• Journal of the Korean Ceramic Society
• /
• v.36 no.10
• /
• pp.1062-1068
• /
• 1999

The flexural strength distribution of alumina ceramics was observed using ball-on-3 ball test after thermal shock into the distilled water of 25$^{\circ}C$ Crack distribution was also observed by dye-penetration after thermal shock test. Fracture probability of alumina ceramics by ball-on-3 ball test was studied and compared with that by 3-point bending test. The crack distance from the center of thespecimen showed the stronger effect on the flexural strength by ball-on-3 ball test than the crack density.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.19 no.2
• /
• pp.463-474
• /
• 1995

Modified Vainshtok weight function method is developed. The thermal shock stress intensity factors for elliptical surface cracks existed in the thin and thick walled cylinders are determined. The present results are compared with previous solutions and shown to be good agreement with them.

• Proceedings of the KSME Conference
• /
• 2004.11a
• /
• pp.90-95
• /
• 2004

The probabilistic fracture analysis is used to determine the effects of uncertainties involved in material properties, location and size of flaws, etc, which can not be addressed using a deterministic approach. In this paper the probabilistic fracture analysis is applied for evaluating the RV(Reactor Vessel) under PTS(Pressurised Thermal Shock). A semi-elliptical axial crack is assumed in the inside surface of RV. The selected random parameters are initial crack depth, neutron fluence, chemical composition of material (copper, nickel and phosphorous) and $RT_{NDT}$. The deterministically calculated $K_I$ and crack tip temperature are used for the probabilistic calculation. Using Monte Carlo simulation, the crack initiation probability for fixed flaw and PNNL(Pacific Northwest National Laboratory) flaw distribution is calculated. As the results show initiation probability of fixed flaw is much higher than that of PNNL distribution, the postulated crack sizes of 1/10t in this paper and 1/4t of ASME are evaluated to be very conservative.

• Proceedings of the KSME Conference
• /
• 2001.06a
• /
• pp.441-446
• /
• 2001

In the integral type reactor, SMART, all the major components such as steam generators, pressurizer and pumps are located inside the single reactor pressure vessel. The objective of this study is to evaluate the structural integrity for RPV of SMART under the postulated pressurized thermal shock by applying the finite element analysis. Input data for the finite element analysis were generated using the commercial code I-DEAS, and the fracture mechanics analysis was performed using the ABAQUS. The crack configurations, the crack aspect ratio and the clad thickness were considered in the parametric study. The effects of these parameters on the reference nil-ductility transition temperature were also investigated.

• Structural Engineering and Mechanics
• /
• v.8 no.1
• /
• pp.103-118
• /
• 1999

The structural integrity of the reactor pressure vessel under pressurized thermal shock (PTS) is evaluated in this study. For given material properties and transient histories such as temperature and pressure, the stress distribution is found and stress intensity factors are obtained for a wide range of crack sizes. The stress intensity factors are compared with the fracture toughness to check if cracking is expected to occur during the transient. A round robin problem of the PTS during a small break loss of coolant transient has been analyzed as a part of the international comparative assessment study, and the evaluation results are discussed. The maximum allowable nil-ductility transition temperatures are determined for various crack sizes.

• Proceedings of the Computational Structural Engineering Institute Conference
• /
• 2004.04a
• /
• pp.309-316
• /
• 2004

A probabilistic structural integrity assessment is performed for a reactor pressure vessel under PTS(Pressurized Thermal Shock). A semi-elliptical finite axial crack is assumed to he in the beltline region(either base metal or weld meta)1 of the reactor vessel inside surface. The selected random variables are initial crack depth, neutron fluence on the vessel inside surface, copper, nickel, and phosphorus content of the vessel material, and RT/sub NDT/. The probabilities of crack initiation or vessel failure where the crack is propagated through vessel wall are calculated. The probabilities obtained with random crack size are compared to these obtained with deterministic us. Since the failure function cannot to explicitly by selected by selected random variables, Monte Carlo Simulation is applied to perform probabilistic analysis The influence of the amount of neutron fluence is also examined to assess the structural reliability for vessel life time.

• Computational Structural Engineering
• /
• v.9 no.2
• /
• pp.153-161
• /
• 1996

In this paper, theory of fracture mechanics for the pressurized thermal shock is investigated and numerical procedure for the evaluation of the pressure vessel under pressurized thermal shock is developed. For the given material properties, transient history such as temperature and pressure, and postulated flaw, the stress distribution is obtained to calculate stress intensities for a wide range of assumed crack sizes. The stress intensities are compared with the material fracture toughness values corresponding to the chemical compositions and the distribution of the nil ductility transition temperature, to determine the crack growth during the transient. Plant-specific calculations have been performed for several transients and the evaluation results are discussed.

• Structural Engineering and Mechanics
• /
• v.53 no.5
• /
• pp.867-880
• /
• 2015

Mechanical fastening is still one of the main methods used for joining components. Different techniques have been applied to reduce the effect of stress concentration of notches like fastener holes. In this work we evaluate the feasibility of combining laser shock peening (LSP) and cold expansion to improve fatigue crack initiation and propagation of open hole specimens made of 6061-T6 aluminum alloy. LSP is a new and competitive technique for strengthening metals, and like cold expansion, induces a compressive residual stress field that improves fatigue, wear and corrosion resistance. For LSP treatment, a Q-switched Nd:YAG laser with infrared radiation was used. Residual stress distribution as a function of depth was determined by the contour method. Compact tension specimens with a hole at the notch tip were subjected to LSP process and cold expansion and then tested under cyclic loading with R=0.1 generating fatigue cracks on the hole surface. Fatigue crack initiation and growth is analyzed and associated with the residual stress distribution generated by both treatments. It is observed that both methods are complementary; cold expansion increases fatigue crack initiation life, while LSP reduces fatigue crack growth rate.

• Proceedings of the KSME Conference
• /
• 2000.11a
• /
• pp.286-291
• /
• 2000

The reactor pressure vessel is usually cladded with stainless steel to prevent corrosion and radiation embrittlement, and number of subclad cracks have been found during an in-service-inspection. Therefore assessment for subclad cracks should be made for normal operating conditions and faulted conditions such as PTS. Thus, in order to find the optimum fracture assessment procedures for subclad cracks under a pressurized thermal shock condition, in this paper, three different analyses were performed, ASME Sec. XI code analysis, an LEFM(Liner elastic fracture mechanics) analysis and an EPFM(Elastic plastic fracture mechanics) analysis. The stress intensity factor and the Maximum $RT_{NDT}$ were used for characterizing. Analysis based on ASME Sec. XI code does not completely consider the actual stress distribution of the crack surface, so the resulting Maximum allowable $RT_{NDTS}$ can be non-conservative, especially for deep cracks. LEFM analysis, which does not consider elastic-plastic behavior of the clad material, is much more non-conservative than EPFM analysis. Therefore, It is necessary to perform EPFM analysis for the assessment of subclad cracks under PTS.

• Nuclear Engineering and Technology
• /
• v.32 no.2
• /
• pp.99-107
• /
• 2000

A probabilistic integrity analysis method is presented for a reactor vessel under pressurized thermal shock(PTS) based on Monte Carlo simulation. This method can be applied to the structural integrity assessment of a reactor vessel subjected to pressurized thermal shock where the coolant temperature transient cannot be expressed explicitly as a time function. An axially or circumferentially oriented infinite length surface crack is assumed to be in the beltline weld region of the rector vessel's inside surface. The random variables are the initial crack depth, neutron fluence on the vessel's inside surface, the copper and nickel content of the vessel materials, R $T_{NDT}$ , $K_{IC}$ , and K/aub la/. The reliability of a sample reactor vessel under PTS is assessed quantitatively and the influence of the amount of neutron fluence is also examined by applying the present method.sent method.