CIIR/soft clay/CB compounds.

• Carbon letters
• /
• v.7 no.2
• /
• pp.87-96
• /
• 2006

This paper describes the physical properties of filled Nylon6 composites resin with nano-sized carbon black particle and graphite nanofibers prepared by melt extrusion method. In improving adhesions between resin and fillers, the surface of the carbon filler materials were chemically modified by thermo-oxidative treatments and followed by treatments of silane coupling agent. Crystallization temperature and rate of crystallization increased with increases in filler concentration which would act as nuclei for crystallization. The silane treatments on the filler materials showed effect of reduction in crystallization temperature, possibly from enhancement in wetting property of the surface of the filler materials. Percolation transition phenomenon at which the volume resistivity was sharply decreased was observed above 9 wt% of carbon black and above 6 wt% of graphite nanofiber. The graphite nanofibers contributed to more effectively in an increase in electrical conductivity than carbon black did, on the other hand, the silane coupling agent negatively affected to the electrical conductivity due to the insulating property of the silane. Positive temperature coefficient (PTC) phenomenon, was observed as usual in other composites, that is, temperature increase results conductivity increase. The dispersity of the fillers were excellently approached by melt extrusion of co-rotational twin screw type and it could be illustrated by X-ray diffraction and SEM.

• Carbon letters
• /
• v.19
• /
• pp.47-56
• /
• 2016

In this study, the fracture behavior of a thermoplastic-modified epoxy resin reinforced with continuous carbon fibers for two levels of fiber-matrix adhesion was performed. A carbon fiber with commercial sizing was used and also treated with a known silane, (3-glycidoxy propyl trimethoxysilane) coupling agent. Toughness was determined using the double cantilever test, together with surface analysis after failure using scanning electron microscope. The presence of polysulfone particles improved the fracture behavior of the composite, but fiber-matrix adhesion seemed to play a very important role in the performance of the composite material. There appeared to be a synergy between the matrix modifier and the fiber-matrix adhesion coupling agent.

• Proceedings of the KIEE Conference
• /
• 1989.07a
• /
• pp.353-355
• /
• 1989

Composite insulating materials have the defect of interface. To minimize the defect of interface of GFRP (glass cloth reinforced plastics), coupling agent is treated. In this paper, the method of coupling agent treatment has been studied. The result shows that the optimum electric and mechanical properties is obtained for the sample treated on the glass fiber with 0.3% amino silane water solution.

• Elastomers and Composites
• /
• v.50 no.3
• /
• pp.159-166
• /
• 2015

Silica which is used for reinforcing filler in tire industry is widely known as eco-friendly material exerting $CO_2$ reduction effect through decrease of rolling resistance and improvement of wet grip. Generally silica is classified as a highly polar filler because it contains a large number of silanol (Si-OH) group on its surface. And also silica gives a lower reinforcing effect than carbon black due to its poorer rubber-filler interaction. Therefore silica is treated with silane coupling agent or activator, then following the conventional rubber blend method, vulcanized sheets were prepared using a hot press, and cure characteristics, mechanical properties and abrasion resistance of the test specimens were investigated. It was found that with an increase in the silane coupling agent content the tensile strength, 300% modulus and abrasion resistance increased while Mooney viscosity decreased and crosslink density slightly increased with an increase of activator.

• Applied Chemistry for Engineering
• /
• v.31 no.2
• /
• pp.230-236
• /
• 2020

In this study, an adhesive tape with water and impact resistance for mobile devices was developed using a UV-curable urethane acrylate based polymer as a substrate. The substrate fabricated by UV-curable materials shows hydrophobicity and poor wettability, which significantly deteriorates the interface-adhesions between the substrate and acrylic adhesive. In order to improve the interface adhesion, 3-glycidoxy-propyl trimethoxysilane (GPTMS), a silane coupling agent having epoxy functional groups, was selected and incorporated into UV-curable urethane acrylate based polymer resins in various contents. The changes of the chemical composition according to the contents of GPTMS was studied with Fourier-transform infrared spectroscopy (FT-IR), energy-dispersive X-ray spectroscopy (EDX) and X-ray photoelectron spectroscopy (XPS) to know the surface bonding properties. Also mechanical properties of the substrate were characterized by tensile strength, gel fraction and water contact angle measurements. The peel strengths at 180° and 90° were measured to compare the adhesion between the substrate and adhesive according to the silane coupling agent contents. The mechanical strength of the urethane acrylate adhesive tape decreased as the silane coupling agent increased, but the adhesion between the substrate and adhesives increased remarkably at an appropriate content of 0.5~1 wt%.

• Elastomers and Composites
• /
• v.49 no.3
• /
• pp.239-244
• /
• 2014

Reaction between silica and silane coupling agent without solvent was investigated using transmission mode Fourier transform infrared spectroscopy (FTIR) and thermogravimetric analysis (TGA). Bis[3-(triethoxysilylpropyl) tetrasulfide] (TESPT) was used as a silane coupling agent. After removing the unreacted TESPT, formation of chemical bonds was analyzed using FTIR and content of reacted TESPT was determined using TGA. Content of the coupling agent bonded to silica increased with increase in the coupling agent content, but the oligomers were formed by condensation reaction between coupling agents when the coupling agent was used to excess. In order to identify bonds formed among silica, coupling agent, and rubber, a silica-coupling agent-BR model composite was prepared by reaction of the modified silica with liquid BR of low molecular weight and chemical bond formation of silica-coupling agent-BR was investigated. Unreacted rubber was removed with solvent and analysis was performed using FTIR and TGA. BR was reacted with the coupling agent of the modified silica to form chemical bonds. Polarity of silica surface was strikingly reduced and particle size of silica was increased by chemical bond formation of silica-coupling agent-BR.

• Journal of the Korean Society of Safety
• /
• v.16 no.1
• /
• pp.43-47
• /
• 2001

Effect of coupling agent on the mechanical properties of PP/GF blend was investigated. The flexural modulus, Izod impact strength, elongation at yield and tensile strength were improved with using coupling agent. Mopological studies revealed that PP and GF were incompatible and addition of coupling agent was very effective to enhance the compatibility, result in mechanical properties.

• Journal of Adhesion and Interface
• /
• v.14 no.1
• /
• pp.36-42
• /
• 2013

To improve hydrolytic stability of polyurethane (PU) adhesives, a silane coupling agent (SCA) was added. 3-Isocyanatopropyl triethoxy silane (ITS) as a SCA has two functional groups in the main chain and it is used to improve an interfacial interaction between polymer and inorganic material or metal. In this study, PU adhesives with different amounts of ITS from 0 to 1 wt% were synthesized. Pot time, modulus, thermal stablilty, and adhesive force of the obtained samples were measured. The results showed that the adhesives with ITS showed better properties than that of pure one.