• Journal of Powder Materials
• /
• v.27 no.2
• /
• pp.103-110
• /
• 2020

Aluminum (Al) - based powders have attracted attention as key materials for 3D printing because of their excellent specific mechanical strength, formability, and durability. Although many studies on the fabrication of 3D-printed Al-based alloys have been reported, the influence of the size of raw powder materials on the bulk samples processed by selective laser melting (SLM) has not been fully investigated. In this study, AlSi10Mg powders of 65 ㎛ in average particle size, prepared by a gas atomizing process, are additively manufactured by using an SLM process. AlSi10Mg powders of 45 ㎛ average size are also fabricated into bulk samples in order to compare their properties. The processing parameters of laser power and scan speed are optimized to achieve densified AlSi10Mg alloys. The Vickers hardness value of the bulk sample prepared from 45 ㎛-sized powders is somewhat higher than that of the 65 ㎛m-sized powder. Such differences in hardness are analyzed because the reduction in melt pool size stems from the rapid melting and solidification of small powders, compared to those of coarse powders, during the SLM process. These results show that the size of the powder should be considered in order to achieve optimization of the SLM process.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2017.05a
• /
• pp.872-876
• /
• 2017

Laser Based 3D Printing is an recently advance manufacturing technology for making complex shape comopnent such as automobile and aerospace. So in this article, stainless steel 316L was manufactured by Selective Laser Melting (SLM) and Laser Melting Deposition (LMD) method. SLM is an additive manufacturing process that allow for the manufacture of small and complex component by laser melting and solidification of powder in bed using a high intensity laser beam. The results showed that the laser scanning speed and laser power affects the defect, microstructure and the hardness of the components.

• Design & Manufacturing
• /
• v.16 no.3
• /
• pp.58-65
• /
• 2022

Micro-fluidic chip has been fabricated by lithography process on silicon or glass wafer, casting using PDMS, injection molding of thermoplastics or 3D printing, etc. Among these processes, 3D printing can fabricate micro-fluidic chip directly from the design without master or template for fluidic channel fabricated previously. Due to this direct printing, 3D printing provides very fast and economical method for prototyping micro-fluidic chip comparing to conventional fabrication process such as lithography, PDMS casting or injection molding. Although 3D printing is now used more extensively due to this fast and cheap process done automatically by single printing machine, there are some issues on accuracy or surface characteristics, etc. The accuracy of the shape and size of the micro-channel is limited by the resolution of the printing and printing direction or layering direction in case of SLM type of 3D printing using UV curable resin. In this study, the printing direction and thickness of each printing layer are investigated to see the effect on the size, shape and surface of the micro-channel. A set of micro-channels with different size was designed and arrayed orthogonal. Micro-fluidic chips are 3D printed in different directions to the micro-channel, orthogonal, parallel, or skewed. The shape of the cross-section of the micro-channel and the surface of the micro-channel are photographed using optical microscopy. From a series of experiments, an optimal printing direction and process conditions are investigated for 3D printing of micro-fluidic chip.

• Journal of Technologic Dentistry
• /
• v.45 no.1
• /
• pp.1-7
• /
• 2023

Purpose: To evaluate the marginal and internal fit of metal coping fabricated by a metal three-dimensional (3D) printer that uses selective laser melting (SLM). Methods: An extraoral scanner was used to scan a die of the prepared maxillary right first molar, and the coping was designed using computer-aided design software and saved as an stereo lithography (STL) file. Ten specimens were printed with an SLM-type metal 3D printer (SLM group), and 10 more specimens were fabricated by casting the castable patterns output generated by a digital light processing-type resin 3D printer (casting the 3D printed resin patterns [CRP] group). The fit was measured using the silicon replica technique, and 8 points (A to H) were set per specimen to measure the marginal (points A, H) and internal (points B~G) gaps. The differences among the groups were compared using the Mann-Whitney U-test (α=0.05). Results: The mean of marginal fit in the SLM group was 69.67±18.04 ㎛, while in the CRP group was 117.10±41.95 ㎛. The internal fit of the SLM group was 95.18±41.20 ㎛, and that of the CRP group was 86.35±32 ㎛. As a result of statistical analysis, there was a significant difference in marginal fit between the SLM and CRP groups (p<0.05); however, there was no significant difference in internal fit between the SLM group and the CRP group (p>0.05). Conclusion: The marginal and internal fit of SLM is within the clinically acceptable range, and it seems to be applicable in terms of fit.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.21 no.7
• /
• pp.270-276
• /
• 2020

3D printing is an additive manufacturing technology that can produce complex shapes in a single process for a range of materials, such as polymers, ceramics, and metals. Recent 3D printing technology has developed to a level that enables the mass-production through an improvement of the printing speed and the continuous development of applicable materials. In this study, 3D printing technology using a laser was applied to manufacture a heat exchanger for an air compressor in a railway vehicle. First, the optimal design of the heat exchanger was carried out by focusing on weight reduction and compactness as a shape suitable for 3D printing. Based on the design derived, heat exchanger prototypes were made of AlSi10Mg alloy material by applying the SLM technique. Moreover, the manufactured prototypes were attached to an existing air compressor, and the heat exchange performance of the compressed air was tested. The test results of the 3D printed prototypes showed a heat exchange performance of approximately 80% and 85% at low and high-pressure, respectively, compared to the existing heat exchanger. From the 𝓔-NTU method results with an external cooling air condition similar to that of the existing heat exchanger, the calculated heat transfer amount of 3D printed parts showed similar performance compared to the existing heat exchanger. As a result, the 3D printed heat exchanger is lightweight with good performance.

• Journal of Powder Materials
• /
• v.26 no.2
• /
• pp.138-145
• /
• 2019

In this study, Al-Si-Mg alloys are additively manufactured using a selective laser melting (SLM) process from AlSi10Mg powders prepared from a gas-atomization process. The processing parameters such as laser scan speed and laser power are investigated for 3D printing of Al-Si-Mg alloys. The laser scan speeds vary from 100 to 2000 mm/s at the laser power of 180 and 270 W, respectively, to achieve optimized densification of the Al-Si-Mg alloy. It is observed that the relative density of the Al-Si-Mg alloy reaches a peak value of 99% at 1600 mm/s for 180 W and at 2000 mm/s for 270W. The surface morphologies of the both Al-Si-Mg alloy samples at these conditions show significantly reduced porosities compared to those of other samples. The increase in hardness of as-built Al-Si-Mg alloy with increasing scan speed and laser power is analyzed due to high relative density. Furthermore, it was found that cooling conditions after the heat-treatment for homogenization results in the change of dispersion status of Si phases in the Al-Si matrix but also affects tensile behaviors of Al-Si-Mg alloys. These results indicate that combination between SLM processing parameters and post-heat treatment should be considered a key factor to achieve optimized Al-Si alloy performance.

• Journal of Powder Materials
• /
• v.28 no.2
• /
• pp.134-142
• /
• 2021

In this study, AlSi10Mg powders with average diameters of 44 ㎛ are additively manufactured into bulk samples using a selective laser melting (SLM) process. Post-heat treatment to reduce residual stress in the as-synthesized sample is performed at different temperatures. From the results of a tensile test, as the heat-treatment temperature increases from 270 to 320℃, strength decreases while elongation significantly increases up to 13% at 320℃. The microstructures and tensile properties of the two heat-treated samples at 290 and 320℃, respectively, are characterized and compared to those of the as-synthesized samples. Interestingly, the Si-rich phases that network in the as-synthesized state are discontinuously separated, and the size of the particle-shaped Si phases becomes large and spherical as the heat-treatment temperature increases. Due to these morphological changes of Si-rich phases, the reduction in tensile strengths and increase in elongations, respectively, can be obtained by the post-heat treatment process. These results provide fundamental information for the practical applications of AlSi10Mg parts fabricated by SLM.

• The Journal of the Korea Contents Association
• /
• v.21 no.3
• /
• pp.602-608
• /
• 2021

For the comparison of bond strength between the Co-Cr alloy and ceramic, which are clinically used, test samples made with a traditional casting method as a control group), and Milling and SLM(3d printing group) samples were made as an experimental group. The metal-ceramic bond strength was measured with a universal testing machine. For the measurement, a three-point bending test was conducted. After the bond strength was measured, metal-ceramic interface was observed. According to the test result, casting group had 53.59 MPa, milling group had 45.90 MPa, and 3d printing group had 58.34 MPa. There was no statistical significance. With regard to failure pattern, most of the samples in two groups, showed mixed failure. This study showed a clinically applicable value when measuring the bond strength of alloy-ceramic material with an alloy produced by 3D printing.

• Journal of Powder Materials
• /
• v.29 no.2
• /
• pp.132-151
• /
• 2022

The CoCrFeMnNi high-entropy alloy (HEA), which is the most widely known HEA with a single face-centered cubic structure, has attracted significant academic attention over the past decade owing to its outstanding multifunctional performance. Recent studies have suggested that CoCrFeMnNi-type HEAs exhibit excellent printability for selective laser melting (SLM) under a wide range of process conditions. Moreover, it has been suggested that SLM can not only provide great topological freedom of design but also exhibit excellent mechanical properties by overcoming the strength-ductility trade-off via producing a hierarchical heterogeneous microstructure. In this regard, the SLM-processed CoCrFeMnNi HEA has been extensively studied to comprehensively understand the mechanisms of microstructural evolution and resulting changes in mechanical properties. In this review, recent studies on CoCrFeMnNi-type HEAs produced using SLM are discussed with respect to process-induced microstructural evolution and the relationship between hierarchical heterogeneous microstructure and mechanical properties.

• Journal of Technologic Dentistry
• /
• v.40 no.4
• /
• pp.231-237
• /
• 2018

Purpose: The development of the dental technology industry has digitized the dental process. Definition of Digitalization of Dental Implantation Digitalization is the process of model making and prosthodontic processing using 3D CAD and CAM. Currently, it is becoming popular due to the spread of various devices. However, precision evaluation at this stage is an important factor in precision-based dental procedures. Therefore, in this study, we want to analyze the precision of the processed body made with digital dental machine. Methods: The accuracy of digital dental pore devices was evaluated. Specimens were fabricated with 5 types of 3D printers. The external shape was measured with the prepared specimen. The surface roughness was measured. Results: As a result, precision was excellent in order of EP2 specimen, EP1 specimen, and EA2 specimen. The precision of EP3 specimen and EA1 specimen is not excellent. And the precision of the specimen processed with polymer 3D printer is excellent. The accuracy of LCPS type polymer 3D printers is considered to be excellent. Conclusion : 1. Observation of the shape The 3D printer for LCPS system and the 3D printer for SLM $40{\mu}m$ system were found to be precisely processed. 2. Surface roughness results The LCPS system polymer 3D printer has been shown to have a precise surface.