• 한국분말재료학회지
• /
• 제29권1호
• /
• pp.47-55
• /
• 2022

Tungsten carbide is widely used in carbide tools. However, its production process generates a significant number of end-of-life products and by-products. Therefore, it is necessary to develop efficient recycling methods and investigate the remanufacturing of tungsten carbide using recycled materials. Herein, we have recovered 99.9% of the tungsten in cemented carbide hard scrap as tungsten oxide via an alkali leaching process. Subsequently, using the recovered tungsten oxide as a starting material, tungsten carbide has been produced by employing a self-propagating high-temperature synthesis (SHS) method. SHS is advantageous as it reduces the reaction time and is energy-efficient. Tungsten carbide with a carbon content of 6.18 wt % and a particle size of 116 nm has been successfully synthesized by optimizing the SHS process parameters, pulverization, and mixing. In this study, a series of processes for the high-efficiency recycling and quality improvement of tungsten-based materials have been developed.

• 한국결정성장학회지
• /
• 제8권4호
• /
• pp.573-580
• /
• 1998

MgO와 Al 분말을 자전고온연소합성법으로 $MgAl_2O_4$ 스피넬 상을 합성하였다. MgO 와 Al을 테르밋 반응으로 생성하였으며, 가열반응생성으로 $800^{\circ}C$ 예열온도에서 반응시켰다. DTA/TG, 합성생성물, 최고온도 공정조건에 대해 연구하였고, MgO와 Al은 MgO+2Al+ 3/$2O_3$ $\rightarrow$ $MgAl_2O_4$ 로 합성되었다. 미반응된 재료로부터 MgAl2O4 스피넬의 활성화 에너지는 -264.8kcal/mol의 발생열량과 5634K의 최고 반응온도로 계산되었다. 테르밋 반응후의 시험편의 체적느 6% 증가하였다.

• 한국결정성장학회지
• /
• 제15권6호
• /
• pp.269-275
• /
• 2005

Ni/Ni-aluminide//Ti/Ti-aluminide 경사기능 층상 복합재료를 박막 hot press법을 이용하여 제작하였다. NiAl과 $TiAl_3$ 금속간화합물 층이 자전고온합성반응을 통해 비교적 두껍게 형성되었고, 얇고 연속적인 $Ni_3Al$과 TiAl 층이 고상 확산을 통해 형성되었다. 파괴저항은 하중 방향이 crack arrester인 경우가 금속 층이 균열의 성장을 방해하기 때문에 crack divider 방향인 경우보다 높다. $Ni_3Al$과 NiAl 금속간화합물 층은 각각 벽개파괴와 입계파괴 거동을 보였고, $TiAl_3$층의 파괴 형태는 입내벽개파괴이었다. Ni/Ni-aluminide 층에서 관찰되는 기공과 금속 층과 금속간화합물 층의 미결합 부위가 낮은 파괴저항의 원인으로 판단된다. Acoustic emission (AE) 원파형 해석을 통해 제작된 복합재료의 파괴특성을 고찰하였다.