• Carbon letters
• /
• v.10 no.2
• /
• pp.101-108
• /
• 2009

Various silanes, amino silane, vinyl silane, TESPD, and ZS (TESPD/zinc soap complex), are added into chlorinated isobutylene-isoprene copolymer (CIIR)/hard clay/carbon black (CB) compound and they are investigated with respect to the vulcanization characteristics, the processability, and the mechanical properties. In hard clay/CB filled system, only ZS silane added compound shows both lower Mooney viscosity and extrusion torque while vinyl silane added compound showed only a lower extrusion torque. All the ZS added compounds showed the lowest viscosity among them. The silane added compounds showed an increased modulus. In 'fatigue to failure' count test, the ZS added compound showed superior counts compared to other silane (amino, vinyl, TESPD) added compounds. The mechanical properties were significantly increased when the S2 and ZS were added into CIIR/hard clay/CB compound. The ZS added compounds showed a significant improvement on elongation modulus.

• Carbon letters
• /
• v.10 no.3
• /
• pp.190-197
• /
• 2009

Various silanes, amino silane, vinyl silane, sulfur silane (TESPD), and ZS (TESPD/zinc soap complex), are added into chlorinated isobutylene-isoprene copolymer (CIIR)/soft clay/carbon black (CB) and CIIR/hard clay/CB compounds and they are investigated with respect to the vulcanization characteristics, the processability, and the mechanical properties. Comparing hard clay and soft clay filled compounds, hard clay (Suprex) filled system shows a higher die C tear than the soft clay (GK) filled one. The other properties (Mooney, extrusion torque/pressure, torque rise ($M_H-M_L$), modulus at 300%) are close to each other. Among various silanes, the ZS treated hard clay (Suprex) compound shows the highest mechanical property following hard clay(S)/vinyl silane(V) and soft clay(GK)/vinyl silane(V) compounds. The TESPD and the ZS effectively helps a formation of a strong 3-dimensional network structure between silica and CIIR via coupling reaction due to bifunctional nature of TESPD. In addition to that, the ZS added compounds show both a better processability and mechanical properties compared to the S2 ones at low concentration due to improved compatibility between zinc soap and CIIR matrix. Only the ZS added compound shows both improved processabilities (Mooney, Extrusion torque-& pressure) and improved mechanical properties (degree of crosslinking, elongation modulus, tear, and fatigue to failure counts) on both CIIR/hard clay/CB and CIIR/soft clay/CB compounds.

• Korean Journal of Materials Research
• /
• v.30 no.6
• /
• pp.273-278
• /
• 2020

This research is conducted to analyze the compatibility of used monomers and produce the high functional hydrogel ophthalmic polymer containing silane and nanoparticles. VTMS (vinyltrimethoxysilane), TAVS [Triacetoxy(vinyl)silane] and cobalt oxide nanoparticles are used as additives for the basic combination of SilM (silicone monomer), MMA (methyl methacrylate) and MA (methyl acrylate). Also, the materials are copolymerized with EGDMA (ethylene glycol dimethacrylate) as cross-linking agent, AIBN (thermal polymerization initiator) as the initiator. It is judged that the lenses of all combinations are optically excellent and thus have good compatibility. Measurement of the optical and physical characteristics of the manufactured hydrophilic ophthalmic polymer are different in each case. Especially for TAVS, the addition of cobalt oxide nanoparticles increases the oxygen permeability. These materials are considered to create synergy, so they can be used in functional hydrogel ophthalmic lenses.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1076-1077
• /
• 2006

Conductive pastes consist of conductive fillers( Au, Ag, Ni, Cu etc.), organic binders, solvents and additives. Meanwhile, there are some metal powders such as copper, nickel etc that are used for pastes which have serious surface corrosion problems. This problem leads to change of the color and decrease in conductivity and affect storage stability of conductive pastes. By using silane coupling agent and dispersion agent, we can ensure both the corrosion stability and long term storage stability, and enhance the high performance electrical and mechanical properties of EMI shielding silicone sealant.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.30 no.12
• /
• pp.751-756
• /
• 2017

A molding-type power inductor is an inductor that uses a hybrid material that is prepared by mixing a ferrite metal powder coated with an insulating layer and an epoxy resin, which is injected into a coil-embedded mold and heated and cured. The fabrication of molding-type inductors requires various techniques such as for coil formation and insertion, improving the magnetic properties of soft magnetic metal powder, coating an insulating film on the magnetic powder surface, and increasing the packing density by well dispersing the powder in the epoxy resin. Among these aspects, researches on additives that can disperse the metal soft magnetic powder having the greatest performance in the epoxy resin with high charge have not been reported yet. In this study, we investigated the effect of silanes, KBM-303 and KBM-403, and a commercial dispersant on the dispersion of metal soft magnetic powders in epoxy resin. The sedimentation height and viscosity were measured, and it was confirmed that the silane KBM-303 was suitable for dispersion. For this silane, the packing density was as high as about 72.49%. Moreover, when 1.2 wt% of dispersant BYK-103 was added, the packing density was about 80.5%.

• Korean Journal of Materials Research
• /
• v.25 no.11
• /
• pp.590-597
• /
• 2015

In this article, poly methyl triethoxy silane was compounded with an inorganic waterproof admixture at a certain ratio to improve the performance of gypsum products; a new type of high-efficiency compound water-proofing additive was also investigated. Furthermore, the waterproof mechanism and the various properties on the hardened gypsum plaster were investigated in detail by XRD and SEM. The results show that the intenerate coefficient of gypsum plaster increased to more than 0.9; the water absorbing rate decreased to less than 10 %. Both the bending strength and the compressive strength of gypsum plaster increased by various degrees. The intenerate coefficient reached a maximum value of 0.73 and the strength of the samples showed almost no change when 5% cement alone was added. In this new type of the high-efficiency compound with waterproof additive, the optimal technological parameters for formulas were obtained to be: 5% cement, 18 % mineral powder, and 0.8% poly methyl triethoxy silane, to compound gypsum plaster. Meanwhile, the production of high performance gypsum as a building material has become possible.

• Polymer(Korea)
• /
• v.25 no.2
• /
• pp.240-245
• /
• 2001

The effect of additives on the orientation of magnetic Sr-ferrite powders has been studied during powder injection molding under applied magnetic field for fabricating multi-pole anisotropic sintered Sr-ferrite magnets. The orientation of the Sr-ferrite powders depends sensitively on the fluidity of powder-binder mixture, related to the binder additives and the injection molding temperature, and the magnetic field intensity. The orientation of Sr-ferrite powders is good for the compacts with stearic acid added in the binder system of paraffin wax/carnauba wax/HDPE, but it is poor for the compacts with silane coupling agent added. The orientation of Sr-ferrites higher than 80% is achieved at the following useful conditions; apparent viscosity lower than 2500 poise in 1000 sec$^{-1}$ shear rate and applied magnetic field higher than 4 kOe.

• Journal of the Semiconductor & Display Technology
• /
• v.18 no.3
• /
• pp.47-51
• /
• 2019

The three different polymer compounds were manufactured with the three different fire retardant (silane coated magnesium dihydroxide) contents, 180, 200, 220 phr, for making cable sheath for ship industry. In the research, ethylene-vinylacetate, polyethylene as matrix polymers and ethylene-vinylacetate grafted maleic anhydride as coupling agent were selected for compounding with fire retardant, closslinking agent, plasticizer, and other additives. In the evaluation. ΔT, Mooney viscosity, and tensile strength increased with the content of fire retardant. But it was found that too much fire retardant damaged aging resistance and cold resistance of the polymer compound.

• Journal of the Semiconductor & Display Technology
• /
• v.18 no.1
• /
• pp.42-47
• /
• 2019

The four different polymer compounds were manufactured to make cable sheath for ship industry. Two kinds of ethylene-vinyl acetate (EVA) were selected as main matrix polymers for compounding with fire retardant, crosslinking agent, filler, plasticizer, and other additives. The properties of the four compounded materials were investigated with the contents of fire retardant, silane coated aluminum hydroxide (S-ATH). Rheology, Mooney viscosity, and tensile strength increased with S-ATH contents by reinforcing effect. With increasing fire retardant amount, fire resistance increased, but cold resistance didn't show an obvious enhancement due to polar effect of vinyl acetate in EVA.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.15 no.7
• /
• pp.4653-4658
• /
• 2014

A study of the improvement in the impact strength is required to apply Nylon 66/silicate composites as an automobile material. Nylon 66/silicate composites were prepared using a twin screw extruder in case of a silicate treatment by ${\gamma}$-APS (S-silicate) and the addition of an octene ${\alpha}$ olefin grafted by maleic anhydride (PE-g-MAH). The chemical structure of the silane treated silicate was measured by Fourier transform infra-red (FT-IR) spectroscopy. The chemical reaction was confirmed by the decrease in the FT-IR intensity of the OH stretching vibration. The thermal properties, intercalation structure, and Izod impact strength were measured by DSC, TGA, XRD, and Izod impact tester. There was no significant effect on the degradation temperature of the Nylon66/silicate composite, but the crystallization temperature and crystallinity increased slightly in the case of the Nylon66/silicate composites. This suggests that the additives act as heterogeneous nuclei on the Nylon 66 matrix. The Izod impact test indicated that S-silicate enhanced the impact performance by up to 24%.