• Korean Journal of Materials Research
• /
• v.16 no.4
• /
• pp.225-230
• /
• 2006

Nanoimprint lithography (NIL) is a novel method of fabricating nanometer scale patterns. It is a simple process with low cost, high throughput and resolution. NIL creates patterns by mechanical deformation of an imprint resist and physical contact process. The imprint resist is typically a monomer or polymer formulation that is cured by heat or UV light during the imprinting process. Stiction between the resist and the stamp is resulted from this physical contact process. Stiction issue is more important in the stamps including narrow pattern size and wide area. Therefore, the antistiction layer coating is very effective to prevent this problem and ensure successful NIL. In this paper, an antistiction layer was deposited and characterized by PECVD (plasma enhanced chemical vapor deposition) method for metal stamps. Deposition rates of an antistiction layer on Si and Ni substrates were in proportion to deposited time and 3.4 nm/min and 2.5 nm/min, respectively. A 50 nm thick antistiction layer showed 90% relative transmittance at 365 nm wavelength. Contact angle result showed good hydrophobicity over 105 degree. $CF_2$ and $CF_3$ peaks were founded in ATR-FTIR analysis. The thicknesses and the contact angle of a 50 nm thick antistiction film were slightly changed during chemical resistance test using acetone and sulfuric acid. To evaluate the deposited antistiction layer, a 50 nm thick film was coated on a stainless steel stamp made by wet etching process. A PMMA substrate was successfully imprinting without pattern degradations by the stainless steel stamp with an antistiction layer. The test result shows that antistiction layer coating is very effective for NIL.

• Journal of Sensor Science and Technology
• /
• v.8 no.3
• /
• pp.283-290
• /
• 1999

The $n^+/p/p^+$ junction PERL solar cell of $0.1{\sim}2{\Omega}{\cdot}cm$ (100) p type silicon wafer was fabricated through the following steps; that is, wafer cutting, inverted pyramidally textured surfaces etching by KOH, phosphorus and boron diffusion, anti-reflection coating, grid formation and contact annealing. At this time, the optical characteristics of device surface and the efficiency of doping concentration for resistivity were investigated. And diffusion depth and doping concentration for n+ doping were simulated by silvaco program. Then their results were compared with measured results. Under the illumination of AM (air mass)1.5, $100\;mW/cm^2$ $I_{sc}$, $V_{oc}$, fill factor and the conversion efficiency were 43mA, 0.6 V, 0.62. and 16% respectively.