• Korean Journal of Heritage: History & Science
• /
• v.53 no.2
• /
• pp.4-23
• /
• 2020

The purpose of this study was to explore the diversity of Korea's iron casting technology and to examine various casting methods. The study involved a literature review, analysis of artifacts, local investigation of production tools and technology, and scientific analysis of casting and cast materials. Bellows technology, or Bulmi technology, is a form of iron casting technology that uses bellows to melt cast iron before the molten iron is poured into a clay cast. This technology, handed down only in Jeju Island, relies on use of a clay cast instead of the sand cast that is more common in mainland Korea. Casting methods for cast iron pots can be broadly divided into two: sand mold casting and porcelain casting. The former uses a sand cast made from mixing seokbire (clay mixed with soft stones), sand and clay, while the latter uses a clay cast, formed by mixing clay with rice straw and reed. The five steps in the sand mold casting method for iron pot are cast making, filling, melting iron into molten iron, pouring the molten iron into the cast mold, and refining the final product. The six steps in the porcelain clay casting method are cast making, cast firing, spreading jilmeok, melting iron into molten iron, pouring the molten iron, and refining the final product. The two casting methods differ in terms of materials, cast firing, and spreading of jilmeok. This study provided insight into Korea's unique iron casting technology by examining the scientific principles behind the materials and tools used in each stage of iron pot casting: collecting and kneading mud, producing a cast, biscuit firing, hwajeokmosal (building sand on the heated cast) and spreading jilmeok, drying and biyaljil (spreading jilmeok evenly on the cast), hapjang (combining two half-sized casts to make one complete cast), producing a smelting furnace, roasting twice, smelting, pouring molten iron into a cast, and refining the final product. Scientific analysis of the final product and materials involved in porcelain clay casting showed that the main components were mud and sand (SiO₂, Al₂O₃, and Fe₂O₃). The release agent was found to be graphite, containing SiO₂, Al₂O₃, Fe₂O₃, and K₂O. The completed cast iron pot had the structure of white cast iron, comprised of cementite (Fe₃C) and pearlite (a layered structure of ferrite and cementite).

• Korean Journal of Materials Research
• /
• v.24 no.5
• /
• pp.243-248
• /
• 2014

Silicon-carbon composite was prepared by the magnesiothermic reduction of mesoporous silica and subsequent impregnation with a carbon precursor. This was applied for use as an anode material for high-performance lithium-ion batteries. Well-ordered mesoporous silica(SBA-15) was employed as a starting material for the mesoporous silicon, and sucrose was used as a carbon source. It was found that complete removal of by-products ($Mg_2Si$ and $Mg_2SiO_4$) formed by side reactions of silica and magnesium during the magnesiothermic reduction, was a crucial factor for successful formation of mesoporous silicon. Successful formation of the silicon-carbon composite was well confirmed by appropriate characterization tools (e.g., $N_2$ adsorption-desorption, small-angle X-ray scattering, X-ray diffraction, and thermogravimetric analyses). A lithium-ion battery was fabricated using the prepared silicon-carbon composite as the anode, and lithium foil as the counter-electrode. Electrochemical analysis revealed that the silicon-carbon composite showed better cycling stability than graphite, when used as the anode in the lithium-ion battery. This improvement could be due to the fact that carbon efficiently suppressed the change in volume of the silicon material caused by the charge-discharge cycle. This indicates that silicon-carbon composite, prepared via the magnesiothermic reduction and impregnation methods, could be an efficient anode material for lithium ion batteries.

• Resources Recycling
• /
• v.31 no.6
• /
• pp.44-51
• /
• 2022

In the steelmaking process using an electric arc furnace (EAF), light-burnt dolomite, which is a flux containing MgO, is used to protect refractory materials and improve desulfurization ability. Furthermore, a recarburizing agent is added to reduce energy consumption via slag foaming and to induce the deoxidation effect. Herein, a waste MgO-C based refractory material was used to achieve the aforementioned effects economically. The waste MgO-C refractory materials contain a significant amount of MgO and graphite components; however, most of these materials are currently discarded instead of being recycled. The mass recycling of waste MgO-C refractory materials would be achievable if their applicability as a flux for steelmaking is proven. Therefore, experiments were performed using a target composition range similar to the commercial EAF slag composition. A pre-melted base slag was prepared by mixing SiO₂, Al₂O₃, and FeO in an alumina crucible and heating at 1450℃ for 1 h or more. Subsequently, a mixed flux #2 (a mixture of light-burnt dolomite, waste MgO-C based refractory material, and limestone) was added to the prepared pre-melted base slag and a melting reaction test was performed. Injecting the pre-melted base slag with the flux facilitates the formation of the target EAF slag. These results were compared with that of mixed flux #1 (a mixture of light-burnt dolomite and limestone), which is a conventional steelmaking flux, and the possibility of replacement was evaluated. To obtain a reliable evaluation, characterization techniques like X-ray diffraction (XRD) analysis and X-ray fluorescence (XRF) spectrometry were used, and slag foam height, slag basicity, and Fe recovery were calculated.

• Resources Recycling
• /
• v.2 no.2
• /
• pp.27-38
• /
• 1993

In this study, we investigated the grinding and sedimentation(elutriation) process of the dusts for the effective separation of high purity iron and iron oxides. For characterization of the dust, particle size distribution and chemical composition, were examined. The results obtained in this study may be summarized as follows : 1. The converter CF(clarifier) dust of the Pohang 1st, 2nd steel making factory and EC(Evaporation Cooler), EP(Eltrostatic precititator) dust of the Kwangyang 2nd steel making factory are composed $\alpha$-Fe(21~50%), FeO(wustite)$Fe_3$$O_4$(magnetite), $Fe_2$$O_3$, CaO, $Al_2$$O_3$, $SiO_2$, and etc. 2. Pure iron has ductile characteristic in nature, particle size of the pure iron increase by increasing the grinding time. On the other hand, it is conformed that bo고 particles of hematite and magnetite become less than 325 mesh after 10 minutes grinding. 3. By applying the elutriation technique for the EC dust of the Kwangyang 2nd steel making factory, the iron powder of high content more than 99.17% of pure Fe was recovered with 37.8% yield at grinding time for 40 minutes. 4. By applying the elutriation technique for the CF dust of the Pohang 2nd steel making factory, the iron powder of high content more than 98.38% of pure Fe was recovered with 44.42% yield at grinding time for 40 minutes. 5. When magnetic separation was performed using plastic bonding magnet of 70 gauss, more than 98% Fe grade of iron powder was recovered in the size range +65 -200 mesh but the recovery of it was low.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.32 no.1
• /
• pp.7-11
• /
• 2022

Recently, Hanmi Gemological Institute & Laboratory (HGI) had an opportunity to examine 5 transparent synthetic moissanite. The round brilliants ranged from 0.93 to 0.96 ct and had a colorless, pink, yellow, blue, and red color. Advanced testing results, including Fourier-transform infrared (FTIR) and Raman spectroscopy, identified all the specimens as synthetic moissanite. Under the microscope, all samples except the colorless were confirmed to be a synthetic moissanite coated with a colored film. EDXRF chemical analysis detected very weak X-ray fluorescence peak characteristics of Ca, Ti, and Co in the colored samples. These features were not detected in the colorless sample. Raman spectroscopy investigation was unable to detect the 1332 cm^-1 (produced by sp³ bonding of carbon atoms) or the ~1550 cm^-1 (produced by graphite-related sp² bonding) peak in the colorless sample. The SEM image of the colorless sample showed no indication of a coating. The TEM image of the colorless sample revealed the presence of a 3~8 nm thick layer on the moissanite. Moreover, from the corresponding STEM Z-contrast image combined with the energy-dispersive X-ray spectroscopy (EDX) line profiles and EDX elemental maps, this layer was estimated to be carbon, silicon and oxygen.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.08a
• /
• pp.351-352
• /
• 2011

그래핀(Graphene)은 2차원 평면구조의 $sp^2$ 탄소 결합으로 이루어진 물질이다. 일반적으로 그래핀은 탄소 원자 한층 정도의 얇은 두께를 가지면서 강철의 100배 이상 높은 강도, 다이아몬드보다 2배 이상 뛰어난 열 전도성, 그리고 규소보다 100배 이상 빠른 전자이동도 등의 매우 우수한 특성을 지닌다. 그래핀을 합성하거나 얻는 방법에는, 기계적 박리법(Micro mechanical exfoliation), 산화흑연(graphite oxide)을 이용한 reduced graphene oxide(RGO)방법과 탄화 규소(SiC)를 이용한 epitaxial growth 방법 등이 있지만, 대 면적화가 어렵거나 구조적 결함이 큰 문제점이 있다. 반면, 탄화수소(hydrocarbon)를 탄소 공급원으로 하는 열화학 기상 증착법(Thermal chemical vapor deposition, TCVD)은 구조적 결함이 상대적으로 적으면서 대 면적화가 가능하다는 이점 때문에 최근 가장 많이 이용되고 있는 방법이다. TCVD를 이용, 니켈, 몰리브덴, 금, 코발트 등의 금속에서 그래핀 합성연구가 보고되었지만, 대부분 수 층(fewlayer)의 그래핀이 합성되었다. 하지만, 구리 촉매를 이용하는 것이 단층 그래핀 합성에 매우 효율적이라는 연구결과가 보고되었다. 구리의 경우, 낮은 탄소융해도(solubility of carbon) 때문에 표면에서 self limiting 과정을 통하여 단층 그래핀이 합성된다. 그러나 단층 그래핀 일지라도 면저항(sheet resistance)이 매우 높고, 이론적 계산값에 비해 전자이동도(electron mobility)가 낮게 측정된다. 이러한 원인은 구조적 결함에서 기인된 것으로써 산업으로의 응용을 어렵게 만들기 때문에 양질의 단층 그래핀 합성연구는 필수적이다[1,2]. 본 연구에서는 TCVD를 이용하여 구리 포일(25 ${\mu}m$, Alfa Aeser) 위에 메탄가스를 탄소공급원으로 하여 수소를 함께 주입하고, 메탄가스의 양과 합성시간, 열처리 시간을 조절하면서 균일한 단층 그래핀을 합성하였다. 합성된 그래핀을 $SiO_2$ (300 nm)기판위에 전사(transfer)후 라만 분광법(raman spectroscopy)과 광학 현미경(optical microscope)을 통하여 분석하였다. 그 결과, 열처리 시간이 증가할수록 촉매로 사용된 구리 포일의 grain size가 커짐을 확인하였으며, 구리 포일 위에 합성된 그래핀의 grain size는, 구리 포일의 grain size에 의존하여 커짐을 확인하였다. 또한 동일한 grain 내의 그래핀은 균일한 층으로 합성되었다. 이는 기계적 박리법, RGO 방법, epitaxial growth 방법으로 얻은 그래핀과 비교하여 매우 뛰어난 결정성을 지님이 확인되었다. 본 연구를 통하여 면적이 넓으면서도 결정성이 매우 뛰어난 양질의 단층 그래핀 합성 방법을 확립하였다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2000.11a
• /
• pp.3-4
• /
• 2000

Many researchers are interested in the synthesis and characterization of carbon nitride and diamond-like carbon (DLq because they show excellent mechanical properties such as low friction and high wear resistance and excellent electrical properties such as controllable electical resistivity and good field electron emission. We have deposited amorphous carbon nitride (a-C:N) thin films and DLC thin films by shielded arc ion plating (SAIP) and evaluated the structural and tribological properties. The application of appropriate negative bias on substrates is effective to increase the film hardness and wear resistance. This paper reports on the deposition and tribological OLC films in relation to the substrate bias voltage (Vs). films are compared with those of the OLC films. A high purity sintered graphite target was mounted on a cathode as a carbon source. Nitrogen or argon was introduced into a deposition chamber through each mass flow controller. After the initiation of an arc plasma at 60 A and 1 Pa, the target surface was heated and evaporated by the plasma. Carbon atoms and clusters evaporated from the target were ionized partially and reacted with activated nitrogen species, and a carbon nitride film was deposited onto a Si (100) substrate when we used nitrogen as a reactant gas. The surface of the growing film also reacted with activated nitrogen species. Carbon macropartic1es (0.1 -100 maicro-m) evaporated from the target at the same time were not ionized and did not react fully with nitrogen species. These macroparticles interfered with the formation of the carbon nitride film. Therefore we set a shielding plate made of stainless steel between the target and the substrate to trap the macropartic1es. This shielding method is very effective to prepare smooth a-CN films. We, therefore, call this method "shielded arc ion plating (SAIP)". For the deposition of DLC films we used argon instead of nitrogen. Films of about 150 nm in thickness were deposited onto Si substrates. Their structures, chemical compositions and chemical bonding states were analyzed by using X-ray diffraction, Raman spectroscopy, X-ray photoelectron spectroscopy and infrared spectroscopy. Hardness of the films was measured with a nanointender interfaced with an atomic force microscope (AFM). A Berkovich-type diamond tip whose radius was less than 100 nm was used for the measurement. A force-displacement curve of each film was measured at a peak load force of 250 maicro-N. Load, hold and unload times for each indentation were 2.5, 0 and 2.5 s, respectively. Hardness of each film was determined from five force-displacement curves. Wear resistance of the films was analyzed as follows. First, each film surface was scanned with the diamond tip at a constant load force of 20 maicro-N. The tip scanning was repeated 30 times in a 1 urn-square region with 512 lines at a scanning rate of 2 um/ s. After this tip-scanning, the film surface was observed in the AFM mode at a constant force of 5 maicro-N with the same Berkovich-type tip. The hardness of a-CN films was less dependent on Vs. The hardness of the film deposited at Vs=O V in a nitrogen plasma was about 10 GPa and almost similar to that of Si. It slightly increased to 12 - 15 GPa when a bias voltage of -100 - -500 V was applied to the substrate with showing its maximum at Vs=-300 V. The film deposited at Vs=O V was least wear resistant which was consistent with its lowest hardness. The biased films became more wear resistant. Particularly the film deposited at Vs=-300 V showed remarkable wear resistance. Its wear depth was too shallow to be measured with AFM. On the other hand, the DLC film, deposited at Vs=-l00 V in an argon plasma, whose hardness was 35 GPa was obviously worn under the same wear test conditions. The a-C:N films show higher wear resistance than DLC films and are useful for wear resistant coatings on various mechanical and electronic parts.nic parts.

• Korean Journal of Soil Science and Fertilizer
• /
• v.40 no.5
• /
• pp.418-428
• /
• 2007

Physical and chemical properties of the aggregate by-products including sludge and crushed dust samples collected from the 21 private companies throughout the country were analyzed to evaluate possible usage of the by-products as artificial soil materials for plantation. The pH of the materials ranged from 8.0 to 11.0. The organic matter content was $2.85g\;kg^{-1}$, and the total nitrogen content and available phosphate content were low as 0.7 percents and $12.98mg\;kg^{-1}$, respectively. Exchangeable $Ca^{2+}$, $Mg^{2+}$, $K^+$, and $Na^+$ were 2.29, 0.47, 0.02 and $0.05cmol\;kg^{-1}$, respectively. Heavy metal contents were lower than the limits regulated by environmental law of Korea. Textural analysis showed that most of the materials were silt loam with low water holding capacity ranged from 0.67 to 7.41 percents, and with low hydraulic conductivity ranged from 0.4 to $2.8m\;s^{-1}$. Mineralogical analysis showed that the aggregate by product materials were mostly composed of silicate, alumina and ferric oxides except calcium oxide dominant materials derived from limestones. The primary minerals were quartz, feldspars and dolomites derived from granite and granitic gneiss materials. Some samples derived from limestone material showed calcite and graphite together with the above minerals. According to the result, it can be concluded that the materials could be used as the artificial soil material for plantation after proper improvement of the physico-chemical properties and fertility.