• 한국신재생에너지학회:학술대회논문집
• /
• 2009.06a
• /
• pp.295-298
• /
• 2009

Oxygen ionic conductors of CeScSZ electrolyte in SOFC unit cell are applied to anode and cathode as well as electrolyte to have the triple-phase-boundaries of electrochemical reaction, and it is required to decrease the sintering temperature of anode-supported electrolyte by the nanoscale of CeScSZ electrolyte powder. In this report, nanoscale CeScSZ electrolyte powder was synthesized by chemical synthesis method. The particle size, surface area and morphology of the powder were observed by SEM and BET. Thin film electrolyte of under $10{\mu}m$ was fabricated by tape casting using the synthesized CeScSZ electrolyte powder, and ionic conductivity and gas permeability of electrolyte film were evaluated. Finally the SOFC unit cell was fabricated using the anode-supported electrolyte prepared by a tape casting method and co-sintering, in which the active layer, measuring $20{\mu}m$, was introduced in the anode layer to provide a more efficient reaction. Electrochemical evaluations of the SOFC unit cell, including measurements such as power density and impedance, were performed and analyzed.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.06a
• /
• pp.138.2-138.2
• /
• 2010

Scandium-doped zirconium, ScSZ-based electrolyte, provides higher oxygen conductivity than YSZ and nano-based electrolyte materials are ideal for fabricating thin film electrolyte membrane of SOFC unit cell. Moreover, it may be applied to anode and cathode as well as electrolyte as ionic conductor. In this report, nano-based ScSZ-based electrolyte powder was prepared by co-precipitation synthesis. The particle size, surface area and morphology of the powder were observed by SEM and BET. Thin film electrolyte of under $10{\mu}m$ was fabricated by tape casting and co-firing using the synthesized ScSZ-based powders, and ionic conductivity and gas permeability of electrolyte film were evaluated. Finally, the SOFC unit cell was fabricated using the anode-supported electrolyte prepared by a tape casting method and co-sintering. Electrochemical evaluations of the SOFC unit cell, including measurements such as power density and impedance, were performed and analyzed.

• 한국전기화학회:학술대회논문집
• /
• 2004.10a
• /
• pp.35-35
• /
• 2004

• Ceramist
• /
• v.21 no.4
• /
• pp.378-387
• /
• 2018

The optimal fabrication conditions for $Gd_{0.1}Ce_{0.9}O_{2-{\delta}}$(GDC) buffer layer and $La_{0.6}Sr_{0.4}Co_{0.2}Fe_{0.8}O_{3-{\delta}}$ (LSCF) cathode on 1mol% $CeO_2-10mol%\;Sc_2O_3$ stabilized $ZrO_2$ (CeScSZ) electrolyte were investigated for application of IT-SOFCs. GDC buffer layer was used in order to prevent undesired chemical reactions between LSCF and CeScSZ. These experiments were carried out with $5{\times}5cm^2$ anode supported unit cells to investigate the tendencies of electrochemical performance, Microstructure development and interface reaction between LSCF/GDC/CeScSZ along with the variations of GDC buffer layer thickness, sintering temperatures of GDC and LSCF were checked, respectively. Electrochemical performance was analyzed by DC current-voltage measurement and AC impedance spectroscopy. Microstructure and interface reaction were investigated by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). Although the interfacial reaction between these materials could not be perfectly inhibited, We found that the cell, in which $6{\mu}m$ GDC interlayer sintered at $1200^{\circ}C$ and LSCF sintered at $1000^{\circ}C$ were applied, showed good interfacial adhesions and effective suppression of Sr, thereby resulting in fairly good performance with power density of $0.71W/cm^2$ at $800^{\circ}C$ and 0.7V.

• Journal of the Korean Electrochemical Society
• /
• v.10 no.4
• /
• pp.288-294
• /
• 2007

The LSCF cathode far Solid Oxide Fuel Cell was investigated to develop high performance unit cell at intermediate temperature by modified oxalate method with different electrolytes and different pH. The LSCF powders employed La, Sr, Co and Fe oxides, oxalic acid, ethanol and $NH_4OH$ solution were synthesized with pH controlled as 2, 6, 7, 8, 9 and 10 at $80^{\circ}C$ Single crystalline phase was obtained from pH $2{\sim}9$. on the other hand, $La_2O_3$ appeared from pH 10. Very fine powder with particle size of 50 nm was obtained at calcination temperature of $800^{\circ}C$ for 4 hours. LSCF cathode synthesized at pH 7 showed the highest electric conductivity in the temperature range of $600^{\circ}C$ to $900^{\circ}C$ its value was 950 S/cm at $900^{\circ}C$ Under same synthesis conditions, polarization resistance of each LSCF cathode was changed with different calcination temperatures. As-prepared powder presented 2.52, 1.54 and $2.58\;{\Omega}$ at $600^{\circ}C$ with ScSZ, 8Y-YSZ and GDC as its electrolyte respectively after calcination at $800^{\circ}C$ for 4 hours.