• 한국세라믹학회지
• /
• 제44권12호
• /
• pp.690-695
• /
• 2007

Scandia stabilized zirconia (ScSZ) is adapted for electrolyte material of solid oxide fuel cell (SOFC) because of its high ionic conductivity and chemical stability. ScMnSZ1 powder having a composition of $((ZrO_2)_{0.89}(Sc_2O_3)_{0.1}(MnO_2)_{0.01})$ is synthesized by ultrasonic spray pyrolysis (USP) method. Porous ScMnSZ1 powder is obtained by using a pore forming agent. Microstructure and morphology, particle size distribution of porous powder synthesized with 3wt% pore forming agent are investigated. Sintered ScMnSZ1 sample with ground fine powder are also investigated their microstructure and electrical conductivity. The electrical conductivity of sintered ScMnSZ1 samples with ground fine powder was 0.082 S/cm, 0.127 S/cm and 0.249 S/cm at $750^{\circ}C$, $800^{\circ}C$ and $900^{\circ}C$, respectively.

• 한국세라믹학회지
• /
• 제45권12호
• /
• pp.788-795
• /
• 2008

An electrolyte supported SOFC cell was tested at $800^{\circ}C$ in air for 3600 h with an applied current density of $200\;mA/cm^2$ to examine possible cathode degradation issues. A scandium- stabilized zirconia (ScSZ) with additional manganese doping (ScSZ: Mn) was used as electrolyte. A strontium and copper-doped lanthanum ferrite (LaSrCuFe) and platinum were used as cathode and quasi-anode material, respectively. The DC resistance was logged over the complete testing period. Additionally, impedance spectroscopy was used from time to time to track changes of the cell in-situ. Post-test analysis of the cell using methods like scanning electron microscopy imaging and other electrochemical testing methods allow the identification of different degradation sources. The results indicate a promising combination of electrolyte and cathode material in terms of chemical compatibility and electrical performance.

• 한국세라믹학회지
• /
• 제53권5호
• /
• pp.500-505
• /
• 2016

Scandia-stabilized zirconia co-doped with $CeO_2$ is a promising electrolyte for intermediate temperature SOFC, but still shows rapid degradation during a long-term operation. In this study, $CeO_2$ (1 mol%) as a stabilizer is partially substituted with lanthanum oxides ($M_2O_3$, M=Yb, Gd, Sm) to stabilize a cubic phase and thus durability in reducing atmosphere. 0.5M0.5Ce10ScSZ electrolytes were prepared by solid state reaction and sintered at $1450^{\circ}C$ for 10 h to produce dense ceramic specimens. With addition of the lanthanum oxide, 0.5M0.5Ce10ScSZ showed lower degradation rates than 1Ce10ScSZ. Since $Gd_2O_3$ showed the highest ionic conductivity among the co-dopants, an electrolyte-supported cell with 0.5Gd0.5Ce10ScSZ was prepared to compare its long-term performance with that of 1Ce10ScSZ-based cell. Maximum power density of 0.5Gd0.5Ce10ScSZ-based cell was degraded by about 2.3% after 250 h, which was much lower than 1Ce10ScSZ-based cell (4.2%).

• 한국세라믹학회지
• /
• 제45권12호
• /
• pp.760-765
• /
• 2008

In this study, the effects of small amounts (${\leq}3\;mol%$) of Li doping on the sintering characteristics and electrochemical performance of $(ZrO_2)_{0.89}(ScO_{1.5})_{0.1}(CeO_2)_{0.01}$ (ScSZ) were investigated. By adding 3 mol% lithium, the densification temperature of ScSZ was reduced from the conventional temperature of $1400^{\circ}C$ to $1200^{\circ}C$. It was found that Li doping also led to changes in the Zr:Sc ratio at the grain boundaries. Correspondingly, the dispersion of lithium zirconia at the grain boundaries accelerated the growth of ScSZ grains and increased the grain boundary resistance at temperatures below $450^{\circ}C$. At elevated temperatures of $450{\sim}750^{\circ}C$, the electrical conductivity of the ScSZ after doping remained almost unchanged under air and reducing atmospheres. These results suggest that the addition of lithium is promising for use in low temperature co-firing of ScSZ-based components for intermediate temperature solid oxide fuel cells.

• 한국세라믹학회지
• /
• 제43권6호
• /
• pp.369-375
• /
• 2006

[ $(Ba_{0.5}Sr_{0.5})_{0.99}Co_{x}Fe_{1-x}O_{3-{\delta}}$ ] [x=0.8, 0.2](BSCF) powders were synthesized by a Glycine-Nitrate Process (GNP) and the electrochemical performance of the BSCF cathode on a scandia stabilized zirconia, $[(Sc_{2}O_3)_{0.11}(ZrO_2)_{0.89}]-1Al_{2}O_3$ was investigated. In order to prevent unfavorable solid-state reactions between the cathode and zirconia electrolyte, a GDC ($Gd_{0.1}Ce_{0.9}O_{2-{delta}}$) buffer layer was applied on ScSZ. The BSCF (x = 0.8) cathode formed on GDC(Buffer)/ScSZ(Disk) showed poor electrochemical property, because the BSCF cathode layer peeled off after the heat-treatment. On the other hand, there were no delamination or peel off between the BSCF and GDC buffer layer, and the BSCF (x = 0.2) cathode exhibited fairly good electrochemical performances. It was considered that the observed phenomenon was associated with the thermal expansion mismatch between the cathode and buffer layer. The ohmic resistance of the double layer cathode was slightly lower than that of the single layer BSCF cathode due to the incorporation of platinum particle into the BSCF second layer.

• 신재생에너지
• /
• 제5권1호
• /
• pp.11-17
• /
• 2009

To improve the performance of the anode-supported Solid Oxide Fuel Cell (SOFC) which can be operated at an intermediate temperature, the functional layer (FL) is introduced on a anode substrate. And the scandia-stabilized zirconia (ScSZ) and samaria-doped ceria (SDC) which have higher ionic conductivity and better chemical stability than yttria-stabilized zirconia (YSZ) are used as material for the anode FL with the Ni, The fabrication process of anode-supported single cell with the anode FL was established and the power density of those was evaluated. As a result, the sample with anode FL (Ni-YSZ) has higher power density than normal cell. The single cell which was composed of the FL (Ni-YSZ) and electrolyte (YSZ) showed about $550mW/cm^2$ of the maximum power density at $650^{\circ}C$ and $1430mW/cm^2$ at $750^{\circ}C$ respectively, In case of the single cell using the ScSZ and SDC as anode FL, the performance of samples decreased rapidly and those showed unstable voltage during long-term test. In case of using methane as a fuel, the cell performance with each FL decreased comparing with $H_2$ fuel. In the region of a high current density, there are large concentration polarizations.

• 한국세라믹학회지
• /
• 제53권5호
• /
• pp.489-493
• /
• 2016

Scandia ($Sc2O_3$)-stabilized zirconia (ScSZ) electrolyte-supported symmetrical solid oxide electrolyzer cells (SOECs), in which lanthanum strontium cobalt ferrite (LSCF)-gadolinia ($Gd_2O_3$)-doped ceria (GDC) composite materials are used as both the cathode and anode, were fabricated and their high temperature steam electrolysis (HTSE) performance was investigated. Current density-voltage curves were obtained for cells operated in 10% $H_2O$/90% Ar at 750, 800, and $850^{\circ}C$. It was possible to determine the ohmic, cathodic, and anodic contributions to the total overpotential using the three-electrode technique. The HTSE performance was significantly improved in the symmetrical cell with LSCF-GDC electrodes compared to the cell consisting of an Ni-YSZ cathode and LSCF-GDC anode. It was found that the overpotential due to the LSCF-GDC cathode largely decreased and, at a given current density, the total cell voltage decreased, which resulted in the enhanced hydrogen production rate in the symmetrical cell.

• 전기화학회지
• /
• 제10권4호
• /
• pp.288-294
• /
• 2007

Modified oxalate method에 의해 합성한 중온형 Solid Oxide Fuel Cell 용 LSCF cathoded의 pH 변화에 따른 분말특성 및 여러 종류의 전해질에 따른 전극특성에 대해 연구하였다. LSCF를 합성하기 위한 출발물질로는 La, Sr, Co 및 Fe의 염화물과 oxalic acid, ethanol 및 $NH_4OH$를 사용하여, $80^{\circ}C$ 에서 pH 2, 6, 7, 8, 9 및 10에서 합성하였다. 합성한 LSCF 분말은 pH $2{\sim}9$까지는 단일상의 LSCF 결정상을 생성하였다. 그러나, PH 10에서는 LSCF결정상 외에 이차상인 $La_2O_3$ 결정상이 나타났으며, 또한 $800^{\circ}C$에서 4시간 하소한 경우 50 nm정도의 작은 크기를 나타내었다. 합성한 LSCF cathode 분말의 전기전도도는 pH 7에서 합성한 LSCF 분말의 경우 $600^{\circ}C$부터 $900^{\circ}C$까지 측정하였을 때 약 950 S/cm의 높은 값을 나타내었다. 또한 분극저항의 경우 같은 합성 조건에서 합성한 LSCF 분말이라도 하소조건에 따라 다른 결과를 나타내었는데, $800^{\circ}C$에서 하소한 분말의 경우 $1200^{\circ}C$에서 하소한 분말 보다 낮은 분극저항을 나타내었다. 특히 $800^{\circ}C$에서 4시간 하소하여 합성한 LSCF 분말은 $600^{\circ}C$에서 Scandia Stabilized Zirconia (ScSZ), yttria (8mol.%)-stabilized zirconia(8Y-YSZ) 및 Gadolinium Doped Ceria(GDC) 전해질을 사용하였을 때, 전극면적이 $0.5\;cm^2$일 때 각각 2.52, 1.54 및 $2.58\;{\Omega}$을 나타내었다.