SiCp/6061Al합금복합재료의 시효거동 (Age-Hardening Behavior of SiCp Reinforced 6061 Aluminum Alloy Composites)

  • 안행근;유정희;김석원;우기도
    • 한국재료학회지
    • /
    • 제10권12호
    • /
    • pp.793-798
    • /
    • 2000
  • 석출경화형 6061Al기지합금과 SiC입자크기를 0.7$\mu\textrm{m}$ 및 7.0$\mu\textrm{m}$로 변화시켜 강화한 SiCp/6061Al 합금복합재료의 시효 거동을 경도측정, DSC 시험 및 TEM관찰을 통하여 조사하였다. 17$0^{\circ}C$에서 등온시효시 6061Al기지합금에 비하여 복합화한 0.7$\mu\textrm{m}$SiCp/6061Al합금복합재료 및 7.0$\mu\textrm{m}$SiCP/6061Al합금복합재료에서 최고경도에 도달하는 시간이 짧았으며, 또한 강화재의 크기가 큰 7.0$\mu\textrm{m}$SiCp/6061Al합금복합재료에서 시효촉진이 보다 크게 나타났다. 이것은 복합화 및 SiC입자크기 증가에 따른 전위 밀도 상승에 기인한다. 6061Al기지합금 및 복합재료에서 최고시효처리시의 주강화상은 봉상의 중간상 $\beta$(Mg$_2$Si)이며,$\beta$상 생성의 활성화에너지는 복합화 및 SiG입자크기의 증가에 따라 감소되었다

  • PDF

분무성형법에 의해 제조된 $Al-SiC)_p$ 금속기 복합재료의 미세조직과 성질에 관한 연구 (A Study on the Microstructures and Properties of $Al-SiC)_p$ Metal Matrix Composites Fabricated by Spray Forming Process)

  • 김춘근
    • 한국분말재료학회지
    • /
    • 제1권1호
    • /
    • pp.42-51
    • /
    • 1994
  • 6061Al-SiCP metal matrix composite materials(MMCs) were fabricated by injecting SiCP particles directly into the atomized spray. The main attraction of this technique is the rapid fabrication of semi-finished, composite products in a combined atomization, particulate injection(10 $\mu\textrm{m}$, 40 $\mu\textrm{m}$, SiCP) and deposition operation. Conclusions obtained are as follows; The microstructure of the unreinforced spray formed 6061Al alloy consisted of relatively fine(50 $\mu\textrm{m}$) equiaxed grains. By comparision, the microstructure of the I/M materials was segregated and consisted of relatively coarse(150 $\mu\textrm{m}$) grains. The probability of clustering of SiCP particles in co-sprayed metal matrix composites increased it ceramic particle size(SiCP) was reduced and the volume fraction was held constant. Analysis of overspray powders collected from the spray atomization and deposition experiments indicated that morphology of powders were nearly spherical and degree of powders sphercity was deviated due to composite with SiCp particles. Interfacial bonding between matrix and ceramics was improved by heat treatment and addition of alloying elements(Mg). Maximum hardness values [Hv: 165 kg/mm2 for Al-10 $\mu\textrm{m}$ SiCp Hv--159 kg/mm2 for Al-40 $\mu\textrm{m}$SiCp] were obtained through the solution heat treatment at $530^{\circ}C$ for 2 hrs and aging at $178^{\circ}C$, and there by the resistance were improved.