• Journal of Sensor Science and Technology
• /
• v.16 no.4
• /
• pp.319-323
• /
• 2007

This paper describes the mechanical characteristics of poly 3C-SiC thin films grown on Si wafers with thermal oxide. In this work, the poly 3C-SiC thin film was deposited by APCVD method using only Ar carrier gas and single precursor HMDS at $1100^{\circ}C$. The elastic modulus and hardness of poly 3C-SiC thin films were measured using nanoindentation. Also, the roughness of surface was investigated by AFM. The resulting values of elastic modulus E, hardness H and the roughness of the poly 3C-SiC film are 305 GPa, 26 GPa and 49.35 nm respectively. The mechanical properties of the grown poly 3C-SiC film are better than bulk Si wafers. Therefore, the poly 3C-SiC thin film is suitable for abrasion, high frequency and MEMS applications.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.346-347
• /
• 2007

Aluminum nitride (AlN) thin films were deposited on Polycrystalline (poly) 3C-SiC buffer layers using pulsed reactive magnetron sputtering. Characteristics of AlN films were investigated experimentally by means of FE-SEM, X-ray diffraction, and FT-IR, respectively. As a result, highly (002) oriented AlN thin films with almost free residual stress were achieved using 3C-SiC buffer layers. Therefore, AlN thin films grown on 3C-SiC buffer layers can be used for various piezoelectric fields and M/NEMS applications.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.93-93
• /
• 2008

This paper presents the Raman scattering characteristics of poly (polycrystalline) 3C-SiC thin films deposited on AlN buffer layer by atmospheric pressure chemical vapor deposition (APCVD) using hexamethyldisilane (MHDS) and carrier gases (Ar + $H_2$).The Raman spectra of SiC films deposited on AlN layer of before and after annealings were investigated according to the growth temperature of 3C-SiC. Two strong Raman peaks, which mean that poly 3C-SiC admixed with nanoparticle graphite, were measured in them. The biaxial stress of poly 3C-SiC/AlN was calculated as 896 MPa from the Raman shifts of 3C-SiC deposited at $1180^{\circ}C$ on AlN of after annealing.

• Journal of the Korean Ceramic Society
• /
• v.32 no.10
• /
• pp.1103-1110
• /
• 1995

Silicon carbide (SiC) films have been deposited on the isotropic graphite by chemical vapor deposition. Change of deposition parameters affected significantly the microstructure and preferred orientation of SiC films. Preferred orientation of SiC films was (111) or (220), and microstructure showed the startified structure consisting of small crystallite or faceted columnar structure depending on the deposition parameters. For microhardness, (111) oriented film and stratified structure were superior to (220) oriented film and faceted columnar structure, respectively. Surface of (111) oriented films was less rough than that of (220) oriented films. Adhesion force between graphite substrate and SiC films was above 100N for crystalline films and 49N for amorphous film.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.735-738
• /
• 2002

Single crystal 3C-SiC(cubic silicon carbide) thin-films were deposited on Si(100) substrate up to a thickness of $4.3{\mu}m$ by APCVD method using HMDS(hexamethyildisilane) at $1350^{\circ}C$. The HMDS flow rate was 0.5 sccm and the carrier gas flow rate was 2.5 slm. The HMDS flow rate was important to get a mirror-like crystal surface. The growth rate of the 3C-SiC films was $4.3{\mu}m/hr$. The 3C-SiC epitaxical films grown on Si(100) were characterized by XRD, AFM, RHEED, XPS and raman scattering, respectively. The 3C-SiC distinct phonons of TO(transverse optical) near $796cm^{-1}$ and LO(longitudinal optical) near $974{\pm}1cm^{-1}$ were recorded by raman scattering measurement. The heteroepitaxially grown films were identified as the single crystal 3C-SiC phase by XRD spectra$(2{\theta}=41.5^{\circ})$.

• Journal of the Korean Vacuum Society
• /
• v.12 no.S1
• /
• pp.1-6
• /
• 2003

SiC-C films were deposited with r. f. magnetron sputtering on substrates followed by argon ion bombardment. These films were then permeated by hydrogen gas under the pressure of $3.23\times10^{7}$ Pa for 3 hours at temperature of 500K or bombarded with hydrogen ion beam at 5 keV and a dose of $1\times10^{18}$ ions/$\textrm{cm}^2$. SIMS, AES and XPS were used to analyze hydrogen related species, chemical bonding states of C, Si as well as contamination oxygen due to hydrogen participation in the SiC-C films in order to study the different behaviors of hydrogen in carbon-carbide films due to different hydrogen introduction. Related mechanism about the effects of hydrogen on the element of the SiC-C films was discussed in this paper.

• Journal of Sensor Science and Technology
• /
• v.16 no.6
• /
• pp.462-466
• /
• 2007

Aluminum nitride (AlN) thin films were deposited on Si substrates by using polycrystalline (poly) 3C-SiC buffer layers, in which the AlN film was grown by pulsed reactive magnetron sputtering. Characteristics of grown AlN films were investigated experimentally by means of FE-SEM, X-ray diffraction, and FT-IR, respectively. The columnar structure of AlN thin films was observed by FE-SEM. X-ray diffraction pattern proved that the grown AlN film on 3C-SiC layers had highly (002) orientation with low value of FWHM (${\Theta}=1.3^{\circ}$) in the rocking curve around (002) reflections. These results were shown that almost free residual stress existed in the grown AlN film on 3C-SiC buffer layers from the infrared absorbance spectrum. Therefore, the presented results showed that AlN thin films grown on 3C-SiC buffer layers can be used for various piezoelectric fields and M/NEMS applications.

• Proceedings of the KIEE Conference
• /
• 1999.07d
• /
• pp.1514-1516
• /
• 1999

This paper covers our efforts to improve the low carrier mobility and light instability of hydrogenated amorphous silicon (a-Si:H) films with microcrystalline silicon $({\mu}c-Si)$ films. We successfully prepared ${\mu}c-Si$ films on $CaF_2$/glass substrate by decomposition of $SiH_4$ in RPCVD system. The $CaF_2$ films on glass served as a seed layer for ${\mu}c-Si$ film growth. The XRD analysis on $CaF_2$/glass illustrated a (111) preferred $CaF_2$ grains with the lattice mismatch less than 5 % of Si. We achieved ${\mu}c-Si$ films with a crystalline volume fraction of 61 %, (111) and (220) crystal orientations. grain size of $706\AA$, activation energy of 0.49 eV, and Photo/dark conductivity ratio of 124. By using a $CaF_2$/glass structure. we were able to achieve an improved ${\mu}c-Si$ films at a low substrate temperature of $300^{\circ}C$.

• Journal of Power System Engineering
• /
• v.9 no.4
• /
• pp.118-123
• /
• 2005

We have investigated the fabrication of Si nanoparticles and $C_{60}$ thin films by pulsed laser ablation. By atomic force microscopy(AFM), the laser-deposited $C_{60}$ thin film was verified to have surface far smoother than the surfaces of films produced by the conventional evaporation method. The Si deposited at a He atmosphere of 0.2 Torr was with about $60{\AA}$ height of the Si nanoparticles, suggesting that it was uniformly deposited. We observed visible green emissions spectra in the $Si/C_{60}$ multilayer films after laser annealing. It is considered that this green emissions is occurred from SiC particles, which is produced reaction of Si nanoparticles with $C_{60}$ by laser annealing.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.8
• /
• pp.732-736
• /
• 2006

This paper describes the physical characterizations of polycrystalline 3C-SiC thin films heteroepitaxially grown on Si wafers with thermal oxide, In this work, the 3C-SiC film was deposited by LPCVD (low pressure chemical vapor deposition) method using single precursor 1, 3-disilabutane $(DSB:\;H_3Si-CH_2-SiH_2-CH_3)\;at\;850^{\circ}C$. The crystallinity of the 3C-SiC thin film was analyzed by XPS (X-ray photoelectron spectroscopy), XRD (X-ray diffraction) and FT-IR (fourier transform-infrared spectometers), respectively. The surface morphology was also observed by AFM (atomic force microscopy) and voids or dislocations between SiC and $SiO_2$ were measured by SEM (scanning electron microscope). Finally, residual strain was investigated by Raman scattering and a peak of the energy level was less than other type SiC films, From these results, the grown poly 3C-SiC thin film is very good crystalline quality, surface like mirror, and low defect and strain. Therefore, the polycrystalline 3C-SiC is suitable for harsh environment MEMS (Micro-Electro-Mechanical-Systems) applications.