• Journal of the Microelectronics and Packaging Society
• /
• v.29 no.1
• /
• pp.49-54
• /
• 2022

The copper plating process used to fabricate the submicron damascene pattern of Cu wiring for Si wafer was applied to the plating of a PCB pattern of several tens of microns in size using the same organic additives and current density conditions. In this case, the non-uniformity of the plating thickness inside the pattern was observed. In order to quantitatively analyze the cause, a numerical calculation considering the solution flow and electric field was carried out. The calculation confirmed that the depletion of Cu²⁺ ions in the solution occurred relatively earlier at the bottom corner than the upper part of the pattern due to the plating of the sidewall and the bottom at the corner of the pattern bottom. The diffusion coefficient of Cu²⁺ ions is 2.65 10^-10 m²/s, which means that Cu²⁺ ions move at 16.3 ㎛ per second on average. In the cases of small damascene patterns, the velocity of Cu²⁺ ions is high enough to supply sufficient ions to the inside of the patterns, while sufficient time is required to replenish the exhausted copper ions in the case of a PCB pattern having a size of several tens of microns. Therefore, it is found that the thickness uniformity can be improved by reducing the current density to supply sufficient copper ions to the target area.

• 한국신재생에너지학회:학술대회논문집
• /
• 2005.06a
• /
• pp.205-208
• /
• 2005

최근 열선 화학 기상 증착법(HWCVD)은 낮은 온도에서 TFT용 Poly Si 중착을 할 수 있다는 점과 실리콘 박막을 빠른 속도로 증착할 수 있다는 점에서 각광을 받고 있다. 본 연구에서는 HWCVD를 이용하여 태양전지를 제조하고 그 특성을 평가하였다. 조건에 따른 실리콘 박막의 특성 변화를 알기 위해 corning glass 및 실리콘 wafer에 다양한 조건에서 단위 박막(intrinsic layer)을 증착하였고 이 결과를 바탕으로 p/i/n 구조의 태양전지를 제조하였다. Ta 열선 온도는 1700-2000도였고 가스 원료인 $SiH_4$와 수소의 비율을 조절하면서 그 영향을 관찰하였다. 태양전지의 경우 p충과 n충은 PECVD로 증착하였으며 단위박막 및 태양전지 i충 증착시 기판과 열선간의 거리는 7cm, 기판 온도는 $200^{\circ}C$와 $250^{\circ}C$로 고정하였고 작업압력은 30mTorr였다. 단위 박막 특성 평가를 위해 암/광 전도도, SEM, Raman Scattering, FT-IR등을 사용하였으며 태양전지 특성 평가를 위해 I-V 및 Spectral response를 측정하였다. 열선 온도가 증가함에 따라 증착속도 및 결정화 분율은 증가하였다. 특히 비정질에서 결정질로 전이되는 구간은 매우 좁았으며 여러 분석 방법에서 일치되는 결과를 보였다. $SiH_4$ 유량이 늘어날수록 비정질이 결정질로 바뀌는 열선 온도가 증가하였으며 기판 온도가 낮을 경우 또한 결정으로 바뀌는 열선 온도가 증가하였다. 태양전지의 경우 열선 온도가 증가함에 따라 $V_{oc}$ 및 W가 낮아졌으며 $J_{sc}$, 는 증가하는 경향을 보였으며 결정질 비율이 증가하는 것을 관찰할 수 있었다. 이러한 경향은 quantum efficiency 결과에서도 확인할 수 있었다.용을 반복하면서 석재 내부와 외부의 암석 및 결정에 균열과 미세열극 등이 생성되어 석재 자체의 구조적 안정성에 영향을 주고 있다. 따라서 감은사지 석탑은 지리적 환경 차이로 인해 일반적인 환경의 석조물들과는 다른 형태의 풍화양상을 보이고 있어서 풍화양상 및 풍화형태에 대한 정확한 연구와 이해를 바탕으로 보존대책이 마련되어야 한다.되었다. 이런 모든 시편들을 각 탈염방법에 따라 탈염처리한 후 XRD와 SEM-EDS으로 분석한 결과 인철광과 침철광은 어떠한 변화도 보이지 않았고, 다만 적금광으로 동정된 시편만이 잔존하지 않았다. 철기 제작별 $Cl^-$ 이온 추출량과 탈염효과에 대한 비교 실험은 이온 크로마토그래피 분석 결과와 마찬가지로 단조 철제유물이 주조 철제보다 $Cl^-$ 이온을 많이 가지고 있었으며, 탈염 처리 후에는 $Cl^-$ 이온은 전혀 발견되지 않았다. 이상의 결과 $K_2CO_3$와 Sodium 용액은 탈염처리에서 가장 적합한 탈염처리 용액으로 알수가 있었으며 특히 어떠한 탈염 용액으로 유물을 처리한다 해도 철제유물에 생성된 부식물은 제거되지 않는다는 것을 알게 되었다. 따라서 보존처리자는 유물 표면의 부식 상태만을 보고 처리하기 보다는 철기제작물로 고려하여 처리하는 것이 필요하다. 또한 금속에 부식을 야기시키는 $Cl^-$ 이온과 부식물을 완전하게 제거하여 탈염처리를 하는 것이 유물 부식을 최대한 지연시킬 수 있는 것이라 생각된다.TEX>$88\%$)였다.(P=0.063). 결론: 본 연구에서는 MTHFR C/T & T/T 유전자 다형성이 위암의 발생과 그 위치에 대해 관련이 있는 것으로 여겨지고, 흡연력, 음주력과는 관련이 없는 것으로 여겨진다.험이 커지는 경향을 보였으나, 나이 및 병기, 종양의 크기, MD-BED $Gy_{10}$ 등의 예후 인자를 보정한 다변

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.320-320
• /
• 2016

Nanocrystalline Carbon thin films have numerous applications in different areas such as mechanical, biotechnology and optoelectronic devices due to attractive properties like high excellent hardness, low friction coefficient, good chemical inertness, low surface roughness, non-toxic and biocompatibility. In this work, we studied the comparison of pure DC power and pulsed DC power in plasma sputtering process of carbon thin films synthesis. Using a close field unbalanced magnetron sputtering system, films were deposited on glass and Si wafer substrates by varying the power density and pulsed DC frequency variations. The plasma characteristics has been studied using the I-V discharge characteristics and optical emission spectroscopy. The films properties were studied using Raman spectroscopy, Hall effect measurement, contact angle measurement. Through the Raman results, ID/IG ratio was found to be increased by increasing either of DC power density and pulsed DC frequency. Film deposition rate, measured by Alpha step measurement, increased with increasing DC power density and decreased with pulsed DC frequency. The electrical resistivity results show that the resistivity increased with increasing DC power density and pulsed DC frequency. The film surface energy was estimated using the calculated values of contact angle of DI water and di-iodo-methane. Our results exhibit a tailoring of surface energies from 52.69 to $55.42mJ/m^2$ by controlling the plasma parameters.

• Applied Chemistry for Engineering
• /
• v.10 no.5
• /
• pp.644-651
• /
• 1999

In this experiment the Iron phthalocyanine (FePc) films on Si-wafer and alumina pallet were prepared using vacuum sublimation with conditions of changing reaction time, temperature, and deposition rate. Then, some samples were annealed following annealing. Techniques such as XRD, SEM, and resistance measurement method, were dedicated to characterize the changes of surface structure, phase transformation and electric resistance sensitivity in accordance with change of film thickness. In proportion to the decrease of deposition temperature from $370^{\circ}C$ to $350^{\circ}C$, intensities of (200), (011), (211) and (114) planes of $\alpha$-phase were decreased and (100) plane of $\beta$-phase were appeared. The film thickness were controlled by regulating the volume of precursor material during rapid deposition. As a result, it was observed that crystalline particle size had been increased according to the increase of film thickness and $\alpha$-phase transformed to $\beta$-phase. In consequence of measuring the crystallinity of films annealed between $150^{\circ}C$ and $350^{\circ}C$, $\alpha$- to $\beta$-phase transformation was appeared to begin at $150^{\circ}C$ and completely transformed to $\beta$-phase at $350^{\circ}C$. Electric resistance sensitivity of FePc film to $NO_x$ gas along temperature change of FePc films was observed to be more stable with the decrease of the film thickness.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.137-137
• /
• 2009

Thin-film transistors (TFTs) that can be prepared at low temperatures have attracted much attention due to the great potential for flexible electronics. One of the mainstreams in this field is the use of organic semiconductors such as pentacene. But device performance of the organic TFTs is still limited by low field effect mobility or rapidly degraded after exposing to air in many cases. Another approach is amorphous oxide semiconductors. Amorphous oxide semiconductors (AOSs) have exactly attracted considerable attention because AOSs were fabricated at room temperature and used lots of application such as flexible display, electronic paper, large solar cells. Among the various AOSs, a-IGZO was considerable material because it has high mobility and uniform surface and good transparent. The high mobility is attributed to the result of the overlap of spherical s-orbital of the heavy pest-transition metal cations. This study is demonstrated the effect of thickness channel layer from 30nm to 200nm. when the thickness was increased, turn on voltage and subthreshold swing were decreased. a-IGZO TFTs have used a shadow mask to deposit channel and source/drain(S/D). a-IGZO were deposited on SiO2 wafer by rf magnetron sputtering. using power is 150W, working pressure is 3m Torr, and an O2/Ar(2/28 SCCM) atmosphere at room temperature. The electrodes were formed with Electron-beam evaporated Ti(30nm) and Au(70nm) structure. Finally, Al(150nm) as a gate metal was evaporated. TFT devices were heat treated in a furnace at $250^{\circ}C$ in nitrogen atmosphere for an hour. The electrical properties of the TFTs were measured using a probe-station to measure I-V characteristic. TFT whose thickness was 150nm exhibits a good subthreshold swing(S) of 0.72 V/decade and high on-off ratio of 1E+08. Field effect mobility, saturation effect mobility, and threshold voltage were evaluated 7.2, 5.8, 8V respectively.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.448-448
• /
• 2013

최근 생물학적 분석 기구에서 시료를 처리, 분리, 검출, 샘플링 또는 분석하기 위해 사용되는 마이크로펌프(Micropump)에 대한 관심이 높아지고 있다. 또한 전자소자의 성능과 신뢰성의 증진을 위한 전자소자의 열 문제를 해결하기 위해 냉각장치로 마이크로 펌프가 적용되기도 한다. 그 외에도 마이크로펌프는 다양한 분야에 응용이 가능하다. 마이크로펌프는 작동 방식에 따라 압전형, 공압형, 열공압형, 연동형 등의 여러 종류로 분류되고 있다. 그중에서도 최근에는 연동형 마이크로 펌프의 개발이 각광받고 있다. 기존의 연동형 펌프들은 다중 챔버를 가지고 있으며, 각각의 챔버 내에서 Dead volume이 많이 발생할 뿐만 아니라 이상적인 연동운동과는 차이가 많이 나는 문제점을 가지고 있다. 또한 압전방식과 열공압방식은 느린 응답성으로 인해 효율적인 유체 이동이 어렵다. 본 논문에서는 이상적인 연동운동을 구현하기 위하여 기존의 연동형 펌프의 단점을 보완하고, 하나의 챔버에 다중전극 구조를 가지는 정전기력방식의 연동형 펌프를 개발하였다. 정전기력방식으로 펌프를 구동함으로써, 저전력으로 펌프구동이 가능하며, 하나의 챔버에 다중전극을 설치함으로써 이상적인 연동운동을 재현하였다. 그리고 Dead volume을 최소화 하였다. 또한, 빠른 반응속도로 인해 효율적인 유체 이동을 실현시킬 수 있었다. 본 연구에서 제안된 마이크로 펌프의 구성은 크게 챔버, 박막, Inlet/outlet hole으로 구성되었다. 챔버는 Si-wafer에 wet etching 공정으로 제작 하였고 그 위에 알루미늄 박막을 200 nm 증착시켰다. 챔버는 가로 32 mm, 세로 5 mm, 깊이는 $15{\mu}m$, 부피는 $200{\mu}l$으로 제작되었다. 박막은 폴리이미드(polyimide)를 사용하여 $3{\mu}m$의 두께로 제작 되었으며, 폴리이미드 박막 사이에는 200 nm 두께의 4개의 알루미늄 박막 전극을 삽입시켰다. 삽입된 4개의 전극에 개별적인 전기신호를 보냄으로써 연동운동이 가능하다. Inlet/outlet hole은 직경 2 mm의 크기로 제작되었으며, 튜브를 연결하여 유체가 흐를 수 있는 체널을 형성하였다. 제작된 마이크로 펌프의 구동전압은 115 V이며, 인가되는 주파수를 1 Hz~100 KHz까지 변화시켜 유량을 측정하였다. 작동 유체는 공기이며, 유량측정은 튜브 내에 물방울을 삽입하여 시간에 따른 이동거리를 관측하였다. 측정결과 2.2 KHz에서 2.4 mm/min의 가장 높은 유량을 확인할 수 있었다. 본 연구를 통해 제안된 연동형 마이크로펌프는 이상적인 연동운동이 가능함으로써 기존의 연동형 방식의 문제점을 보완하였으며, 생명과학, 의학, 화학 등의 분야에서 적용이 가능하리라 기대된다.

• Journal of Astronomy and Space Sciences
• /
• v.21 no.4
• /
• pp.481-492
• /
• 2004

We report the successful fabrication and I-V curve superconductivity test results of the Nb/Al-based superconducting tunnel junctions. STJs with side-lengths of 20, 40, 60 and $80{\mu}m$ were fabricated by deposition of polycrystalline Nb/Al/AlOx/Al/Nb 5-layer thin films incorporated on a 3-inch Si wafer. STJ was designed by $Tanner^{TM}$ L-Edit 8.3 program, and fabricated in SQUID fabrication facility, KRISS. S-layer STJ thin-films were fabricated using UV photolithography, DC magnetron sputtering, Reactive ion etching, and CVD(Chemical Vapor Deposition) techniques. Superconducting state test for STJ was succeeded in 4K with liquid helium cooling system. Their performance indicators such ie energy gap, normal resistance, normal resistivity, dynamic resistance, dynamic resistivity, and quality factor were measured from I-V curve. Fabricated Nb/Al STJ shows $11\%$ higher FWHM energy resolution than genuine Nb STJ.

• Journal of Powder Materials
• /
• v.22 no.5
• /
• pp.321-325
• /
• 2015

The triboelectric property of a material is important to improve an efficiency of triboelectric generator (TEG) in energy harvesting from an ambient energy. In this study, we have studied the TEG property of a semiconducting $SnO_2$ which has yet to be explored so far. As a counter triboelectric material, PET and glass are used. Vertical contact mode is utilized to evaluate the TEG efficiency. $SnO_2$ thin film is deposited by atomic layer deposition on bare Si wafer for various thicknesses from 5.2 nm to 34.6 nm, where the TEG output is increased from 13.9V to 73.5V. Triboelectric series are determined by comparing the polarity of output voltage of 2 samples among $SnO_2$, PET, and glass. In conclusion, $SnO_2$, as an intrinsic n-type material, has the most strong tendency to be positive side to lose the electron and PET has the most strong tendency to be negative side to get the electron, and glass to be between them. Therefore, the $SnO_2$-PET combination shows the highest TEG efficiency.

• Journal of the Microelectronics and Packaging Society
• /
• v.8 no.1
• /
• pp.33-38
• /
• 2001

We investigate the via-size dependance of as-electroplated- and reflow-bump shapes for realizing both high-density and high-aspect ratio of solder bump. The solder bump is fabricated by subsequent processes as follows. After sputtering a TiW/Al electrode on a 5-inch Si-wafer, a thick photoresist for via formation it obtained by multiple-codling method and then vias with various diameters are defined by a conventional photolithography technique using a contact alinger with an I-line source. After via formation the under ball metallurgy (UBM) structure with Ti-adhesion and Cu-seed layers is sputtered on a sample. Cu-layer and Sn/pb-layer with a competition ratio of 6 to 4 are electroplated by a selective electroplating method. The reflow-bump diameters at bottom are unchanged, compared with as-electroplated diameters. As-electroplated- and reflow-bump shapes, however, depend significantly on the via size. The heights of as-electroplated and reflow bumps increase with the larger cia, while the aspect ratio of bump decreases. The nearest bumps may be touched by decreasing the bump pitch in order to obtain high-density bump. The touching between the nearest bumps occurs during the overplating procedure rather than the reflowing procedure because the mushroom diameter formed by overplating is larger than the reflow-bump diameter. The arrangement as zig-zag rows can be effective for realizing the flip-chip-interconnect bump with both high-density and high-aspect ratio.

• Journal of the Microelectronics and Packaging Society
• /
• v.20 no.2
• /
• pp.65-74
• /
• 2013

The through-silicon via (TSV) technology is essential for 3-dimensional integrated packaging. TSV technology, however, is still facing several reliability issues including interfacial delamination, crack generation and Cu protrusion. These reliability issues are attributed to themo-mechanical stress mainly caused by a large CTE mismatch between Cu via and surrounding Si. In this study, the thermo-mechanical reliability of copper TSV technology is investigated using numerical analysis. Finite element analysis (FEA) was conducted to analyze three dimensional distribution of the thermal stress and strain near the TSV and the silicon wafer. Several parametric studies were conducted, including the effect of via diameter, via-to-via spacing, and via density on TSV stress. In addition, effects of annealing temperature and via size on Cu protrusion were analyzed. To improve the reliability of the Cu TSV, small diameter via and less via density with proper via-to-via spacing were desirable. To reduce Cu protrusion, smaller via and lower fabrication temperature were recommended. These simulation results will help to understand the thermo-mechanical reliability issues, and provide the design guideline of TSV structure.