• 한국생산제조학회지
• /
• 제6권1호
• /
• pp.45-50
• /
• 1997

It is not clearly known how surface defects or inclusions of a medium carbon steel affect a fatigue strength. In this study, we used SM35C specimens with spheroidized cementite structure to eliminate dependence of micro structure of fatigue crack. The investigation was carried out by behavior of crack closure at non-propagation crack and effect of the fatigue limit according to the artificial defects size. Experimental findings are obtained as follows : (1) Fatigue crack initiation point of medium carbon steel with spheroidized cementite structure is at the surface defects. (2) Non-propagating crack length of smooth specimen is equal to the critical size of defect. (3) Considering the opening and closure behavior of fatigue crack, the defect shape results in various crack opening displacement, while it does not affects the fatigue limit level of medium carbon steel with spheroidized cementite structure. (4) The critical length of the non-propagation crack of smooth specimen is the same as critical size of defect in transient area which determines threshold condition in steel with spheroidized cementite structure.

• 한국공작기계학회논문집
• /
• 제17권1호
• /
• pp.50-58
• /
• 2008

The SM45C metallic coupons have been tested under static tensile loading with acoustic emission (AE) as the load-deflection curve mainly. In this study, we used AE to detect the yielding of material and AE techniques was applied to rapidly estimate the mechanical characteristics of a material. First, coupons without an artificial defect were tested at different cross-head speed. For all cases in this analysis, yielding point of SM45C coupons did not appear definitely compared to mild steel, whereas coupons start to generate AE counts upon yielding. So all cases are normalized to know the possibility of accelerated life test of a material. And next, coupons with different from sizes of circular hole defects were tested at the same cross-head speed of 5 mm/min. Results were classified into 3 classes and analyzed by AE amplitude & signal strength as a function of time. Summarizing the specific conclusions, we need to additional research considering plate with width-ratio in order to estimate the fracture mechanism.

• 한국해양공학회지
• /
• 제14권2호
• /
• pp.99-105
• /
• 2000

This paper describes the effect of specimen size on fatigue crack growth rate for the offshore structural high-tensile-strength steel BS4360 and machine structural steel SM45C. The purpose of the present study is to investigate the effect of stress ratio aspect ratio specimen width and specimen thickness of the fatigue crack growth behavior. Compact tension specimens with a LT orientation for BS4360 and SM45C steels were used, All testing was done at constant stress intensity factor range controlled fatigue crack growth condition. The investigation demonstrates that the fatigue crack growth rate is increased with increasing stress ratio and specimen thickness and is decreased with increasing specimen width. The fatigue crack growth rate is unaffected by aspect ratio until a/W=0.50 but is increased by increasing spect ratio from a/W=0.55.

• 한국기계기술학회지
• /
• 제13권2호
• /
• pp.93-100
• /
• 2011

This study deals with the high frequency induction hardening (HF at $850^{\circ}C$, 120kHz & 50kW condition) SM45C steel. (1) The HF specimen, which was tempered at $150^{\circ}C$, did not show any tempering effect. A brittle fracture occurred at rounded area of the tensile specimen. AE (acoustic emission) amplitude distribution showed between 45dB and 60dB. (2) A slip and fracture occurred at the hole area of the HF specimen which was tempered at $300^{\circ}C$. As they pass the yield point, the AE energy is increased intermittently and AE amplitude distribution exists between 70dB and 85dB. In addition, after imposing the maximum tensile load, AE signals showed high amplitude and energy distribution. The AE amplitude showed between 45dB and 70dB. (3) A brittle fracture occurred at HF specimen which was tempered at $450^{\circ}C$ as if it is torn in the direction of $45^{\circ}$ on parallel area over the both sides of the tensile specimen, which lead to several peak appeared in AE energy. It was found that the AE amplitude was relatively low and the AE energy was high.

• 한국정밀공학회지
• /
• 제23권7호
• /
• pp.39-50
• /
• 2006

Laser heat treatment technologies have been used to improve characteristics of wear and to enhance the fatigue resistance for automotive parts. The bjective of this research work is to investigate the influence of the process parameters, such as power of laser and defocused spot position, on the characteristics of laser heat treatment for the case of SM45C medium carbon steel. CW Nd:YAG laser is selected as the heat source. The optical lens with the elliptical profile is designed to obtain a wide heat treatment area with a uniform hardness. From the results of the experiments, it has been shown that the maximum hardness is approximatly 780 Hv when the power and the travel of laser are 1,095 W and 0.6 m/min, respectively. In addition, the hardening width using the elliptical lens was three time larger than that using the defocusing of laser beam.

• 대한안전경영과학회:학술대회논문집
• /
• 대한안전경영과학회 2009년도 추계학술대회
• /
• pp.471-481
• /
• 2009

This study is deal with the high frequency induction hardening (HF at $850^{\circ}C$, 120kHz & 50kW condition) SM45C steel. (1) The HF specimen which was tempered at $150^{\circ}C$, did not appear any tempering effect. A brittle fracture occurred at rounded area of the tensile specimen. AE amplitude distribution showed between 45~60dB. (2) The HF specimen which was tempered at $300^{\circ}C$, slip and fracture occurred at the hole area of the tensile specimen. As it passes the yield point, the AE energy increased intermittently and AE amplitude distribution showed between 70~85dB. In addition, after the maximum tensile load, it showed high amplitude and energy distribution. The AE amplitude showed between 45~70dB. (3) The HF specimen which was tempered at $450^{\circ}C$, a brittle fracture occurred as if it is torn in the direction of $45^{\circ}$ on parallel area over the both sides of the tensile specimen, which led to several peak to be appeared in AE energy. It was found that the AE amplitude was relatively low and the AE energy was high.

• 한국생산제조학회지
• /
• 제21권6호
• /
• pp.932-937
• /
• 2012

In the presented study, SM45C carbon steel parts were joined by friction welding. The welding process was carried out under optimized conditions using statistical approach. The study of SM45C is conducted with various combinations of process parameters. Parameter optimization, microstructure and mechanical property correlation are the major contribution of the study. The welded joints were produced by varying spindle revolution speed, friction pressure, upset pressure and burn-off length. Tension tests were applied to welded parts to obtain the strength of the joints. Fracturs properties were additionally obtained experimentally under fluctuated tensile loads. Microstructures using microphotographs were examined in the weld interface and weld region and heat affected zone and base metal and flash zone of welded parts. Finally, Hardness variations in welding zone and base metal were also obtained. Through these tests, the optimum conditions of parameters for ${\phi}20$ SM45C in friction welding were obtained when the friction spindle revolution was 1,950 rpm, the friction pressures was 30 MPs, upset pressures was 50 MPs.

• 한국산학기술학회논문지
• /
• 제16권3호
• /
• pp.1620-1625
• /
• 2015

본 연구에서는 산업현장에서 각종 기어나, 축, 체인, 롤러, 금형, 자동차강판 등으로 널리 쓰여 지는 기계구조용 탄소강인 SM45C를 실험소재로 사용하였다. 실험에 사용되는 시험편 표면에 표면경화를 수행하기 위하여 #200 ~ #1500의 순서대로 미세연마 후 거친연마의 연마가공을 실시하였으며, 다이오드 레이저의 표면경화 열처리 후에 자기냉각효과를 고려하여 $100{\times}50{\times}10$의 판재로 시험편을 제작하여 실험하였다. 소재 표면에 다이오드 레이저를 이용하여 국소부위에 표면경화 열처리를 수행하였다. 이때 다이오드 레이저의 출력과 이송속도를 공정조건으로 하여, 미세경도시험, 미세조직시험, 전자 주사 현미경(SEM), 입열량을 분석하였다. 분석 후에는 실험소재의 기계적 특성을 비교하여, 타 표면 경화법에 비해 다이오드 레이저를 이용하였을 때의 표면경화 열처리 신뢰성과 우수함 그리고 최적의 공정조건을 도출하였다. 열처리 후 경화부는 판상 마르텐사이트로 경화 되었으며. 경도값은 Hv729.5로 열처리 후 약 2.3배 이상 표면경도가 향상되있는 것을 확인하였다.

• 한국정밀공학회지
• /
• 제5권3호
• /
• pp.71-80
• /
• 1988

This paper dealt with experimentally the effect of $N_2$ and $H_2$ gas mixtures ratio in the fatigue characteristics of SM45C on Ion-nitrided. The specimen were treated water cooling after Ion-nitriding at $500^{\circ}C$ and 5 torr. in 80% $N_2$and 50% $N_2$gas mixtures ratio in the atmosphere for 3 hrs. The hardness distribution and the depth of nitriding layer shows more increase in 80% $N_2$gas mixture ratio than 50% $N_2$. Ion-nitrided specim- en for 80% $N_2$gas mixture ratio show more increase infatigue strenght in the $>1.5{\times}10^5$ cycles region than 50% $N_2$. In the $<1.5{\times}10^5$cycles region, fatigue failure is due to cracking of the brittle nitrided case, and the propergation of the surface cracks into the core. But in the $>1.5{\times}10^5$cycles region, it is found that cracks propagate from the non-metallic inclusions in the subsurface.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2004년도 추계학술발표대회 개요집
• /
• pp.153-155
• /
• 2004

Vibration occurs due to the wind and vehicles, etc., in the field welded joints of steel bridges. However, the effect of vibration on the fatigue strength of field welded joints in steel bridge are not yet clearly understood. In this paper, the effect of vibration on the fatigue strength of welded joints was elucidated in order to improve reliability in the field welded joints of steel bridge. The base material used in this investigation was SM 490A steel of weldable grade. Flux Cored Arc Welding(FCAW) process was used to fabricate the doubte 'V' butt joints. Welding was performed on the steel under the mechanical vibration of given frequency. The applied frequency was resonant frequency. Also, weldments formed under no vibration were fabricated. Fatigue tests were conducted using a servo hydraulic controlled 50ton1 capacity UTM with a frequency of 5Hz under constant amplitude loading.