• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.1
• /
• pp.41-46
• /
• 2009

The low dielectric SiOCH films were deposited on p-type Si(100) substrates through the dissociation of BTMSM $(((CH_3)_3Si)_2CH_2)$ precursors with oxygen gas by using PECVD method. BTMSM precursor was introduced with the flow rates from 42 to 60 sccm by 2 sccm step into reaction chamber but with the constant flow rate of 60 sccm $O_2$. SiOCH thin films were annealed at $450^{\circ}C$ for 30 minutes. The electrical property of SiOCH thin films was studied by MIS, Al/SiOCH/p-Si(100), structure. Annealed samples showed large reduction of the maximum capacitance yielding low dielectric constant owing to reductions of surface charge density. After exposure at room temperature and atmospheric pressure, dielectric constant of SiOCH films was totally increased. However, annealed SiOCH thin films were more stable than as-deposited SiOCH thin films for natural oxidation.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.12
• /
• pp.1083-1089
• /
• 2008

We studied the dielectric characteristics of low-k SiOCH thin films by Ellipsometry. The SiOCH thin films were prepared by deposition of BTMSM precursors on p-Si wafer by CCP-PECVD method. The nano-porous structural organic/inorganic hybrid-type of SiOCH thin films correlated directly to the formation of low dielectrics close to pore(k=1). The structural groups including highly dense pores in SiOCH thin films originated the anisotropic geometry type of network structure directing to complex refractive characteristics of SiOCH single layer on the p-Si wafer. The linearly polarized beam of Xe-ramp in the range from 190 nm to 2100 nm introduced to the surface of SiOCH thin film, and the reflected beam was Elliptically polarized by complex refractive coefficients of SiOCH dipole groups. The amplitude variation $\Psi$ and phase variation $\Delta$ of the relative reflective coefficients between perpendicular and parallel components to the incident plane were measured by Ellipsometry. The complex optical constants n and k as well as the dielectric constant and thickness of SiOCH thin films were driven by the measured value of $\Psi$ and $\Delta$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.1
• /
• pp.47-52
• /
• 2009

We studied the electrical characteristics of low-k SiOCH interlayer dielectric(ILD) films fabricated by plasma enhanced chemical vapor deposition (PECVD). BTMSM precursor was evaporated and introduced with the flow rates from 16 sccm to 25 sccm by 1 sccm step with the constant flow rate of 60 sccm $O_2$ in process chamber. The vibrational groups of SiOCH thin films were analyzed by FT!IR absorption lines, and the dielectric constant of the low-k SiOCH thin films were obtained by measuring C-V characteristic curves. The heat treatment on SiOCH thin films reduced the FTIR absorption intensity of the Si-O-$CH_3$ bonding group and Si-$CH_3$ bonding group but increased the intensity of Si-O-Si(C) bonding group. The SiOCH ILD films could have low dielectric constant $k\;{\simeq}\;2$ and also be reduced further by decreasing the $CH_3$ group density and increasing Si-O-Si(C) group density through annealing process.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.11a
• /
• pp.144-147
• /
• 2003

Cu+ ions drift diffusion in formal oxide film and SiOCH film for interlayer dielectric is evaluated. The diffusion is investigated by measuring shift in the flatband voltage of capacitance/voltage measurements on Cu gate capacitors after bias temperature stressing. At a field of 0.2MV/cm and temperature $200^{\circ}C,\;300^{\circ}C,\;400^{\circ}C,\;500^{\circ}C$ for 10min, 30min, 60min. The Cu+ ions drift rate of $SiOCH(k=2.85{\pm}0.03)$ film is considerable lower than termal oxide. As a result of the experiment, SiOCH film is higher than Thermal oxide film for Cu+ drift diffusion resistance. The important conclusion is that SiOCH film will solve a causing reliability problems aganist Cu+ drift diffuion in dielectric materials.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.12
• /
• pp.1090-1095
• /
• 2008

The SiOCH films that low dielectric interlayer dielectric materials were deposited on p-type Si(100) substrates through the dissociation of BTMSM precursors with oxygen gas by using PECVD method. BTMSM precursor was introduced with the flow rates from 42 sccm to 60 sccm by 2 sccm step in the constant flow rate of 60 sccm $O_2$. SiOCH thin films were annealed at $450^{\circ}C$ for 30 minutes. The electrical property of SiOCH thin films was studied by MIS, Al/SiOCH/p-Si(100), structure. Annealed samples showed even greater reductions of the maximum capacitance and the dielectric constant of the SiOCH samples, owing to reductions of surface charge density. we confirmed this result with derivative of C-V characteristic, leakage current density. The maximum capacitance and leakage current density were respectively decreased about 4 pF, 60% after annealing. The average of low-k value is approximatly 2.07 after annealing.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.3
• /
• pp.228-233
• /
• 2010

We studied the optical characteristics correlated with low dielectric constants of low-k SiOCH thin films through ellipsometry. The low-k SiOCH thin films were prepared by CCP-PECVD method using BTMSM(Bis-trimethylsilylmethane) precursors deposited on p-Si wafer. The Si-O-CHx, Si-O-Si, Si-CHx, CHx and Si-H bonding groups were specified by FTIR spectroscopic spectra, and the groups coupled with the nano-porous structural organic/inorganic hybrid-type of SiOCH thin films which has extremely low dielectric constant close to 2.0. The structural groups includes highly dense pore as well as ions in SiOCH thin films affecting to complex refraction characteristics of single layer on the p-Si wafer. The structural complexity originate the complex refractive constants of the films, and resulted the elliptical polarization of the incident linearly polarized light source of Xe-light source in the range from 190 nm to 2100 nm. Phase difference and amplitude ratio between s wave and p wave propagating through SiOCH thin film was studied. After annealing, the amplitude of p wave was reduced more than s wave, and phase difference between p and s wave was also reduced.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.41-42
• /
• 2008

p-type(100) Si 위에 BTMSM과 산소를 혼합한 전구체를 가지고 PECVD 방법을 사용 하여 저유전상수를 갖는 SiOCH막을 형성하였다. 알루미늄 전극을 구현한 MIS (Al/SiOCH/p-si(100)) 구조의 커패시터를 가지고 C-V 특성을 측정하여 유전상수를 계산하였다. 상온에서 증착된 SiOCH 박막의 유전상수는 $450^{\circ}C$에서 30분 동안 열처리 후 뚜렷하게 감소하는 경향을 나타냈으며, 상온 및 대기압에서 공기 중에 노출시켜 자연 산화과정을 겪은 후에 각각의 유전상수는 전체적으로 증가하였지만, 열처리한 박막이 상대적으로 경시효과(aging effects)에 대하여 안정화된 것을 확인하였다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.4
• /
• pp.362-367
• /
• 2008

We have Manufactured the low-k dielectric interlayer fabricated by plasma enhanced chemical vapor deposition (PECVD), The thin film of SiOCH is studied correlation between components and Dielectric constant. The precursor was evaporated and introduced with the flow rates from 16 sccm to 25 sccm by 1sccm step in the constant flow rate of 60 sccm $O_2$ in process chamber. The chemical characteristics of SiOCH were analyzed by measuring FT/IR absorption lines and obtained each dielectric constant measuring C-V. Then compare respectively. ILD of BTMSM/$O_2$ could have low dielectric constant about $k\sim2$, and react sensitively. Also dielectric constant could be decreased by the effects of decreasing $CH_3$ and growing Si-O-Si(C) after annealing process.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.4
• /
• pp.354-361
• /
• 2008

The dielectric characteristics of low-k interlayer dielectric materials was fabricated by plasma enhanced chemical vapor deposition (PECVD). BTMSM precursor was evaporated and introduced with the flow rates from 16 sccm to 25 sccm by 1sccm step in the constant flow rate of 60 sccm $O_2$ in process chamber. Manufactured samples are analyzed components by measuring FT/IR absorption lines. Decomposition each Microscopic structures through two-dimensional correlation analysis about mechanisms for the formation of SiOCH in $SiOCH_3$, Si-O-Si and Si-$CH_3$ bonding group and analyzed correlation between the micro-structure of each group. It is a tendency that seems to be growing of Si-O-Ci(C) bonding group and narrowing of Si-O-$CH_3$ bonding group relative to the increasing flow-rate BTMSM. The order of changing sensitivity about changes of flow-rate in Si-O-Si(C) bonding group is cross link mode$(1050cm^{-1})$ $\rightarrow$ open link mode$(1100cm^{-1})\rightarrow$ cage link mode $(1140cm^{-1})$.

• Proceedings of the KIEE Conference
• /
• 2004.07c
• /
• pp.1697-1699
• /
• 2004

In this investigation, we have studied the diffusion of the $Cu^+$ ion in the Cu/Ta/SiOCH/Si and Cu/Ta/$SiO_2$/Si MIS-C structure. The Cu ions diffusion into the Ta barrier and SiOCH was examined by shift in flatband voltage of capacitance-voltage measurement and leakage current of current-voltage measurement. These evalution indicated that $Cu^+$ ion diffusion rate in Ta/SiOCH is considerably lower then the Ta/$SiO_2$ structure. And diffusion barrier Ta(50[nm]) is useful barrier against $Cu^+$ ion diffusion up to 450$^{\circ}C$.