• The korean journal of orthodontics
• /
• v.37 no.4
• /
• pp.283-292
• /
• 2007

The purpose of this study was to evaluate the clinical usefulness of 4 self etching primers by measuring the shear bond strength of orthodontic brackets and examining the failure pattern of bracket-tooth interfaces. Methods: Seventy-five, defect-free, premolars were randomly assigned into five groups: control group (37% phosphoric acid + Transbond XT primer) and self etching primer treated groups (Transbond Plus self etching primer, Unifil bond, Clearfil SE bond, and Adhese). The shear bond strength was measured with a universal testing machine and the amount of residual adhesive remaining on the brackets after debonding was assessed by the adhesive remnant index (ARI). Results: The results showed that the groups conditioned with self etching primer had significantly lower shear bond strength than the control group (p < 0.05), although clinically acceptable. However, there were no significant differences in shear bond strength among the self etching primer groups (p > 0.05). Evaluation of the ARI scores indicated there was less resin remnant on the teeth in the groups conditioned with self etching primers, although not statistically significant. Conclusion: The results of this study suggest that all four of the self etching primers have shown acceptable bond strength for clinical use.

• The korean journal of orthodontics
• /
• v.34 no.4 s.105
• /
• pp.325-332
• /
• 2004

A self-etching primer that combines the etchant and primer in one chemical compound saves time and should be mote cost-effective to the clinician and patient. The purpose of this study was to evaluate the clinical effectiveness of a self-etching primer by measuring shear bond strengths according to various conditions and observing adhesive failure patterns. For this Investigation, 120 upper and lower premolars extracted for orthodontic purposes were used and randomly divided into six groups of twenty teeth each. Human premolars were embedded in a metal cylinder with orthodontic resin. Metal brackets and ceramic brackets were bonded with XT primer and self-etching primer by means of XT adhesive. Upon curing, plasma arc light and visible light were used. After bonding, the shear bond strength was tested by Instron universal testing machine, and the amount of residual adhesive that remained on the tooth after debonding was measured by stereoscope and assessed with an adhesive remnant index. The results were as fellows: 1. When brackets were bonded, if other conditions remained the same, there was no significant difference in shear bond strength due to the type of primer - either self-etching primer or XT primer. 2. When metal brackets were bonded, there was no significant difference in shear bond strength according to the source of light - plasma arc light or visible light - and type of primer. 3. There was a very significant difference in shear bond strength according to the type of brackets - metal or ceramic brackets. The shear bond strength of ceramic brackets was stronger than metal brackets. 4. When the adhesive failure patterns of metal brackets bonded with self-etching primer were observed by using the adhesive remnant index, the bond failure of the metal bracket occurred more frequently at the bracket-adhesive. The failure of the ceramic bracket, however, occurred more frequently at the enamel-adhesive interface. The adhesive failure patterns of metal brackets bonded with XT primer observed the same patterns. The above results suggest that self-etching primer can be clinically useful for bonding the brackets without fear of a decrease in shear bond strength.

• Proceedings of the KACD Conference
• /
• 2003.11a
• /
• pp.625-625
• /
• 2003

I. Objectives Self-etching primer adhesive system is affected to dentin surface conditioning and priming. Especially application time of self-etching primer is very important factor of clinical procedure which has direct influence on smear layer, etching reaction and primer penetration to dentin. This study evaluated the influence of application time of self-etching primers on microtensile bond strength (${\mu}{\;}TBS$) to dentin using three self-etching primer adhesive systems.(omitted)

• The korean journal of orthodontics
• /
• v.33 no.1 s.96
• /
• pp.51-61
• /
• 2003

The purpose of this study was to evaluate the effects of a self-etching primer on the shear bond strength of orthodontic brackets and on the failure pattern of bracket-adhesive interfaces in dry or wet condition. Brackets were bonded to extracted human teeth according to one of three experimental protocols. In the Group P, teeth were etched with $37\%$ phosphoric acid. After the Transbond XT Primer was applied onto the etched surfaces, the brackets were bonded with Transbond XT(3M, Unitek, Monrovia, Calif) and light cured for 40 seconds. In the Group SD, a self-etching primer(3M, Unitek, Monrovia, Calif) was placed on the enamel for 3 seconds and gently evaporated with air, as suggested by the manufacturer. The brackets were then bonded with Transbond XT as in the Group P In the Group SW, artificial saliva was applied to the enamel surface for 10 seconds to allow complete hydration of the surface before application self-etching primer The brackets were then bonded following the procedures of Group SD. Each group was divided into 2 sub-groups(0.5h, 24h) according to debonding time. Shear bond strengths were measured by Instron universal testing machine. After debonding, the teeth and brackets were examined under scanning electron microscope and assessed with the adhesive remnant index. The result obtained were summarized as follows ; 1. The shear bond strengths were high enough to use clinically in all testing groups, but the shear bond strengths of Group SD and SW were significantly lower than Group P(p<0.05). 2. With respect to comparison of debonding time, 24h debonding samples exhibited heigher shear bond strength than 0.5h debonding samples in Group P, SD and SW(p<0.05). 3. In the self etching primer groups(Group SD and Group SW), there was no significant difference in mean shear bond strength between under dry and wet state(p>0.05). 4. There was a greater frequency of ARI score of 0 and 1 with the Group P. On the other hand, there was a higher frequency of ARI scores of 2 and 3 with Group SD and Group SW(p<0.05).

• The korean journal of orthodontics
• /
• v.41 no.1
• /
• pp.16-24
• /
• 2011

Objective: The purpose of this study was to determine (1) the shear bond strength (SBS) of an antimicrobial monomer-containing self-etching primer according to ceramic bracket types and (2) the bracket-adhesive failure mode using an adhesive remnant index (ARI). Methods: A total of 90 extracted human teeth were randomly divided into 6 groups. Each group consisted of one of two ceramic brackets (monocrystalline, polycrystalline) and one of three primers (Transbond XT primer, Transbond Plus SEP, Clearfil Protect Bond) with each group containing 15 specimens. The SBS was measured, and adhesive residues left on the tooth surface were assessed. Results: The SBS of polycrystalline ceramic bracket groups was Significantly higher than that of the monocrystalline ceramic bracket groups (p < 0.001). The SBS of Transbond XT primer groups was significantly higher than those of Transbond Plus SEP groups and Clearfil Protect Bond groups (p < 0.001). All the groups showed bonding failures between the bracket base and adhesive. Conclusions: The combination of a self-etching primer with a monocrystalline bracket is recommended for clinical use, considering its acceptable SBS and mode of failure.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.35 no.2
• /
• pp.216-224
• /
• 2008

The purpose of this study was to evaluate the effectiveness of fissurotomy and double application time of acidic primer of self-etching adhesive system of acid treatment on enamel surfaces for prevention of microleakage of pit and fissure sealants. The microleakage of pit and fissure sealants was evaluated by measuring the penetration depth of methylene blue solution. Specimens were divided by 4 groups according to the method of treatment. Group I: 35% phosphoric acid etching, 20 seconds. Group II: Priming with self-etching primer, 20 seconds. Group III: Priming with self-etching primer, 40 seconds. Group IV: Priming with self-etching primer, 20 seconds, after fissurotomy. The etched pattern produced on enamel was observed using a scanning electron microscope. Obtained data were analysed statistically using Kruscal-Wallis test followed by Mann-Whitney test for comparison of groups. The results are as follows: 1. Microleakage scores of group IV priming with self-etching primer 20 seconds after fissurotomy was the lowest. 2. Microleakage scores between group II and group III were not shown significant difference. 3. Enamel for 20 seconds etching with 35% phosphoric acid was observed the most effective etching pattern. And the etching pattern on the fissure enamel with self-etching adhesive 20 seconds after fissurotomy was more prominent than group II, III only using self-etching primer.

• Restorative Dentistry and Endodontics
• /
• v.25 no.4
• /
• pp.543-549
• /
• 2000

Gutta-percha와 근관sealer를 사용한 근관 충전은 가장 많이 이용되고 성공률이 높은 방법이지만, 현재 사용되는 모든 근관sealer는 미세누출을 나타낸다. 따라서 더 효과적인 근관 폐쇄를 이루기 위한 재료 및 방법들이 연구되어왔다. 이중 상아질 접착제는 근관 충전재와 함께 사용되어 미세누출을 감소시키지만, 근관 내에 사용하기에 술식이 복잡하고 기술이 요구된다. 본 연구의 목적은 gutta-percha와 레진계 근관 sealer로 충전한 근관에서 self-etching primer를 미리 도포한 경우와 도포하지 않은 경우의 치근단 미세누출을 비교하고, self-etching primer를 도포함에 있어 근관 내에 적용하는 방법에 따른 미세누출을 비교하는 것이다. 또한 근관sealer와 상아질 계면을 주사전자현미경으로 관찰하여, 이 결과를 미세누출과 관련시켜보고자 하였다. 36개의 발거된 사람의 단근치에서 치관부를 절단, 제거하고 ProFile로 근관 형성한 후, 무작위로 선택하여 4개의 군으로 분류하였다. 1군에서는 주사기와 30게이지 주사 바늘로 self-etching primer를 근관 내에 적용하였고, 2군에서는 self-etching primer를 paper point에 적셔 근관 내에 적용하였다. 3군에서는 self-etching primer를 적용하지 않았다. 1, 2, 3군의 치아를 gutta-percha와 AH26 sealer를 사용하여 continuous wave 충전법으로 충전한 후 치근단공 주위 3mm를 제외한 치근변에 nail polish를 2회 도포하였고, 4군(음성 대조군)은 치근면 전체에 도포하였다. 1군과 2군에서 각각 2개의 치아는 주사전자현미경적 관찰을 위해 준비하였다. 모든 치아를 Methylene Blue 수용액에 48시간동안 침적, 수세한 후 치아 장축에 평행하게 양분하여 10배의 실물확대현미경 하에서 치근단 색소 침투를 관찰하였다. Self-etching primer를 도포한 군과 도포하지 않은 군 사이에는 평균 미세누출량에 유의한 차이가 없었다. 주사 바늘로 적용한 군과 paper point로 적용한 군 사이에도 평균 미세누출량에 유의한 차이가 없었다. 상아질과 근관 sealer계면의 주사전자현미경 관찰 결과 일부분에서 긴밀한 접착 관계를 나타내었고, 다른 부분에서는 간극을 나타내었다.

• Restorative Dentistry and Endodontics
• /
• v.27 no.4
• /
• pp.363-369
• /
• 2002

최근에 많이 사용되어지고 있는 치과용 접착제는 산 부식 후 수분이 있는 상태에서 적용하는 wet-bonding 술식을 많이 추천하고 있다. 하지만 self-etching primer의 경우 산부식과 priming 과정이 동시에 시행되고, 제조자들은 건조된 치아표면에 적용할 것을 추천하고 있다. 그러나 건조된 정도에 대하여서는 별다른 추천사항이 없으며. 수분이 self-etching primer에 어떤 영향을 미치는지에 대하여서는 별다른 연구가 이루어져 있지 않은 상태이다. 이에 본 연구에서는 치질 삭제 후 남아있는 수분이 self-etching primer의 레진 접착 강도에 어떤 영향을 미치는 지를 알아보고자 하였다. 발거한 대구치 96개를 이용하여 물기가 있는 상태에서 #600 사포로 표면을 연마하고, 법랑질 면을 노출시킨 군과 상아질을 노출시킨 군으로 분류 후, 30분 공기 중 방치 군 (1군), 5초 공기 건조 군 (2군), 1초 공기 건조 군 (3군), 솜으로 약간의 물기를 제거한 군(blot dry) (4군) 등 총 8개의 군으로 나누었다. Self-etching adhesive system인 Clearfil SE Bond primer를 20초간 적용하고, bonding제 도포 후 10초간 광중합 시행하였다. 접착제 처리한 치아면에 몰드를 고정한 후 Clearfil AP-X 복합레진을 2mm 충전하고, 40초간 광중합을 시행하였다. 24시간 후 전단 응력 결합강도를 측정하였으며, 그 결과는 다음과 같이 나타났다. 법랑질과 상아질 모두에서, 30분 건조군과 5초 공기건조군이 1초와 blot drying 군보다 높은 결합강도를 보였으며 통계학적으로 유의한 차이를 보였다(p＜0.05). 본 실험 결과에 의하면 self-etching adhesive system을 사용함에 있어서 법랑질과 상아질군 공히 건조된 상태에서 사용하여야 하며 수분의 존재시 치아와의 결합력이 감소하는 것으로 나타났다. 따라서 임상에서 접착제의 적용시 수분의 조절에 주의하여야 할 것으로 사료된다.

• Journal of Korean Dental Science
• /
• v.2 no.2
• /
• pp.5-11
• /
• 2009

Objectives : This study investigated the hypothesis that the dentin bond strength of self-etching adhesives (SEAs) may be improved by applying a coat of hydrophobic, neutral adhesive resin in addition to SEA. Method and Materials : The bond strengths of two SEAs - Experimental SEA (EX) and Adper Prompt (AP) - were measured with three bonding protocols. The D/E resin of All-Bond 2 was applied as the hydrophobic, neutral adhesive. Clearfil SE Bond (SE, self-etching primer system) and All-Bond 2 (AB, total etching system) were used as references. The following protocols were used: (1) EX1 (EX 1 coat); (2) EX2 (EX 2 coats); (3) EX+ (EX 1 coat + D/E resin); (4) AP1 (AP 1 coat); (5) AP2 (AP 2 coats); (6) AP+ (AP 1 coat + D/E resin); (7) SE (SE primer + SE bond); (8) SE+ (SE primer + D/E resin); (9) AB (etching + AB primer + D/E resin). Filtek Z250 composite resin was built up and the microtensile bond strength (MTBS) values of the specimens were compared. The fractured surfaces were observed using SEM. Results : When SEA was used as self-etching primer and hydrophobic, neutral adhesive was applied as well, MTBS was significantly higher than that when either one coat or two coats of SEA only were used (p < 0.05). Conclusion : The hydrophobic, neutral adhesive improved the integrity of the bonded interface obtained with SEA.

• The korean journal of orthodontics
• /
• v.35 no.6 s.113
• /
• pp.433-442
• /
• 2005

The purpose of this study was to evaluate and compare the shear bond strength of orthodontic brackets depending on the variety of adhesives and whether saliva exists, by using self-etching primer (SEP). Groups were divided according to the type of adhesive into resin adhesive (Trans bond XT) and resin-modified glass ionomer cement (Fuji Ortho LC). One group of resin adhesive used XT primer after etching with 37% phosphoric acid, and the other group used self-etching primer. One group of resin-modified glass ionomer cement only used etching for bonding, and the other group used SEP. Each of the groups were also classified by whether saliva was contaminated or not. and then the shear bond strength was measured. The results showed that when using resin adhesive, the shear bond strength of SEP was lower than the XT primer. In the resin-modified glass ionomer cement groups, the shear bond strength which depends on the priming method, did not have a meaningful difference statistically When saliva was contaminated, the group which used SEP, regardless of the adhesive variety, had a greater shear bond strength than the normal priming group. From these results, SEP showed a shear bond strength that is possible to be used clinically, regardless of the adhesive variety. It can especially be clinically useful to use SEP to bond brackets even on tooth surfaces contaminated with saliva, because it offers the appropriate bonding strength as well as shorter treatment time and easy application.