• Proceedings of the KSME Conference
• /
• 2001.11a
• /
• pp.117-122
• /
• 2001

For two kinds of 25Cr-20Ni stainless steels, SUS310J1TB TB and SUS310S with and without a small amount of Nb and N, creep behavior has been studied in a stress and temperature range from 147 to 392MPa and from 923 to 973K with a special reference to tertiary creep. The average creep life of SUS310J1TB was about 100 times longer than that of the SUS310S. The apparent activation energy for the initial creep rate was 330 kJ/mol in SUS310J1TB, while that of the SUS310S was 274 kJ/mol in a power law creep region and 478 kJ/mol in a region of power law breakdown (PLB). The activation energy for SUS310S below PLB is close to the that for self-diffusion. When compensating for the temperature dependence of the Young's modulus and the omega value, it was found that the apparent activation energy for SUS310J1TB was reduced to the activation energy for diffusion of chromium atom in a gamma steel. The stress exponent of SUS310S was about 12 above PLB and 5.1 in a power law creep region. Notwithstanding that the creep condition for SUS310J1TB was in a power law creep region, its stress exponent was 8.3 larger than that of SUS310S corresponding to the same creep conditions. This was ascribed to the presence of fine precipitates in SUS310J1TB.

• 한국전기화학회:학술대회논문집
• /
• 1999.10a
• /
• pp.36-36
• /
• 1999

• Journal of Energy Engineering
• /
• v.10 no.2
• /
• pp.132-139
• /
• 2001

석탄가스화 복합발전의 집진 공정에 사용하기 위한 금속제 safety filter의 재질 선정을 위하여 황화수소 가스 분위기에서 합금강의 부식 특성을 규명하였다. 사용 합금강은 SUS 310, SUS 316, Inconel 600과 Hastelloy X이다. 전기로 내에 설치된 지름 50mm의 qualtz 튜브 반응기에서 부식실험이 행하여졌다. 40$0^{\circ}C$부터 $700^{\circ}C$까지의 등은 조건에서 실험이 행하여졌고, 분위기 가스의 영향을 보기 위하여 H$_2$S 가스를 함유한 $N_2$(dry), $N_2$(saturation), $CO_2$(dry), 그리고 석탄가스 분위기에서 실험하였다. 부식 생성물을 파악하기 위하여 X-ray 회절기와 주사전자현미경 분석이 함께 이루어졌다. 1.7% H$_2$S, $600^{\circ}C$ 이하 온도 조건에서는 니켈계 내식강 중 Hastelloy X와 철계 내식강 중 SUS 310 등 고크롬 합금강이 IGCC 용 필터 소재 금속으로서 높은 내부식성을 나타내었다. 0.3%~4.99% 황화수소 농도 범위에서 황화수소 농도 변화에 따라서 SUS 310의 경우 3~237mg/d$m^2$.day, Inconel 600의 경우 4~660mg/d$m^2$.day로 부식속도는 크게 증가되었다. 50$0^{\circ}C$, 석탄가스 분위기에서 부식속도는 SUS 310은 45mg/d$m^2$.day, SUS 316은 110mg/d$m^2$.day, Inconel 600은 576mg/d$m^2$.day, 그리고 Hastelloy X 는 140mg/d$m^2$.day로서 합금강 시편 중 SUS 310 합금강이 가장 우수한 내식성을 나타내었다. 부식 표면에는 황화니켈, 황화철 피막이 형성되었다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.360-360
• /
• 2011

In this work, SUS310S used for valve plate assembly was electron beam (EB) welded to determine the influence of the parametric conditions on the characteristics of the weld and to minimize porosity and micro-fissures among others. The evolution in the weld geometry and microstructure was examined as a function of the process conditions such as beam current and focusing current under a constant welding speed and accelerating voltage. The integrity of the EB welds in SUS310S was examined for defects (e.g. cracking, porosity, etc.), adequate penetration depth, and tolerable weld width deviation for the various welding conditions. Optical microscopy (OM), x-ray photoelectron spectroscopy analysis (XPS), scanning electron microscopy (SEM) and 3D micro-computed tomography (Micro-CT) for the cross section analysis of the electron beam welded SUS310S were utilized. The tensile strength and hardness were analyzed for the mechanical properties of the EB weld. At the 6 kV accelerating voltage, it was determined that a satisfactory penetration depth and desirable weld width deviation requires a beam current of 30 mA and a focusing current of 0.687 A at the welding speed of 25 mm/sec.

• Proceedings of the KWS Conference
• /
• 1994.05a
• /
• pp.113-114
• /
• 1994

• Progress in Superconductivity
• /
• v.12 no.2
• /
• pp.118-123
• /
• 2011

The properties of $2^{nd}$ generation high temperature superconducting wire, coated conductor strongly depend on the quality of superconducting oxide layer and property of metal substrate is one of the most important factors affecting the quality of coated conductor. Good mechanical and chemical stability at high temperature are required to maintain the initial integrity during the various process steps required to deposit several layers consisting coated conductor. And substrate need to be nonmagnetic to reduce magnetization loss for ac application. Hastelloy and stainless steel are the most suitable alloys for metal substrate. One of the obstacles in using stainless steel as substrate for coated conductor is its difficulties in making smooth surface inevitable for depositing good IBAD layer. Conventional method involves several steps such as electro polishing, deposition of $Al_2O_3$ and $Y_2O_3$ before IBAD process. Chemical solution deposition method can simplify those steps into one step process having uniformity in large area. In this research, we tried to improve the surface roughness of stainless steel(SUS310). The precursor coating solution was synthesized by using yttrium complex. The viscosity of coating solution and heat treatment condition were optimized for smooth surface. A smooth amorphous $Y_2O_3$ thin film suitable for IBAD process was coated on SUS310 tape. The surface roughness was improved from 40nm to 1.8 nm by 4 coatings. The IBAD-MgO layer deposited on prepared substrate showed good in plane alignment(${\Delta}{\phi}$) of $6.2^{\circ}$.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2013.05a
• /
• pp.100-101
• /
• 2013

가스 터빈, 석유 화학 공장 등에 널리 사용되고 있는 합금들은 IGCC 분위기에서 심각한 부식이 야기된다. 특히 고온에서 가스터빈 재료로 사용되는 초내열 합금 등도 열악한 고온 황화분위기에서는 열악한 내부식성을 보였다. 따라서 이러한 조건에서 견딜 수 있는 재료의 개발이 필요하다. 일반적으로 알려진 내부식성 증가 방법은 내부식성 합금원소 첨가와 재료 표면에 직접 코팅을 하는 방법이 있으며, 본 연구에서는 고온의 $H_2S$ 가스 분위기에서 Pack cementation으로 Al과 Cr 확산코팅 시킨 시편을 이용하여 부식실험을 실시하여 부식 특성을 살펴보았다.

• Transactions of Materials Processing
• /
• v.32 no.6
• /
• pp.303-310
• /
• 2023

Electrohydraulic forming(EHF), one of the high-speed forming method, can supplement the weak point of previous forming process such as deep-drawing and electromagnetic forming. Indeed, EHF is time-consuming process during installing wire before experiment that hard to apply to industry. In this research, applying wireless electrode, the formability of SUS430 sheet was compared through EHF experiments using wire-installed electrode and the other, wireless. Although the power was a little lacking, the advantages of the experiment using wireless electrode could be confirmed with checking the optimal location of electrodes where the plasma is generated and comparing free-bulging height depending on former and later condition of electrodes with performing several single and multistage experiments for same voltage, 6 kV.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 1998.05a
• /
• pp.21-21
• /
• 1998

새로운 에너지원으로 각광받고 있는 연료전지는 우주선 동력윈으로서의 이용이래, 보다 실용적인 발전 시스템을 목적으로 많은 연구개발이 시도되고 있다. 이러한 연료전지는 사용하는 전해질의 특성으로 인하여 저온형($<300^{\circ}C$) 과 고온형($500^{\circ}C<$)으로 구분된 수 있는데, 저온형 연료전지의 경우는 전극반응 특성상 귀금속 촉매가 필요한 데 비해, 고온형 연료전지는 이러한 귀금속 촉매가 필요없다는 점등에서 다양한 장점을 가지게 된다. 즉, 저온형에 비해 다양한 연료가 가능하고, 대형화에 유리함며, 고온 페열을 이용할 수 있는 점 등을 들 수 있다. 용융탄산염형 연료전지(MFCFC)는 이러한 고온형 연료진지의 장점을 배경으로 현재 대규모의 개발이 진행되고 있다. 그러나 여기에 주로 사용되는 Li-K, Li-Na와 같은 용융탄신엽은 고부식성 전해질로서 대부분의 금속이 산화물을 형성하는 것으로 알려져 있다. MCFC의 분리판은 셀간을 전기적으로 이어주는 역할, 가스의 유로제공 및 가스 Sealing의 역할을 담당하는 부분으로서, 분리판의 부식은 이러한 특성의 저하 및 전해질의 소모를 유발시켜 MCFC의 내구성에 커다란 영향 을 미치는 요인으로 생각되고 있다. 이러한 배경으로부터 Uchida 그룹은 MCFC의 분라판 재료 의 부식거동을 계동적으로 검토하였다. 먼저 Fe에 Ni 과 Cr을 첨가한 재료를 산화성가스 분위기하에서 $(Li+K)CO_3$에 대하여 검토한 결과, Ni과 Cr 둘다 20wt%이상 첨가시, 내식성융 가지는 결 과를 보고하였다2) 이 경우 보호피막으로서 NiO 와 $LiCrO_2$가 작용하는데, $LiCrO_2$가 용융탄산염 중에서 보다 안정한 것으로 부터, Cr의 첨가가 내식성에 기여하는 것으로 판단하였다. 다음 단계 로서 Fe/Cr재료에 용-융탄산염 중에서 안정한 산화물을 형성하는 Al의 첨가효과를 검토하였다. Al의 첨가는 더욱 내식성을 향상시키는 것이 발견되었고, 약 4wt%의 첨가로 충분한 내식성을 가지 는 것을 보고 하였다. 그러나 이러한 안정한 산화물에 의한 내식성 향상은 전기진도도의 희생을 바탕으로 한 것으로서, 다읍 단계로서 Ti산화물의 반도체적인 특성을 이용하고자 제 4의 원소로서 Ti첨가를 시도하였다. 그러나 Fe/Cr/AVTi재료가 뛰어난 내식성을 가지는 것은 관찰되었으나, 전도도 향상에는 기여하지 못하는 것이 보고되었다. 현재 MCFC는 실용화를 위한 고성능화의 하나로서 가압하에서의 운전을 시도하고 있다. 이 러한 가압하에서의 운전은 기전력의 향상 및 전극반응의 촉진 등으로 출력의 향상을 가져오나. 현재 문제로 되고 있는 Cathode극인 NiO의 용해/석출 현상을 가속화하는 결과를 초래해, 이에대 한 대책으로서 Li-K보다 NiO의 용해가 적은 Li-Na탄산염으로의 전환이 진행되고 있다. 이러한 배경으로부터 Uchida그룹에서 개발한 FeiCr/AVTi재료와 현재 분리판 재료로 사용증인 SUS 310, S SUS 316재료에 대해. 산화성 분위기의 5기압까지의 가압하에서, Li-K, Li-Na탄산염에 대하여 부 식거동을 검토한 결과, 가압하에서 내식성이 향상되는 것이 발견되었다. 이유로서는 가압하에서 용융탄산엽의 증가된 산화력으로 보다 치밀한 내식성 산화물 피막이 형성되기 때문으로 생각되고 있다. 또한 Li-K, Li-Na탄산염에서의 부식의 정도에는 차이가 거의 없었으나, SUS 316의 경우 탄산염에 젖은 부분에서 내식성 피막이 형성되지 않는 이상부식현상이 관찰되었다. 재료간의 내식성 정도에서는 Fe/Cr/Al/Ti이 가장 내식성이 뛰어났으며, SUS 310 또한 뛰어난 내식성을 보였다.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2003.05a
• /
• pp.303-306
• /
• 2003

To reduce the storage space of spent fuels used at the atomic power plants all over the world, the uranium elements contained in the spent fuels is being extracted and effectively stored. For this, the spent fuel are oxidized and deoxidized. In this study, it is produced conceptual design specification about the spent fuel management technology research and test facilities have been produced. The first considered processes in the facilities is the metal conversion furnace in the dry environment. Since this process is operates at the high temperature range, we have to consider heat-resisting designs for the device. For the heat-resisting designs, we have surveyed and analyzed technical references for material properties. Also, we have determined the temperature distribution condition of the device based on experimental results. We have calculated thermal stress and strain of each devices by the commercial analysis software, I-DEAS. By using the results, we have analyzed design configurations of the point at issue by thermal effects, and suggested alternative design configurations. It is experimented for inspecting confidence rate of heat strain. Based on these results, necessary design specifications for heat-resisting design have been produced.