• 한국세라믹학회지
• /
• 제45권12호
• /
• pp.788-795
• /
• 2008

An electrolyte supported SOFC cell was tested at $800^{\circ}C$ in air for 3600 h with an applied current density of $200\;mA/cm^2$ to examine possible cathode degradation issues. A scandium- stabilized zirconia (ScSZ) with additional manganese doping (ScSZ: Mn) was used as electrolyte. A strontium and copper-doped lanthanum ferrite (LaSrCuFe) and platinum were used as cathode and quasi-anode material, respectively. The DC resistance was logged over the complete testing period. Additionally, impedance spectroscopy was used from time to time to track changes of the cell in-situ. Post-test analysis of the cell using methods like scanning electron microscopy imaging and other electrochemical testing methods allow the identification of different degradation sources. The results indicate a promising combination of electrolyte and cathode material in terms of chemical compatibility and electrical performance.

• 신재생에너지
• /
• 제5권1호
• /
• pp.11-17
• /
• 2009

To improve the performance of the anode-supported Solid Oxide Fuel Cell (SOFC) which can be operated at an intermediate temperature, the functional layer (FL) is introduced on a anode substrate. And the scandia-stabilized zirconia (ScSZ) and samaria-doped ceria (SDC) which have higher ionic conductivity and better chemical stability than yttria-stabilized zirconia (YSZ) are used as material for the anode FL with the Ni, The fabrication process of anode-supported single cell with the anode FL was established and the power density of those was evaluated. As a result, the sample with anode FL (Ni-YSZ) has higher power density than normal cell. The single cell which was composed of the FL (Ni-YSZ) and electrolyte (YSZ) showed about $550mW/cm^2$ of the maximum power density at $650^{\circ}C$ and $1430mW/cm^2$ at $750^{\circ}C$ respectively, In case of the single cell using the ScSZ and SDC as anode FL, the performance of samples decreased rapidly and those showed unstable voltage during long-term test. In case of using methane as a fuel, the cell performance with each FL decreased comparing with $H_2$ fuel. In the region of a high current density, there are large concentration polarizations.

• 한국세라믹학회지
• /
• 제53권5호
• /
• pp.489-493
• /
• 2016

Scandia ($Sc2O_3$)-stabilized zirconia (ScSZ) electrolyte-supported symmetrical solid oxide electrolyzer cells (SOECs), in which lanthanum strontium cobalt ferrite (LSCF)-gadolinia ($Gd_2O_3$)-doped ceria (GDC) composite materials are used as both the cathode and anode, were fabricated and their high temperature steam electrolysis (HTSE) performance was investigated. Current density-voltage curves were obtained for cells operated in 10% $H_2O$/90% Ar at 750, 800, and $850^{\circ}C$. It was possible to determine the ohmic, cathodic, and anodic contributions to the total overpotential using the three-electrode technique. The HTSE performance was significantly improved in the symmetrical cell with LSCF-GDC electrodes compared to the cell consisting of an Ni-YSZ cathode and LSCF-GDC anode. It was found that the overpotential due to the LSCF-GDC cathode largely decreased and, at a given current density, the total cell voltage decreased, which resulted in the enhanced hydrogen production rate in the symmetrical cell.

• 한국세라믹학회지
• /
• 제53권5호
• /
• pp.500-505
• /
• 2016

Scandia-stabilized zirconia co-doped with $CeO_2$ is a promising electrolyte for intermediate temperature SOFC, but still shows rapid degradation during a long-term operation. In this study, $CeO_2$ (1 mol%) as a stabilizer is partially substituted with lanthanum oxides ($M_2O_3$, M=Yb, Gd, Sm) to stabilize a cubic phase and thus durability in reducing atmosphere. 0.5M0.5Ce10ScSZ electrolytes were prepared by solid state reaction and sintered at $1450^{\circ}C$ for 10 h to produce dense ceramic specimens. With addition of the lanthanum oxide, 0.5M0.5Ce10ScSZ showed lower degradation rates than 1Ce10ScSZ. Since $Gd_2O_3$ showed the highest ionic conductivity among the co-dopants, an electrolyte-supported cell with 0.5Gd0.5Ce10ScSZ was prepared to compare its long-term performance with that of 1Ce10ScSZ-based cell. Maximum power density of 0.5Gd0.5Ce10ScSZ-based cell was degraded by about 2.3% after 250 h, which was much lower than 1Ce10ScSZ-based cell (4.2%).

• 전기화학회지
• /
• 제10권4호
• /
• pp.288-294
• /
• 2007

Modified oxalate method에 의해 합성한 중온형 Solid Oxide Fuel Cell 용 LSCF cathoded의 pH 변화에 따른 분말특성 및 여러 종류의 전해질에 따른 전극특성에 대해 연구하였다. LSCF를 합성하기 위한 출발물질로는 La, Sr, Co 및 Fe의 염화물과 oxalic acid, ethanol 및 $NH_4OH$를 사용하여, $80^{\circ}C$ 에서 pH 2, 6, 7, 8, 9 및 10에서 합성하였다. 합성한 LSCF 분말은 pH $2{\sim}9$까지는 단일상의 LSCF 결정상을 생성하였다. 그러나, PH 10에서는 LSCF결정상 외에 이차상인 $La_2O_3$ 결정상이 나타났으며, 또한 $800^{\circ}C$에서 4시간 하소한 경우 50 nm정도의 작은 크기를 나타내었다. 합성한 LSCF cathode 분말의 전기전도도는 pH 7에서 합성한 LSCF 분말의 경우 $600^{\circ}C$부터 $900^{\circ}C$까지 측정하였을 때 약 950 S/cm의 높은 값을 나타내었다. 또한 분극저항의 경우 같은 합성 조건에서 합성한 LSCF 분말이라도 하소조건에 따라 다른 결과를 나타내었는데, $800^{\circ}C$에서 하소한 분말의 경우 $1200^{\circ}C$에서 하소한 분말 보다 낮은 분극저항을 나타내었다. 특히 $800^{\circ}C$에서 4시간 하소하여 합성한 LSCF 분말은 $600^{\circ}C$에서 Scandia Stabilized Zirconia (ScSZ), yttria (8mol.%)-stabilized zirconia(8Y-YSZ) 및 Gadolinium Doped Ceria(GDC) 전해질을 사용하였을 때, 전극면적이 $0.5\;cm^2$일 때 각각 2.52, 1.54 및 $2.58\;{\Omega}$을 나타내었다.