• Bulletin of the Korean Chemical Society
• /
• 제22권11호
• /
• pp.1255-1260
• /
• 2001

The expansion of two different kinds of hydrodynamic size of polymethyl methacrylate (PMMA Mw: 1.56- 2.04 ${\times}$ 106 g/mol) has been measured by dynamic light scattering and viscometry above the Flory $\theta$ temperature of the variou s solvents such as n-butyl chloride, 3-heptanone, and 4-heptanone. The expansion of PMMA chains was analyzed in terms of universal temperature parameters and also compared with previous results of polystyrene (PS) system. First it was found that simple $\tau/{\tau}c$ parameter no longer had its universality for the expansion behavior of hydrodynamic size in the chemically different linear polymer chains. However after modifying ${\tau}/{\tau}c$ parameter into $(Mw/Ro2)3}2(\tau/\tauc)$, we observed a much better universality for both PMMA and PS systems. Here Mw, Ro, $\tau[=(T-{\theta}$)/${\theta}$]$, and ${\tau}c[=({\theta}-Tc)/Tc]$ are defined as the weight average molecular weight, the unperturbed end-to-end distance, the reduced temperature and the reduced critical temperature, respectively.

• 폴리머
• /
• 제27권3호
• /
• pp.255-264
• /
• 2003

세팔 별모양 폴리스타이렌 (PS, $M_{w}$=2.80$\times$$10^{5}$ , 2.49$\times$$10^{6}$ g/mol)의 여러 종류의 사슬 크기를 t-decalin 용액의 온도 20~7$0^{\circ}C$ 사이에서 점성도법, 레이저 광산란법을 이용하여 측정하였다. 별모양 고분자들의 팽창이 만능성을 갖기 위하여서는 그들 자신의 교란되지 않은 회전 반경 $R_{G,Br,o}$이 포함된 (N/ $R_{G,Br,o}$$^{2}$)$^{3}$2/$ au$/$\tau$$_{C}$ 파라미터가 사용될 것으로 예측하였으나, 실험 결과는 오히려 선형 폴리스타이렌 고분자의 교란되지 않은 회전 반경이 사용된 (N/ $R_{G,Br,o}$$^{2}$)$^{3}$2/$\tau$/$\tau$$_{C}$ 파라미터가 보다 우수한 만능성을 보여 주었다. 이러한 이유는 가지 효과가 $\tau$/$\tau$$_{C}$(=[(Τ-Θ$_{Tc}$ )/Θ$_{Tc}$ ]/[(Θ$_{Tc}$ -Τ$_{c}$)/ $T_{c}$])부분에서 이미 반영되어 척도 상수 N/ $R_{G,O}$$^{2}$ 부분에서는 나타나지 않는 것으로 생각되어진다. 여기서 N은 고분자 사슬을 이루고 있는 단량체의 개수, Θ$_{Tc}$ 는 고분자의 분자량이 무한대일 때의 임계 용액 온도로써의 Θ 온도를 각각 의미한다.미한다.미한다.다.