• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.897-900
• /
• 2001

Space charge distributions in silane crosslinked polyethylene (SXLPE)/ crosslinked polyethylene (XLPE) laminates was investigated using a pulsed electroacoustic (PEA) method. XLPE shows heterocharge while SXLPE shows homocharge. Positive charge is accumulated at the interface of SXLPE/XLPE laminate when applied electric field is more than 20 kV/mm. The charge profile at various temperatures was also acquired using temperature-controllable PEA system. Although applied electric field is only 8.6 kV/mm, positive interfacial charge starts to appear near 50$^{\circ}C$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.2
• /
• pp.127-132
• /
• 2002

Space charge distributions and behaviors in silane crosslinked polyethylene(SXLPE)/ crosslinked polyethylene(XLPE) laminates were investigated using a pulsed electroacoustic (PEA) method. In case of monolayer, XLPE shows heterocharge while SXLPE shows homocharge. It was observed that charges were accumulated at the interface of SXLPE/XLPE laminate when applied electric field was more than 20kV/mm. The charge profile at various temperatures was also acquired using temperature-controllable PEA system. Although applied electric field is only 8.6 kV.mm, positive interfacial charge starts to appear near 50$^{\circ}C$. It was found that the interfacial charge behavior of SXLPE/XLPE laminate under low voltage at high temperature is corresponding to that under high voltage at room temperature.